Low Temperature Sintering Process of Sol-gel Derived Ferroelectric Sr0.9Bi2.1Ta1.8Nb0.2O9 Thin films

Ferroelectric S $r_{0.9}$B $i_{2.1}$T $a_{1.8}$N $b_{0.2}$ thin films with 200 nm thicknesses were deposited on Pt/Ti $O_2$/ $SiO_2$/Si Substrates by a sol-gel method. In these experiments, Sr(O $C_2$ $H_{5}$)$_2$, Bi(TMHD)$_3$, Ta(O $C_2$ $H_{5}$)$_{5}$ and Nb(O $C_2$ $H_{5}$)$_{5}$ were used as precursors, which were dissolved in 2-methoxyethanol. After UV-irradiation and RTA processes, the remanent polarization value (2 $P_{r}$) of SBTN thin films with annealed at $650^{\circ}C$ was 8.49 and 11.94 $\mu$C/$\textrm{cm}^2$ at 3 V and 5 V, respectively.

Sol-gel 법으로 제조된 강유전체 Sr0.9Bi2.1Ta1.8Nb0.2O9 박막의 저온결정화 공정

Sol-gel 법으로 200 nm 정도의 두께를 가진 강유전성 S $r_{0.9}$B $i_{2.1}$T $a_{1.8}$ N $b_{0.2}$ 박막을 Pt/Ti $O_2$/ $SiO_2$/Si 기판 위에 증착하였다. 본 실험에서는 Sr(O $C_2$ $H_{5}$)$_2$, Bi(TMHD)$_3$, Ta(O $C_2$ $H_{5}$)$_{5}$ 그리고, Nb(O $C_2$ $H_{5}$)$_{5}$를 출발 물질로 사용하였으며 2-methoxyethanol을 용매로 사용하였다. UV 노광과 급속열처리가 SBTN 박막의 구조와 전기적 특성에 어떤 영향을 주는 가를 연구하였다. UV 노광과 급속열처리를 한 후에 $650^{\circ}C$ 열처리한 SBTN 박막의 3V와 5V 인가 전압하에서의 잔류분극 값은 각각 8.49와 11.94 $\mu$C/$ extrm{cm}^2$이었다.