• Journal of the Korean Ceramic Society
• /
• v.36 no.12
• /
• pp.1390-1395
• /
• 1999

Zr(Y,Ce)O2 TZP ceramics were prepared by sintering compacts of 3 mol% Y2O3-TZP(3Y-TZP) powders with different amount of 12 mol% CeO2-TZP(12Ce-TZP) in air at 140$0^{\circ}C$ for 2 h. The phase changes microstructure and mechanical properties of Zr(Y. Ce)O2 TZP after hydrothermal aging(20$0^{\circ}C$ 5h) were investigated. Although an addition of 12Ce-TZP accelerated the grain growth of Zr(Y, Ce)O2 TZP it restrained the transformation of tetragonal to the monoclinic phase during aging. The degradation in mechanical properties of sintered bodies was governed by the formed monoclinic phase and chemical composition. Induced Vickers indentation crack was propagated intergranually. From SEM observation of the fracture surfaces the pull-out of individual grain was confirmed.

• Journal of the Korean Ceramic Society
• /
• v.33 no.10
• /
• pp.1177-1185
• /
• 1996

Y-TZP/Ce-TZP ceramics having relative sintered densities of>95% average grain sizes of 0.36$\mu\textrm{m}$ microhar-dness of 1150 kg/mm2 fracture strength of 390-830 MPa and toughness of 6.4-10.2 MPa$.$mm1/2 were prepared by conventional sintering of 3 mol% Y2O3-ZrO2 and 12 mol% CeO2-ZrO2 powders at 1400 and 1500$^{\circ}C$ The average grain sizes of Y-TZP/Ce-TZP ceramics were mainly governed by those of Ce-TZP. White increasing Ce-TZP content toughness increased while microhardness and fracture strength decreased. With comparing microhardness and toughness fracture strength was more sensitive on not only grain size but also other factors such as microstructural and compositional variations. The densification of Y-TZP/Ce-TZP cermaics was not greatly affected by composition and soaking time at temperature over 1400$^{\circ}C$ With increasing CE-TZP content the stability of t-ZrO2 decreased under thermal aging in air whereas increased in hydrothermal atmosphere and aqueous solution.

• Journal of the Korean Ceramic Society
• /
• v.28 no.7
• /
• pp.541-548
• /
• 1991

Sinterability and stability of TZP ceramics co-stabilized by 12 mol% CeO2 and divalent or trivalent oxides less than 1 mol% were investigated. Divalent and trivalent oxides increased stability of tetragonal ZrO2. 100% tetragonal ZrO2 phase was obtained by doping 12 mol% CeO2 and 0.2 mol% CaO and MgO respectively when sintering was carried out at 1500$^{\circ}C$ for 2 hours. Divalent and trivalent oxides improved sinterability and inhibit grain growth of ZrO2. And it was found that CaO was the most effective sintering aid and grain growth inhibitor for ZrO2 in this study. Incorporation of divalent and trivalent oxides into 12Ce-TZP increased the strength of 12Ce-TZP and particulary 12Ce, 0.4Ca-TZP exhibited a flexural strength of about twofold greater than 12Ce-TZP.

• Journal of the Korean Ceramic Society
• /
• v.27 no.2
• /
• pp.233-243
• /
• 1990

For theinvestigation of MgO addition effect on 12Ce-TZP ceramics, MgO-CeO2-ZrO2 ceramics was fabricated using commercial powders under sintering condition of 130$0^{\circ}C$-1$600^{\circ}C$ for 2hr. Fully tetragonal phase could be obtained by proper heat treatment and MgO addition amount. Minor cubic phase was appeared in relatively high MgO content composition at each sintering temperature. As alloying amount of MgO increased, tetragonal stability increased and grain size decreased. Grain size dependence on MgO content was verified by SEM observation of fractured surface. Surface bloating was observed from the 2 m/o to 6m/o in the temperature range of 150$0^{\circ}C$ to 1$600^{\circ}C$. In spite of very porous microstructure owing to surface bloating, 100% TZP could be maintained in 2.0m/o MgO composition by heat treatment of 150$0^{\circ}C$. This result indicated that MgO was more powerful stabilizer than CeO2. Mechanical proprties of MgO-CeO2-ZrO2 ceramics were consistent with the stability observation of tetragonal phase very well.

• Journal of the Korean Ceramic Society
• /
• v.47 no.5
• /
• pp.439-444
• /
• 2010

The usual ceramic process of mixing and milling in state of oxide of $ZrO_2$ and $CeO_2$ was adopted in wet process to manufacture Ce-TZP in this study. The maximum dispersion point of every slurry manufactured with mixture of $ZrO_2$ and $CeO_2$ was neat at pH10. The stable slurry in average particle size of 90 nm can be manufactured when it is dispersed with use of ammonia water and polycarboxylic acid ammonium. The sintered Ce-TZP ceramics manufactured with addition of $CeO_2$ less than 10 mol% was progressed to the fracture of specimen due to the monoclinic phase existence more than 30% at the room temperature. More than 99% of tetragonal phase was created for the sintered body with addition of $CeO_2$ beyond 18 mol%, but the mechanical property degrade on the entire specimen was brought due to the $CeO_2$ existing above 3%. Consequently, the optimal Ce-TZP combined in oxide state was identified in 16 mol% of $CeO_2$ contents.

• Journal of the Korean Ceramic Society
• /
• v.31 no.7
• /
• pp.703-714
• /
• 1994

Sintering and microstructure of Ce-TZP/Al2O3 composite with $\alpha$-Al2O3 matrix containing dispersed 5~50 vol% ZrO2 were discussed. Sintered density was increased with elevating forming pressure in range of 6~300 MPa and about >99.2% of theoretical density was obtained at 1$600^{\circ}C$ for 2h in case of 300 MPa of 6~300 MPa uniaxially cold-pressed compacts containing 20 vol% ZrO2. All kinds of different batch composition exhibited nearly the same shrinkage behaviour with end-point shrinkage between 20 and 24%, and had the maximum shrinkage rate (0.41~0.54%/min) around 140$0^{\circ}C$. Grain growth was occurred faster in $\alpha$-Al2O3 than in {{{{ gamma }}-Al2O3 starting matrix during sintering at 1$600^{\circ}C$. Bimodal pore size distribution of interaglomerate pores with size of 0.03~0.2 ${\mu}{\textrm}{m}$ and of interaglomerate pores with size of around 60 ${\mu}{\textrm}{m}$ was obtained in Ce-TZP/$\alpha$-Al2O3 composite sintered at 130$0^{\circ}C$. But unimodal pore size distribution with around 0.1 ${\mu}{\textrm}{m}$ was observed in Ce-TZP/{{{{ gamma }}-Al2O3 composite sintered at the same temperature. Microcracks were occurred due to the tlongrightarrowm transformation of ZrO2 on cooling process.

• Journal of the Korean Ceramic Society
• /
• v.26 no.5
• /
• pp.719-727
• /
• 1989

By using commercial zirconia powder CeO2-ZrO2 ceramics containing 8~16mol% CeO2 was made by heat treatment at 1350~155$0^{\circ}C$ for 1~10hr. The minimum amount of CeO2 for obtaining complete tetragonal phase was 12mol%, and in the tetragonal phase region fracture toughness of Ce-TZP was decreased with increasing CeO2 content and the maximum value was obtained when 12mol% CeO2 was added. The bending strength goes through maximum at 14mol% CeO2. Fracture mode of Ce-TZP transformed from intergranular to transgranular fracture with increasing CeO2 content, so the morphology of fracture surface of 16mol% Ce-TZP was wholly transgranular and this tendency was independent on grain size. The crystal structure of the 12mol% Ce-TZP was monoclinic with fringes along the grain boundaries which are lying in the particular plane from the TEM observation. The chemical composition of the sintered body was homogeneous as a whole and some amorphism or air pocket was observed at the triple junction.

• Korean Journal of Materials Research
• /
• v.20 no.7
• /
• pp.379-384
• /
• 2010

The usual ceramic process of mixing and milling in state of oxides $ZrO_2$ and $CeO_2$ was adopted in this study in a wet process to manufacture Ce-TZP. $CeO_2$-$ZrO_2$ ceramics containing 8~20 mol% $CeO_2$ were made by heat treatment at $1250\sim1500^{\circ}C$ for 5hr. The maximum dispersion point of every slurry manufactured with a mixture of $ZrO_2$ and $CeO_2$ was neat at pH10. A stable slurry with average particle size of 90 nm can be manufactured when it is dispersed with the use of ammonia water and polycarboxylic acid ammonium. The sintered Ce-TZP ceramics manufactured with the addition of $CeO_2$ in a concentration of less than 10 mol% progressed to the fracture of the specimen due to the existence of a monoclinic phase of more than 30% at room temperature. More than 99% of the tetragonal phase was created for the sintered body with the addition of $CeO_2$ beyond 18 mol%, but the degradation of the mechanical properties on the entire specimen was brought about due to the $CeO_2$ existing in a percentage above 3%. Consequently, the optimal Ce-TZP level combined in the oxide state was identified to be 16 mol% of $CeO_2$ contents.

• Journal of the Korean Ceramic Society
• /
• v.27 no.1
• /
• pp.55-61
• /
• 1990

Effect of Al2O3 addition on the mechanical properties and microstructure of Ce-TZP were studied. 12, 14, 16Ce-TZP containing 0-40wt% Al2O3 were prepared by sintering at 155$0^{\circ}C$ for 2h. in air. Density, linear shrinkage, bending strength, Vickers hardness, microstructuer and the amount of stress induced phase transformation were examined. Vickers hardness increased linearly with increasing amounts of Al2O3. The amount of transformation and fracture toughness decreased linearly with increasing amount of Al2O3. Linear shrinkage and relative density decreased with increasing Al2O3 content in all composition of Ce-TZP. Grain growth of Ce-TZP was inhibited by Al2O3 dispersion and fracture mode of Ce-TZP/Al2O3 composites transformed from intergranular to transgranular fracture as the amount of Al2O3 increased. TEM observation revealed that Al2O3 particles were located mainly at grain boundaries of ZrO2.

• The Korean Journal of Ceramics
• /
• v.5 no.1
• /
• pp.1-11
• /
• 1999

The effect of aliovalent dopents, $Nb_3O_5$ and MnO, on the grain growth kinetics of 12 mol% ceria stabilized tetragonal zirconia polycrystals (Ce-TZP) was studied. All specimens were sintered at $1550^{\circ}C$ for 20 minutes prior to annealing at different temperatures to study grain growth kinetics. Grain growth kinetics of Ce-TZP and 1 mol% $Nb_2O_5$ doped Ce-TZP (Ce-TZP/$Nb_3O_5$) during annealing at 1475, 1550, and $1600^{\circ}C$ adequately matched with square law $(D^2-D_\;o^2=k_at)$. However, grain growth in 1 mol% MnO suppressed grain growth in Ce-TZP by drag force exerted by $Mn^{+2}$ ions which segregated strongly to the positively-charged grain boundaries of Ce-TZP, $Nb_2O_5$ enhanced grain growth by increasing the concentration of vacancies of $Zr^{+4}$ ion and $Ce^{+4}$ ions. Surface analysis with X-ray photoelectron spectroscopy (XPS) showed the segregation of Mn+2 ions to grain boundaries. The kinetics of grain growth obtained in the base Ce-TZP and the Ce-TZPs with the aliovalent dopants were examined in the context of impurity drag effect and space charge effect.