• 한국신재생에너지학회:학술대회논문집
• /
• 한국신재생에너지학회 2006년도 춘계학술대회
• /
• pp.51-54
• /
• 2006

Cathode material, $(Ba_{0.5}Sr_{0.5})_{0.99}Co_{0.8}Fe_{0.2}O_{3-{\delta}}$, for low temperature SOFC was prepared by the glycine-nitrate synthesis process (GNP). The characteristics of the synthesized powders were studied with controlling pH of a precursor. The synthesis BSCF powders with pH were agglomeration state and calcinations temperature has not influence on particles. Highly acidicprecursor solution increased a single phase forming the temperature. Also, synthesis BSCF powder was show result for thermal analysis and alteration of difference crystal with pH. It is considered that Ba and Sr cannot complex by carboxylic acid group of glycine, because under highly acidic condition the caboxylic group mainly combined with $H^+$ insead of alkali and alkaline earth cations. In case of using precursor solution with pH $2{\sim}3$, a single perovskite phase was obtained at $1000^{\circ}C$. Polarization resistance of $(Ba_{0.5}Sr_{0.5})_{0.99}Co_{0.8}Fe_{0.2}O_{3-{\delta}}$ was measured by AC impedance spectroscopy from the two electrode symmetric cell. Area specific resistance of the $(Ba_{0.5}Sr_{0.5})_{0.99}Co_{0.8}Fe_{0.2}O_{3-{\delta}}$ air electrode at $500^{\circ}C\;and\;600^{\circ}C$ were $0.96{\Omega}?cm^2$ and $0.16{\Omega}?cm^2$, respectively.

• 한국세라믹학회지
• /
• 제38권9호
• /
• pp.787-793
• /
• 2001

고상 반응법으로 제조된 $La_{0.6}Sr_{0.4}Co_{0.2}Fe_{0.8}O_{3-{\delta}}$ 분리막의 소결거동을 살펴보고, 분리막 양면에 산소농도의 차이를 부여하여 산소투과량을 측정하였다. 최적 소결조건에서 제조된 상대밀도 98%의 치밀한 분리막 자체의 산소공공을 통한 혼합전도에 기인해 750$^{\circ}$C∼950$^{\circ}$C의 온도구간에서 산소가 투과되었으며, 850$^{\circ}$C에서 약 0.1ml/$cm^2{\cdot}$min의 투과량을 나타내었다. 안정한 산소 투과량에 도달하기 위해서는 산소투입 후 일정한 시간이 요구되었고, 이러한 산소투과량은 산소부분압의 조절로 제어가 가능하였다.

• 한국세라믹학회지
• /
• 제44권12호
• /
• pp.740-746
• /
• 2007

The potential candidates for IT-SOFCs cathode materials, $Ba_{0.5}Sr_{0.5}Co_{0.8}Fe_{0.2}O_{3-{\delta}}$ (BSCF) and $La_{0.6}Ba_{0.4}Co_{0.2}Fe_{0.8}O_{3-{\delta}}$ (LBCF) powders, were synthesized by a EDTA-citrate combined method from $Sr(NO_3)_2$, $Ba(NO_3)_2$, $La(NO_3)_3{\cdot}6H_2O$, $Co(NO_3)_2{\cdot}6H_2O$, $Fe(NO_3)_3{\cdot}9H_2O$, citric acid and $EDTA-NH_3$. The cathode performance of symmetrical electrochemical cells consisting of BSCF-GDC or LBCF-GDC composite electrodes and a GDC electrolyte was investigated using by AC impedance spectroscopy at the temperature range of 500 to $700^{\circ}C$. It was found that a single phase perovskite could be successfully synthesized when the precursor is heated at $850^{\circ}C$ for 2 h. Due to thermal expansion mismatch between BSCF and GDC, the composite cathodes with lower GDC content than 45 wt% were peeled off from the GDC electrolyte and their electrode polarization resistance was estimated to be high. The thermal expansion coefficient of BSCF-GDC composites was decreased with increasing the GDC content and the electrode peeling off did not occur in BSCF-45 and 55 wt% GDC composites. BSCF-45 wt% GDC composite electrode showed the lowest area specific resistances (ASR) of 0.15 and $0.04{\Omega}{\cdot}cm^2$ at 600 and $700^{\circ}C$, respectively. On the other hand, LBCF-GDC composite cathodes showed higher ASR than the BSCF-45 and 55 wt% GDC and their cathode performance were decreased with the GDC content.

• 한국세라믹학회지
• /
• 제52권5호
• /
• pp.308-314
• /
• 2015

The electrochemical performance and Cr poisoning behavior of $La_{1-x}Ba_xCo_{0.9}Fe_{0.1}O_{3-{\delta}}$ (LBCF, x = 0.3, 0.4, 0.5) and $La_{0.6}Sr_{0.4}Co_{0.2}Fe_{0.8}O_{3-{\delta}}$ (LSCF) cathodes were investigated for solid oxide fuel cells (SOFCs). The polarization resistance of the LBCF/GDC/LBCF symmetrical cell was found to decrease with increasing Ba content (x value). This phenomenon might be associated with the high oxygen vacancy concentration in the LBCF sample, with x = 0.5. In addition, there was no chromium poisoning in the LBCF cathode. On the other hand, the polarization resistance of the LSCF cathode was found to significantly increase after exposure to gaseous chromium species; it appears that this result stemmed from the formation of $SrCrO_4$ phase. Therefore, it can be expected that LBCF can be a durable potential cathode material for intermediate-temperature solid oxide fuel cells (IT-SOFC).

• 한국세라믹학회지
• /
• 제43권6호
• /
• pp.369-375
• /
• 2006

[ $(Ba_{0.5}Sr_{0.5})_{0.99}Co_{x}Fe_{1-x}O_{3-{\delta}}$ ] [x=0.8, 0.2](BSCF) powders were synthesized by a Glycine-Nitrate Process (GNP) and the electrochemical performance of the BSCF cathode on a scandia stabilized zirconia, $[(Sc_{2}O_3)_{0.11}(ZrO_2)_{0.89}]-1Al_{2}O_3$ was investigated. In order to prevent unfavorable solid-state reactions between the cathode and zirconia electrolyte, a GDC ($Gd_{0.1}Ce_{0.9}O_{2-{delta}}$) buffer layer was applied on ScSZ. The BSCF (x = 0.8) cathode formed on GDC(Buffer)/ScSZ(Disk) showed poor electrochemical property, because the BSCF cathode layer peeled off after the heat-treatment. On the other hand, there were no delamination or peel off between the BSCF and GDC buffer layer, and the BSCF (x = 0.2) cathode exhibited fairly good electrochemical performances. It was considered that the observed phenomenon was associated with the thermal expansion mismatch between the cathode and buffer layer. The ohmic resistance of the double layer cathode was slightly lower than that of the single layer BSCF cathode due to the incorporation of platinum particle into the BSCF second layer.

• 한국세라믹학회지
• /
• 제38권10호
• /
• pp.886-893
• /
• 2001

공침법, 구연산법 그리고 고상 반응법을 이용하여 $La_{0.6}Sr_{0.4}Co_{0.2}Fe_{0.8}O_{3-\delta}$ 분말을 합성하고 정수압 성형 후 대기 중에서 소결하여 산소 투과 분리막을 제조하였다. 모든 분말 및 소결체는 페롭스카이트 결정구조를 보였다. 분말의 비표면적은 공침 분말이 가장 높은 값($7.5m^2/g$)을 보였지만 Sr원소의 유실이 일어났고 구연산법은 상대적으로 낮은 밀도를 나타내었다. 고상 반응법은 가장 작은 비표면적을 갖는 분말이 제조되었으나 상대밀도 95%이상의 치밀한 분리막을 제조할 수 있었고 기계적 특성에서도 상대적으로 우수한 성질을 보였다. 특히 6 : 4 : 2 : 8의 몰비의 조성제어가 상대적으로 용이하였다.

• 한국신재생에너지학회:학술대회논문집
• /
• 한국신재생에너지학회 2009년도 추계학술대회 논문집
• /
• pp.184-186
• /
• 2009

Composites of LSCF($La_{0.6}Sr_{0.4}Co_{0.2}Fe_{0.8}O_{3-\delta}$ and CGO(gadolinium doped ceria) is an efficient candidate cathode material with CGO electrolytes. In this study, LSCF with exact perovskite structure was synthesized by using solid state reaction(SSR) method. The optimized temperature to synthesize $La_{0.6}Sr_{0.4}Co_{0.2}Fe_{0.8}O_{3-\delta}$ with rhombohedral structure. was $1100^{\circ}C$. The polarization resistance of the LSCF/CGO(50:50 wt.%) was smaller than those of other composite cathodes. The analysis of the EIS data of LSCF/CGO suggests that the diffusion and adsorption-desorption of oxygen can be the key process in the cathodic reaction of SOFC using LSCF/CGO as cathode material.

• 멤브레인
• /
• 제11권4호
• /
• pp.143-151
• /
• 2001

고상 반응법을 이용하여 L $a_{0.6}$S $r_{0.4}$ $Co_{0.2}$F $e_{0.8}$ $O_{3-}$$\delta$/ 및 L $a_{0.7}$S $r_{0.3}$G $a_{0.6}$F $e_{0.4}$ $O_{3-}$$\delta$/ 분말을 합성하고 혼합전도체 분리막을 소결하여 제조하였다. 제조된 분리막들은 정확한 페롭스카이트 결정구조를 나타내었으며, 95% 이상의 높은 상대밀도를 나타내었다. 산소이온 변환 능력을 향상시키기 위해 L $a_{0.7}$S $r_{0.3}$G $a_{0.6}$F $e_{0.4}$ $O_{3-}$$\delta$/ disk의 양 표면에 L $a_{0.6}$S $r_{0.4}$Co $O_{3-}$$\delta$/ paste를 스크린 프린팅 방법으로 코팅하였으며 코팅 막은 비교적 치밀한 미세구조를 나타내었다. 코팅되지 않은 L $a_{0.6}$S $r_{0.4}$ $Co_{0.2}$F $e_{0.8}$ $O_{3-}$$\delta$/ 및 L $a_{0.7}$S $r_{0.3}$G $a_{0.6}$F $e_{0.4}$ $O_{3-}$$\delta$/ 분리막과 코팅된 L $a_{0.7}$S $r_{0.3}$G $a_{0.6}$F $e_{0.4}$ $O_{3-}$$\delta$/ 분리막의 산소투과 성능을 비교 실험한 결과, 90$0^{\circ}C$에서 L $a_{0.6}$S $r_{0.4}$ $Co_{0.2}$F $e_{0.8}$ $O_{3-}$$\delta$/ 분리막이 정상상태에서 0.266 mL/min.$\textrm{cm}^2$로 가장 많은 투과량을 보였으며 코팅된 L $a_{0.7}$S $r_{0.3}$G $a_{0.6}$F $e_{0.4}$ $O_{3-}$$\delta$/ 분리막의 정상상태 산소 투과 유속은 최고 0.19 mL/min.$\textrm{cm}^2$ 정도로 코팅되지 않은 분리막에 비해 약 2~3배로 높게 나타났다.정도로 코팅되지 않은 분리막에 비해 약 2~3배로 높게 나타났다.코팅되지 않은 분리막에 비해 약 2~3배로 높게 나타났다. 높게 나타났다.

• 한국세라믹학회지
• /
• 제39권10호
• /
• pp.994-1000
• /
• 2002

고상 반응법을 통해 $La_{0.6}Sr_{0.4}Co_{0.2}Fe_{0.8}O_{3-{\delta}}$ 페롭스카이트계 산소투과 분리막을 제조하였으며, 미세구조에 따른 산소투과 특성 및 기계적 특성을 고찰하였다. 분리막의 미세구조는 소결온도 및 소결 유지시간을 달리함으로써 조절하였으며, 미세구조에 따른 평균 입경 및 상대밀도의 변화를 평가하였다. 입계 분율의 감소에 따라 산소투과유속이 증가하는 경향을 나타내었으며, 본 연구에서 고찰한 소결조건 중에서는 1300${\circ}C$에서 10시간 유지하여 제조한, 상대밀도가 높고 비교적 입경이 조대한 분리막 시편의 경우, 최대 0.37 ml/$cm^2$${\cdot}$min의 산소투과유속이 특정되었다. 파괴강도는 소결체의 상대밀도에 의존적이었으며, 파괴인성은 결정립의 크기에 따라 증가하는 경향을 나타내었다.

• 공업화학
• /
• 제19권4호
• /
• pp.382-387
• /
• 2008

착체중합법을 이용하여 $Ba_{0.5}Sr_{0.5}Co_{0.8}Fe_{0.2}O_{3-{\delta}}$ 조성의 산화물을 합성하였으며, 합성된 분말은 압축 성형 후 $1080^{\circ}C$에서 소결하여 치밀한 페롭스카이트 분리막을 제조하였다. 밀봉 재료로 gold ring, Pyrex ring 및 Pyrex 분말을 사용하여 가스누출 실험을 수행하였다. $Ba_{0.5}Sr_{0.5}Co_{0.8}Fe_{0.2}O_{3-{\delta}}$ 분리막의 산소투과량 분석결과 온도가 증가함에 따라 산소투과량은 증가하였고, $900^{\circ}C$에서 $0.74mL/min{\cdot}cm^2$의 값을 나타내었다. $950^{\circ}C$에서 밀봉 재료에 따른 투과 특성 분석 결과, gold ring을 이용할 경우 높은 산소투과량을 보인 반면, Pyrex를 밀봉재로 사용할 경우 낮은 투과량을 보였다. 이는 Pyrex를 밀봉재로 이용할 경우 분리막 표면으로 유리가 침투하여 유효 산소투과면적을 감소시켰기 때문이며, 광화학 현미경 분석으로 Pyrex 유리의 확산 침투를 확인하였다.