• 한국초전도ㆍ저온공학회논문지
• /
• 제11권2호
• /
• pp.7-10
• /
• 2009

Effects of $BaCO_3$ purity on the superconducting properties of top seeded melt growth (TSMG) processed $Y_{1+x}Ba_2Cu_3O_{7-y}$ (Y1+x, x=0.1 and 0.2) superconductors were investigated. $YBa_2Cu_3O_{7-y}$ (Y123) powder prepared using $BaCO_3$ with 99.75% purity and commercially available Y123 powder of 99.9% were used for the fabrication of single Y123 grain superconductors. $T_c$ values of the Y1+x samples prepared using low purity Y123 powder were slightly lower than those of the samples prepared using a high purity powder. In addition to the lower $T_c$, an anomalous peak effect in the intermediate magnetic fields was observed in Y1+x samples prepared using the low purity $BaCO_3$ powder. The slight decrease in $T_c$ and the anomalous peak effect are ascribed to the possible incorporation of a Y123 phase with impurity elements such as strontium and calcium included in the $BaCO_3$powder of 99.7%. The result suggests that the low purity $BaCO_3$ powder of a low price can be used as a raw power for the fabrication of single grain YBCO bulk superconductors.

• 한국진공학회지
• /
• 제1권3호
• /
• pp.389-394
• /
• 1992

용액분무법으로 (100) MgO 단결정 기판위에 YBa2Cu3O7-x 초전도박막을 제조하 였다. YBa2Cu3O7-x 초전도 박막의 Y, Ba, Cu 원자의 상대적인 비는 EDX의 검출 한계내에 서 1 : 2 : 3이었고, 이는 분무 용액속의 금속이온의 비와 같았다. YBa2Cu3O7-x 초전도 박 막의 결정구조는 단일 상의 사방구조였으며, 기판에 수직인 c축의 방향으로 grain이 성장되 었고, 격자상수 c0는 11.678$\AA$였다. 95$0^{\circ}C$의 공기중에서 10분간 열처리한 박막의 Tc-on=100K, Tc-zero=80K, Jc=2.5 $\times$ 104A/cm2였고, 95$0^{\circ}C$의 흐르는 산소분위기에서 10분간 열처리한 박막의 Tc-on=103K, Tc-zero=80K, Jc=1.0 $\times$ 105A/cm2였다. 초전도 박막의 미세구 조, grain 크기와 grain 경계폭은 제조후 열처리(post-annealing) 시간과 가스 분위기에 강 한 영향을 받았다.

• 한국재료학회:학술대회논문집
• /
• 한국재료학회 1992년도 추계학술발표강연 및 논문개요집
• /
• pp.16-16
• /
• 1992

We have studied the effect of platinum addition on the supercon ducting properties of YB $a_2$C $u_3$$O_{7-x}$ (123) compound and elucidated the mechanism of fine dispersion of $Y_2$BaCu $O_{5}$(211) particles in YB $a_2$C $u_3$$O_{7-x}$ superconductor prepared by melting method from the metallurgical point of view. In this study, BaCu $O_2$ and CuO-rich phase unreacted during the peritecitc reaction markedly decreased by the 211 powder addition. The 211 particle of Pt-fee sintered samples exhibited 8~10$\mu$m in size, but in 1wt%Pt-added sample, 211 particles were finely dispersed in 123 matrix and the size of 211 particle was about 1~2$\mu$m. And, the critical temperature( $T_{c. zero}$) of Pt doped samples was 91.5K and the transport critical current density ( $J_{c}$) of Pt-doped samples was much more than 10$^4$A/$\textrm{cm}^2$. The high $J_{c}$ and fine dispersion of 211 particles of Pt doped YB $a_2$C $u_3$$O_{7-x}$ superconductor are attributed to $Ba_4$CuP $t_2$ $O_{8}$ compounds formed during the partial melting, which were considered als nucleation sites of 211 particles, rather than Pt inself.han Pt inself.

• 한국자기학회지
• /
• 제2권3호
• /
• pp.228-232
• /
• 1992

고온초전도체 $Y_1Ba_2Cu_3O_{7-y}$의 grain을 높은 자기장에서 정렬시켜 여러가지 자기적 특성을 조사하였다. Grain이 정렬된 초전도체는 단결정과 같이 Cu-O layer에 수직, 수평 방향에 대해 자기이방성을 가진다. 2~77 K의 온도영역에서 측정한 lower critical field$(H_{c1})$은 온도가 증가하면서 선형적으로 감소하였는데, Cu-O layer에 대하여 외부 자기장이 수직인 경우가 더욱 급격히 감소하였다. 온도변화에 따른 자율화$(4{\pi}\;X)$의 측정으로부터 극저온의 자화율이 -1에 가까운 값을 가진다는 것을 알 수 있었다. 또한 이 자화 곡선을 London의 공식과 two-fluid model을 이용해 최소자승법으로 fitting하여 절대 영도에서 침투깊이$({\lambda}_0)$를 구하였다. 또한 2 K에서 외부 자기장에 따른 자화곡선을 측정하였으며, Bean의 critical state model을 이용한 임계전류밀도$(J_c)$의 계산으로부터 grain내부는 단결정 수준의 높은 $(J_c)$를 가지고 있음을 알 수 있었다.

• 대한화학회지
• /
• 제36권1호
• /
• pp.16-23
• /
• 1992

고온초전도체 $YBa_2Cu_3O_{7-{\delta}}$에서 Y를 Eu로 치환시킨 $(Y_{1-x}Eu_x)Ba_2Cu_3O_{7-{\delta}}$ (x = 0.0, 0.2, 0.4, 0.6, 0.8, 1.0)를 제조한 후 물성변화를 관찰하였다. X-선 회절분석결과 모든 시료가 사방정계 구조를 갖고 있었으며 x값이 증가함에 따라 격자상수 a, b 및 c도 증가하였다. 전기저항과 자화율측정으로부터 순수한 90K 이상의 고온초전도상이 생성되었음을 알았으며, x값이 커짐에 따라 임계온도가 상승하였다. 주사전자현미경을 사용하여 구한 낟알크기와 자화측정결과로부터 각각의 시료들에 대한 부피 반자성자화율을 구하였으며, x값이 커질수록 이 값은 감소하였다. Eu의 농도가 증가함에 따라 결정격자내의 Ba의 양이 감소됨을 EPMA로 확인하였으며, 이것은 부피반자성 자화율의 감소에 직접적인 영향을 주는 것으로 판단된다.

• 한국결정성장학회지
• /
• 제21권5호
• /
• pp.199-204
• /
• 2011

존멜팅법을 이용해서 $(YSmNd)_{1.8}Ba_{2.4}Cu_{3.4}O_{7-x}$계 고온초전도체를 대기 중에서 용융성장실험을 하였다. 존멜팅법의 최적용융온도는 $1100^{\circ}C$였으며 성장속도는 3.5 mm/h 였다. 한 방향으로 용융성장 된 (YSN)1.8 초전도체는 XRD, 광학현미경, TEM을 이용하여 미세구조를 관찰하였으며 SQUID magnetometer와 직접전류수송법을 이용해 초전도특성을 평가하였다. 특히 용융성장 된 (YSN)1.8 초전도체의 광학현미경에 의한 미세구조 관측 결과 초전도상인 (YSN)123 matrix내에 비초전도상인 (YSN)211 inclusions이 균질하게 분포되어 있는 것이 관측되었다. 또한 용융성장 된 (YSN)1.8 초전도체는 90 K 이상의 임계온도 특성을 보였으며 액체질소 안에서 직접전류수송법으로 측정한 결과 수송전류 830 A에서 $3.93{\times}10^4$(A/$cm^2$)를 갖는 높은 임계전류밀도 특성을 보였다.

• 동굴
• /
• 제76호
• /
• pp.49-55
• /
• 2006

The submicron $YBa_2Cu_3O_x$ powder was prepared by the sol-gel method. The particle size is distributed from 0.2 to 1.0 ${\mu}m$, which benefits to eliminate the micro-cracks formed in the $YBa_2Cu_3O_x$ films deposited by electrophoresis. The powder was single phase of $YBa_2Cu_3O_x$ examined by X-ray diffraction. In the sol-gel process the citrate gel was formed from citric acid and nitrate solution of $Y_2O_3$, $Ba(NO_3)_2$ and CuO. When pH values were adjusted to 6.4-6.7, $Ba(NO_3)_2$ could be dissolved in the citrate solution completely. Appropriate evaporative temperature of the sol-gel formation is discussed. Acetone is used as electrophoreticsolution, in which some water and iodine (0.2 g/1) and polyethylene glycol (2 vol. %) are added. The concentrations of $YBa_2Cu_3O_x$ powders is 20g/l. The thickness of deposited film could be more than 50 ${\mu}m$ in 3 minutes of depositing time. The most EPD films could be 90K zero resistance and the Jc values were over 1000A/cm2 (0 H, 77 K).

• E2M - 전기 전자와 첨단 소재
• /
• 제5권2호
• /
• pp.189-197
• /
• 1992

고온 초전도체 $Y_{1}$Ba$_{2}$Cu$_{3}$O$_{7-y}$에서 Y를 Sm으로 치환시켰을 때의 자기 임계 전류밀도와 저항은 각각 30K와 80-160K의 온도에서 측정되었다. 그리고 X-선 회절분석 및 적외선 투과율 측정은 실온에서 수행되었으며 시료들은 고상 반응법에 의해서 제조되었다. 93K근에의 값을 갖는 초전도 전이온도 T$_{c}$는 치환양에 따라 거의 변하지 않았다. 시료들의 결정구조는 X-선 회절무늬로 부터 모두 직방정계임이 판명되었다. 적외선 투과율 측정에서 날카로운 peak들은 472.78-618.53$cm^{-1}$ /범위에 있었다. 이것은 특이할 정도로의 low-lying plasmalike edge와 낮은 에너지의 전자적인 여기가 존재함을 나타내는 것이다. 자기 임계 전류밀도는 $10^{3}$~$10^{4}$A/$cm^{2}$범위에 있었다. 전이온도 T$_{c}$에 상자성 불순물의 영향이 거의 없는 것으로 보아 123phase에서 Y가 고온 초전도성에 주된 역할을 하지 않음을 알수 있었다.다.

• 한국세라믹학회지
• /
• 제35권1호
• /
• pp.79-87
• /
• 1998

Melt spun YbBa2Cu3Agx(x=0, 5, 12, 16 and 53) precursor alloy ribbons were oxidized at 263-330$^{\circ}C$ and treated at 820$^{\circ}C$, 855$^{\circ}C$ and 885$^{\circ}C$ under 1.0 atm oxygen pressure. In the ribbons treated at 820$^{\circ}C$, 855$^{\circ}C$and 885$^{\circ}C$ 1-2-4 phase (YbBa2Cu4O8) and 1-2-3 phase (YbBa2Cu3O{{{{ OMICRON _7-$\delta$ }})were formed respectively. The shape of 1-2-4 phase was distorted or ellipsoid. The 2-4-7 and 1-2-3 phases tooked the shape of bar. All the ribbons showed zero critical current density Jc at 77K in zero magnetic field. By considering the shape and the highest critical temperature (among the three phases) of the 1-2-3 phase we tried to increase the critical current density of the ribbons treated at 885$^{\circ}C$ by press deformation. About tenribbons were stacked and coupled by press deformation and then treated at 885$^{\circ}C$ These 1-2-3 phase did not show any texture in any of the ribbons. However they exhibited weak texture in the multilayered specimens. Among the multilayered specimens YbBa2Cu3Ag16 exhibited a Jc of 180 A/cm2 Among the above ribbons YbBa2Cu3Ag16 ribbon has the optimum composition to produce textured superconducting oxide with improved Jc by press deformation. Onset critical temperatures Ton of the multilayered YbBa2Cu3Agx(x=5, 12, 16 and 53) were measured as 88-90 K.

• 한국세라믹학회지
• /
• 제28권3호
• /
• pp.243-251
• /
• 1991

High-Tc YBa2Cu3O7-x superconducting thin films have been prepared by single-target off-axis RF magnetron sputtering. Optimal ratio of Y : Ba : Cu of the single-target was determined as 1 : 1.65 : 3.35 in order to obtain the stoichiometric films. Tc, crystalline phase, and microstructures of the surface and cross-section of the ex-situ YBa2Cu3O7-x thin films on MgO(100) had a Tc, zero of 80K, and the films on LaAlO3/Si had a Tc, on-set of 90 K and a Tc, zero of 70 K.