• 한국세라믹학회지
• /
• 제33권10호
• /
• pp.1138-1146
• /
• 1996

Al2TiO5 powder was prepared by the sol-gel processing from th metal alkoxides ; aluminium sec-butoxide (Al(OC4H9)3 and tetraethyl orthotitanate (Ti(OC2H5)4) The particles of Al2TiO5 produced from alkoxides were measured to be below $1.5mutextrm{m}$ and mre than 90% weere below 1 ${\mu}{\textrm}{m}$ however those from commercial alumina and titania were over 0.5-7${\mu}{\textrm}{m}$ and only 60% were below 1${\mu}{\textrm}{m}$ and 90% were below 2.5${\mu}{\textrm}{m}$ Therefore Al2TiO5 powder produced from alkoxides had the narrower distributionin size than that produced from the commercial alumina and titania powders. The addition of mullite or Al2O3 powder to the prepared aluminum titanate inhibited the grain growth and this resulted in decreased and increase in density.

• 한국세라믹학회지
• /
• 제26권3호
• /
• pp.438-444
• /
• 1989

The role of TiC and the effect of Y2O3 addition on the densification, microstructure and mechanical properties of Al2O3-TiC composite have been studied. The amount of Y2O3 has been varied from 0 to 2 wt.% while keeping the TiC content at 10, 20 or 30 wt.%. The powder compacts have been sintered at 1,75$0^{\circ}C$ for various times in 1 atm Ar atmosphere and hot isostatically pressed (HIPed) at 1,$600^{\circ}C$ for 0.5h under 1,500atm Ar. Considerable increase in sintered density(over 95%) has been achieved by adding 0.5 wt.% Y2O3 in specimens containing high TiC volume. More addition of Y2O3 does not affect the densification. With increasing the sintering time from 0.5 to 4h, slight increase in density results. The growth of Al2O3 grain has been enhanced by Y2O3 addition ; this tendency is reduced with increasing TiC content because of grain boundary dragging effect of TiC particles. The hardness of specimens increases considerably by an addition of 0.5wt.% Y2O3 owing to the density increase. Further addition of Y2O3 has no effect on hardness. Fracture toughness augments with TiC content by crack deflection around the particles. By adding 0.5wt.% Y2O3, all the specimens can be densified to isolated pore stage and thus can be HIPed to full densification and better mechanical property. In particular, the fracture toughness of Al2O3-30 TiC specimen increases about 50% by HIPing. Fully dense Al2O3-30 TiC with good mechanical properties can be prepared by normal Sintering/HIPing process.

• 공업화학
• /
• 제21권2호
• /
• pp.162-168
• /
• 2010

최근에 염료감응형 태양전지(dye-sensitized solar cells, DSSCs)의 에너지 변환 효율을 증가시키기 위한 방법으로 흡착된 염료에서 발생되는 광전자가 전해질 속의 산화/환원되는 요오드 이온($I_3^-/I^-$)과의 재결합(recombination)을 방지하기 위하여 발생된 광전자를 효율적으로 $TiO_{2}$ 전극을 통해 이동시키는 방법에 관한 연구가 활발히 연구되고 있다. 본 연구에서는 이러한 재결합을 방지하기 위하여, 졸-겔(sol-gel)법으로 합성한 보헤마이트(bohemite) 졸을 이용하여 $TiO_{2}$ 전극에 비해 높은 에너지 밴드갭(band-gap)을 가지고 있는 $Al_2O_3$가 코팅된 이중층의 다공질 나노 $TiO_{2}$ 전극을 제조하고 염료감응형 태양전지에 응용하였다. 특히, 다양한 입자의 크기가 조절된 보헤마이트 졸을 통해 최고의 에너지 변환 효율을 가진 $Al_2O_3$가 코팅된 $TiO_{2}$ 광전극 제조 조건을 조사하였다. 입자 크기 100 nm 보헤마이트 졸로부터 제조한 $Al_2O_3$가 코팅된 $TiO_{2}$ 전극이 순수 $TiO_{2}$로 제조한 광전극 층(7.5%)에 비해 높은 에너지 변환 효율(9.0%)을 보였다.

• 열처리공학회지
• /
• 제20권5호
• /
• pp.231-236
• /
• 2007

High velocity oxy-fuel (HVOF) spraying was used to coat Ti(Al,O)/$Al_2O_3$ powder onto the SS41 steel plate. Macrostructure of the coated specimen has been investigated by scanning electron micrograph (SEM). High temperature oxidation behavior of the coated specimen and SS41 steel have been studied. From the results of SEM observation, Ti(Al,O)/$Al_2O_3$ powder was coated well onto the substrate SS41 steel. Porosity onto the coated layer was only 0.38%. The oxidation results showed that Ti(Al,O)/$Al_2O_3$ powder coated SS41 steel have improved little oxidation resistance at $900^{\circ}C$ in air, but improved remarkably oxidation resistance at $800^{\circ}C $ in air compare to the substrate SS41 steel.

• 한국자원식물학회지
• /
• 제20권1호
• /
• pp.12-21
• /
• 2007

토양에서 화강암 지역은 $Al_2O_3,\;Na_2O$, 천매암 지역은 $Fe_2O_3,\;MnO,\;MgO$, 혈암 지역은 $SiO_2,\;CaO$에서 높았다. 이 화강암 지역과 천매암 토양의 원소 특성은 이들 토양 중의 광물 차이를 반영한다. 상관관계에서 화강암, 천매암, 혈암 3지역 공히, 정의 관계가 $Al_2O_3-K_2O,\;Fe_2O_3-MgO$ 쌍에서, 부의 관계가 $SiO_2-CaO$ 쌍에서 나타났다. 인삼에서 동일 연생 인삼의 지역적 비교 시 2, 3년에 관계없이 혈암 지역이 높은 함량 원소가, 화강암 지역이 낮은 함량의 원소가 많았다. 즉 2년생은 천매암 지역의 Fe, Ca, 혈암 지역의 Al, Mn, Na, Ti에서, 3년생은 화강암 지역의 Mn, Na, 천매암 지역의 Ca, 혈암 지역의 Al, Fe, Ti에서 높은 값이 나타났다. 같은 지역 인삼의 연생 차이별 비교에서 3지역 공히 2년생에서 Al, Na, Ti가 높았다. 또한 화강암 지역은 2년생의 Al, Mn, Mg, Na, Ti, 3년생의 Fe, Ca에서, 천매암 지역은 2년생의 Al, Fe, Mg, Ca, Na, Ti, 3년생은 Mn, K에서 높았다. 지상부의 무기성분 함량에 대한 2, 3년의 지역 별 비교에서 혈암 지역이 높은 원소가 많았고 화강암 지역이 낮은 원소가 많았다. 2년생의 경우 화강암 지역은 Ca, 천매암 지역은 Fe, Ca, 혈암 지역은 Al, Mn, Na, Ti에서, 3년생의 화강암 지역은 Mn, 천매암 지역은 Ca, 혈암 지역은 Al, Fe에서 높았다. 상관관계에서 2, 3년생의 경우 공히 Al-Ti, Mn-Na쌍에서 정의 관계가 나타났다. 뿌리의 무기성분 함량에서 2년생은 화강암 지역에서 높은 원소가 많았고, 천매암 지역이 낮은 원소가 많았다. 3년생은 혈암 지역에서 높은 원소가 많았고, 천매암 지역이 낮은 원소가 많았다. 즉 2년생은 화강암의 Al, Mn, Na, 천매암 지역의 Fe, Ca, 혈암지역의 Ti에서, 3년생은 화강암 지역의 Ca, Na, 혈암 지역의 Al, Fe, Mn, Ti에서 높았다. 2년생은 화강암 지역의 Fe, 천매암 지역의 Al, Mn, Na, Ti, 혈암 지역의 Ca, 3년생은 화강암 지역의 Fe, 천매암 지역의 Al, Mn, Na, Ti, 혈암 지역의 Ca, K에서 낮았다. 지상부와 뿌리 부분 비교에서 지역에 관계없이 수 배 차이로 Fe, Mn, Ca는 지상부가, Ti는 하부가 높았다. 지역에 관계없이 Mn, Ca, Fe, Al, Na, Ti 순서로 지상/하부 비율이 내려갔다. 토양과 인삼의 무기성분 함량관계에서 지역에 관계없이 Ca는 수 십 배의 차이로, Mn는 수 배에서 수 십 배 차이로 인삼이 높았고, Na, Fe, Ti, Al은 수배의 차이로 토양이 높았다. 인삼과 토양의 비에서 대부분 지역이 2년생이 크고 3년생이 작았으며, 지역에 관계없이 공히 Al, Mn, Na는 2년생이 크고 3년생이 작았다. 이 결과는 인삼의 연령이 증가함에 따라 토양 중 원소를 흡수하여, 더욱더 토양의 특성을 반영하기 때문으로 생각된다.

• 공업화학
• /
• 제31권4호
• /
• pp.390-397
• /
• 2020

To synthesize non-corrosive metallic gold colored α-Al₂O₃ nanoplate-TiO₂ core-shell pigments with controlled roughness, we systematically checked the morphological variation of the TiO₂ shell with the mole ratio of TiCl₄ and NaOH from 1 : 1 to 1 : 1.5, 1 : 2, 1 : 2.5, 1 : 3, 1 : 3.5, and 1 : 4. The more increased mole ratio of TiCl₄ and NaOH resulted in the smoother TiO₂ shell due to the promoted formation of anatase TiO₂ than that of the rutile one. By the heat-treatment of pigments at 500 ℃, we could improve the adhesiveness between TiO₂ shell and α-Al₂O₃ nanoplates without changing their topology and roughness. In addition, the α-Al₂O₃ nanoplate with the robust TiO₂ by heat-treatment exhibited comparable photo-stability against photo-catalytic degradation by UV exposure compared with the commercially available α-Al₂O₃/TiO₂ lustering pigment.

• 한국세라믹학회지
• /
• 제30권2호
• /
• pp.115-122
• /
• 1993

Transparent Al2O3 and TiO2 clear sols prepared by hydrolysis and subsequent peptization were mixed into wet gel. EDS analysis for this gel showed that wet gel was extremely homogeneous in chemical composition. Calcination of the wet gel at 120$0^{\circ}C$ for 50 minutes resulted in Al2O3-TiO2 nanocomposite powders where TiO2 particles of 101~102 nanometer were dispersed in the Al2O3 matrix. Both powders were sintered for 4 hours in the temperature range over 1500~1$650^{\circ}C$ with and without 5wt% MgO sintering aid. Among these sintered bodies, nanocomposite powder compacts sintered at 1$650^{\circ}C$ for 4 hours with 5wt% MgO showed the most dense structure with the grain size under 5${\mu}{\textrm}{m}$ and highest relative density of 98.2%.

• 한국세라믹학회지
• /
• 제47권6호
• /
• pp.498-502
• /
• 2010

Aluminium titanate($Al_2TiO_5$) has extremely anisotropic thermal expansion properties in single crystals, and polycrystalline material spontaneously microcracks in the cooling step after sintering process. These fine intergranular cracks limit the strength of the material, but provide an effective mechanism for absorbing strain energy during thermal shock and preventing catastrophic crack propagation. Furthermore, since machinable BN-ceramics used as an insulating substrate in current micro-electronic industry are very expensive, the development of new low-cost machinable substrate ceramics are consistently required. Therefore, cheap $Al_2TiO_5$-machinable ceramics was studied for the replacement of BN ceramics. $Al_2O_3-Al_2TiO_5$ ceramic composite was fabricated via in-situ reaction sintering. $Al_2O_3$ and $TiO_2$ powders were mixed with various mol-ratio and sintered at 1400 to $1600^{\circ}C$ for 1 h. Density, hardness and strength of sintered ceramics were systematically measured. Phase analysis and microstructures were observed by XRD and SEM, respectively. Machinability of each specimens was tested by micro-hole machining. The results of research showed that the $Al_2TiO_5$-composites could be used for low-cost machinable ceramics.

• 한국세라믹학회지
• /
• 제38권9호
• /
• pp.806-810
• /
• 2001

$La_{2/3}TiO_3$, $La_2Ti_2O_7$는 유전성을 갖는 특징으로 인해 여러 분야에 이용되고 있다. 본 연구는 perovskite 구조의 $La_{2/3}TiO_3$와 pyrochlore 구조의 $La_2Ti_2O_7$를 모체로 하여 $Al^{3+},\;Pr^{3+}$가 첨가된 형광체의 발광 특성을 알아보고자 하였다. 두 구조 모두 $Pr^{3+}의\;^1D_2{\rightarrow}^3H_4$ 전이에 의한 적색 발광을 나타내었다. 본 연구에서는 perovskite 구조의 $La_{2/3}TiO_3$:Pr 형광체의 에너지 전이 과정과 그 임계거리에 대한 조를 통해 에너지 전달체로서의 $Al^{3+}$의 역할을 제시하였다. 또한, perovskite 구조의 $La_{2/3}TiO_3$와 pyrochlore 구조의 $La_2Ti_2O_7$ 사이의 발광특성 차이를 알아보기 위해서 trap-involved process와 charge transfer band를 조사하였다.

• 한국분말야금학회:학술대회논문집
• /
• 한국분말야금학회 2006년도 Extended Abstracts of 2006 POWDER METALLURGY World Congress Part 1
• /
• pp.543-544
• /
• 2006

The effect of the additives, $Y_2O_3$ and MgO, on the sintering and properties of $Al_2O_3-TiC$ composites was investigated. It is known that MgO is used as additive for improving densification and $Y_2O_3$ is applied as sintering aid. In this study, the amounts of TiC were varied in the range of 30-47 wt%. The 0.5 wt% MgO and also varied amounts of $Y_2O_3$ from 0.3 to 1 wt% were added into the composites. The sintering of $Al_2O_3-TiC$ composites was performed in a graphite-heating element furnace at different sintering temperature, 1700 and $1900\;^{\circ}C$, for 2 hr under an argon atmosphere. The results demonstrated that the properties of the composites sintered at $1700\;^{\circ}C$ were much better than those sintered at $1900\;^{\circ}C$. The comparisons on physical properties, mechanical properties and microstructure of composites with and without additives were reported. Comparing with other samples, $Al_2O_3-30wt%TiC$ composites with 0.5wt% MgO and $1\;wt%Y_2O_3$ exhibited the highest density of approximately 98% of theoretical and flexural strength of 302 MPa.