• 대한기계학회논문집A
• /
• 제33권6호
• /
• pp.560-567
• /
• 2009

This paper was designed to estimate the adhesion strength of galvannealed coatings on steel sheets. The adhesion strength were evaluated using single lap - shear tests where the lap joint was bonded by structural adhesive. Tests were performed for overlap length of 5mm, 10mm and 15 mm and three directions (0, 45, 90) of steel sheets used as the adherend of the overlap joint. After the tests, FE simulations of the single lap-shear test were also carried out to observe the stress distribution in the interface between the adhesive and the coated sheet. The results showed that the joint failure loads obtained from the tensile tests of bonded single lap-joints were the same, regardless of overlap lengths and directions of steel sheets. Also, the failure of galvannealed coatings greatly depended on shear stress distribution in the interface and the value was about 30MPa.

• 대한기계학회:학술대회논문집
• /
• 대한기계학회 2007년도 춘계학술대회A
• /
• pp.238-243
• /
• 2007

This paper is designed to estimate the adhesion strength of coating layer on galvannealed steel sheet using lap shear test. The single lap shear test is the most commonly used standard test for determining the strength of medium-strength and high strength bonds. The bond strength of bonded single lap joints on subjecting the substrates to loads is determined by lap shear forces in the direction of the bonded joint. In this study, specimen for adhesion strength test was made to attach coated sheet to cold rolled sheet and were heated in temperature of 180 for 20minutes. After test, detached parts of coatings on coated sheet were observed using SEM and EDX to identify substrate and complete detachment. The tested results showed that adhesive strength of coating is unrelated to anisotropy of sheet and is difficult to be extracted using conventional theory because of fine cracks of coating layers which were created during annealing process.

• 대한기계학회논문집A
• /
• 제34권10호
• /
• pp.1367-1375
• /
• 2010

본 연구에서는 핫스템핑 소재로 사용되는 보론합금강판 22MnB5의 단일 겹치기 점용접에서 용접부의 강도 향상을 위한 최적화를 수행하였다. 최적화 과정은 다구찌 실험계획법에 의해 행해졌으며 공정변수는 전류, 가압력 및 통전시간으로 선정하였고, 잡음인자로서 핫스템핑 시 소재의 가열온도와 유지시간을 고려하였다. 가열조건에 따라 22MnB5 표면의 알루미늄 도금층과 모재 간의 확산반응에 의해 화합물층 두께에 산포가 발생하였으며 이러한 산포는 너겟의 형성에 영향을 미치는 것을 알 수 있었다. 한편 용접부의 인장전단강도를 목적함수로 하였을 때, 이러한 가열조건에 강건한 최적의 용접 조건은 전류 8kA, 가압력 4kN, 통전시간 18cycle로 선정되었다. 최적 조건의 검증 결과 용접부의 인장전단강도 는 32kN으로서 요구되는 규격인 23kN보다 크게 증가되었다.