• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.32 no.5
• /
• pp.212-217
• /
• 2022

Large thermal stress due to the difference between silicon carbide and graphite's coefficients of thermal expansion could be formed during crystal growing process of silicon carbide (SiC) at high temperature. The large thermal stress could separate the SiC seed crystals from graphite components, which bring about the drop of the seed crystal during crystal growth. However, the bonding properties of SiC seed crystal module has hardly reported so far. In this study, SiC and graphite were bonded using 3 types of bonding agents and a three-point bending tests using a mixed-mode flexure test were conducted for the bonded samples to evaluate the bonding characteristics between SiC and graphite. Raman spectroscopy, X-ray Photoelectron Spectroscopy, and X-ray Computed Tomography were used to analyze the bonding characteristics and the microstructures of the SiC-graphite interfaces bonded with the bonding agents. As results, an excellent bonding agent was chosen to fabricate SiC seed crystal module with 50 mm in diameter. An SiC single crystal with 50 mm in diameter was successfully grown without falling out during top seeded solution growth of SiC at high temperature.

• The korean journal of orthodontics
• /
• v.31 no.2 s.85
• /
• pp.173-185
• /
• 2001

The orthodontic osseointegrated titanium implant, a kind of intraoral skeletal anchorage can be an alternative to tooth-borne anchorage, in case that the conventional tooth-borne anchorage is not available or the anchorage is critical. This study was conducted to elucidate the effect of early loading on the osseointegration of the orthodontic titanium implant and the healing process of the impaired bone at the site of implant after removing it. In two adult beagle dogs24 osseointegrated titanium implants were inserted into the alveolar bone, with 12 implants placed in each dog. In dog1, 6 out of 12 implants were loaded with 200-300gm of force immediately after placing, and the remaining 6 implants were not loaded for 4weeks. In dog2, all 12 implants had healing period of 4weeks, and then were loaded with 200-300gm of force for another 4weeks. Following an observation period of 4 and 8 weeks, the animals were sacrificed. Then the implants and the surrounding bone of dog1 and dog2 were removed, respectively. Undecalcified sections along the long axis of implant were made and the degree of osseointegration was examined under the light microscope. The results were as follows. 1. In the histologic features of tissues around implants anchored in dog1, there was no difference between immediately loaded implants and unloaded implants. Immature woven bone was ingrowing into the thread spaces from the original compacta and in direct contact with the implant surface in part. 2. The premature loading just after 4weeks healing period did not halt the progress of the osseointegration between bone and implant surface. The woven bone around the implants was maturing into the lamellar bone which resembled the structure of the original compacta at the end of 8weeks observation period. 3. Most implants with the inflammed surrounding mucosa were lost or mobile. The mobile implants were encapsulated by fibrous connective tissue which separated the implant surface from the bone. 4. The impaired bone at the site of the implant failed to anchor was showing recovery without inflammatory reaction 2weeks after removing, with the immaure woven bone lined by active osteoblasts and osteoid. Based on the results of this study, the integration of this orthodontic implant seemed to be impaired by the inflammation of the tissue surrounding the Implant rather than by early loading on implant, and increased with time lapsed after placing the implant. The use of implant described in this report can be recommended as an orthodontic anchorage unit immediately after insertion under the careful control of orthodontic force applied and plaque.

• The korean journal of orthodontics
• /
• v.33 no.4 s.99
• /
• pp.307-317
• /
• 2003

Conventional osseointegrated titanium implants have many limitations; large size, limited location for placement of the implant, severity of the surgery, discomfort of initial healing, difficulty of oral hygiene and uncontrollable force direction. Recently titanium miniscrew and miniplate have been used for an alternative to conventional dental implant. But in relation to miniplate, miniscrew has disadvantages in that more potential inflammation, light orthodontic force application and limited orthodontic application. This study was conducted to evaluate the effectiveness of miniplate by observing the reactions of peri-implant tissues to early orthodontic and orthopedic loading of titanium miniplate. In four adult beagle dogs 10 miniplates were inserted into the alveolar bone using 20 osseointegrated titanium screws. 4 miniplates were placed in two dogs(dogA, B) and 6 miniplates in two dogs(dogC, D). In dogA, B miniplates were loaded with 200gm of force immediately after placement for 15 weeks. In dogc, D, miniplates were loaded with 400gm of force immediately after placement for 8 weeks. Miniplates of dogA were removed, dogA was healed for 4 weeks, and the area which was removed of miniscrew was examined. Following an observation period, the miniplates including miniscrews and the surrounding bone of dogB and dogC, D were removed, respectively. Undecalcified section along the long axis of miniscrews were made and the degree of osseointegration was examined under the light microscope. The results were as follows. 1. In the histologic features there was direct contact between bone and miniscrew in all groups except one, dogC control group. The loaded miniscrew demonstrated only a slight increase of the osseous proximaty when compared with unloaded miniscrew 2. There was no significant difference of the osseointegration of Peri-miniscrew surface between dogB and dogC, D. But dogB showed slightly more increased bone apposition than dogC, D 3. The gingiva overlapping the miniplate and miniscrew showed no inflammatory sign in clinical and histological aspects. 4. The impaled hard and soft tissues at the area which was removed of miniscrews showed good healing without inflammatory reaction. 5. The mobility showed slight increase in un-loaded miniplate but that was insignificant. Based on the results of this study, miniplate(C-tube) can be used as a firm osseous orthodontic and orthopedic anchorage unit immediately after insertion.

• Journal of the Korean GEO-environmental Society
• /
• v.22 no.10
• /
• pp.21-29
• /
• 2021

Most concrete gravity-type dams in and out of the country were constructed by column method to control cracks caused by concrete hydration heat generated during construction, resulting in a certain level of leakage after impoundment through various causes, such as contraction joints and construction joints. However, due to the characteristics of concrete structures that shrink and expand according to temperature, concrete dams have vertical joints and drains to allow penetration. PVC waterproof shows excellent effects in completion of the dam, which however increases the possibility of interfacial failure due to different thermal expansion. Other causes of penetration may include problems with quality control during installation, generation of cracks due to heat of hydration of concrete, waterproofing methods, etc. In the case of Bohyunsan Dam in Yeongcheon, North Gyeongsang Province, the amount of drainage in the gallery was checked and underwater, and it was confirmed that there are many penetrations from drainage holes connected to vertical joints, and that some of the PVC waterproofs are not fully operated. As a new method to prevent penetration through vertical joints, D.S.I.M. (Dam Sealing Innovation Method) developed by World E&C was applied to Bohyunsan Dam and checked the amount of drainage in the gallery. As a result of first testing three most leaking vertical joints, the drain in the gallery was reduced by 87% on the average and then applied to the remaining 13 locations, which showed a 83% reduction effect based on the total drain in the gallery. Summing up these results, it was found that D.S.I.M. preventing water leakage from the upstream face is a valid construction method to reduce the water see-through and penetration quantity seen in downstream faces of concrete dams. If D.S.I.M. is applied to other concrete dams at domestic and abroad, it is expected that it will be very effective to prevent water leakage through vertical joints that are visible from downstream faces.