• Journal of the Korea Convergence Society
• /
• v.7 no.6
• /
• pp.193-198
• /
• 2016

The texture of electrodeposits varies with deposition conditions. Texture of electrodeposits is also related to microstructure, surface morphology and mechanical properties. When the electrodeposits annealed, the recrystallization texture may be different from the original deposition texture. The surface morphology, the microstructure and the initial and recrystallization textures of copper electrodeposits vary with deposition conditions. The texture, microstructure, surface morphology and mechanical properties of electrodeposits are known to vary with electrolysis conditions, such as bath composition, over potential, pH, current density, bath temperature, etc. The (111) and (110) textures of copper electrodeposits can be obtained from copper sulfate bath. In this study, copper electrodeposits with (111) and (110) textures are obtained from a copper sulfate bath, and the change from (111) to (110) textures of copper electrodeposits can be explained.

• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.39 no.12
• /
• pp.1297-1303
• /
• 2015

The internal chromium plating of a long-axis tube is widely used in military and industrial application, with the thick hard plating formed using a mixed solution of Chromium acid and catalytic $H_2SO_4$. A large-caliber gun can endure a high explosive force as a result of the increased stiffness and wear resistance provided by this internal hard chromium surface. The internal chromium layer of a tube is prone to exfoliation caused by the high kinetic energy of the projectile and high pressure of the explosion. Therefore, we reviewed the plating process. Chromium plating comprises many steps, including the removal of Grease, water cleaning, electrolytic abrasion, etching, plating, water cleaning, and hydrogen brittleness removal. The exfoliated chromium plating layer is affected by the adhesion property of the plating. In particular, the Fe concentration of the electrolyte affects the adhesion property. The optimum Fe concentration for effectively suppressing the exfoliation of the plating layer was established by using a scanning electron microscope to determine the surface roughness, and the effectiveness was proved in an adhesion test, etc.

• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 2016.11a
• /
• pp.142-142
• /
• 2016

무전해 니켈 도금은 산업기계 부품, 자동차 부품, 항공 및 전자 통신 부품 등에 이르기까지 산업 전반에서 폭넓게 사용되고 있다. 이는 무전해 니켈 도금 층이 우수한 균일성, 내마멸성, 내식성 등을 지녀 관련 연구가 지속적으로 활발하게 진행되어 왔기 때문이다. 특히, 최근에 이르기까지 도금 층이 얇고, 우수한 내마멸성 및 낮은 마찰계수를 활용한 무전해 니켈 도금은 산업현장에서 기계 부품들의 수명을 연장시키고, 그 성능을 개선시키는데 용이하게 적용되고 있다. 본 연구에서는 이와 같이 무전해 니켈 도금 층의 우수한 특성을 활용하여 해수 부식과 캐비테이션-침식 복합 환경 하에 놓여 있는 금속 재료의 손상을 방지하고자 하였다. 이는 선박의 경우 최근 고속화, 대형화 추세에 따라 부품의 내구성 향상과 연비 효율성이 더욱 강조되고 있으며, 그에 따라 해수 속에서 고속 회전으로 더욱 가혹해진 캐비테이션 침식-부식 환경하에 놓인 선박의 프로펠러, 펌프 임펠러 및 케이싱 등의 금속재료 자체를 보호할 수 있는 고성능 재료의 개발이 요구되고 있기 때문이다. 또한 해양환경 하에서 무전해 니켈 도금 층에 대한 캐비테이션 침식 손상에 대한 연구는 미비한 실정이다. 본 연구에서는 회주철 표면에 무전해 니켈 도금을 실시하여 캐비테이션 침식 손상을 방지하고자 하였다. 무전해 니켈 도금을 실시하기 전 도금 층을 균일하게 형성하기 위해 샌드 페이퍼 #1200까지 연마 후 알칼리 탈지 실시하고, 산세(10% HCl)와 수세를 순차적으로 실시하여 전처리하였다. 이후 무전해 니켈 도금은 황산니켈, 차아인산나트륨, 구연산, 아세트산나트륨 그리고 미량의 질산납으로 구성된 도금욕에서 pH 4-6, $80-90^{\circ}C$의 조건으로 실시하였으며, pH는 NaOH를 이용하여 조정하였다. 이렇게 제작된 무전해 니켈 도금 층에 대하여 천연 해수 속에서 ASTM-G32 규정에 의거한 캐비테이션 침식실험을 통해 내구성을 평가하였다. 캐비테이션 실험 후에는 무게 감소량, 표면 손상깊이, 침식 손상 경향 등을 종합적으로 분석 비교하였다. 그 결과, 회주철에 대하여 무전해 니켈 도금을 실시할 경우 현저한 캐비테이션-침식 저항성 향상이 관찰되었다.

• Proceedings of the Materials Research Society of Korea Conference
• /
• 2007.11a
• /
• pp.34.2-34.2
• /
• 2007

• Applied Chemistry for Engineering
• /
• v.17 no.2
• /
• pp.150-157
• /
• 2006

The alternate plating method was suggested by a tin-cobalt alloy plating process which has excellent mechanical characteristics and also favorable to environment. Tin-cobalt alloy plating has many advantages such as nontoxicity, variable color-tone, and no post-treatment process. In this study, the plating conditions such as temperature, pH, current density, plating time, and amount of additive (glycine) were determined in the tin-cobalt alloy plating process through Hull-cell test and surface analysis. As the result of Hull-cell analysis, brightness became superior as the amount of glycine increased. It was found that the optimum alloy ratio was 0.03 M of $SnCl_{2}{\cdot}2H_{2}O$ and 0.05 M of $CoSO_{4}{\cdot}7H_{2}O$ at $50^{\circ}C$, pH 8.5, and $0.5A/dm^2$. The optimum amount of additive was 15 g/L of glycine and 0.1 g/L of organic acid. Then, the solution including glycine was recommended as an optimum plating solution for a chromium plating process.

• Analytical Science and Technology
• /
• v.12 no.1
• /
• pp.40-46
• /
• 1999

Zn-Ni alloy electrodeposition on steel has been examined by means of X-ray diffraction and scanning electron microscopy. The effect of current density, $Ni^{2+}$ ion concentration, and $Cl^-$ ion concentration on the structure as well as morphology of the electrodeposit have been studied. The Ni content of the electrodeposit increased with decreasing current density in the range studied in this work. The Ni content of the electrodeposit also increased with increasing $Ni^{2+}$ ion and $Cl^-$ ion concentrations. The structure change of the electrodeposit was closely related to the Ni content. In fact, the mixture phase of ${\eta}$ and ${\gamma}$ was found below 10 wt.% of Ni while the ${\gamma}$ phase only was observed above 10 wt.% of Ni. In addition, the lattice parameter, a, of then phase structure increased and the lattice parameter, c, of it decreased as the Ni content of the electrodeposit increased. The morphology of the electrodeposit varied from the plate-like shape to the fine granular shape depending upon the change in composition and structure of the electrodeposit.

• Journal of the Korea Academia-Industrial cooperation Society
• /
• v.12 no.9
• /
• pp.4015-4021
• /
• 2011

The purpose of this study is to investigate the effect of compositional ratio of additives, such as potassium ferrocyanide, aminoacetic acid (=glycine) and 2,2'-dipyridyl, on the physical properties of copper layer deposited by environment-friendly electroless plating reaction. The highest plating rate of copper layer, $9.5mg{\cdot}cm^{-2}{\cdot}hr^{-1}$, was obtained at 20 mg/L of potassium ferrocyanide and 0.01 mol/L of aminoacetic acid, which coincided with the change in the hardness of the copper layer. In the additives used in this study, potassium ferrocyanide was considered to improve the plating rate, aminoacetic acid increased the hardness value of deposited films and 2,2'-dipyridyl enhanced the brightness of copper deposited films.

• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 2018.06a
• /
• pp.108-108
• /
• 2018

무전해 니켈도금 층은 마모, 마찰, 스크래치, tribology 등에 대한 내구성뿐만 아니라 내식성도 우수하여 산업현장에서 널리 적용되고 있다. 일반적으로 무전해 니켈도금 층의 내구성은 경도 값과 직접적인 상관관계를 가지며, 그 값은 약 $400-500H_V$ 정도이다. 이러한 무전해 도금 층에 대하여 약 $400^{\circ}C$에서 1시간 정도 열처리를 실시하면 경도 값은 약 $800-1000H_V$ 정도로 현저히 증가되고 내구성 역시 크게 향상시킬 수 있다. 그러나 해양환경에서 발생되는 캐비테이션 침식 부식에 대한 무전해 니켈도금 층의 열처리에 관한 연구는 거의 전무한 상태이다. 따라서 본 연구에서는 회주철의 캐비테이션 침식 부식을 방지하기 위해 무전해 니켈도금 후 다양한 온도와 시간으로 열처리를 실시하여 도금 층의 캐비테이션 침식 부식 특성을 평가하고자 하였다. 무전해 니켈코팅을 위한 모재는 회주철(FC250)을 $19.5mm{\times}19.5mm{\times}5mm$의 크기로 가공하였다. 도금조로 500mL 비커를 사용하였으며, 모든 시험편은 2시간 동안 무전해 니켈도금을 실시하였다. 그리고 캐비테이션 실험은 ASTM G32 규정에 의거하여 천연해수 내 $30^{\circ}C$에서 $50{\mu}m$의 진폭으로 실시하였다. 그 결과 열처리 적용 시 EN 도금의 표면경도가 현저히 증가하여 캐비테이션 침식 부식 저항성이 상당히 개선되었다.

• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 2013.05a
• /
• pp.59-59
• /
• 2013

Ni-P 도금 피막층에 W를 함유시켜 고내식성을 목적으로 하는 Ni-W-P 도금에 대하여 연구 하였다. 도금액 조건의 최적화 및 도금온도와 pH 등이 가 피막특성에 미치는 영향을 조사하여 피막 크랙이 발생하지 않고 내식성 및 내마모성이 우수한 무전해 Ni-W-P 도금 공정을 확립하였다.

• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 2015.11a
• /
• pp.331-331
• /
• 2015

차세대 원자로 핵연료의 성능을 제한하는 금속연료-피복관 상호반응 현상(FCCI)을 방지하기 위한 방안으로 Cr 도금기술의 적용성을 연구하였다. 도금 성능을 평가하기 위한 예비 시험 결과 Cr 도금층은 핵연료와 피복관의 상호반응을 억제함이 확인되었다. 도금층 성질을 개선하기 위한 연구와 함께 Cr층을 피복관 내면에 도금하는 연구를 수행하였다.