• Journal of the Korea institute for structural maintenance and inspection
• /
• v.24 no.5
• /
• pp.86-94
• /
• 2020

When the Superabsorbent Polymer (SAP) is added into concrete, the slump decreases rapidly, deteriorating the workability, the internal curing effect can be obtained through the water absorption and discharge process, and the internal voids of the concrete are increased. In this study, the effects of internal curing and voids were evaluated by evaluating the compressive strength, freeze-thaw resistance, and chloride penetration resistance of SAP-adding concrete that secured workability using a water reducing agent. Also, the internal curing effect of SAP was evaluated by dividing the curing conditions of concrete into water curing and sealed curing. From the result, as the SAP adding ratio increased, the amount of water reducing agent increased, and as for the compressive strength, the SAP adding ratio of 1.5% showed the greatest compressive strength. In particular, in the case of sealed curing showed higher compressive strength than the water curing. It is considered that the compressive strength increased due to the reduction of the effective water-cement ratio and the internal curing effect. Adding 1.0~1.5% of SAP improved the freeze-thaw resistance similar to the case of adding the AE agent, and the addition of more than 1.0% of SAP improved the chloride penetration resistance. The optimal adding ratio of SAP is 1.5%, and the adding ratio of 2.0% or more adversely affects the compressive strength and freeze-thaw resistance.

• Journal of the Korea institute for structural maintenance and inspection
• /
• v.24 no.2
• /
• pp.50-59
• /
• 2020

Superabsorbent Polymer (SAP) expands inside concrete by absorbing water and contracts as it discharges water. Through this process, concrete can achieve the internal curing effect, but the space occupied by the expanded SAP remains as a void. In this study, the effects of SAP internal curing and voids were evaluated by evaluating the fundamental properties and chloride penetration resistance of SAP mixed concrete. Also, to evaluate the internal curing effect by SAP, the tests were carried out under water and sealed curing conditions, respectively. From the result, the compressive strength of water curing did not differ significantly according to the mixing ratio of SAP. In the case of sealed curing, however, the compressive strength tended to increase as the mixing ratio of SAP increased. The internal curing effect of sealed curing was considered to have influenced the increase in compressive strength. In the case of the chloride diffusion coefficient, the diffusion coefficient tended to decrease as the mixing ratio of SAP increased. In particular, as the sealed curing is applied, the chloride penetration resistance is further improved due to internal curing effect. If the curing conditions are different, it is considered inappropriate to estimate the chloride penetration resistance by the surface electrical resistivity.

• Proceedings of the Optical Society of Korea Conference
• /
• 2001.02a
• /
• pp.162-163
• /
• 2001

폴리머를 이용한 광통신 소자는 실리카를 재료로 사용하는 소자와는 달리 고품질의 박막을 얻는 과정이 단순하고, 소자의 제조단가를 줄일 수 있어 많은 주목을 받고 있다 광통신 소자에 응용되는 여러 폴리머 중에서도 폴리이미드는 PMMA (Poly Methyl MethAcrylate) 등 다른 고분자 물질에 비해서 매우 높은 열적 및 환경적 안정성을 가지고 있는 것으로 알려져 있다. 또한 최근에는 폴리이미드가 가지는 단점인 복굴절과 흡수를 낮추기 위하여 불소기 등을 함유한 폴리이미드가 개발되었으며, 굴절률 조정 또한 용이하게 되었다. (중략)

• Polymer(Korea)
• /
• v.28 no.1
• /
• pp.18-23
• /
• 2004

Superabsorbent poly(potassium acrylate-co-acrylamide)s were synthesized in particle form using inverse suspension polymerization technique. Mean diameter of the prepared polymer particles decreased from 300 to 50 $\mu\textrm{m}$ with increasing surfactant concentration. The dynamic and equilibrium swelling behaviors during water absorption and drying process were investigated by weight measurement. The swelling ratio of polymer particles in water changed according to not only polymer crosslinking density, but particle size, saline concentration of aqueous medium, and copolymer compositions. Water sorption amount was increased with decreasing particle size, crosslinking agent concentration, and ion concentration in bulk solution. Being different from the water sorption process, the drying process was not significantly affected by particle size, polymer composition, or crosslinking amount.

• Journal of the Korean Recycled Construction Resources Institute
• /
• v.8 no.1
• /
• pp.88-96
• /
• 2020

In this study, the effect of cyclic wetting-drying on the self-healing of cementitious materials containing superabsorbent polymers (SAPs) were experimentally evaluated. In each cycle, cracked cement paste specimens containing various SAP dosages were exposed to wet conditions for 1 h, during which the capillary water absorption tests and water flow tests were conducted, and then exposed to dry conditions for 47 h. The capillary water absorption test results showed that the sorptivity values of the specimen without SAPs, SAP 0.5%, SAP 1.0%, and SAP 1.5% specimens were decreased by approximately 22.9%, 36.8%, 42.8%, and 46.3%, respectively, after 8 cycles. In addition, the water flow test results showed that the amount of water runoff through the cracks of all cracked specimens gradually decreased over wet/dry cycles, especially the reduction ratio of the amount of water runoff increased with increasing SAP dosage. Furthermore, the swelling behavior of SAPs in cracks by in gress water was con firmed via X-ray computed tomography (CT) analysis. These results indicate that the effective crack width can be reduced as SAPs absorb water and swell, while the water absorbed in SAPs can be released to crack surfaces under dry conditions, further promoting healing product formation. This study demon strates that the in corporation of SAPs can in crease the water tightness of cracks, thereby improving the self-healing efficiency of cementitious materials.

• The Proceedings of the Korean Institute of Illuminating and Electrical Installation Engineers
• /
• v.18 no.3
• /
• pp.44-51
• /
• 2004

오늘날 대부분의 에너지를 전기에 의존함에 따라 전력사용이 급증하고 부하가 대용량화되어 및 정적 전력공급이 중요한 문제로 대두되었다. 이러한 추세에 따라 송ㆍ배전 설비도 점차 대용량화 및 고전압화 되고 신뢰성을 요구하게 되며, 각종 배전 설비의 제조기술이 더욱 복합 다양하게 발전하고 있다. 그 중 전력계통에서 뇌 혹은 개폐서지 등의 과전압을 흡수ㆍ억제하여, 전력설비와 계통보호를 위해 설치하는 것이 피뢰기이다. 따라서 어떻게 과전압을 낮게 억제할 수 있을까 하는 것이 피뢰기의 가장 중요한 성능이라고 말할 수 있다. (중략)

• Proceedings of the Korean Society of Crop Science Conference
• /
• 2001.09a
• /
• pp.98-99
• /
• 2001

• Applied Chemistry for Engineering
• /
• v.10 no.7
• /
• pp.1066-1072
• /
• 1999

The physical properties of polymer concrete were investigated for development of high-performance construction materials. Various specimens of polymer concrete were prepared using unsaturated polyester resin as the polymer-binder with the various dosage of calcium carbonate as microfiller (5~20 wt %) and fine aggregate(10~50 wt %). For the evaluation of the physical properties of polymer concretes, tests such as compressive strength, flexural strength, water absorption test, hot water immersion test, acid resistance test and pore size distribution analysis were conducted. As a result, it is concluded that compressive and flexural strengths of polymer concretes increased up to 4 times than those of conventional cement concrete. Whereas the compressive and flexural strengths of polymer concretes tested after hot water immersion, compared with those of polymer concretes tested before hot water immersion, decreased about 67%, 47%, respectively. By hot water immersion, total pore volume and porosity(%) of polymer concretes were remarkable increased due to decomposition of polymer binder. And also, it is showed that water absorption(%) and weight loss(%) of polymer concrete specimens by acid immersion, compared with those of ordinary portland cement concrete, decreased about 1/100, 1/27, respectively.

• Polymer(Korea)
• /
• v.38 no.6
• /
• pp.760-766
• /
• 2014

Bead type super-absorbent resins to be used for release-control were prepared by modification of the inverse suspension polymerization, and their physical properties were characterized. Acrylic acid and acrylamide were used as monomers, and N,N-methylenebisacrylamide was used as crosslinker, controlling the viscosity of monomer solution by adding hydroxyethylcellulose (HEC). SEM studies of the synthesized beads verified that the bead surfaces had many pores with their diameters of several tens nm. The bead sizes were in the range of $500{\sim}3000{\mu}m$, depending on the viscosity of the monomer solution. Both absorbent amount and absorbent rate of the beads were inversely proportional to the bead size, and the maximum water absorbent amount of 1 g beads was determined to be ca. 170~200 g for 5 hrs. The absorbent rate was also dependent on pH change of the aqueous solution, exhibiting the maximum rate in pH ranging from 5 to 11. The absorbent rate decreased as the concentration of salt (NaCl and $MgCl_2$) or ethanol and ethylene glycol increased. Release time of the water absorbed into the bead resins was 700 hrs, confirming the usefulness of the resin for the good release-control materials.

• Polymer(Korea)
• /
• v.37 no.4
• /
• pp.478-485
• /
• 2013

In this study, hydrogels with fast swelling and high absorbent properties were prepared using biopolymers approved as a food additive and their swelling properties were characterized. To improve the swelling properties of conventional hydrogels, we formed gas bubbles using a foaming agent in the process of preparing hydrogels and characterized in terms of equilibrium swelling ratio, swelling kinetics and cytotoxicity. In particular, alginate hydrogels observed by a digital microscope have an open-pore channels structure with the sizes of hundreds micrometers. Also, the cell viability of all hydrogels were found to be much higher than that of poly(acrylic acid).