• Bulletin of the Korean Chemical Society
• /
• 제28권12호
• /
• pp.2288-2292
• /
• 2007

The catalytic activities of nickel-based catalysts were estimated for oxidizing acetaldehyde of VOCs exhausted from industrial facilities. The catalysts were prepared by sol-gel methods of SiO2 and SiO2-TiO2 as a xerogel followed by impregnating Al2O3 powder with the nickel nitrate precursor. The crystalline structure and catalytic properties for the catalysts were investigated by use of BET surface area, X-ray diffraction (XRD), Xray photoelectron spectroscopy (XPS) and temperature programmed reduction (TPR) techniques. These results show that nickel oxide is transformed to NiAl2O4 spinel structure at the calcination temperature of 400 °C in response to the steps with after- and co-impregnation of Al2O3 powder in sol-gel process. The NiAl2O4 could suppress the oxidation reaction of acetaldehyde by catalysts. The NiO is better dispersed on SiO2-TiO2/Al2O3 support than SiO2/Al2O3 and SiO2-TiO2-Al2O3 supports. From the testing results of catalytic activities for oxidation of acetaldehyde, Catalysts showed a big difference in conversion efficiencies with the way of the preparation of catalysts and the loading weight of nickel. The catalyst of 8 wt.% Ni/TiO2-SiO2/Al2O3 showed the best conversion efficiency on acetaldehyde oxidation with 100% conversion efficiency at 350 °C.

• 한국재료학회지
• /
• 제24권3호
• /
• pp.152-158
• /
• 2014

We report the effect of the fabric of the surface microstructure on the CO gas sensing properties of $SnO_2$ thin films deposited on self-assembled Au nanodots ($SnO_2$/Au) that were formed on $SiO_2/Si$ substrates. We characterized structural and morphological properties, comparing them to those of $SnO_2$ thin films deposited directly onto $SiO_2/Si$ substrates. We observed a significant enhancement of CO gas sensing properties in the $SnO_2$/Au gas sensors, specifically exhibiting a high maximum response at $200^{\circ}C$ and quite a low detection limit of 1 ppm level in dry air. In particular, the response of the $SnO_2/Au$ gas sensor was found to reach the maximum value of 32.5 at $200^{\circ}C$, which is roughly 27 times higher than the response (~1.2) of the $SnO_2$ gas sensor obtained at the same operating temperature of $200^{\circ}C$. Furthermore, the $SnO_2/Au$ gas sensors displayed very fast response and recovery behaviors. The observed enhancement in the CO gas sensing properties of the $SnO_2/Au$ sensors is mainly ascribed to the formation of a nanostructured morphology in the active $SnO_2$ layer having a high specific surface-reaction area by the insertion of a nanodot form of Au nucleation layer.

• 한국세라믹학회지
• /
• 제44권3호
• /
• pp.147-151
• /
• 2007

An improvement for the efficiency of the $Sr_{2}SiO_{4}:Eu$ yellow phosphor under the $450{\sim}470\;nm$ excitation range have been achieved by adding the co-doping element ($Mg^{2+}\;and\;Ba^{2+}$) in the host. White LEDs were fabricated through an integration of an blue (InGaN) chip (${\lambda}_{cm}=450\;nm$) and a blend of two phosphors ($Mg^{2+},\;Ba^{2+}\;co-doped\;Sr_{2}SiO_{4}:Eu$ yellow phosphor+CaS:Eu red phosphor) in a single package. The InGaN-based two phosphor blends ($Mg^{2+},\;Ba^{2+}\;co-doped\;Sr_{2}SiO_{4}:Eu$ yellow phosphor+CaS:Eu red phosphor) LEDs showed three bands at 450 nm, 550 nm and 640 nm, respectively. The 450 nm emission band was due to a radiative recombination from an InGaN active layer. This 450 nm emission was used as an optical transition of the $Mg^{2+},\;Ba^{2+}\;co-doped\;Sr_{2}SiO_{4}:Eu$ yellow phosphor+CaS:Eu red phosphor. As a consequence of a preparation of white LEDs using the $Mg^{2+},\;Ba^{2+}\;co-doped\;Sr_{2}SiO_{4}:Eu$ yellow phosphor+CaS:Eu red phosphor yellow phosphor and CaS:Eu red phosphor, the highest luminescence efficiency was obtained at the 0.03 mol $Ba^{2+}$ concentration. At this time, the white LEDs showed the CCT (5300 K), CRI (89.9) and luminous efficacy (17.34 lm/W).

• 공업화학
• /
• 제7권1호
• /
• pp.34-42
• /
• 1996

합성에메랄드[$(BeO)_3(Al_{2-x}Cr_xO_3)(SiO_2)_6$]단결정을 flux법에 의하여 육성하였다. 출발물질로 BeO, $Al_2O_3$와 $SiO_2$ 시약을 화학양론비로 혼합하여 사용하였다. 에메랄드 단결정의 성장 조건은 다음과 같다. 온도범위 ; $1150{\sim}900^{\circ}C$, 냉각속도 ; 2, 4, $10^{\circ}C/hr$, 융제 : $Li_2CO_3$, $V_2O_5$, 첨가제 ; $Cr_2O_3$. 에메랄드 단결정의 크기는 2, 4, $10^{\circ}C/hr$의 냉각속도에 의존하였다. 얻어진 에메랄드 단결정을 동정하였고, 그 결과는 다음과 같다. 즉, 결정계 ; 육방정계, 격자상수 ; a=0.921nm, c=0.917nm, 결정의 크기 ; 최대 $0.80{\times}0.95mm^2(c{\times}m)$, 방위 ; c(1000), $m(10{\bar{1}}0)$.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2010년도 하계학술대회 논문집
• /
• pp.214-214
• /
• 2010

The 0.65Pb($Mg_{1/3}Nb_{2/3})O_3-0.35PbTiO_3$ (PMN-PT) thin films with $La_{0.5}Sr_{0.5}CoO_{3-\delta}$ (LSCO) bottom electrodes were grown on $CeO_2$/YSZ/Si(001), Pt/$TiO_2$/Si and $SrTiO_3$ (STO) substrates using conventional pulsed laser deposition (PLD) at a substrate temperature of $550^{\circ}C$. Since generally the crystallographic orientation of the bottom electrode induces the orientation of the films deposited on it, it allows us to observe the influence of the PMN-PT film orientation on the electrical properties. Phi scan done on PMN-PT/LSCO thin films shows epitaxial behavior of the films grown on sto substrates and $CeO_2$/YSZ buffered Si(001) substrates, and (110) texture on Pt/$TiO_2$/Si substrates. Polarization-electricfield (P-E) measurement shows good hysteresis behavior of PMN-PT films with remnant polarization of 18.2, 8.8, and $4.4{\mu}C/cm^2$ on $CeO_2$/YSZ/Si, Pt/TiO2/Si and STO substrates respectively.

• Journal of Magnetics
• /
• 제8권3호
• /
• pp.118-120
• /
• 2003

As an alternative promising way of producing high coercivity Sr-ferrite for a permanent magnet application, intensive mechanical milling process was applied to the raw materials of the Sr-ferrite with different composition. Synthesising reactivity for the Sr-ferrite of the mechanically milled raw material containing $SrCO_3$, $La_2O_3$, $Fe_2O_3$, $Co_3O_4$, and $SiO_2$ was inferior to that of the raw material containing $SrCO_3$ and $Fe_2O_3$, The Sr-ferrite prepared from mechanically milled raw materials had profoundly improved magnetic properties compared to the Sr-ferrite prepared by conventional method. Beneficial effect of the substituting ($La_2O_3$, $Co_3O_4$) and additive ($SiO_2$) oxides for improving the magnetic properties was not exploited in the Sr-ferrite prepared from the mechanically milled raw material. The Sr-ferrite powder prepared from the mechanically milled raw materials was magnetically isotropic in nature.

• 한국재료학회지
• /
• 제3권5호
• /
• pp.497-504
• /
• 1993

기본조성 52.5mol% $Fe_2O_3$, 25.5mol% MnO, 22mol% ZnO로 구성된 Mn-Zn페라이트에 $Bi_2O_3$ 및 $CaCO_3$을 각각 0.02, 0.05wt%첨가한 시편에 대해서 $Ta_2O_5,ZrO_2$및 $SiO_2$의 미량 첨가한 따른 미세구조와 자기적 특성변화를 조사하였다. $Ta_2O_5,ZrO_2$첨가에 따라 결정립 크기가 감소되었고, 전기시 균일한 입자로 형성된 미세구조를 가진 재료를 얻었다. $SiO_2$첨가에 따라 결정립의 이상성장이 관찰되었고 소결밀도, 전기저항, 초투자율은 감소하고 고주파 영역에서 상대손실이 증가되었다. 본 연구결과 초투자자율은 균일한 결정립에서 최대의 값을 가지며 0.02wt%$Bi_2O_3$, 0.05wt%$CaCO_3$, 0.1wt%$Ta_2O_5$ 첨가시편의 경우 10kHz, $25^{\circ}C$에서 초투자율($\mu_i$)은 6260이고 상대손실 계수(tan$\delta /\mu_i$)는 $4.2 \times 10^{-6}$ 인 높은 투자율과 낮은 손실 특성을 가진 자성재료를 얻었다.

• 한국재료학회지
• /
• 제20권7호
• /
• pp.370-373
• /
• 2010

In fabricating plasma display panels, the photolithographic process is used to form patterns of barrier ribs with high accuracy and high aspect ratio. It is important in the photolithographic process to control the refractive index of the photosensitive paste. The composition of this paste for photolithography is based on the $B_2O_3-SiO_2-Al_2O_3$ glass system, including additives of alkali oxides and rare earth oxides. In this work, we investigated the density, structure and refractive index of glasses based on the $B_2O_3-SiO_2-Al_2O_3$ system with the addition of $Li_2O$, $K_2O$, $Na_2O$, CaO, SrO, and MgO. The refractive index of the glasses containing K2O, Na2O and CaO was similar to that of the [BO3] fraction while that of the SrO, MgO and Li2O containing glasses were not correlated with the coordination fraction. The coordination number of the boron atoms was measured by MAS NMR. The refractive index increased with a decrease of molar volume due to the increase in the number of non-bridging oxygen atoms and the polarizability. The lowest refractive index (1.485) in this study was that of the $B_2O_3-SiO_2-Al_2O_3-K_2O$ glass system due to the larger ionic radius of $K^+$. Based on our results, it has been determined that the refractive index of the $B_2O_3-SiO_2-Al_2O_3$ system should be controlled by the addition of alkali oxides and alkali earth oxides for proper formation of the photosensitive paste.

• 한국대기환경학회지
• /
• 제21권6호
• /
• pp.639-647
• /
• 2005

A single particle analytical technique, named low-Z particle electron probe X-ray microanalysis (EPMA), was applied to characterize samples collected at a subway station and ambient samples in Seoul. According to their chemical composition, many distinctive particle types were identified. For samples collected at the subway station platform, the major chemical species are carbon-rich, organic, aluminosilicates (AlSi), AlSi/C, AlSi/$CaCO_{3},\;CaCO_{3},\;SiO_{2},\;and\;Fe_{2}O_{3}$. For outdoor samples, carbon-rich, organic, AlSi, $CaCO_{3},\;SiO_{2},\;NaNO_{3},\;(Na,Mg)NO_{3},\;Na(CO_{3},NO_{3},SO_{4}),\;and\;(NH_{4})_2SO_4$, are abundantly encountered. Samples collected at the subway station show very high contents of $Fe_{2}O_{3}$, both in coarse and fine fractions, which come from brake block, subway train wheel, electric contact materials, etc. It is demonstrated that the single-particle characterization using this low-Z particle EPMA technique provided detailed information on various types of chemical species in indoor and outdoor samples.

• 한국전기전자재료학회논문지
• /
• 제26권1호
• /
• pp.22-26
• /
• 2013

PTCR ceramics of $(Ba_{0.998}Sm_{0.002})TiO_3+0.001MnCO_3+xSiO_2$ (x=1, 2, 3, 4, 5, 6 mol%) were fabricated by solid state method. Disk samples of diameter 5 mm and thickness about 1mm were sintered at $1,290^{\circ}C$ for 2 h in reduced atmosphere of $5%H_2-95%N_2$ followed by re-oxidation at $600^{\circ}C$ for 30 min. in $20%O_2-80%N_2$.and their microstructures and electrical properties were investigated with SEM and Multimeter. The color of sintered samples was strongly dependent on $SiO_2$ content showing that the color of samples with $SiO_2$ of 1~2 mol% was gray but that of samples with $SiO_2$ of 4~6 mol% was changed from gray to blue, which seems to be related with the reduction of samples due to the oxygen vacancies created during the sintering in reduced atmosphere. $SiO_2$ content had a great influence on the microstructure and the electrical properties. With increasing $SiO_2$ content, the grain size of samples increased and the resistivity as well as the resistivity jump ($R_{285}/R_{min}$) decreased, which is considered to be attributed to the resistivity change at grain interior and grain boundary due to the fast mass transfer through $SiO_2$ liquide phase during the sintering. Samples with 2 mol% $SiO_2$ has the resistivity of $202{\Omega}cm$ and the resistivity jump of 3.28. It is expected that $SiO_2$ doped $BaTiO_3$ based PTC ceramics can be used for multilayered PTC thermistor due to the resistance to the sintering in reduced atmosphere.