A thinner film has superior electrical properties and a better amorphous structure. Amorphous structures can be effective in improving conductivity through a depletion effect. Research is needed on the Schottky contact, where potential barriers are formed, as a way to identify these characteristics. $SiO_2/SnO_2$ thin films were prepared to examine the amorphous structure and Schottky contact, $SiO_2$ thin films were prepared using Ar = 20 sccm. $SnO_2$ thin films were deposited using mixed gas with a flow rate of argon and oxygen at 20 sccm, and $SnO_2$ thin films were added by magnetron sputtering and treated at $100^{\circ}C$ and $150^{\circ}C$. To identify the conditions under which the amorphous structure was constructed, the XRD patterns were investigated and C-V and I-V measurements were taken to make Al electrodes and perform electrical analysis. The depletion layer was formed by the recombination of electrons and holes through the heat treatment process. $SiO_2/SnO_2$ thin films confirmed that the pores were well formed when heat treated at $100^{\circ}C$ and an electric current was applied over the micro area. An amorphous $SiO_2/SnO_2$ thin film with heat treatment at $100^{\circ}C$ showed no reflection at $33^{\circ}\;2{\theta}$ in the XRD pattern, and a reflection at $44^{\circ}2\;{\theta}$. The macroscopic view (-30 V

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.13 no.9
• /
• pp.745-750
• /
• 2000

The (S $r_{0.85}$C $a_{0.15}$) Ti $O_3$(SCT) thin films are deposited on Pt-coated electrode (Pt/TiN/ $SiO_2$/Si) using RF sputtering method at various deposition temperature. The crystallinity of SCT thin films were increased with increase of deposition temperature in the temperature range of 200~500[$^{\circ}C$]. Also, the composition of SCT thin films were closed to stoichiometry (1.080~1.111 in A/B ratio). V-I characteristics of SCT thin films show the increasing leakage current with the increases of deposition temperature. The conduction mechanism of the SCT thin films observed in the temperature range of 25~100[$^{\circ}C$] can be divided into four regions with different mechanism by the increasing current. The region I below 0.8[MV/cm]shows the ohmic conduction. The region II between 0.9~2[MV/cm] is in proportion to J∝ $E^{1.5}$ , the region III between 2~4[MV/cm] can be explained by the Child’s law, and the region IV above 4[MV/cm]is dominated by the tunneling effect.ect.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.14 no.9
• /
• pp.695-699
• /
• 2001

Cerium dioxide (CeO$_2$) was used as the intermediate layer between the ferroelectric thin film and Si substrate in a metal-ferroelectric-semiconductor field effect transistor (MFSFET), to improve the interface property by preventing the interdiffusion of the ferroelectric material and the Si substrate. In this study, CeO$_2$ thin films were etched with a CF$_4$/Ar gas combination in inductively coupled plasma (ICP). The maximum etch rate of CeO$_2$ thin films was 270$\AA$/min under CF$_4$/(CF$_4$+Ar) of 0.2, 600 W/-200V, 15 mTorr, and $25^{\circ}C$. The selectivities of CeO$_2$ to PR and SBT were 0.21, 0.25, respectively. The surface reaction in the etching of CeO$_2$ thin films was investigated with x-ray photoelectron spectroscopy (XPS). There is a chemical reaction between Ce and F. Compounds such as Ce-F$_{x}$ remains on the surface of CeO$_2$ thin films. Those products can be removed by Ar ion bombardment. The results of secondary ion mass spectrometry (SIMS) were consistent with those of XPS. Scanning electron microscopy (SEM) was used to examine etched profiles of CeO$_2$ thin films. The etch profile of over-etched CeO$_2$ films with the 0.5${\mu}{\textrm}{m}$ line was approximately 65$^{\circ}$.>.

• Journal of the Korean Electrochemical Society
• /
• v.3 no.4
• /
• pp.219-223
• /
• 2000

All-solid state lithium rechargeable thin film batteries were fabricated with the configuration of$Cu_{0.5}V_2O_5/Lipon/Li$ using sequential thin film techniques. Copper vanadium oxide thin films and Lipon thin films were prepared by DC reactive dual source magnetron sputtering and RF magnetron sputtering, respectively. According to XRD analysis, we found out that copper vanadium oxide thin films were amorphous. The electrochemical behaviour of them was examined in half cell system using EC : DMC(1:1 in IM $LiPF_5$) liquid electrolyte. The ionic conductivity of Lipon thin film was $1.02\times10^{-6}S/cm$ at $25^{\circ}C$ and $Cu_{0.5}V_2O_5/Lipon/Li$ cell showed that the discharge capacity was about $50{\mu}Ah/cm^2{\mu}m$ beyond 500cyc1es.

• Korean Journal of Materials Research
• /
• v.2 no.5
• /
• pp.353-359
• /
• 1992

Thermal oxidation and plasma enhanced chemical vapor deposition of tantalum oxide thin films on p-type (100) Si substrates were studied to examine the dielectric nature of T$a_2O_5$ as a Al/T$a_2O_5$/p-Si capacitor. Microstructure and dielectric properties of the capacitors were investigated by XRD, AES, high frequency C-V analyzer, I-V meter and TEM. XRD analysis showed that the structure of T$a_2O_5$ films were amorphous, but the films were crystallized to hexagonal $\delta$-T$a_2O_5$ by 65$0^{\circ}C$ thermal oxidation treatment. It was found that the stoichiometry of the films was more or less close to 2 : 5. Leakage current density and relative dielectric constant of thermal oxidation T$a_2O_5$ film at 60$0^{\circ}C$ was 5.0${ imes}10^{-6}$/A/c$m^2 and 31.5, respectively. In the case of PECVD T$a_2O_5$film deposited at 0.47W/c$m^2 they were 2.5${ imes}10^{-5}$/A/$ extrm{cm}^2$ and 24.0, respectively. The morphology of the films and interfaces were investigated by TEM.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2007.06a
• /
• pp.99-100
• /
• 2007

ZnO films on $Al_2O_3$ substrates were grown using a pulsed laser deposition method. Through photoluminescence (PL) and X-ray diffraction (XRD) measurements, the optimum growth conditions for the ZnO growth were established. The results of the XRD measurements indicate that ZnO films were strongly oriented to the c-axis of the hexagonal structure and epitaxially crystallized under constraints created by the substrate. The full width half maximum for a theta curve of the (0002) peak was $0.201^{\circ}$. Also, from the PL measurements, the grown ZnO films were observed to give free exciton behaviour, which indicates a high quality of the epilayer. The Hall mobility and carrier density of the ZnO films at 293 K were estimated to be $299\;cm^2/V\;s$ and $8.27\;{\times}\;10^{16}\;cm^{-3}$, respectively. The absorption spectra revealed that the temperature dependance of the optical band gap on the ZnO films was $E_g(T)\;=\;3.439\;eV\;-\;(5.30\;{\times}\;10^{-4}\;ev/K)T^2(367\;+\;T)$.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2004.07b
• /
• pp.809-812
• /
• 2004

(Pb,Sr)TiO3 (PST) thin films were fabricated by using the alkoxide-based sol-gel method. The PST stock solution was made and then spin-coated onto a PUTi/SiO2/Si substrate. The coating and drying procedures were repeated several times, and the PST thin films were sintered at 450-650 C for 1 h. All PST thin films showed dense and homogeneous structures without the presence of any rosette structure. The thicknesses of the PST thin films were approximately 200 nm. The dielectric constant and the dielectric loss of the PST thin films sintered at 550 C were about 404 and 0.0023, respectively. The leakage current density of the PST thin film sintered at 550 C was 3.13 x 10-8 A/cm2 at 1 V.

• Transactions on Electrical and Electronic Materials
• /
• v.9 no.2
• /
• pp.67-72
• /
• 2008

Al-doped p-type ZnO thin films were fabricated by RF magnetron sputtering on n-Si (100) and homo-buffer layers in pure oxygen ambient. ZnO ceramic mixed with 2 wt% $Al_2O_3$ was selected as a sputtering target. XRD spectra show that the Al-doped ZnO thin films have ZnO crystal structure. Hall Effect experiments with Van der Pauw configuration show that p-type carrier concentrations are arranged from $1.66{\times}10^{16}$ to $4.04{\times}10^{18}\;cm^{-2}$, mobilities from 0.194 to $198\;cm^2V{-1}s^{-1}$ and resistivities from 0.0963 to $18.4\;{\Omega}cm$. FESEM cross section images of different parts of a p-type ZnO:Al thin film annealed at $800^{\circ}C$ show a compact structure. Measurement for same sample shows that density is $5.40\;cm^{-3}$ which is smaller than theoretically calculated value of $5.67\;cm^{-3}$. Photoluminescence (PL) spectra at 10 K show a shoulder peak of p-type ZnO film at about 3.117 eV which is ascribed to electron transition from donor level to acceptor level (DAP).

• Transactions on Electrical and Electronic Materials
• /
• v.8 no.2
• /
• pp.84-88
• /
• 2007

[ $Bi_{1.5}Zn_{1.0}Nb_{1.5}O_7$ ] (BZN), $Bi_2Mg_{2/3}Nb_{4/3}O_7$ (BMN), and $Bi_2Cu_{2/3}Nb_{4/3}O_7$ (BCN) pyrochlore thin films were prepared on $Cu/Ti/SiO_2/Si$ substrates by pulsed laser deposition and the micro-structural and electrical properties were characterized for embedded capacitor applications. The BZN, BMN, and BCN films deposited at $25\;^{\circ}C$ and $150\;^{\circ}C$, respectively show smooth surface morphologies and dielectric constants of about $39\;{\sim}\;58$. The high dielectric loss of the films deposited at $150\;^{\circ}C$ compared with films deposited at $25\;^{\circ}C$ was attributed to the defects existing at interface between the films and copper electrode by an oxidation of copper bottom electrode. The leakage current densities and breakdown voltages in 200 nm thick-BMN and BZN films deposited at $150\;^{\circ}C$ are approximately $2.5\;{\times}\;10^{-8}\;A/cm^2$ at 3 V and above 10 V, respectively. Both BZN and BMN films are considered to be suitable materials for embedded capacitor applications.

• Korean Journal of Materials Research
• /
• v.29 no.7
• /
• pp.456-462
• /
• 2019

ZnO thin-films are grown on a p-Si(111) substrate by RF sputtering. The effects of growth temperature and $O_2$ mixture ratio on the ZnO films are investigated by scanning electron microscopy (SEM), X-ray diffraction (XRD), and room-temperature photoluminescence (PL) measurements. All the grown ZnO thin films show a strong preferred orientation along the c-axis, with an intense ultraviolet emission centered at 377 nm. However, when $O_2$ is mixed with the sputtering gas, the half width at half maximum (FWHM) of the XRD peak increases and the deep-level defect-related emission PL band becomes pronounced. In addition, an n-ZnO/p-Si heterojunction diode is fabricated by photolithographic processes and characterized using its current-voltage (I-V) characteristic curve and photoresponsivity. The fabricated n-ZnO/p-Si heterojunction diode exhibits typical rectifying I-V characteristics, with turn-on voltage of about 1.1 V and ideality factor of 1.7. The ratio of current density at ${\pm}3V$ of the reverse and forward bias voltage is about $5.8{\times}10^3$, which demonstrates the switching performance of the fabricated diode. The photoresponse of the diode under illumination of chopped with 40 Hz white light source shows fast response time and recovery time of 0.5 msec and 0.4 msec, respectively.