• Composites Research
• /
• v.18 no.2
• /
• pp.20-29
• /
• 2005

To evaluate the flexural deformation and strength of composite motor case above the glass transition temperature$(T_g),\;170^{\circ}C$, of resin material, a finite element analysis(FEA) model in which material non-linearity and progressive failure mode were considered was proposed. The laminated flexural specimens which have the same lay-up and thickness as the composite motor case were tested by 4-point bending test to verify the validity of FEA model. Also. mechanical properties in high temperature were evaluated to obtain the input values for FEA. Because the material properties related to resin material were highly deteriorated in the temperature range beyond $T_g$, the flexural stiffness and strength of laminated flexural specimen in $200^{\circ}C$ were degraded by also $70\%\;and\;80\%$ in comparison with normal temperature results. Above $T_g$, the failure mode was changed from progressive failure mode initiated by matrix cracking at $90^{\circ}$ ply in bottom side and terminated by delamination at the center line of specimen to fiber compressive breakage mode at top side. From stress analysis, the progressive failure mechanism was well verified and the predicted bending stiffness and strength showed a good agreement with the test results.

• Proceedings of the KSME Conference
• /
• 2001.11a
• /
• pp.137-142
• /
• 2001

In structural applications, brittle materials such as soda-lime glasses and ceramics are often subjected to multiaxial stress. Brittle materials with crack or damaged by foreign object impacts are abruptly fractured from cracks, because of their properities of very high strength and low fracture toughness. But in most cases, the residual strength has been derived from tests under uniaxial stress such as a 4-point bend test. The strengths under multiaxial stresses might be different from the strength. In comparable tests, the residual strength under biaxial stress state by the ball-on-ring test was greater than that under the uniaxial one by the 4-point bend test. In the case that crack having 90deg. to loading direction, the ratio of biaxial to uniaxial flexure strength was 1.12. At a different crack angle to loading direction when it was evaluated by the 4-point bend test, the residual strength was different and the ratio of 45deg. to 90deg. was 1.16.

• Korean Journal of Dental Materials
• /
• v.44 no.3
• /
• pp.273-280
• /
• 2017

The aim of the present study was to investigate the effects of specimen dimension on the flexural properties and testing reliability of dental composite resin. The composite resin was prepared experimentally by mixing a resin matrix with silanated micrometer glass filler at 50 vol%. Flexural specimens with various dimension in specimen's width were fabricated by light curing using a split metal mold; $25{\times}2{\times}2mm$, $25{\times}2{\times}4mm$, $25{\times}2{\times}6mm$ in length ${\times}$ height ${\times}$ width. The flexural strength and modulus were determined according to ISO 4049 test protocol at a span length of 20 mm (normal-flexural strength; NFS). Another flexural test was conducted using mini-sized specimens ($12{\times}2{\times}2mm$, $12{\times}2{\times}4mm$, $12{\times}2{\times}6mm$) from the broken specimens at a span length of 10 mm (mini-flexural strength; MFS). Data were analyzed with ANOVA and Duncan's post-hoc test and the test reliability was evaluated by Weibull analysis. Results showed that there are generally no significant difference in flexural strength with the increase in the specimen width in NFS and MFS tests. However, the test reliability of flexural strength based on Weibull analysis was largely changed with the variables in the dimension of width and span length. The flexural modulus of NFS was increased as the dimension of specimens width increased while there was no trend in flexural modulus of MFS test. Overall results recommend that the evaluation of flexural properties and the reliability of dental composite resins should be performed with more than one test method.

• Journal of Advanced Marine Engineering and Technology
• /
• v.39 no.3
• /
• pp.230-237
• /
• 2015

To improve productivity and improve the welding process, we have studied the automated system of the weld by applying a tandem welding. Then, the speed of the welding process is improved, production of industries is increasing. Productivity of the industrial sector has increased the application of tandem welding for automated system of welding. But quality assurance for the product take place welding defects in the welding process because the speed of the process is increased. Definitive research solutions an dit's actuality, however, there is insufficient. Accordingly, it is a situation that the performance of the weld to ensure quality of the weld is required urgently after the welding process. Comparing and analyzing the results of passing each experiment of the two-electrode welding and the welding electrode1, a study attempted to quality assurance of the welded joint portion.

• Journal of the Microelectronics and Packaging Society
• /
• v.17 no.1
• /
• pp.55-61
• /
• 2010

An impact bending test method was used to evaluate the reliability for the solder joint of lead-free solder ball. In order to standardize the test method, the four point impact bending test was applied under the conditions of various frequencies and amounts of +/-amplitude respectively. Effects on the results were analysed. The optimum condition for impact bending test achieved in this study was the frequency of 10 Hz, and the amplitude of (+12/-1)~(+15/-1). 3 kinds of surface finishes Cu-OSP (Organic Solderability Preservative), ENIG (Electroless Nickel Immersion Gold), and ENEPIG (Electroless Nickel, Electroless Palladium, Immersion Gold) were used. Fracture surface showed that cracks were initiated and fractured along the intermetallic layer in the case of surface finishes of Cu-OSP and ENIG, while in the case of ENEPIG the cracks were initiated and propagated in the solder region.

• Composites Research
• /
• v.12 no.3
• /
• pp.66-74
• /
• 1999

A modified mixed mode bending test was performed to investigate the mixed mode delamination for carbon/epoxy composite material. Various mixed mode ratios could be produced by changing the applied load position on the loading lever and the bending load position on the specimen. The modified mixed mode bending test was analyzed to obtain strain energy release rates using beam theory, compliance method and finite element method, This results were in good agreement with the experimental result, which confirmed the validity of this test.

• Journal of the Korea Academia-Industrial cooperation Society
• /
• v.20 no.8
• /
• pp.649-656
• /
• 2019

Flux cored arc welding (FCAW), which is used widely in many fields, such as shipyards, bridge structures, construction machinery, and plant industry, is an alternative to shielded metal arc welding (SMAW). FCAW is used largely in the welding of carbon and alloy steel because it can be welded in all poses and obtain excellent quality in the field under a range of working conditions. In this study, the mechanical properties of welded parts were analyzed after different welding of SS400 and SM490A using FCAW. The following conclusions were drawn. The tensile test results satisfied the KS standard tensile strength in the range of 400~510 N/mm2 in all welding positions. The bending test confirmed that most of the specimens did not show surface breakage or other defects during bending and exhibited sufficient toughness, even after plastic deformation. The hardness test results were lower than the standard value of 350 Hv of KS B 0893. Similar to the hardness test, were greater than the KS reference value. The macro test revealed no internal flaws, non-metallic inclusions, bubbles or impurities on the entire cross section of the weld, and there were no concerns regarding lamination.

• Journal of the Korean Society for Aeronautical & Space Sciences
• /
• v.31 no.5
• /
• pp.44-54
• /
• 2003

The experiments are performed to evaluate mechanical properties about foam and face materials of sandwich beams. These results are applied to the flexural wrinkling estimation of sandwich beam. The 3 point bending test shows that it is reasonable to include pre-buckling behavior in flexural wrinkling analysis, which is closer to experimental result. It is also conducted to survey the wrinkling behavior.

• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.38 no.10
• /
• pp.1163-1169
• /
• 2014

In this study, a fatigue assessment method for vehicle suspension systems having welded geometries was established under a bending loading condition. For the fatigue life estimation of the actual product's welded joints made of different steels, bending fatigue tests were performed on welded specimens with a simplified shape for obtaining the moment-fatigue-life plot. Further, geometry modeling of the simplified welded specimens was conducted. Results of finite element analysis were used to obtain the stress-fatigue-life plot. The analysis results were also used to calculate the stress concentration factors for notch-factor-based fatigue life estimation. The test results were compared with results of the general notch-factor-based fatigue life estimation for improving fatigue assessment. As a result, it was concluded that both the welded fatigue tests and the notch-factor-based fatigue life estimation are necessary for accurate fatigue assessment.

• Transactions of the Korean Society of Mechanical Engineers
• /
• v.10 no.3
• /
• pp.427-431
• /
• 1986

3점 굽힘 시험편, 중앙균열 인장 시험편, 콤팩트 인장 시험편에 대한 J적분식을 하나의 일반화된 형태로 유도한다. 이 일반식은 Eftis와 Liebowitz에 의해 제안된 하중과 하중점 변위 사이의 관계와 Sumpter에 의한 탄성과 소성성분 J적분의 중첩개념을 이용함으로써 유도된다. 일반식에 포함된 .eta.계수를 위 3가지 시험편에 대해서 결정한다. 위 3가지 시험편에 대한 J적분의 최종식은 하중과 하중점 변위곡선 아래의 면적을 측정하지 않아도 되는 형태로 나타난다. 본 연구의 결과식은 Landes등에 의한 실험치와 비교하여 매우 잘 일치함을 보인다.