• 한국주조공학회지
• /
• 제20권4호
• /
• pp.269-276
• /
• 2000

So far, the study on semi-solid process has been carried out to develop and research new advanced materials without some casting defects. In this study, A356 billets consisted of various dendritic shapes were prepared using electro-magnetic stirring process continuously. As-cast respectively has liquidus temperature of $625.6^{\circ}C$ and solidus temperature of $573.55^{\circ}C$ A356 slugs were reheated homogeneously at different temperatures of 580, 590 and $605^{\circ}C$, followed by squeezing in a mold insulated with applied pressures(0, 25, 50 and 70 MPa). In order to investigate on aging responce for casts, 50 MPa squeezed specimen among all specimens was prepared in aging treatments, which conditions are aging temperature of $160^{\circ}C$ and holding times of 0, 45, 90, 270, 360, 720, 1440 and 2880 min after solution treatment ($540^{\circ}C$ for 10 hr). SSM ingot with the output velocity of 150mm/min appeared more spheroidal shape and fine structure than that with the output velocity of 250 mm/min. According to increasing in reheating temperature, numbers of fatigue cycles, U.T.S and elongation increased at same time.

• 원자력산업
• /
• 제23권3호통권241호
• /
• pp.42-48
• /
• 2003

가압 경수로는 원통형의 원자로 용기 안에서 핵물질을 반응시켜 고온$\cdot$고압의 물을 생성하는데 이 원자로 용기는 환형 주조물들을 서로 용접하여 만들어진다. 이 원자로 용기의 건전성을 확인하기 위해서는 용접부위에 결함이 발생되었는지를 주기적으로 정확하게 검사해야 한다. 한국원자력연구소는 원자력발전소의 핵심 기기인 원자로 용기의 용접부 결함을 수중에서 자동으로 검사, 탐지할 수 있는 $\ulcorner$원자로 자동 탐상 시스템$\lrcorner$을 개발하여, 울진 원전 6호기용 원자로 용기에서 실증 실험을 수행하였다. 이 원자로 자동 탐상 시스템은 물방개처럼 생긴 수중 탐상 로봇이 그 핵심으로서 이 로봇은 원자로 용기의 내벽을 타고 다니면서 수중 초음파 검사를 수행할 수 있는 획기적인 시스템이다. 본고에서는 개발된 원자로 자동 탐상 시스템을 소개하고자 한다.

• 한국재료학회지
• /
• 제10권1호
• /
• pp.69-76
• /
• 2000

반응고 금속의 반응용 성형법은 그 우수한 성형성으로 생산공정에 있어 주조나 단조와 같은 일반 성형법에 비해 많은 장점을 가지고 있는 반면, 정밀한 공정 변수 제어가 요구되므로 실용화에 있어 크게 제한 받고 있다. 본 연구에서는 반응고 금속인 A356합금을 사용하여 밀폐형 가압 성형 전후의 기계적 특성의 변화를 관찰하여, 가압 성형시의 정확한 공정 변수 제어가 이루어지지 않았을 경우에 일어날 수 있는 기계적 특성의 감소 원인이 가압 성형에 의한 미세조직의 응집과 조대화에 있음을 미세조직과 파단면 관찰을 통하여 규명하였다. 또한 가압 성형 후 본 연구에서 \`반응고 열처리\`라 명명한 후 처리 공정을 적용하여 인장 특성을 향상시킬수 있었다.

• 한국산학기술학회논문지
• /
• 제11권5호
• /
• pp.1547-1551
• /
• 2010

통상의 은합금 장신구 재료로 쓰이는 925 은합금 (Ag-7.5wt%Cu)의 가공 중 고온산화에 의한 변색 또는 착용 중 산화에 의한 색변화를 방지하기 위해서 Ag-5wt%Ge-2.5wt%Cu, 5wt%In-2.5wt%Cu의 새로운 조성을 제안하였다. 전체는 기존 925 은합금의 조성을 유지하여 기존 7.5wt%Cu합금원소를 Ge, In으로 대치하여 기존 925 은합금과 비교하여 주조공정 시의 형상변화와 주조능, 가공경화에 의한 물성과 내식성 변화를 확인하였다. 새로이 제안된 Ge, In 은합금은 기존 925은합금과 동일하거나 우수한 주조특성을 보였고, 특히 가공 중에 생기는 가공경화능력이 우수하여 내구성이 증가하였고 고온 내식성과 신체 착용 시의 내부식성이 향상됨을 확인하였다.

• 한국자동차공학회논문집
• /
• 제11권5호
• /
• pp.140-146
• /
• 2003

Metal matrix composites had generated a lot of interest in recent time because of their high specific strength and stiffness in specific properties. It was also highlighted as the material of frontier industry because strength, heat-resistance, corrosion-resistance and wear-resistance were superiored. In this study, the strength properties of $Al_{18}B_{4}O_{33}$/AC4CH composites were represented mixing the binder of $SiO_2$. It was also fabricated by squeeze casting. $Al_{18}B_{4}O_{33}$/AC4CH was fabricated at the melt temperature of $760^{\circ}C$, the perform temperature of $700^{\circ}C$ and mold temperature of $200^{\circ}C$ under the pressure of 83.4MPa. Consequently, fatigue life was observed roughly in the order of AC4CH> nobiner> $SiO_2$, independently on crack propagation direction and stress ratio.

• 한국화재소방학회논문지
• /
• 제26권4호
• /
• pp.18-23
• /
• 2012

이산화탄소 주조법에서 사용되고 있는 방법을 응용하여 목질내에 규산겔과 탄산소다, 이산화규소가 석출된 목재를 제조한 후 외부 복사열원(20, 25, 35 및 50 $kW/m^2$)에 따른 점화시간, 점화온도, 질량감소속도, 임계열유속을 측정하였다. 연구결과, 물유리와 이산화탄소를 이용한 가압함침 처리된 목재는 Pre-Flashover 단계에서의 복사열원(20 $kW/m^2$ 이하)에서 난연성능이 있음을 확인할 수 있었다. 향후 지속적인 연구를 통해 우수한 배합비율을 찾는다면 난연목재로서의 활용가능성이 있다고 판단된다.

• 한국주조공학회지
• /
• 제14권3호
• /
• pp.248-257
• /
• 1994

Research in heat transfer and solidification commonly involves experimentation and mathematical modeling with associated numerical analysis and computation. Inverse problems in heat transfer are part of this paradigm. During the solidification of metal casting, an interfacial heat transfer resistance exists at the boundary between the casting and the mold, and this heat transfer resistance usually varies with time. In the case of the squeeze casting the contact heat transfer resistance is decreased by pressure and ideal contact is almost accomplished. In the present work, heat transfer coefficient, which is inverse value of the heat transfer resistance, was used for convenience. A numerical technique, Non-Linear Estimation has been adopted for calculation of the casting/mold interfacial heat transfer coefficient during the squeeze casting process. In this method, the measured temperature data from experiment were used. The computational results were applied to the analysis of heat transfer and solidification.

• 한국주조공학회지
• /
• 제15권2호
• /
• pp.138-145
• /
• 1995

The mechanical properties of $Al/Al_2O_3$ composites have been investigated in relation with manufacturing factors such as applied pressure of casting and binder amount of preform. It was found that tensile strength increases with an increase of applied pressure, but decreases with binder amount. Increase of tensile strength is attributable to refinement of microstructure, improvement of intefacial bonding between $Al_2O_3$ short fiber and matrix, decrease of porosity in the matrix. Due to the high thermal stability of alumina short fiber, tensile strength of composites at $150^{\circ}C$ was superior to matrix alloy at room temperature. To evaluate the strength of composites, modified Kelly-Tyson's equation was introduced. Manufacturing factor M was obtained calculating from experimental data. M values were increased with applied pressure, but decreased with binder amount. The initiation of microcrack appeared to be at interface and reinforcement colony. Amount of micro-dimple was increased with applied pressure, and interfacial debonding phenomenon was remarkable with an increase of binder amount.

• 한국주조공학회지
• /
• 제21권3호
• /
• pp.163-178
• /
• 2001

The squeeze infiltration process is potentially of considerable industrial importance. The performance enhancements resulting from incorporation of short alumina fiber into aluminum are well documented. These are particularly significant for certain automobile components. Aluminum matrix composite automotive parts, such as diesel engine pistons or engine blocks are produced using squeeze casting apparatus or pressure die-casting apparatus. But the solidification process gets complicated with manufacturing parameters and the factors for porosity formation have not fully understood yet. In this study the formation of porosity during squeeze infiltration has been studied experimentally to achieve an improved understanding of the squeeze infiltration process for manufacture of short-fiber-reinforced components, particularly the mechanism of porosity formation. Al-based MMCs produced under a range of conditions were examined metallographically and the porosity characterised;a kind of matrix, an initial temperature of melt, and a volume fraction of reinforcement. The densimetry and the microscopic image analysis were done to measure the amount of porosity. A correlation between manufacturing parameters and defects was investigated through these.

• 한국재료학회지
• /
• 제9권7호
• /
• pp.715-723
• /
• 1999

마그네슘은 20여년간 자동차 산업에서 휠소재로 사용되어 왔다. 마그네슘 휠은 무게가 알루미늄 휠보다 25% 가벼워서 주행성이 우수하다. 이 연구의 목적은 사형주조 및 영구금형주조 공정에 의한 AZ91D 합금제 췰을 개발하는 것이다 보호개스$(SF_6+CO_2)$를 사용하는 비플럭스 용해기술을 적용하여 용탕의 산화와 불순물의 유입을 배제하였다 마그네슘 용탕은 가압식 펌프시스템을 사용하여 가열된 파이프를 통하여 모울드에 자동으로 공급된다. 열처리 및 인고트의 조성에 따른 AZ91B 합금제 휠의 기계적 특성을 조사하였다.