• 한국해양공학회:학술대회논문집
• /
• 한국해양공학회 2004년도 학술대회지
• /
• pp.370-375
• /
• 2004

Fatigue tests were carried out to find the fatigue characteristics in the super-long life range by using a cantilever type rotational bending fatigue test machine. Three kinds of specimen in bearing steels with the quenched and tempered in air (A and B, B: shot peened after heal treatment) and under vacuum conditions(C:non-shot peened)were tested in this study. S-N curves obtained from fatigue tests of C specimen tend to come dawn again in the super-long life range due to fish-eye type cracking, while most of A and B specimens fractured by surface defects such as scratches and slip lines. This duplex S-N behavior for the high strength steels have to be reviewed by the change of fracture modes.

• 대한기계학회논문집A
• /
• 제36권6호
• /
• pp.707-712
• /
• 2012

본 연구에서는 Ti-6Al-4V 합금에 대한 초고주기 피로시험 연구를 통하여 사이클에 따른 파단면 관찰결과 2가지 타입으로 명확히 구분되는 것을 확인할 수 있었다. 첫번째로 106사이클 범위에서 확인할 수 있는 것은 표면부에서 피로크랙 사이트가 시작된 전형적인 피로 파단면이다. 두번째는 107~109사이클에서는 확연히 다른 피로파단 양상으로, 표면으로부터 $500{\mu}m$ 내부에서 피로크랙 사이트가 시작되어 크게 박리되어 나간 형상으로, 크랙 사이트 주변을 관찰한 결과 미세한 마이크로 크랙들이 입계파괴 양상으로 형성되어 있는 것을 확인 할 수 있었다. 이에 내부 크랙 사이트 피로거동에 대한 연구결과와 본 시험에서 사용된 초음파피로시험기술의 이론 및 적용사례를 소개하고 현재 활발히 진행중인 연구동향을 밝히고자 한다.

• 한국해양공학회지
• /
• 제25권6호
• /
• pp.72-79
• /
• 2011

In this paper, the fatigue characteristics of shot peened A7075-T651 alloy were compared with those of the specimens without the shot peening. The multi-spindle and single-spindle rotating bending fatigue testing machines were employed for the evaluation. Shot peening (SP) with various pressure (5 psi, 10 psi, 15 psi, 25 psi and 35 psi) were used in this test. In order to investigate the effect of the applied pressure during the SP, we carried out the surface roughness test, compressive residual stress test, hardness test, tensile test, VHCF (Very high cycle fatigue) test and SEM observation. SP induced the formation of remarkable compressive residual stress from the surface to certain depth of sample by means of the plastic deformation. The surface hardness and the fatigue characteristics of the specimens were also modified by the SP. According to the S-N curves, fatigue lives of shot peended sample with 25 psi measures 50 times higher than that of the untreated sample. The fatigue lives of shot peened sample with 15 psi and 35 psi measure approximately 10 times higher than that of the untreated ones.

• 대한기계학회논문집A
• /
• 제41권7호
• /
• pp.635-643
• /
• 2017

STS 304L 강재의 냉간압연율의 증가에 따라 t가 1.5 mm에서 1.1 mm까지 감소하면 인장강도, 항복강도, 경도치 및 UFT피로시험의 피로한도는 선형적으로 증가하였다. t=1.5 mm, t=1.4 mm, t=1.3 mm 및 t=1.1 mm인 4가지 시험편의 UFT피로시험(R= -1)결과, 회전굽힘피로시험(R= -1)의 결과처럼 $10^6$ 영역에서 S-N곡선의 피로한도가 절점(knee point)을 형성하였고, 기가사이클 피로에서 생기는 현상인 피로한도가 추가로 감소하지않았다. 또 t=1.1 mm인 경우 가장 높은 피로한도 345 MPa로 되었고, 원소재(t=1.5 mm)에 대하여 64.3 % 증가하였다. 냉간압연율에 따른 UFT피로시험결과 많은 작은 표면균열이 티어링(tearing)하면서 발생, 성장, 서로 합체하였다.