• Journal of Korean Society of Steel Construction
• /
• v.16 no.3 s.70
• /
• pp.387-396
• /
• 2004

In this paper, stress analysis anda 3-point bending fatigue test were conducted on the full-scale specimen to investigate the effects of misalignment at the U-rib welded joint due to misfitting in the steel deck bridge. In addition, the researchers investigated the direction and starting point of fatigue cracks by SEM (Scanning Electron Microscope) and beach mark. The results of the stress analysis show that maximum stress occurred at the bottom corner of the U-rib, and that the stress was large when the magnitude of the misalignment was large. On the other hand, the results of the static loading test of the full-scale specimen show that stress was large at the bottom corner of the U-rib. In addition, fatigue life was short when the misalignment was large and fatigue life was short when the misalignment was large and fatigue life was short when the misalignment was large and fatigue life was large when the misalignment was small, as indicated by the results of both the static loading test and the fatigue test. From the observation of the failure surface, fatigue cracks began manifesting at the root of the base metal and proceeded to the bead surface (weld toe).

• Journal of Korean Society of Steel Construction
• /
• v.11 no.4 s.41
• /
• pp.339-350
• /
• 1999

In this study, blowholes, a kind of solid defects, were intentionally introduced in transverse butt-welded joints which are widely used for the connection of main members in steel structures to evaluate the fatigue characteristics of these joints with blowholes according to the difference of the size and shape of blowholes, and a series of tests were performed. Static test results proved that the static strength of these joints with blowholes was not affected by their size and shape. From the fatigue test results on these joints with blowholes, the size and shape of blowholes inside the weld metals were strongly affected in fatigue strength, and we suggested the relationship between fatigue strength and their size and shape quantitatively. Also, Using the relationship of fatigue crack growth rate and stress intensity factor range, the fatigue life of transverse butt-welded joints with blowholes can be estimated properly.

• Journal of Welding and Joining
• /
• v.17 no.5
• /
• pp.47-54
• /
• 1999

It is well known that solidification cracking often occurs in welds of root pass for one-side welding under the conditions of high welding currents and speeds. In this study, the solidification in 590MPa class steel for pressure vessels SPPV490 was investigated by using flux-cored arc welding(FCAW) with 4 types of welding wires and welding conditions of 200∼280A and 2.8∼ 4.2mm/sec. In order to compared the result of cracking in SPPV490, 0.2%C steel for welded structure of SWS400 and 0.45%C steel for machine structural SM45C were also used as base metals. As the results, all the cracks formed in some welding conditions were observed near the center of weld bead. The solidification cracks were generally initiated near the upper surface of bead and propagated toward the inner part. The solidification cracking generally increased with welding current and welding speed in the same base metal and welding material. In cracking susceptibility, SPPV490 showed higher cracking susceptibility than SWS400 in all welding conditions and welding materials. It was considered that cracking susceptibility could not be evaluated with the hardness of weld metals. The cracking ratio increased with decreasing of a/b(a and b; the width of the upper surface and the back surface of the bead) as shape factor of bead. The cracking tendency with shape factor of bead was extended under the condition of higher welding currents.

• Journal of the Korean Institute of Gas
• /
• v.16 no.3
• /
• pp.29-34
• /
• 2012

Investigating safer ways to design and use to prevent a loss of life and property by failure of the structures are necessary and assessing total fatigue life with initiation and propagation of fatigue crack accurately through fatigue analysis is very important. The object of this study is to examine the initial life and propagation life when the fatigue crack is introduced from the root which is likely to appear in LOP(Lack of Penetration) cruciform fillet welded structure including bridges, ships and gas storage facilities which are impossible to be fully penetrated and to measure the rate of fatigue life until the final cleavage failure. As the result, each rate of fatigue life for fatigue failure is somewhat different in the range of 5% according to the thickness of material, however, the overall rate of initial life is in the range of 34~39% and propagation life showed the range of 61~66%.

• Journal of Korean Society of Steel Construction
• /
• v.10 no.3 s.36
• /
• pp.423-435
• /
• 1998

In this paper fatigue strength reduction of butt weld with penetration defect, which can be seen frequently in the steel bridge, was assessed quantitatively. S-N curves were derived and investigated through the constant amplitude fatigue test of fully or partially penetrated welded specimen made of SWS490 steel. The fracture mechanical method was applied in order to calculate the remaining fatigue life of the partially penetrated butt welds. The fatigue limit of the fully penetrated butt welds was higher than that of category A in AASHTO's fatigue design curves, and the slope of S-N curves with 5.57 was stiffer than that of other result for welded part generally accepted as 3. The fatigue strength of the partially Penetrated butt weld was strongly influenced by the size of lack of penetration, D. It decreased drastically with increasing D from 3.9 to 14.7mm. Fracture behaviour of the partially penetrated butt weld is able to be explained obviously from the beach mark test that a semi-elliptical surface crack with small a/c ratio initiates at a internal weld root and propagates through the weld metal. To estimate the fatigue life of the partially penetrated butt weld with fracture mechanics, stress intensity factors K of 3-dimensional semi-elliptical crack were calculated by appling finite elements method and fracture mechanics parameters such as C and m were derived through the fatigue test of CT-specimen. As a result, the fatigue lives obtained by using the fracture mechanical method agreed well with the experimental results. The results were applied to Sung-Su bridge collapsed due to penetration defects in butt weld of vertical member.

• Journal of the Korean Society for Nondestructive Testing
• /
• v.22 no.4
• /
• pp.422-429
• /
• 2002

The identification of ultrasonic flaw signals is a truly difficult task in the angle beam testing of welded joints due to non-relevant signals from the geometric reflectors such as weld roots and counter bores. This paper describes a new approach called "technique for identification of flaw signal using deconvolution(TIFD)" in order to identify the flaw signals in such a problematic situation. The concept of similarity function based on the deconvolution is introduced in the proposed approach. The "reference" signals from both flaws and geometric reflectors and test signals are acquired and normalized. The similarity functions are obtained by deconvolution of test signals with reference signals. The flaw signals could be identified by the patterns of similarity function. The initiative results show great potential of TIFD to distinguish notch comer signals from the geometric reflections.

• Journal of the Korean Institute of Gas
• /
• v.17 no.1
• /
• pp.19-25
• /
• 2013

The joining methods of steel structures of gas facilities, bridges, ships etc. by welding are composed mostly of T-type or cruciform fillet welding and full penetration or partial penetration according to the uses and the shape of the structures. In this study, it was examined the characteristics of fatigue crack according to penetration depth in relation to material thickness in the cruciform fillet welded joints. From the results, it was investigated the safe design stresses within the range of infinite life. When the LOP length is long the range of infinite life is small with root failure and when the LOP length is short the range of infinite life is large with teo failure. For the specimen of material thickness, 20mm welded by 3 pass compared with 10mm, 15mm welded by 2 pass, the fatigue strength and the range of infinite life was more improved by increasing of notch toughness from formation of micro-ferrite acicular structure.

• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.41 no.3
• /
• pp.225-232
• /
• 2017

Several maintenance issues related to cavitation erosion and fatigue cracks in the water turbine subcomponents of pumped-storage plants, such as a runner and a draft tube, have been reported in the past. Generally, the pumped-storage plants provide ancillary services, such as black-start and system stabilization. The ancillary services are responsible for cyclic low opening operation of the guide vanes. It has been empirically established that this low opening operation further damages the water turbine subcomponents. In this study, the acceleration effect of the low opening operation on the cavitation erosion and fatigue of the water turbine is quantitatively assessed through finite element flow analysis, finite element stress analysis, and fatigue analysis. As a result of the assessment, it is identified that the cavitation potential increases and the turbine efficiency decreases with a decrease in the opening of the guide vane. Also, the low opening operation has an insignificant effect on the fatigue even though it increases the maximum stress values at the runner blade roots.