This paper aims at estimating self-cleaning performance of mortar coated with photocatalytic suspension under various conditions. Experimental variables included the concentration (1.5 % and 3.0 %) of photocatalytic suspension for coating mortar specimen, the presence of hydrophilic agent in photocatalytic suspension, and applying the primer on the surface of mortar. The color change of methylene blue solution increased and accordingly self-cleaning performance increased as photocatalytic concentration increased. The presence of hydrophilic agent in photocatalytic suspension slightly decreased the self-cleaning performance compared to the conventional photocatalytic suspension. Test results also showed that mortar specimen including primer and specimen not including primer did not show significantly different self-cleaning performance. In addition, cracks on the surface of mortar specimens decreased as the photocatalytic concentration increased. Therefore, increase in cracks on the surface of mortar at different photocatalytic concentration might adversely affect the self-cleaning performance of mortar specimens.

• Proceedings of the KAIS Fall Conference
• /
• 2008.11a
• /
• pp.354-357
• /
• 2008

본 연구는 광전자촉매 시스템(PECS) 적용을 위하여 광촉매 금속판과 코팅비드를 제조하여 특성을 고찰하였다. 광촉매 물질의 회수가 용이하고, 실용화하기 위하여 티타늄 금속판을 $400^{\circ}C$에서 $700^{\circ}C$까지 $50^{\circ}C$에서 $100^{\circ}C$간격으로 토치를 사용하여 산화처리 하였으며, 비드의 경우 alumina, glass, silica gel beads에 TTIP([Ti$(OC_3H_7)_4$], Aldrich)을 전구체로 사용하여, 유동층 화학기상증착공정(Fluidized Bed Chemical Vapor Deposition, FB-CVD)으로 박막코팅을 하였다. 광촉매 금속판의 경우 산화처리 후 외관상태와 성분분석 시 최적조건은 $400^{\circ}C{\sim}500^{\circ}C$ 60분간 토치로 산화하였을 때였으며, 광촉매 코팅비드의 경우 silica gel beads가 본연의 다공구조를 나타내며 박막코팅이 되어, 상대적으로 alumina, glass beads에 비해 반응표면적이 크게 나타났다.

• Proceedings of the KAIS Fall Conference
• /
• 2005.05a
• /
• pp.312-314
• /
• 2005

최근 일본이 광촉매 관련 제품에서의 소비자. 보호를 위한 적절한 표준화 규격 제정에 강한 의욕을 보이며, 자국내 JIS 규격 외에 ISO 규격 (ISO/TC 206 fine ceramics)을 제정하기 위하여 노력하고 있다. 이에 국내에서는 산업보호 및 해외시장에서의 종속성을 벗어나기 위하여 2001년부터 선정된 분야에서의 광촉매표준화 시도가 이루어졌다. 그 중의 하나로 본 논문은 광섬유를 빛 전달 매개체와 광촉매 코팅 지지체로 이용해서 광촉매 졸을 구성하는 광촉매 자체의 유기물 분해능을 결정하는 방법을 규정하는 과정과 제안과 관련된 것이다. 이 규격은 코팅 가능한 졸이나 졸로 만들 수 있는 자외선 감응 광촉매 재료에 적용하며, 차후 가시광 및 태양광 감응 광촉매 활성 측정 및 비교에도 응용이 가능할 것으로 판단된다.

• Proceedings of the Korea Air Pollution Research Association Conference
• /
• 2002.11a
• /
• pp.87-88
• /
• 2002

환경오염물질 정화를 위하여 다양하게 시도되고 있는 광촉매는 특별한 장치나 시설 없이 자외선을 에너지원으로 오염물질을 효과적으로 산화분해 시킬 수 있기 때문에 환경 친화적일 뿐만 아니라 경제적인 잇점을 가지고 있다. 그러나 아직까지 본격적인 실용화를 위해서는 선결해야 될 몇 가지 문제가 남아 있다 특히, 환경정화분야에서 광촉매를 적용하기 위해서는 광촉매 입자의 효과적인 코팅이 필수적이다. 광촉매 입자의 코팅은 지지체의 종류와 광촉매의 특성에 따른 최적조건을 찾아 주어야 하는데, 기본적으로 지지체와 광촉매 입자간의 결합 상태가 우수해야하며, 동시에 대상물질제거에 부합할 만한 광촉매 활성을 만족시켜야 한다. (중략)

• Elastomers and Composites
• /
• v.49 no.4
• /
• pp.341-345
• /
• 2014

In this study, self-actuated photocatalyst that titanium dioxide doped by more than two transition metal was coated PU foam. The antibacterial and antifungal activity of self-actuated photocatalyst coated PU foam was characterized without light. The antibacterial property of self-actuated photocatalyst coated PU foam was shown to be reduced more than 96%, and the antifungal property was shown to be reduced more than 99.9%. The durability of self-actuated photocatalyst coated PU foam tested by Weather-O-meter showed the 7% reduction of formaldehyde decomposition from 96.5% before test to 89.8% after test. The observation of surface of PU foam coated with self-actuated photocatalyst showed that the catalyst was firmly attached to the surface of polyester fiber without separation.

• Proceedings of the Materials Research Society of Korea Conference
• /
• 2003.11a
• /
• pp.103-103
• /
• 2003

대기나 물에 용해된 여러 가지 유해한 유기물을 분해하기 위한 방안으로서 다양한 광촉매 재료를 이용하려는 시도가 진행되고 있다. 하지만 광촉매 반응은, 현탁액 내에서 submicrometer 크기를 갖는 반도체재료에서 발생하므로 처리된 폐수로부터 촉매를 제거해야 하는 정제공정 (downstream process)이 필요하며, 이는 경제적인 측면에서 큰 경비를 요구하게 된다. 이를 해결 하기 위하여, 가장 우수한 광촉매 재료로 평가받는 TiO$_2$를 glass beads, sands, silica gel등의 물질에 고정시키거나, TiO$_2$를 자성 입자에 코팅시킨 형태인, 자성 광촉매입자를 응용하려는 연구가 최근 활발하게 진행되고 있다. 따라서 본 연구에서는 광촉매의 고정화와 재활용 효율을 향상시키기 위하여 TiO$_2$ 나노입자를 y-Fe$_2$O$_3$ 나노입자의 표면에 코팅하여 나노입자의 큰 비표면적을 활용하고 미세구조를 제어하여 입자간의 고정특성과 자기적 특성의 제어기술을 확립하고자 하였다.

• Journal of the Korean Recycled Construction Resources Institute
• /
• v.12 no.1
• /
• pp.94-101
• /
• 2024

In this paper, the performance of air pollution reduction by coating the photocatalyst solution on the mortar surface was analyzed to ensure the possibility of applying the photocatalyst to structures with a large specific surface area. The photocatalytic concentrations of the coating solution were set to 1.5 % and 3.0 %, and the types of binders were considered as experimental variables, such as ultra-high performance concrete (UHPC), ordinary portland cement (OPC), and blast furnace slag. As the photocatalyst concentration increases, the air pollution reduction performance increases. In addition, as a result of the air pollution reduction performance, the NO_x concentration reduction rate was the highest for UHPC, and the air pollution reduction performance increased as the blast furnace slag was replaced. Therefore, the amount of TiO₂ remaining on the surface varies depending on the density of the tissue due to the difference in particles caused by the difference in the amount of TiO₂ remaining on the surface.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2014.02a
• /
• pp.479.2-479.2
• /
• 2014

자가 세정 및 김서림 방지가 가능한 투명 코팅 소재로써 $TiO_2$ 코팅박막을 제안하였으며, $TiO_2$ 코팅박막은 스퍼터링 방식으로 제작하였다. 낮은 표면 에너지를 갖는 물질을 화학적으로 변형시키고 유리기판 위 텍스쳐링을 형성함으로써, 수분에 대해 완전히 다른 특성을 갖는 표면을 유도하며, 김서림 방지 기능과 자가세정, 그리고 높은 빛 투과 특성으로 스마트 표면 코팅을 구현할 수 있다. $TiO_2$ 자가세정 코팅기술은 설치 후 1년 안에 먼지 및 오염에 따라 최대 40%의 효율 저하가 나타나는 태양전지, 디스플레이 패널 분야에서 매우 중요한 요소로 자리 잡을 것으로 기대되어진다. 본 연구에서는 $TiO_2$ 세라믹 타겟이 부착된 비대칭 마그네트론 스퍼터링 장치를 이용하여 $TiO_2$ 박막을 증착하였으며 증착되어진 $TiO_2$ 박막의 광촉매 특성과 트라이볼로지 특성을 고찰하였다. 광촉매 특성으로는 표면 접촉각 분석을 통하여 고찰하였으며, 트라이볼로지 특성으로는 경도, 잔류응력, 마찰계수, 표면 거칠기 등을 평가하였다. 또한 XRD, FESEM 분석등 구조분석을 통하여 광촉매 특성과 트라이볼로지 특성등과의 연관성을 규명하였다.

• Proceedings of the KAIS Fall Conference
• /
• 2005.05a
• /
• pp.274-276
• /
• 2005

본 논문에서는 유동층 화학기상증착법(FB CVB; Fluidized Bed Chemical Vapor Deposition)으로 광촉매가 박막증착된 비드를 제조하였고 제조된 광촉매코팅비드의 광반응성을 연속식 반응기에서 아세트알데히드의 분해능력을 측정하여 분석하였다. 광촉매가 박막증착된 비드의 FE-SEM 분석 결과 글라스 비드 위의 티타니아는 비교적 매끄럽게 증착되었고, 실리카 위의 티타니아는 입자의 형태로 증착되었으며 알루미나 위의 티타니아는 결정상을 이루며 증착됨을 확인 할 수 있었다. Acetaldehyde 기체의 광촉매에 의한 분해 실험을 진행하기 위해 연속식 반응기를 설계 제작하였고, 이 반응기를 사용하여 제조된 광촉매 코팅입자의 광반응성을 살펴보았다. 반응기는 가스 주입구와 출구를 갖고 있으며, 중심부에 UV 램프가 설치되었다. 반응기는 내열유리(pyrex)로 제작하였으며, 체적은 100 ml이다. 반응기 내부의 중심부에 UV 램프가 설치되고 UV 램프와 반응기 외부사이에 유동층 화학기상증착법에 의해 티타니아가 박막증착된 광촉매입자가 위치하여 광반응성을 평가하였다. 유량변화에 따른 광반응성을 측정하였으며, 알루미나에 광촉매를 증착시킨 제품의 경우 가스유량 100cc/min에서는 acetaldehyde가 $100\%$ 분해되고, 가스유량 500cc/min에서는 $50\%$정도 분해되는 것을 알 수 있었다.

• Journal of the Korea Academia-Industrial cooperation Society
• /
• v.6 no.4
• /
• pp.331-336
• /
• 2005

Recently, Japan has showed strong demand for protection of consumers against misleading specification provided by producers, establishing the committee for JIS and ISO. To protect domestic market and overcome potential subordinate relationship in overseas market, several universities and institutes in Korea have performed collaborative works on the standardization of test method f3r photocatalytic activity concerning the selected application fields. This article deals with the process and the result for the method of testing photocatalytic sol or suspended powder using optical fiber. Currently, this method is Intended for TiO2, but can be applied for various photocatalytic raw materials that can be activated by visible light and solar irradiation.