• Korean Chemical Engineering Research
• /
• v.46 no.3
• /
• pp.479-485
• /
• 2008

Porous $TiO_2$ nanostructured particles containing both mesopores and macropores were fabricated by utilizing an aerosol templating method from two kinds of starting materials (colloidal mixture of $TiO_2$ nanoparticles and PS particles, and that of TTIP solution and PS particles). The effects of mixing ratio of PS to $TiO_2$ and reactor temperature on the particle properties were investigated. When $TiO_2$ nanoparticles were used as starting materials, the increase of macropores number was observed by SEM and the specific surface area and total pore volume were increased from $31.6m^2/g$ to $39.1m^2/g$ and $0.068cm^3/g$ to $0.089cm^3/g$, respectively, by increasing the weight mixing ratio of $PS/TiO_2$ from 0.79 to 1.31. When TTIP was used as precursor, the specific surface area and mesopore volume of particles prepared at same condition decreased by 67% and 75%, respectively.

• Particle and aerosol research
• /
• v.5 no.1
• /
• pp.1-7
• /
• 2009

Fe- and V-doped titanium dioxide nanoparticles consisting of spherical primary nanoparticles were synthesized from a mixed liquid precursor by using the flame spray pyrolysis. The effects of dopant concentration on the powder properties such as morphology, crystal structure, and light adsorption were analyzed by TEM, XRD, and UV-Vis spectrophotometer, respectively. As the V/Ti molar ratio increased, pure anatase particles were synthesized. On the contrary, rutile phase particles were synthesized as the Fe/Ti ratio increased. Photocatalytic property of as-prepared $TiO_2:Fe,V$ nanoparticles was investigated by measuring the removal efficiency for volatile organic compounds (VOCs) under the irradiation of visible light. After 2 hrs under visible light, the removal efficiencies of benzene, p-xylene, ethylbenzene, and toluene were reached to 21.9%, 21.4%, 19.8% and 17.6% respectively.

• Korean Journal of Materials Research
• /
• v.12 no.3
• /
• pp.169-175
• /
• 2002

Semiconductive nano $(Ba_{1-x}Sb_x)TiO_3$ powders were synthesized by the hydrothermal process and Sb was simultaneously doped in the hydrothermal condition. $(Ba_{1-x}Sb_x)TiO_3$ powders obtained from optimum condition(at 20$0^{\circ}C$ for 3hr) exhibited spherical shape, high purity and nano size. The PTCR characteristics was observed when 0.1 and 0.2 mole% Sb were added and sintered at over 130$0^{\circ}C$ for 1 hour, respectively. And The ceramics exhibit the PTCR characteristics with a resistively jump $ratio($\rho$_{max}/$\rho$_{min})$ of about $10^4$. Also we found that PTCR characteristics were dependent on the microstructure.

• Korean Journal of Materials Research
• /
• v.24 no.1
• /
• pp.33-36
• /
• 2014

This study was aimed at synthesizing and characterizing cerium-doped titania. Cerium-doped anatase titania powders were prepared by sol-gel process, with ammonium (IV) nitrate and titanium (IV) butoxide as the raw materials. The characteristics of pure $TiO_2$ and cerium-doped $TiO_2$ were investigated by XRD, TG/DTA, FE-SEM, and UV-vis spectroscopy. The results of this study show that anatase type of $TiO_2$ was obtained in as-prepared and calcined $TiO_2$ and Ce-$TiO_2$ powder. A DTA curve was also observed as the crystallization temperature decreased with increasing cerium contents. We found that the crystallite size of the obtained anatase particles decreased from 55 nm to 25 nm and the particle size decreased with increasing cerium contents. Moreover, UV-vis spectra showed that anatase titania powders with various cerium contents effectively extend the light absorption properties to the visible region.

• Journal of the Korean Ceramic Society
• /
• v.37 no.7
• /
• pp.625-631
• /
• 2000

In this study, the characteristics and sinterablities of TiO2 powders which were fabricated on sol-gel process and supercritical fluid process were examined. The powders fabricated on sol-gel process were amorphous. The particle size and shape were changed with the amount of water used for hydrolysis of titanium ethoxide. The powders were changed from amorphous to crystalline by heating at 400℃. The crystalline anatase TiO2 powders were directly prepared in ethanol supercritical fluid condition that temperature was 270±3℃ and pressure was 7.3 MPa. It's primary crystalline size was 20 nm and agglomerated as spherical shape whose size was 0.7∼1㎛. The powders prepared on sol-gel process were not sintered densely at 900℃ because of abnormal grain growth. However, the powders which prepared on supercritical fluid process were sintered densely at the comparatively low temperature of 800℃ by ideal growth of grain, which are fired at 900℃.

• Bulletin of the Korean Chemical Society
• /
• v.30 no.1
• /
• pp.219-223
• /
• 2009

$TiO_2$ doped with $Er^{3+\;and\;Yb^{3+}$ was used for fabricating a scattering layer and a nano-crystalline $TiO_2$ electrode layer to be used in dye-sensitized solar cells. The material was prepared using a new sol-gel combustion hybrid method with acetylene black as fuel. The $Er^{3+}$-$Yb^{3+}$ co-doped titanium oxide powder synthesized at 700oC had embossed structure morphology with a size between 27 to 54 nm that agglomerated to produce micron size particles, as observed by the scanning electron micrographs. The XRD patterns showed that the $Er^{3+}$-$Yb^{3+}$ co-doped titanium oxide had an amorphous structure, while using the same method without doping $Er^{3+}\;or\;Yb^{3+},\;TiO_2$ was obtained in the crystallite form with thea dominance of rutile phase. Fabricating a bilayer structure consisting of nano-crystalline $TiO_2$ and the synthesized $Er^{3+}$-$Yb^{3+}$ co-doped titanium oxide showed better scattering property, with an overall increase of 15.6% in efficiency of the solar cell with respect to a single nano-crystalline $TiO_2$ layer.

• Journal of Powder Materials
• /
• v.20 no.5
• /
• pp.376-381
• /
• 2013

Spherical Ti-6Al-4V powders in the size range of 250 and 300 ${\mu}m$ were uniformly doped with nano-sized hydroxyapatite (HAp) powders by Spex milling process. A single pulse of 0.75-2.0 kJ/0.7 g of the Ti-6Al-4V powders doped with HAp from 300 mF capacitor was applied to produce fully porous and porous-surfaced Ti-6Al-4V implant compact by electro-discharge-sintering (EDS). The solid core was automatically formed in the center of the compact after discharge and porous layer consisted of particles connected in three dimensions by necks. The solid core increased with an increase in input energy. The compressive yield strength was in a range of 41 to 215 MPa and significantly depended on input energy. X-ray photoelectron spectroscopy and energy dispersive x-ray spectrometer were used to investigate the surface characteristics of the Ti-6Al-4V compact. Ti and O were the main constituents, with smaller amount of Ca and P. It was thus concluded that the porous-surfaced Ti-6Al-4V implant compacts doped with HAp can be efficiently produced by manipulating the milling and electro-discharge-sintering processes.

• Applied Chemistry for Engineering
• /
• v.24 no.3
• /
• pp.231-238
• /
• 2013

In this study, the $TiO_2$ nano spheres were synthesized by Sol-gel method to give an excellent UV-blocking effect and increase waste adsorption. The pH value was adjusted to obtain a superb UV-blocking effect and adsorption capacity due to the high surface area which is the characteristics of porosity. Base treated $TiO_2$ showed outstanding characteristics. The adsorption of gycerine onto the $TiO_2$ sample using TGA resulted in a high surface area of 1.16 mg/mg. This also showed a high reflectance in the UV-A region. In order to find the optimum dispersion, inorganic powder particles were maintained their sizes as 180 nm for about 6 months. The size of particles were measured using ester oil and silicon oil. Overall, the results reveal that $TiO_2$ has an excellent capability sunscreen in the UV-A region and skin waste adsorption.

• Proceedings of the International Microelectronics And Packaging Society Conference
• /
• 2005.09a
• /
• pp.201-212
• /
• 2005

[ $Epoxy/BaTiO_3$ ] composite embedded capacitor films (ECFs) were newly designed fur high dielectric constant and low tolerance (less than ${\pm}15\%$) embedded capacitor fabrication for organic substrates. In terms of material formulation, ECFs are composed of specially formulated epoxy resin and latent curing agent, and in terms of coating process, a comma roll coating method is used for uniform film thickness in large area. Dielectric constant of $BaTiO_3\;&\;SrTiO_3$ composite ECF is measured with MIM capacitor at 100 kHz using LCR meter. Dielectric constant of $BaTiO_3$ ECF is bigger than that of $SrTiO_3$ ECF, and it is due to difference of permittivity of $BaTiO_3\;and\;SrTiO_3$ particles. Dielectric constant of $BaTiO_3\;&\;SrTiO_3$ ECF in high frequency range $(0.5\~10GHz)$ is measured using cavity resonance method. In order to estimate dielectric constant, the reflection coefficient is measured with a network analyzer. Dielectric constant is calculated by observing the frequencies of the resonant cavity modes. About both powders, calculated dielectric constants in this frequency range are about 3/4 of the dielectric constants at 1 MHz. This difference is due to the decrease of the dielectric constant of epoxy matrix. For $BaTiO_3$ ECF, there is the dielectric relaxation at $5\~9GHz$. It is due to changing of polarization mode of $BaTiO_3$ powder. In the case of $SrTiO_3$ ECF, there is no relaxation up to 10GHz. Alternative material for embedded capacitor fabrication is $epoxy/BaTiO_3$ composite embedded capacitor paste (ECP). It uses similar materials formulation like ECF and a screen printing method for film coating. The screen printing method has the advantage of forming capacitor partially in desired part. But the screen printing makes surface irregularity during mask peel-off, Surface flatness is significantly improved by adding some additives and by applying pressure during curing. As a result, dielectric layer with improved thickness uniformity is successfully demonstrated. Using $epoxy/BaTiO_3$ composite ECP, dielectric constant of 63 and specific capacitance of 5.1nF/cm2 were achieved.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.33 no.5
• /
• pp.373-379
• /
• 2020

In this study, TiN-coated cBN (cubic-structure boron nitride) powders were successfully synthesized by a sol-gel method using titanium (IV) isopropoxide (TTIP) and by controlling the heat treatment conditions. After the sol-gel process, amorphous nano-sized TiO_x was uniformly coated on the surface of cBN powder particles. The obtained TiO_x-coated cBN powders were heated at 1,000~1,300℃ for 1 or 6 h in a flow of 95%N₂-5%H₂ mixed gas. With increasing temperature, the chemical composition of the TiO_x coating layer changed in the order of TiO₂→Ti₆O₁₁→Ti₄O₇→TiN due to reduction of the Ti ions. The TiN coating layer was observable in the samples heated at 1,200℃ and appeared as the main phase in the sample heated at 1,300℃. The resulting thickness of the TiN coating layer of the sample heated at 1,300℃ was approximately 45~50 nm.