• Journal of the Korean Ceramic Society
• /
• v.35 no.6
• /
• pp.543-550
• /
• 1998

A process for the preparation of spherical tungsten oxide powders by the emulsion evaporation method was developed. The characteristics of the powders thus prepared were examined by means of TGA X-ray diffraction SEM and image analysis. The emulsion was prepared by fast mixing of tungsten containing aque-ous phase and the organic phase which contained kerosene surfactant and paraffin oil. The precursor was made by evaporating the emulsion in the kerosene bath at $160^{\circ}C$ and then calcined at $650^{\circ}C$ in order to pro-duce tungsten oxide powders. The average particle size of the tungsten oxide powders was $0.5\;\mu\textrm{m}$ and their shapes were spherical. Water-in-oil type emulsion wasmore advantageous to make less agglmerated. $W_{3}$ powders than the oil-in-water type emulsion for the emulsion evaporation experiments. As the HLB value of the surfactant increased and the concentration of tungsten ions in the aqueous phase decreased the mean particle size of tungsten oxide powders decreased whereas agglomeration increased. The optimum con-centration of Span 80 was 8 percent by volume and the optimum stirring speed in the emulsion formation was 5000 rpm in order to obtain find less agglomerated $W_{3}$ powders.

• Journal of the Korean Applied Science and Technology
• /
• v.34 no.1
• /
• pp.50-57
• /
• 2017

Zinc oxide is, one of metal oxide semiconductor, harmless to human and environment-friendly. It has excellent chemical and thermal stability properties. Wurtzite-zinc oxide is a large band gap energy of 3.37 eV and high exciton binding energy of 60 meV. It can be applied to various fields, such as solar cells, degradation of the dye waste, the gas sensor. The photocatalytic activity of zinc oxide is varied according to the particle shape and change of crystallinity. Therefore, It is very important to specify the additives and the experimental variables. In this study, the zinc oxide were synthesized by using a microwave assisted hydrothermal synthesis. The precursor was used as the zinc nitrate, the pH value was controlled as 11 by NaOH. Surfactants are the ethanolamine, cetyltrimethylammonium bromide, sodium dodecyl sulfate, sorbitan monooleate was added by changing the concentration. The composite particles had the shape of a star-like, curcular cone, seed shape, flake-sphere. Physical and chemical properties of the obtained zinc oxide was characterized using x-ray diffractometer, field emission scanning electron microscopy, thermogravimetric analysis and optical properties was characterized using UV-visible spectroscopy, photoluminescence and raman spectroscopy.