• Nuclear Engineering and Technology
• /
• v.55 no.5
• /
• pp.1855-1862
• /
• 2023

Graphite crucibles are used for melting uranium and its alloys in VIM furnace. Various coating materials namely Al₂O₃, ZrO₂, MgO etc. are applied on the inner surface of the crucibles using paint brush or thermal spray technique to mitigate U-C interaction. These leads to significant amount of carbon pick-up in uranium. In this study, the attempts are made to develop multilayer coatings comprising of SiC/Y₂O₃ and Mo/Y₂O₃ on graphite to study the feasibility of minimizing U-C interaction. The parameters are optimized to prepare SiC coating of about 70㎛ thickness using CVD technique on graphite coupons and subsequently Y₂O₃ coating of about 250㎛ thickness using plasma spray technique. Molybdenum and Y₂O₃ layers were deposited using plasma spray technique with 70㎛ and 250㎛ thickness, respectively. Interaction studies of the coated graphite with molten uranium at 1450℃ for 20 min revealed that Y₂O₃ coating with SiC interlayer provides physical barrier for uranium-graphite interaction, however, this led to the physical separation of coating layer. Y₂O₃ coating with Mo interlayer provided superior barrier effect showing no degradation and the coatings remained intact after interaction tests. Therefore, the Mo/Y₂O₃ coating was found to be a promising solution for minimizing carbon pick-up during uranium/uranium alloy melting.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.13 no.5
• /
• pp.241-246
• /
• 2003

The transparent conducting thin film of ATO (antimony-doped tin oxide) was successfully fabricated on$SiO_2$/glass substrate by a sol-gel dip coating method. The crystalline phase of the ATO thin film was identified as SnO$_2$ major phase and the film thickness was about 100 nm/layer at the withdrawal speed of 50 mm/minute. Optical transmittance and electrical resistivity of the 400 nm-thick ATO thin film which was annealed under nitrogen atmosphere were 84% and $5.0\times 10^{-3}\Omega \textrm{cm}$, respectively. It was found that the $SiO_2$ layer inhibited Na ion diffusion and the formation of impurities like $Na_2SnO_3$ or SnO while increasing Sb ion concentration and higher ratio of $Sb^{5+}/Sb^{3+}$in the film. Annealing at nitrogen atmosphere leads to the reduction of $Sn^{4+}$ as well as $Sb^{5+}$ resulting in decrease of the electrical resistivity of the film.

• Proceedings of the Korean Powder Metallurgy Institute Conference
• /
• 2006.09b
• /
• pp.1097-1098
• /
• 2006

The Powder characteristics and sintering behavior of $SiO_2$ coated $BaTiO_3$ were studied. Silica coated $BaTiO_3$ powders were prepared by sol-gel method. The particle size of the $BaTiO_3$ powders were $\sim35$ nm and the thickness of the $SiO_2$ coating layer was $\sim5$ nm. As the $SiO_2$ content increased, the $SiO_2$ layers improved the powder dispersion. The Zeta potential of $SiO_2$ coated $BaTiO_3$ was getting close to that of pure silica with a more negative charge, compared with that of the uncoated $BaTiO_3$. The onset temperature of shrinkage curves shifted to higher temperatures with increasing $SiO_2$ contents

• Journal of the Korean Vacuum Society
• /
• v.19 no.5
• /
• pp.341-346
• /
• 2010

In this paper, anti-reflection coating was investigated for decreasing the reflection in visible range of 400~650 [nm] through four staked layers of $Si_xO_y$ and $Si_xN_y$ thin films prepared by reactive sputtering method. Si single crystal of 6 [inch] diameter was used as a sputtering target. Ar and $O_2$ gases were used as sputtering gases for reactive sputtering for the $Si_xO_y$ thin film, and Ar and $N_2$ gases were used for reactive sputtering for the $Si_xN_y$ thin film. DC pulse power of 1900 [W] was used for the reactive sputtering. Refractive index and deposition rate were 1.50 and 2.3 [nm/sec] for the $Si_xO_y$, and 1.94 and 1.8 [nm/sec] for the $Si_xN_y$ thin film, respectively. Considering the simulation of the four layer anti-reflection coating structure with the above mentioned films, the $Si_xO_y-Si_xN_y$ stacked four-layer structure was prepared. The reflection measurement result for that structure showed that a "W" shaped anti-reflection was obtained successfully with a reflection of 1.7 [%] at 550 [nm] region and a reflection of 1 [%] at 400~650 [nm] range.

• Journal of the Korean Ceramic Society
• /
• v.34 no.7
• /
• pp.677-684
• /
• 1997

The effects of fluxes on MgO coating materials for tundish were investigated. As the number of charge in continuous casting was increased, the basicity of tundish slag was decreased due to the increase of silica formed by dissolution from rice hull. As a result, the wear of magnesia lining was increased. In aggregates of MgO coating materials, magnesioferrite was formed by the reaction between magnesia and ferric oxide formed by the oxidation of molten steel, while matrix parts of MgO coating materials were worn by CaO-Al2O3-SiO2 compounds. Silica in rice hull extracted to the molten slag reduced basicity of slag and formed forsterite in the result of its reaction with magnesia lining. Also, fayalite was formed from the reaction between silica and ferric oxide and it caused the increment of magnesia lining's wear. The wear of magnesia lining by flux of CaO-SiO2 was larger than that of Cao-Al2O3 and calcia in the flux increased the wear of magnesia lining through the formation of rankinite.

• Journal of the Korean Ceramic Society
• /
• v.46 no.2
• /
• pp.189-199
• /
• 2009

The Powder characteristics and sintering behavior of $SiO_2$ coated $BaTiO_3$ were studied. $BaTiO_3$ powders were synthesized by the liquid mix method developed by Pechini, and silica coating was prepared by alkoxide hydrolysis method with TEOS and ethanol. The particle size of the $BaTiO_3$ powders was 35 nm and the thickness of the $SiO_2$ coating layer was 5 nm. As the $SiO_2$ content increased, the $SiO_2$ layers improved the powder dispersion by increasing electrostatic repulsion between the $BaTiO_3$ particles. Effects of MgO coating on microstructure and dielectric properties of $BaTiO_3$ have been studied compared with mechanically MgO mixed $BaTiO_3$. MgO coated $BaTiO_3$ particles were prepared by a homogeneous precipitation method using $MgCl_2\cdot 6H_2O$ and urea. MgO coated $BaTiO_3$ exhibited homogeneous microstructure compared with mixed samples. XRD analysis revealed that Mg substitution for the Ti site in the MgO mixed sample was much greater than in the coated one. Electrical properties of MgO mixed and coated $BaTiO_3$ were affected by the diffusion behavior of Mg in $BaTiO_3$ lattice.

• Corrosion Science and Technology
• /
• v.21 no.2
• /
• pp.111-120
• /
• 2022

To solve the corrosion problem of industrial equipment and other constructions containing metals, corrosion protection can be performed by using coating which provides a barrier between the metal and its environment. Coatings play a significant role in protecting irons and steels in harsh marine and acid environments. This study was conducted to identify an anti-corrosive epoxy coating for carbon steel composite with 0.1, 0.3, and 0.5 wt% concentrations of nanoparticles of SiO₂ using the dip-coating method. The electrochemical behavior was analyzed with open circuit potential (OCP) technics and polarization curves (Tafle) in 3.5 wt% NaCl and 5 vol% H₂SO₄ media. The structure, composition, and morphology were characterized using different analytical techniques such as X-ray Diffraction (XRD), Fourier Transform Infrared spectrum (FT-IR), and Scanning Electron Microscopy (SEM). Results revealed that epoxynano SiO₂ coating demonstrated a lower corrosion rate of 2.51 × 10^-4 mm/year and the efficiency of corrosion protection was as high as 99.77%. The electrochemical measurement showed that the nano-SiO₂ / epoxy coating enhanced the anti-corrosive performance in both NaCl and H₂SO₄ media.

• Journal of the Korean Ceramic Society
• /
• v.27 no.5
• /
• pp.583-588
• /
• 1990

Glass films in the binary system B2O3-SiO2 and Al2O3-SiO2 were prepared on soda-lime-silica slide glass by the dip-coating technique from TEOS and boric acid or aluminum nitrate. Thickness of the films varying with viscosity and withdrawal speed were measured and effect of composition and firing temperature on the properties such as transmittance and refractive index were investigated. nM2O3.(100-n)SiO2(M=B or Al) films containing up to 20mol% B2O3 and 40mol% Al2O3 were transparent. Maximum transmittance at visible range were obtained for the sample containing 15mol% Ba2O3 and 32.5mol% Al2O3 and heat-treated at 50$0^{\circ}C$, respectively. Refractive index of the film containing 15mol% B2O3 was mininum in the B2O3-SiO2 binary system and minimal refractive index was appeared at the film containing 32.5mol% Al2O3. In IP spectra, addition of B2O3 were increased absorption peak intensity of B-O and Si-O-B bond and addition of Al2O3 were decreased absorption peak intensity of Si-O bond, respectively.

• Proceedings of the Korean Ceranic Society Conference
• /
• 2002.10a
• /
• pp.183.2-183
• /
• 2002

• Journal of the Korean Ceramic Society
• /
• v.32 no.10
• /
• pp.1212-1218
• /
• 1995

Al2O3-coated SiC composite powder and mechanically mixed Al2O3-SiC composite powder were synthesized using Al-isopropoxide and commercial SiC as the starting materials. Experiment results showed that the sinterability of Al2O3-coated SiC composite powder was more improved than the mechanically mixed Al2O3-SiC composite powder by the effect of homogeneous coating of alumina around SiC particles. Hence, the mechanical properties of the former was also much more improved than the latter.