• Journal of the Korean Vacuum Society
• /
• v.8 no.3A
• /
• pp.224-230
• /
• 1999

$SrBi_{2x}Ta_2O_9$ (SBT) thin films were prepared on platinized silicon substrates by MOD process, and their ferroelectric and leakage current characteristics were investigated. The grain size of the MOD derived SBT films increased with increasing the BI/Ta mole ration. Although the SBT films with x of 0.8~1.2 were composed of the equiaxed grains, the elongated grains were also observed for the SBT films with x of 1.4 and 1.6. The SBT film with x of 1.2 exhibited the optimum ferroelectric properties of 2PR : 9.79 $\muC/\textrm{cm}^2$ and Ec : 24.2kV/cm at applied voltage of 5V. The leakage current density of the SBT films increased with increasing the BI/Ta mole ratio. With post annealing process, 2Pr and $E_c$of the SBT film with x of 1.2 increases 11.3 $\muC/\textrm{cm}^2$ and 39.6kV/cm, respectively. decrement of the leakage current density by post annealing process increased remarkably with increasing the Bi/ta mole ratio, and the SBT film with x=1.6 exhibited the lowest leakage current density after post annealing process.

• Journal of the Korean Ceramic Society
• /
• v.40 no.3
• /
• pp.279-285
• /
• 2003

Ferroelectric S $r_{0.9}$B $i_{2.1}$T $a_{1.8}$N $b_{0.2}$ thin films with 200 nm thicknesses were deposited on Pt/Ti $O_2$/ $SiO_2$/Si Substrates by a sol-gel method. In these experiments, Sr(O $C_2$ $H_{5}$)$_2$, Bi(TMHD)$_3$, Ta(O $C_2$ $H_{5}$)$_{5}$ and Nb(O $C_2$ $H_{5}$)$_{5}$ were used as precursors, which were dissolved in 2-methoxyethanol. After UV-irradiation and RTA processes, the remanent polarization value (2 $P_{r}$) of SBTN thin films with annealed at $650^{\circ}C$ was 8.49 and 11.94 $\mu$C/$\textrm{cm}^2$ at 3 V and 5 V, respectively.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 1996.11a
• /
• pp.175-179
• /
• 1996

Ferroelectric SrBi$_2$Ta$_2$$O_{9}$ thin films were fabricated by tole Sol-Gel method using a spin-on coating with MOD(Metal Organic Dccomposition) solution on Pt/Ti/SiO$_2$/Si(100) substratcs. The films were anncalcd at 80$0^{\circ}C$ for one hour in oxygen atmosphere. The effects of Bi/Ti mole ratios on crystalline orientations, surface morphologies, and subface composition SBT thin films with a Bi/Ta mole ratios from 1.1 to 1.3 were investigated using X-ray Diffractometry (XRD). Atomic Force (AFM), X-Ray Photoelectron Spectroscopy(XPS). Ferroelectric properties of these films were also measured.d.

• Korean Journal of Materials Research
• /
• v.13 no.6
• /
• pp.360-364
• /
• 2003

$Sr_{l}$ $\pm$x/$Bi_{2}$ $\pm$y/$Ta_2$ $O_{9}$ and $Sr_{l}$ $\pm$$Bi_{x}$ $2\pm$y$Nb_2$$O_{9}$ ceramics were prepared by a solid state reaction method. X-ray diffraction analysis indicated that single-phase of Bi-layered perovskite was obtained. According to Sr/Bi content ratio, Curie temperature( $T_{c}$), electromechanical factor($K_{p}$ ) and mechanical quality factor($Q_{m}$ ) were measured. The Curie temperature of SBN(SBT) rose from $414^{\circ}C$(314$^{\circ}C$) to $494^{\circ}C$(426$^{\circ}C$) when Sr/Bi content ratio was increased. In the case of Sr/Bi content ratio = 0.55/2.3, the maximum value of the mechanical quality factor $Q_{m}$ of SBT and SBN were obtained 3320 and 1010, respectively.

• Proceedings of the Korean Ceranic Society Conference
• /
• 2003.10a
• /
• pp.30.2-30
• /
• 2003

• Journal of the Korean Ceramic Society
• /
• v.40 no.2
• /
• pp.184-190
• /
• 2003

$Sr_{0.9}Bi_{2.1}Ta_2O_9$thin films were deposited on $IrO_2$ electrode by spin coating method using photosensitive sol-gel solution. To ensure the UV-exposure effect on SBT thin films, UV irradiated films and non-UV irradiated films were analyzed by XRD, SEM. As a result, UV-irradiation on SBT thin films promoted grain growth of SBT compared with no UV irradiation. In case of the UV irradiated films annealed at$740{\circ}C$for 1 h in an oxygen ambient, the 2Pr value and Pr/Ps at${pm}5$V were$11.48{mu}C/cm^2$and 0.53, respectively. 2Pr values of the UV irradiated SBT thin films at$660-740{circ}C were approximately 12% higher than those of non-UV irradiated thin films.

• Journal of the Korean institute of surface engineering
• /
• v.29 no.6
• /
• pp.621-627
• /
• 1996

$SrBi_{2x}TaO_9$ ferroelectric thin films were prepared on platinized silicon substrates using MOD proces, and crystallization behavior of the films was investigated with variation of the annealing temperature and Bi content x. Crystalline phase of bismuth layered perovskite structure was formed even by baking the films at $800^{\circ}C$ for 5 minutes in air, and was not changed by annealing at temperatures raning from $700^{\circ}C$ to $900^{\circ}C$ for 1 hour in oxygen ambient. When $SrBi_{2x}TaO_9$ thin films ($0.8\lex\ie1.6$) were annealed at $800^{\circ}C$, Preferred orientation of the films along c-axis was observed with $x\ge1.2$. With increasing Bi content x, surface morphology of the films was changed from equiaxed grains to elongated grains.

• Proceedings of the Korean Ceranic Society Conference
• /
• 2002.10a
• /
• pp.188.2-188
• /
• 2002

• Journal of the Korean Vacuum Society
• /
• v.9 no.4
• /
• pp.360-366
• /
• 2000

$Sr_xBi_{2.4}Ta_2O_9$ (SBT) thin films of 150 nm thickness were prepared using LSMCD (Liquid Source Misted Chemical Deposition) process with variation of the Sr/Ta mole ratio of 0.35~0.65, and their crystalline phase, microstructure, ferroelectric properties and leakage current characteristics were investigated. Ferroelectric characteristics of the LSMCD-derived SBT films were optimized at the Sr/Ta moleratio of 0.425. The remanent polarization (2Pr) and coercive field (Ec) of the SBT film with the Sr/Ta mole ratio of 0.425 were measured as 15.01 $\mu$C/$ \textrm{cm}^2$ and 41 kV/cm at an applied voltage of $\pm$5 V respectively. LSMCD-derived SBT films with the Sr/Ta mole ratio of 0.35~0.5 exhibited leakage current densities lower than $10^{-5} A/\textrm{cm}^2$ at an applied field of 100 kV/cm, and excellent fatigue-free characteristics of the remanent polarization decrement less than 1% after $10^{10}$ switching cycles at$\pm$5 V.

• Korean Journal of Materials Research
• /
• v.7 no.5
• /
• pp.381-385
• /
• 1997

PEMOCVD에 의해서 SrBi$_{2}$Ta$_{2}$O$_{9}$밥막이 낮은 온도에서 성공적으로 Pt/Ti/SiO$_{2}$Si위에 증착되었다. 5$50^{\circ}C$에서 증착된 200nm박막은 치밀하고 작은 결정립을 보였으며 3V의 인가전압하에서 이력곡선은 포화되기 시작하였다. 3V에서 박막은 잔류분극 (P$_{r}$)과 항전계(E$_{c}$)는 각각 15$\mu$/$\textrm{cm}^2$과 50kV/cm이었다. 6V bipolar square pulse의 피로측정에서 박막은 1.0x$10^{11}$cycles까지 피로 현상을 보이지 않았다. PEMOCVD에 의해서 5$50^{\circ}C$에서 증착된 SBT박막은 비휘발성 기억소자에 충분히 활용할 수 있다.다.