• Proceedings of the Korean Radioactive Waste Society Conference
• /
• 2004.02a
• /
• pp.73-82
• /
• 2004

This paper studies the leaching behaviors of pyrochlore-rich synroc incorporated 46.8wt% simulated actinides waste under the five simulated geological disposal media, which included the bentonite, granite, granite ＋ ferroferric oxide, granite ＋ cement, bentonite ＋ ferroferric oxide, respectively. The mass loss rates reached to equilibrium after 182 day and was 10-7 g/$\textrm{mm}^2{\cdot}d$. That suggests the mass loss rate of pyrochlore-rich synroc, loaded 46.8wt% actinides waste, was very low. The surfaces of the leached specimens were analyzed by XRD, SEM/EDS. The experimental results show that the pyrochlore-rich synroc samples in the systems, which contained bentonite and cement, have two new phases formed on the leached specimens surface at $90^{\circ}C$ for 728d; The bentonite and cement can retard the elements leaching; $Fe_3O_4$ can speed the elements leaching; Expect for Ti ion depleted on the sample surface, other ion, such as U, Zr, AI, Ca, were in equable states and Ba ion was enriched during test time, which indicated the simulated disposal media have good ability to retard the leaching behavior of the pyrochlore-rich synroc.

• Transactions on Electrical and Electronic Materials
• /
• v.6 no.5
• /
• pp.238-242
• /
• 2005

The Pt counter electrode of a dye-sensitized solar cell (DSSC) plays a role in helping redox reaction of iodine ions in electrolyte, also, transferring electrons into electrolyte. In this case, it is expected that characteristics of Pt electrodes strongly depend on fabrication process and its surface condition. In this study, Pt electrodes were prepared by a electro-deposition and a RF magnetron sputtering. Electrochemical behavior of Pt electrodes was compared using cyclic-voltammetry and impedance spectroscopy. Surface morphology of Pt electrodes was investigated by FE-SEM and AFM. I-V characteristics of DSSC were measured and discussed in association with the surface properties of counter electrode. As a result, electrochemical properties of electro-deposited Pt electrode were superior to that of sputtered Pt electrode. This is likely that enlarged area of surface in electro-deposited Pt electrode in comparison with the case of sputtered Pt electrode playa role in enhancing such electrochemical properties.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2002.07b
• /
• pp.581-584
• /
• 2002

In this work, a CPW resonator was designed and fabricated to investigate the basic microwave properties, such as effective dielectric constant, of BST thin films. Their properties were used as basic data to simulate and design CPW tunable bandpass filter. We also report on gold/$Ba_{0.5}Sr_{0.5}TiO_3$(BST) ferroelectric thin film C-band tunable bandpass filters(BPFs) designed and fabricated on magnesium oxide substrates using CPW structure. The 2 pole filter was designed for a center frequency of 5.88 GHz with a bandwidth of 9 %. The BST based CPW filter offers a high sensitivity parameter as well as a low loss parameter. The tuning range for the bandpass filter with CPW structure was determined to be 170 MHz.

• Bulletin of the Korean Chemical Society
• /
• v.32 no.8
• /
• pp.2611-2616
• /
• 2011

We studied the physical properties of the mercaptopyruvic-acid layer formed on gold surfaces, which has the interactions with the titanium dioxide surface for design of gold- titanium dioxide distribution. Surface force measurements were performed, using the atomic force microscope (AFM), between the surfaces as a function of the salt concentration and pH value. The forces were analyzed with the DLVO (Derjaguin-Landau-Verwey-Overbeek) theory, to evaluate the potential and charge density of the surfaces quantitatively for each salt concentration and each pH value. The difference in the properties reflected the effect of the isoelectric point on the surface forces. The forces were interpreted for the evaluation with the law of mass action and the ionizable groups on the surface. The salt concentration dependence of the surface properties, found from the measurement at pH 8.0, was consistent with the prediction from the law. It was found that the mercaptopyruvic-acid layer had higher values for the surface charge densities and potentials than the titanium dioxide surfaces at pH 8, which may be attributed to the ionized-functional-groups of the mercaptopyruvic-acid layer.

• Journal of Environmental Science International
• /
• v.23 no.6
• /
• pp.1151-1156
• /
• 2014

The photocatalytic decomposition characteristics of single n-pentane, n-pentane mixed with methyl ethyl ketone (MEK), and n-pentane mixed with ethyl acetate (EA) by cylindrical UV reactor installed with $TiO_2$-coated perforated plane were studied. The effects of the residence time, the inlet gas concentration, and the oxygen concentration were investigated. The removal efficiency of n-pentane was increased with increasing the residence time and the oxygen concentration, but decreased with increasing the inlet concentration of n-pentane. The photocatalytic decomposition rates of single n-pentane, n-pentane mixed with MEK, and n-pentane mixed with EA fitted well on Langmuir-Hinshelwood kinetics equation. The maximum elimination capacities of single n-pentane, n-pentane mixed with MEK, and n-pentane mixed with EA were obtained to be $465g/m^3{\cdot}day$, $217g/m^3{\cdot}day$, and $320g/m^3{\cdot}day$, respectively. The presence of coexisting MEK and EA vapor had a negative effect on the photocatalytic decomposition of n-pentane and the negative effect of MEK was higher than that of EA.

• Journal of the Korean Ceramic Society
• /
• v.31 no.2
• /
• pp.155-160
• /
• 1994

PZT ceramics substituted by La3+ and Nd3+ were fabricated according to the formula: [Pb1-x(La or Nd)x][Zr0.58Ti0.42]1-x/4$\square$x/4O3(x=0.00, 0.02, 0.05, 0.08, 0.15, 0.20). The crystal structure and microstructure were investigated by XRD and SEM. It was observed that the phase transitions among rhombohedral, tetragonal, and cubic symmetry occured as the substitutional quantity increased. Dielectric constant, dissipation factor and piezoelectric coefficient (d33), of each sample were measured. The dielectric properties were changed as the substitutional quanity of rare earth ion increased. These changes could be explained by crystal structure and compositional fluctuaction. Its d33 was higher at tetragonal region near to phase boundry between rhombohedral and tetragonal, which was explained by reorientation of domain wall.

• 한국정보디스플레이학회:학술대회논문집
• /
• 2005.07b
• /
• pp.1572-1575
• /
• 2005

Poly(vinyl phenol)(PVP)/$TiO_2$ nanocomposite the films have been prepared incorporating metal alkoxide with vinyl polymer to obtain high dielectric constant gate insulating material for a organic thin film transistor. The surface composition, the morphology, and the thermal and electrical properties of the hybrid nanocomposite films were observed by ESCA, scanning electron microscopy (SEM), atomic force microscopy(AFM), and thermogravimetric analysis (TGA). Thin hybrid films exhibit much higher dielectric constants (7.79 at 40wt% metal alkoxide).

• Biotechnology and Bioprocess Engineering:BBE
• /
• v.11 no.3
• /
• pp.268-272
• /
• 2006

A dense, pellicular UpFront adsorbent ($p=1.5 g/cm^3$, UpFront Chromatography, Cophenhagen, Denmark) was characterized in terms of hydrodynamic properties and protein adsorption performance in expanded bed chromatography. Cibacron Blue 3GA was immobilised into the adsorbent and protein adsorption of bovine serum albumin (BSA) was selected to test the setup. The Bodenstein number and axial dispersion coefficient estimated for this dense pellicular adsorbent was 54 and $1.63{\times}10^{-5}m^2/s$, respectively, indicating a stable expanded bed. It could be shown that the BSA protein was captured by the adsorbent in the presence of 30% (w/v) of whole-yeast cells with an estimated dynamic binding capacity $(C/C_o = 0.01)$ of approximately 6.5 mg/mL adsorbent.

• The Transactions of the Korean Institute of Electrical Engineers C
• /
• v.55 no.9
• /
• pp.429-433
• /
• 2006

PZT(80/0) powder was prepared by a sol-gel method and PZT thick films were fabricated by the screen-printing method on the alumina substrates. The coating and drying procedure was repeated 4 times. And then the PZT(20/80) precusor solution was spin-coated on the PZT thick films. A concentration of a coating solution was 0.5mol/L and the number of coating was varied from 0 to 6. The porosity decreased and the grain size increased with increasing the number of coatings. The thickness of the PZT-6(6: number of coatings) films was about $60{\mu}m$. The relative dielectric constant increased and the dielectric loss decreased with increasing the number of PZT(20/80) sol coatings. The relative dielectric constant and dielectric loss of the PZT-6 thick film were 275 and 3.5%, respectively. The remanent polarization, coercive field and breakdown strength of the PZT-6 film were $19.8{\mu}C/cm^2$, 13.7kV/cm and 130kV/cm, respectively.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.19 no.12
• /
• pp.1106-1111
• /
• 2006

To improve warpage, delamination and the chemical reaction between 2 different co-fired materials, the bonding behavior with common glass was studied. As shown in the previous paper, the phenomenon of the infiltration is different with the composition of the glass. In particular, in the case of low temperature melting glass, infiltration is experimented in this study. GA-1 glass is infiltrated among $BaTiO_3$ particles below $800^{\circ}C$ and is made by glass/ceramic composite. Until the laminate is fired under $850^{\circ}C$, provskite phase is observed. Although in the case of GA-12 glass, the temperature of the glass infiltration is lower than it of GA-l glass, the perovskite phase already disappears at $800^{\circ}C$. As a result, GA-1 and GA-12 glasses are infiltrated among particles at low temperature, however, the chemical reactivity of the glass/ceramic and sintering temperature should be considered.