• The Journal of Korean Academy of Prosthodontics
• /
• v.27 no.2
• /
• pp.155-172
• /
• 1989

The purpose of this study is to measure the bonding strength at the enamel and dentin of extracted bovine incisors when they are irradiated by W Nd: YAG, EoQ Nd: YAG, and CW $CO_2$ laser, etched and then attached by composite resin. The laser-irradiated surface, the etched surface after the laser-irradiation and the interface of the treated surface and resin are observed by using scanning electron microscope. The NP Nd:YAG laser is used at the peam power of 207 KW. The EOQ Nd: YAG laser is used at the peak power of 1.15Mk. The CW $CO_2$ laser is used at the energy output of 5W and 10W in enamel; in dentin, at the energy output of 2W. The obtained results were as follows: 1. The shear bond strength of enamel decreased in the following order: EOQ Nd:YAG laser group, NP Nd:YAG laser group, CW $CO_2$ laser groups, unlased group. The unlased group showed a significant difference from EOQ Nd:YAG laser group (P<0.01), NP Nd:YAG laser group (P<0.05), but no significant difference from CW $CO_2$ laser group (P>0.05). 2. The shear bond strength of dentin decreased in the following order: CW $CO_2$ laser group, NP Nd:YAG laser group, unlased group, EOQ Nd:YAG laser group. The unlased group showed a significant difference from CW $CO_2$ laser group (P<0.01), but no significant difference from Nd:YAG laser groups (P>0.05). 3. The scanning electron microscope of enamel revealed irregular microcrack and pore at the surface in the NP Nd:YAG laser group and CW $CO_2$ laser group, but the crackless flat surface in the EOQ Nd:YAG laser group. 4. The scanning electron microscope of dentin revealed obstruction of in most of dentinal tubule and decrease of diameter. 5. The scanning electron microscope of the interface of resin and enamel revealed prominent penetration of resin tag in the EOQ Nd:YAG laser group.

• Restorative Dentistry and Endodontics
• /
• v.33 no.1
• /
• pp.1-8
• /
• 2008

The purpose of this study was to evaluate the effect of a new resin monomer, filler size and polishing technique on the surface roughness of composite resin restorations using confocal laser scanning microscopy. By adding new methoxylated Bis-GMA (Bis-M-GMA, 2,2-bis[4-(2-methoxy-3-methacryloyloxy propoxy) phenyl] propane) having low viscosity, the content of TEGDMA might be decreased. Three experimental composite resins were made: EX1 (Bis-M-GMA/TEGDMA = 95/5 wt%, 40 nm nanofillers); EX2 (Bis-M-GMA/TEGDMA = 95/5 wt%, 20 nm nanofillers); EX3 (Bis-GMA/TEGDMA = 70/30 wt%, 40 nm nanofillers). Filtek Z250 was used as a reference. Nine specimens (6 mm in diameter and 2 mm in thickness) for each experimental composite resin and Filtek Z250 were fabricated in a teflon mold and assigned to three groups. In Mylar strip group, specimens were left undisturbed. In Sof-lex group, specimens were ground with #1000 SiC paper and polished with Sof-lex discs. In DiaPolisher group, specimens were ground with #1000 SiC paper and polished with DiaPolisher polishing points. The Ra (Average roughness), Rq (Root mean square roughness), Rv (Valley roughness), Rp (Peak roughness), Rc (2D roughness) and Sc (3D roughness) values were determined using confocal laser scanning microscopy. The data were statistically analyzed by Two-way ANOVA and Tukey multiple comparisons test (p = 0.05). The type of composite resin and polishing technique significantly affected the surface roughness of the composite resin restorations (p < 0.001). EX3 showed the smoothest surface compared to the other composite resins (p < 0.05). Mylar strip resulted in smoother surface than other polishing techniques (p < 0.05). Bis-M-GMA. a new resin monomer having low viscosity, might reduce the amount of diluent, but showed adverse effect on the surface roughness of composite resin restorations.

• Journal of the korean academy of Pediatric Dentistry
• /
• v.31 no.4
• /
• pp.685-695
• /
• 2004

The aim of this study was to evaluate the resistance to degradation and to compare the wear resistance characteristics of four composite resins in an alkaline solution. The resistance to degradation was evaluated on the basis of mass loss(%), degradation depth(${\mu}m$), Si loss(ppm) and wear depth. The brands studied were Heliomolar flow, Filtek supreme, Point4, Tetric flow. The results were as follows: 1. The sequence of the mass loss was in descending order by Heliomolar flow, Filtek supreme, Point4, Tetric flow. There was significant differences among the materials except Heliomolar flow and Filtek supreme. 2. The sequence of the degree of degradation layer depth was in descending order by Filtek supreme, Heliomolar flow, Tetric flow, Point4. There were significant differences among the materials except Heliomolar flow and Tetric flow. 3. The sequence of Si loss was in descending order by Filtek supreme, Heliomolar flow, Point4, Tetric flow. There were significant differences among the materials except Point 4 and Tetric flow. 4. The sequence of maximum wear depth was in descending order by Heliomolar flow, Point4, Fillet supreme, Tetric flow and there was increasing wear depth on soaking in 0.1N NaOH solution. 5. When observed with SEM, destruction of bonding between matrix and filler was observed and when observed with CLSM, the depth of degradation layer of specimen surface was observed. There results indicate that wear and hydrolytic degradation could be considered to be evaluation factors of composite resins.