• Journal of the Korean Society for Nondestructive Testing
• /
• v.22 no.2
• /
• pp.155-169
• /
• 2002

The objective of this study was to investigate the effect of crack opening and closure in the AE activities during fatigue test. Laboratory experiment using various materials and test conditions were carried out to identify AE characteristics of fatigue crack propagation. Compact tension specimens of 2024-T4 and 6061-T6 aluminum alloy were prepared for fatigue test. AE activities were analyzed based on the phase of the loading cycle. Generally, most of AE were generated when the crack begins' opening and the crack closes fully, whereas a few in the pull opening of the crack. Also AE activity in the peak loading of cycle was different with each specimen. However, in the same material, AE activity was not affected by the change of cyclic frequency (0.1, 0.2, 1.0Hz). It was found that AE activities during crack opening and closure depend on material properties such as micro-structure, tensile strength and yield strength.

• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.29 no.8 s.239
• /
• pp.1078-1084
• /
• 2005

The relationship between fatigue crack opening behavior and the reversed plastic zone sizes is studied. An elastic-plastic finite element analysis (FEA) is performed to examine the opening behavior of fatigue crack, where the contact elements are used in the mesh of the track tip area. The smaller element size than reversed plastic zone size is used fer evaluating the distribution of reversed plastic zone. In the author's previous results the FEA could predict the crack opening level, which crack tip elements were in proportion to the theoretical reversed plastic zone size. It is found that the calculated reversed plastic zone size is related to the theoretical reversed plastic zone size and crack opening level. The calculated reversed plastic zone sizes are almost equal to the reversed plastic zone considering crack opening level obtained by experimental results. It can be possible to predict the crack opening level from the reversed plastic zone size calculated by finite element method. We find that the experimental crack opening levels correspond with the opening values of contact nodes on the calculated reversed plastic zone of finite element simulation.

• Proceedings of the KSME Conference
• /
• 2005.11a
• /
• pp.113.1-113.1
• /
• 2005

• Proceedings of the KSME Conference
• /
• 2008.11a
• /
• pp.725-726
• /
• 2008

This paper proposes elastic stress intensity factors and crack opening displacements (CODs) for a slanted axial through-wall cracked cylinder under an internal pressure based on detailed 3-dimensional (3-D) elastic finite element (FE) analyses. Based on the elastic FE results, the stress intensity factors along the crack front and CODs through the thickness at the center of the crack were provided. These values were also tabulated for three selected points, i.e., the inner and outer surfaces and at the mid-thickness. The present results can be used to evaluate the crack growth rate and leak rate of a slanted axial through-wall crack due to stress corrosion cracking and fatigue. Moreover, the present results can be used to perform a detailed Leak-Before-Break analysis considering more realistic crack shape development.

• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.25 no.11
• /
• pp.1873-1880
• /
• 2001

The effects of restraint of pressure induced bending(PIB) on crack opening for circumferential through-wall crack in a pipe were investigated. In this study, the elastic and elastic-plastic finite element analyses were performed to evaluate crack opening displacement(COD) for various restraint conditions and crack size. The results showed the restraint of PIB decreased crack opening for a given crack size and tensile stress, and the decrease in crack opening was considerable for large crack and short restraint length. A1so, the effect was more significant in tole results of elastic-plastic analysis compared with in the elastic analysis results. In the elastic-plastic analysis results, tole restraint effect was increased with increasing applied tensile stress corresponding to internal pressure. Additionally, the restraint effect on COD was independent on the variation in pipe diameter and decreased with increasing pipe thickness, and It depended on not total restraint length but shorter restraint length for non-symmetrically restrained.

• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.27 no.6
• /
• pp.960-968
• /
• 2003

The objective of this study is to investigate the effect of AE activities in the crack opening and closure during the fatigue test. The laboratory experiments for various materials and test conditions were carrie out to identify AE characteristics of fatigue crack propagation. Compact tension specimens of SWS 490B and Al 7075-T6 alloy were prepared for fatigue test. AE activities were analyzed based on the phase of the loading cycle. In case of SWS 490B, the most of AE was generated when the crack began opening and the crack closed fully, whereas a few in the full opening of the crack. On the other hand, in case of Al 7075-T6, a distinct AE activity was observed during crack opening process. AE activity in the peak loading of cycle was different with each specimen. However, in the same material, AE activity was not affected by the change of cyclic frequency (0.1, 0.2, 1.0 ㎐). It was found that AE activities during crack opening and closure depend on material properties such as micro-structure, yield strength and elongation.

• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.30 no.1 s.244
• /
• pp.60-65
• /
• 2006

The present paper provides experimental J estimation equation for the circumferential through-wall cracked pipe under four-point bending, based on the load-crack opening displacement (COD) record. Based on the limit analysis and the kinematically admissible rigid-body rotation field, the plastic ${\eta}$-factor for the load-COD record is derived and is compared with that for the load-load line displacement record. Comparison with the J results from detailed elastic-plastic finite element (FE) analysis shows that the proposed method based on the load-COD record provides reliable J estimates even for shallow cracks, whereas the conventional approach based on the load-load line displacement record gives erroneous results for shallow cracks. Thus, the proposed J estimation method could be recommended for testing the circumferential through-wall cracked pipe, particularly with shallow cracks.

• Transactions of the Korean Society of Mechanical Engineers
• /
• v.14 no.3
• /
• pp.603-609
• /
• 1990

Detection and non-propagating cracks of small fatigue crack for smooth and pre-cracked specimens were examined in a carbon steel. The fretting oxide induced crack closure triggered by the roughness induced crack closure has an important role in determing the length. The fatigue limit for the with no cracks or with a short pre-crack is lower at R=-1 than that at R=0. A non-propagating crack are quite different between points near the specimen's surface and those of deepest penetration.

• Journal of the Korean Society for Precision Engineering
• /
• v.18 no.5
• /
• pp.74-83
• /
• 2001

In this study, internal fatigue crack initiation and propagation behavior were investigated by triple piece spot welded specimen. To estimate fatigue life of the specimen varied with shape and thickness, Crack tip opening angle(CTOA) correlated with stress intensity factor was used as the stiffness parameter. The relation between fatigue life and CTOA can be arranged by the quantitative equation for each specimen by experiment. In addition, the variation of stress distribution was solved and the effect on fatigue crack behavior was examined by finite element method(FEM).

• Transactions of the Korean Society of Mechanical Engineers
• /
• v.13 no.6
• /
• pp.1193-1202
• /
• 1989

본 논문에서는 발전소의 소재로 많이 쓰이고 있는 304 스테인리스강(앞으로는 304SS로 표기함)과 316스테인리스강(앞으로는 316SS로 표기함)의 크립 균열 발생 거동 을 각각 600.deg. C와 625.deg. C에서 조사한다. 이 온도는 발전소의 반응기(reactor)에 사용 되는 304SS와 316SS이 받는 온도이다. 즉 304SS와 316SS의 크립 균열 발생을 지배 하는 파괴 매개변수가 무엇인지가 크립 파괴 실험을 통하여 조사된다. 실험 결과는 이미 제안되어 있는 크립 균열 발생 모델에서 예측된 결과와 비교된다. 특히 304SS 와 316SS은 고온에서의 연성도가 변형률 속도에 따라 변하는 것으로 알려져 있다. 본 연구에서는 '변형률 속도에 따른 재료의 연성도의 변화에 근거한 균열 발생 모델' 을 제안하고, 그 모델에서 예측된 크립 발생 거동을 실험 결과와 비교한다.