• Journal of the korean academy of Pediatric Dentistry
• /
• v.29 no.4
• /
• pp.509-518
• /
• 2002

The purpose of this study was to evaluate the bonding of compomer to deciduous dentin which is known to have been developed to improve the weak properties of glass ionomer cement and composite resin. 120 sound primary molars were used for the shear bond strength test and another 24 for the scanning electron microscopic evaluation. Each material was ailed into polyethylene mold attached to exposed dentinal surface($3{\times}4mm$ in diameter) of sample blocks. Shearbond strength was measured using Universal testing machine and data were analyzed statistically with Oneway-ANOVA and Scheffe test. Scanning electron microscopic observation was performed in order to evaluate the pattern of distribution and penetration of resin tags and hybrid layer. Compomer groups(II-V) showed significantly higher bond strength values than glass ionomer group(I)(p<.05). Etching-compomer groups(III, V) showed the significantly higher bond strength than non-etching compomer groups(II, IV)(p<.05), but slightly lower values than composite resin group(VI) with no statistically significant difference(p>.05). No significantly different bond strength was found between compomer groups of different bonding system(p>.05). Scanning electron micrographs showed more irregular distribution of short and thin resin tags in non-etching compomer groups(II, IV) whereas the more regular and intimate distribution of long and thick tags in etching compomer groups(III, V) and composite resin group(VI). The evaluation of hybrid layer also showed more regular formation of thicker layer in etching compomer groups(III, V). Based on the results of present study, the use of compomer as an esthetic restorative material for primary molars might be justified.

• Journal of the korean academy of Pediatric Dentistry
• /
• v.33 no.4
• /
• pp.661-672
• /
• 2006

This study was performed to compare the shear bond strength of AQ Bond $Plus^{TM}$ with AQ $Bond^{TM}$ and Single $Bond^{TM}$. Also by observing the fractured interface under scanning electro-microscope, the fracture pattern and the quality of hybrid layer were analyzed. The possibility of clinical application of all-in-one system which has an advantage to reduce chair time for children with difficult behavior pattern was evaluated, The results obtained are as follows ; 1. There was no significant difference between AQ $Bond^{TM}$ and AQ Bond $Plus^{TM}$ in shear bond strength and Single Bond showed the highest bond strength with statistical significant difference (p<0.05). 2. Adhesive fracture pattern was mainly observed in both enamel/dentin in AQ $Bond^{TM}$ and AQ Bond $Plus^{TM}$ group while Single Bond group showed equal numbers for cohesive and adhesive pattern. 3. Under scanning electro-microscope, resin tags observed in AQ $Bond^{TM}$ and AQ Bond $Plus^{TM}$ were very weak and tangled while strong and thick tags were shown with many lateral branches in Single Bond. Careful case selection and accurate clinical application is recommended when using AQ $Bond^{TM}$ and AQ Bond $Plus^{TM}$considering the result showing its weaker strength than Single $Bond^{TM}$.

• Journal of the korean academy of Pediatric Dentistry
• /
• v.28 no.4
• /
• pp.566-574
• /
• 2001

For decades it has been a clinically accepted requirement, in case of salivary contamination, to re-etch conditioned enamel and dentin to proceed with the adhesive technique. Only a few reports have been so far dealing with the potential of one-bottle adhesive system to bond even when applied after salivary contamination and without re-etching. The purpose of this study was to evaluate the influence of the salivary contamination on the shear bond strength of dentin. The results were as follows: 1. In group II, in which saliva contamination and washing occurred before applying of Prime & Bond NT showed high shear bond strength as in control group. In Group III and IV, in which the cured adhesive was contaminated with saliva, showed significantly lower mean bond strength, 2. Relating long resin tags of $70\sim120{\mu}m$ were observed in samples of all groups under SEM. We could observed hybrid layer, resin tag and many lateral branches in every group. And there were no differences between groups.