• Electrical & Electronic Materials
• /
• v.7 no.1
• /
• pp.7-14
• /
• 1994

Structural and optical characteristics in $SnO_2$/a-Se/Al sample by aging variation and applying constant voltage had been investigated. a-Se was varied with monoclinic structure and its surface was greatly exchanged. Its capacitance was first decreased and then increased and its photo-current, photo-voltage and photo-capacitance were increased gradually with day and applying voltage. From the results, crystallization of a-Se and dopant trap level formation had been identified. Also, it was acknowledged $SnO_2$/a-Se/Al sample is useful in photovoltaic and solid thin film cell.

• Korean Journal of Materials Research
• /
• v.6 no.2
• /
• pp.166-174
• /
• 1996

경제적이고 단순성의 공정특성을 갖는 닥터 블레이드법을 이용하여 평판형 고체산화물 연료전지의 고체전해질용 이트리아 안정화 지르코니아 박막을 제조하였다. 슬러리의 최적 제조조건과 그린 필름의 최적 소성조건을 얻었으며, 이 제조 조건에서 제조된 전해질의 결정구조, 미세구조 그리고 전기적 성질을 각각 X-선 회절, 주사전자현미경 그리고 교류 임피던스 분석기를 이용하여 조사하였다. 동량의 8mol% 이트리아를 첨가한 경우, 닥터 블레이드법에 의해 제조된 이트리아 안정화 지르크니아 박막은 금형가압성형법에 의해 제조된 이트리아 안정화 지르코니아 펠렛과 거의 비슷한 전기전도도를 나타내었다. 닥터 블레이드법에 의해 제조된 이트리아 안정화 지르크니아 박막의 경우, 8mol%이트리아를 첨가한 경우의 전도도가 3mol%이트리아를 첨가한 경우 보다 993K 이상과 523K 8mol% 이트리아를 첨가한 경우의 전도도가 3mol%이트리아를 첨가한 경우의 전도도가 3mol%이트리아를 첨가한 경우 보다 993K이상과 523K이하의 온도에서는 더 높고, 523-933K사이의 온도구간에서는 낮게 나타났다. 게다가, 모든 시편에 있어서 전체 전도도에 대한 벌크 전도도의 기여도에 대한 기여도보다 더 크게 나타났다.

• Journal of the Korean Electrochemical Society
• /
• v.8 no.4
• /
• pp.181-185
• /
• 2005

Lithium cobalt oxide thin film cathode, having thickness of $2.9{\mu}m$ with area of $4cm^2$, was deposited on platinum patterned alumina substrate by radio frequency magnetron sputtering. Li/Co molar ratio, which is an important factor for battery performance, was measured as a function of argon working pressure and applied R.F. power. Constant current charge and discharge performances were characterized with high rate discharge and cycling behavior. Using AC impedance analysis, internal resistance of the thin film battery was measured and simulated by proposed equivalent circuit model.

• Journal of the Korean Electrochemical Society
• /
• v.3 no.4
• /
• pp.219-223
• /
• 2000

All-solid state lithium rechargeable thin film batteries were fabricated with the configuration of$Cu_{0.5}V_2O_5/Lipon/Li$ using sequential thin film techniques. Copper vanadium oxide thin films and Lipon thin films were prepared by DC reactive dual source magnetron sputtering and RF magnetron sputtering, respectively. According to XRD analysis, we found out that copper vanadium oxide thin films were amorphous. The electrochemical behaviour of them was examined in half cell system using EC : DMC(1:1 in IM $LiPF_5$) liquid electrolyte. The ionic conductivity of Lipon thin film was $1.02\times10^{-6}S/cm$ at $25^{\circ}C$ and $Cu_{0.5}V_2O_5/Lipon/Li$ cell showed that the discharge capacity was about $50{\mu}Ah/cm^2{\mu}m$ beyond 500cyc1es.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2011.02a
• /
• pp.112-112
• /
• 2011

유기박막 트랜지스터(Organic Thin Film Transistor: OTFT)는 낮은 공정비용과 기존의 고체 실리콘 트랜지스터로서 실혐 할 수 없는 플렉시블 디스플레이, 스마트카드, 태양전지 등의 매우 넓은 활용범위로 각광받고 있는 연구 분야 중 하나이다. 본 연구에서는 열 증발 증착장비(Thermal Evaporator)를 이용하여 펜타센을 활성층으로 사용한 유기박막 트랜지스터를 제작하였다. Heavily doped된 N형 실리콘 기판을 메탄올, 에탄올, 불산 처리를 하여 세척을 한 후 PECVD를 이용하여 SiO2를 200 nm 증착하였다. 그 후 열 증발 증착 장비를 사용하여 펜타센을 활성층으로 사용하였고, 분말 형태의 펜타센의 질량을 15~60 mg으로 조절하여 활성층의 두께를 조절하였다. 펜타센 증착 후 100도에서 열처리를 하고, 그 후 Shadow Mask를 이용하여 전극을 150nm 증착하였다. 이때 전극은 Au, Al, Ni 세가지 종류를 사용하였다. 펜타센의 질량을 조절하여 증착한 활성층의 두께는 60 mg일 때 약 60 nm, 45 mg일 때 약 45 nm로 1:1의 비율로 올라가는 것을 확인 할 수 있었고, 펜타센의 두께가 30 nm일 때 특성이 가장 잘 나오는 것을 볼 수 있었다. 펜타센의 두께가 두꺼울수록 게이트에서 인가되는 전압의 필드가 제대로 걸리지 않아 특성이 나쁘게 나온 것으로 보인다. 또한 활성층을 30 nm로 고정하고 전극의 종류를 바꿔가며 전기적 특성(캐리어 이동도, 문턱전압, 전달특성 등)을 측정 했을 때 전극으로 Al보다는 Au와 Ni를 사용했을 때 전기적 특성이 더 우수하게 나오는 것을 볼 수 있었다. 메탈과 펜타센과의 일함수 차이에 따른 결과로 보여진다.

• Transactions of the Korean Society of Mechanical Engineers B
• /
• v.36 no.9
• /
• pp.931-935
• /
• 2012

In this study, we fabricate and investigate low-temperature solid oxide fuel cells with a ceramic substrate/porous metal/ceramic/porous metal structure. To realize low-temperature operation in solid oxide fuel cells, the membrane should be fabricated to have a thickness of the order of a few hundreds nanometers to minimize IR loss. Yttrium-doped barium zirconate (BYZ), a proton conductor, was used as the electrolyte. We deposited a 350-nm-thick Pt (anode) layer on a porous substrate by sputter deposition. We also deposited a 1-${\mu}m$-thick BYZ layer on the Pt anode using pulsed laser deposition (PLD). Finally, we deposited a 200-nm-thick Pt (cathode) layer on the BYZ electrolyte by sputter deposition. The open circuit voltage (OCV) is 0.806 V, and the maximum power density is 11.9 mW/$cm^2$ at $350^{\circ}C$. Even though a fully dense electrolyte is deposited via PLD, a cross-sectional transmission electron microscopy (TEM) image reveals many voids and defects.

• Journal of the Korean Ceramic Society
• /
• v.36 no.8
• /
• pp.791-798
• /
• 1999

The preparation method of yttria-stabilized zirconia(YSZ) thin film for an anode support type solid oxide fuel cell(SOFC) by electrophoretic deposition(EPD) and dip-coating was studied. And the difference in both preparation method was investigated through basic understanding of processing parameters which may significantly affect weight microstruxcture and defect of film. In dip-coating the thickness of film increased with time until 30 s and then the weight of film decreased with time due to particle falling off from the coagulated film. In EPD although the weight of film increased with time and applied constant-current sagging of the film was observed when the applied current was less that 0.035 mA/$cm^2$ and more than 120 s. Since YSZ thin film by EPD on porous substrate was dense smooth and homogeneous it was expected to be suitable for the electrolyte of an anode support type SOFC.

• 한국전기화학회:학술대회논문집
• /
• 2004.06a
• /
• pp.261-264
• /
• 2004

• Journal of the Korean Ceramic Society
• /
• v.41 no.8
• /
• pp.593-598
• /
• 2004

To make the all-solid-state lithium thin film battery having less than 1 fm in thickness, LiCoO$_2$ thin films were deposited on Pt/TiO$_2$/SiO$_2$/Si substrate as a function of Li/Co mole ratio and the deposition temperature by Pulsed Laser Deposition (PLD). Especially, LiCoO$_2$ thin films deposited at 50$0^{\circ}C$ with target of Li/Co=1.2 mole ratio show an initial discharge capacity of 53 $\mu$Ah/cm$^2$-$\mu$m and capacity retention of 67.6％. The microstructural and electrochemical properies of (Li, La)TiO3 thin films grown on LiCoO$_2$Pt/TiO$_2$/SiO$_2$/Si structures by Pulsed Laser Deposition (PLD) were investigated at various deposition temperatures. The thin films grown at 10$0^{\circ}C$ show an initial discharge capacity of approximately 51 $\mu$Ah/cm$^2$-$\mu$m and moreover show excellent discharge capacity retention of 90％ after 100 cycles. An amorphous (Li, La)TiO$_3$ solid electrolyte is possible for application to solid electrolyte for all-solid-state lithium thin film battery below 1 $\mu$m.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2010.08a
• /
• pp.270-270
• /
• 2010

4족 반도체 원소 양자점들은 원소가 가지고 있는 반도체적 성질과, 양자점에서 나타나는 quantum confinements 적인 특성 때문에 전자재료나 광학적 분야, 특히 태양전지 분야에서 그 쓰임이 대두되고 있다. 이러한 4족 반도체 원소의 양자점들을 만들기 위한 여러 방법들이 시도되고 있는데, 그 중에서 특히 절연체 박막에 4족 반도체 원소의 양자점들을 만드는 방법에는 이온주입, PVD, 그리고 CVD 를 통한 multi-layer 증착후 열처리 과정을 반드시 포함하는 Stranski- krastanov 방법이 주로 사용되고 있다. 본 실험에서는 고체원소 이온주입이라는 방법을 통해 절연체 박막의 증착과 이온주입이 한 진공용기 내에서 연속공정으로 이루어 지면서, 별도의 열처리 과정 없이 결정화된 게르마늄 양자점을 만들어 보았다. 이는 (X-ray diffraction) XRD와 Raman spectroscopy로 결정화된 게르마늄을 확인할 수 있었으며, (X-ray photoelectron spectroscopy)XPS 데이터로도 순수한 게르마늄이 표면에서 깊이 방향으로 약 $1,000\;{\AA}$ 만큼 게르마늄 양자점들이 만들어 짐을 알 수 있었다. 마지막으로 (High resolution transmittance electron microscopy) HRTEM으로 그 양자점의 크기와 분포도 그리고 결정성을 알아 보았다.