• Journal of the Korean Ceramic Society
• /
• v.32 no.7
• /
• pp.809-816
• /
• 1995

Ti1-xAlxN films were successfully deposited on high speed steel and silicon wafer by plasma-assisted chemical vapor deposition using a TiCl4/AlCl3/N2/Ar/H2 gas mixture. Plasma process enabled N2 gas to nitride AlCl3, which is not possible in sense of thermodynamics. XPS analyses revealed that the deposited layer contained Al-N bond as well as Ti-N bond. Ti1-xAlxN films were polycrystalline and had single phase, B1-NaCl structure of TiN. Interplanar distance, d200, of (200) crystal plane of Ti1-xAlxN was, however, decreased with Al content, x. Al incorporation into TiN caused the grain size to be finer and changed strong (200) preferred orientation of TiN to random oriented microstructure. Those microstructural changes with Al addition resulted in the increase of micro-hardness of Ti1-xAlxN film up to 2800Kg/$\textrm{mm}^2$ compared with 1400Kg/$\textrm{mm}^2$ of TiN.

• Journal of the Korean institute of surface engineering
• /
• v.34 no.2
• /
• pp.97-104
• /
• 2001

($Ti_{ 1-x}$$Al_{ x}$)N has been deposited on high speed steel (HSS) substrate using PECVD from the gas mixture of $TiC1_4$, $AlC1_4$, $NH_3$, $H_2$, and Ar. The correlation between the microstructure and the mechanical properties was investigated. ($Ti_{1-x}$$Al_{ x}$)N showed single phase NaCl-structure up to X=0.87, while a mixed phase of NaCl Type (Ti, Al) N and wurtzite structure AlN was observed for 0.87$Ti_{1-x}$ $Al_{x}$ )N became by degrees as increasing X, which made the hardness of the coating higher by Al addition. When the coating was composed of a mixed phase, however, the hardness decreased abruptly due to the effect of soft AlN phase. The wear volume of the coatings could be obtained as the concentration of the coating was varied, and the relation between the wear volume and hardness or the adhesion strength was discussed.