• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.33 no.11
• /
• pp.1233-1238
• /
• 2009

This study analyzed the characterization of high temperature strength of $Si_3N_4$ composite ceramics additive based on variations in the amount of nano colloidal $SiO_2$ added. Semi-elliptical cracks about 100 ${\mu}m$ length were obtained from a Vickers indenter using a load of 24.5 N. The results showed that the heat-treated smooth specimens with $SiO_2$ nano colloidal coating exhibited the highest bending strength at 0.0 wt% $SiO_2$ nano colloidal added, which is amounted to a 187 % increase over that of smooth specimen. Limiting temperature for bending strength of crack-healed zone for bending strength was about 1273 K. However, the bending strength of SSTS-3 and SSTS-4 was considerably increased while that of SSTS-1 and SSTS-2 was decreased at a temperature of 1,573K.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2005.07a
• /
• pp.35-37
• /
• 2005

100, 200nm 크기의 colloidal silica 각각에 나노 ceria 입자를 수열합성법으로 코팅하였다. Colloidal silica 입자에 ceria를 코팅 시 slurry의 pH조절과 수열처리에 이용하여 silica에 ceria가 코팅됨을 TEM과 zeta-potential을 이용하여 확인하였다. 연마 슬러리의 분산 안정성과 연마효율을 높이기 위하여 슬러리의 pH 는 9로 하였으며, 이때의 zeta-potential 값은 -25 mV이었다. 1 wt%로 제조된 연마슬러리를 이용하여, 4 inch $SiO_2$, $Si_3N_4$ wafer를 압력변화에 따른 연마특성을 관찰 하였다. Ceria coated colloidal silica 100 nm, 200 nm와 commercial한 $CeO_2$입자를 연마압력 6 psi로 oxide film을 연마한 결과 연마율이 각각 2490 ${\AA}/min$, 4200 ${\AA}/min$, 4300 ${\AA}/min$으로 측정되었다. 또한 $SiO_2$, $Si_3N_4$ film의 6 psi압력에서 ceria coated colloidal silica 100 nm, 200 nm와 commercial 한 $CeO_2$입자의 선택비는 3, 3.8, 6.7 이었다. 입자크기가 클수록 연마율이 높으며, Preston equation을 따라 연마 압력과 연마율이 비례하였다.

• Journal of the Korean Ceramic Society
• /
• v.41 no.4
• /
• pp.297-301
• /
• 2004

Nano-sized mullite (3Al$_2$O$_3$$.$2SiO$_2$) colloids were prepared by use of the spray combustion method. For combustion reaction, Al(NO$_3$)$_3$$.$9$H_2O$, and CH$_{6}$N$_4$O were used as an oxidizer and a fuel respectively, and then colloidal silica was also added as 2SiO$_2$source for mullite. The temperature of the reaction chamber was kept at 80$0^{\circ}C$ to initiate the ignition of droplets of the mixed precursors. For preventing droplet coagulation, the droplet number concentration was reduced using the metal screen filter, and the residence time of aerosol was kept at 2.5 seconds for laminar flow. The synthesized colloidal particles had an uniform spherical shape with 130 nanometer size and the crystalline phase showed the mullite with stoichiometry in the observations of XRD and TEM.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2005.07a
• /
• pp.107-108
• /
• 2005

Au and $Au/SiO_2$ nanoparticles(NPs) were synthesized by the colloidal method. The formation of Au and $Au/SiO_2$ NPs was confirmed using high resolution transmission electron microscopy (HRTEM). Synthesized solutions were deposited on Si wafer. The electrical properties of structures were measured using a semiconductor analyzer and a LCR meter. Capacitance versus voltage hysterisis curves showed the charge storage effect by Au and $Au/SiO_2$ NPs.

• Journal of the Korean Chemical Society
• /
• v.47 no.6
• /
• pp.619-624
• /
• 2003

The $Gd_{1.9-x}Li_{0.1}Eu_xO_3$ (x=0.02, 0.05, 0.08, and 0.12) powders (${\thickapprox}1{\mu}m$) synthesized by sol-gel method, whose surfaces are modified in a colloidal silica suspension (size of $SiO_2$ particles: ${\sim}30$ nm), have been fabricated to highly stable and effective luminescent films on the glass substrates. Thanks to the fused $SiO_2$ nano particles in the vicinity of the glass softening temperature (at around $700^{\circ}C$), $Gd_{1.9-x}Li_{0.1}Eu_xO_3$ powders are strongly attached onto the surface of glass substrate (>9H, pencil hardness tester). This simple and low-cost method to get $Gd_{1.9-x}Li_{0.1}Eu_xO_3$ phosphor films without any loss of luminescence brightness would promise for applications to display devices.

• Korean Journal of Materials Research
• /
• v.18 no.7
• /
• pp.379-383
• /
• 2008

We report on the light-emitting diode (LED) characteristics of core-shell CdSe/ZnS nanocrystal quantum dots (QDs) embedded in $TiO_2$thin films on a Si substrate. A simple p-n junction could be formed when nanocrystal QDs on a p-type Si substrate were embedded in ${\sim}5\;nm$ thick $TiO_2$ thin film, which is inherently an n-type semiconductor. The $TiO_2$ thin film was deposited over QDs at $200^{\circ}C$ using plasma-enhanced metallorganic chemical vapor deposition. The LED structure of $TiO_2$/QDs/Si showed typical p-n diode currentvoltage and electroluminescence characteristics. The colloidal core-shell CdSe/ZnS QDs were synthesized via pyrolysis in the range of $220-280^{\circ}C$. Pyrolysis conditions were optimized through systematic studies as functions of synthesis temperature, reaction time, and surfactant amount.

• Advances in nano research
• /
• v.13 no.1
• /
• pp.13-28
• /
• 2022

The pumpability of the grouts is significant issue in concept of the rheological and workability properties during penetrating to voids and cracks. To improve the fluidity features of the grout mixes, the usage of Colloidal Nano Particular Powders (CNPPs) with mineral additives such as fly ash (FA) can contribute. Therefore, the main purpose of this study can be explained as investigating the usage effects of four types of Colloidal Nano Particular Powders (n-TiO₂, n-ZnO, n-Al₂O₃ and n-SiO₂) as nano additives on the rheological, workability and bleeding properties of cement-based grout incorporated with fly as. Test results showed that the usage of FA in the grout samples positively contribute to increase on the fluidity of the grout samples as expected. The dilatant behavior was observed from the results for all mixes. Observing the effect of nano-sized additives in such cement-based grout mixtures with high fluidity has presented remarkable effects in this study.

• Journal of Powder Materials
• /
• v.21 no.5
• /
• pp.377-381
• /
• 2014

This work describes the coloration, chemical stability of $SiO_2$ and $SnO_2$-coated blue $CoAl_2O_4$ pigment. The $CoAl_2O_4$, raw materials, were synthesized by a co-precipitation method and coated with silica ($SiO_2$) and tin oxide ($SnO_2$) using sol-gel method, respectively. To study phase and coloration of $CoAl_2O_4$, we prepared nano sized $CoAl_2O_4$ pigments which were coated $SiO_2$ and $SnO_2$ using tetraethylorthosilicate, $Na_2SiO_3$ and $Na_2SiO_3$ as a coating material. To determine the stability of the coated samples and their colloidal solutions under acidic and basic conditions, colloidal nanoparticle solutions with various pH values were prepared and monitored over time. Blue $CoAl_2O_4$ solutions were tuned yellow color under all acidic/basic conditions. On the other hand, the chemical stability of $SiO_2$ and $SnO_2$-coated $CoAl_2O_4$ solution were improved when all samples pH values, respectively. Phase stability under acidic/basic condition of the core-shell type $CoAl_2O_4$ powders were characterized by transmission electron microscope, X-ray diffraction, CIE $L^*a^*b^*$ color parameter measurements.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2010.08a
• /
• pp.281-281
• /
• 2010

Very low refractive index (<1.4) materials have been proved to be the key factor improving the performance of various optical components, such as reflectors, filters, photonic crystals, LEDs, and solar cell. Highly porous SiO2 are logically designed for ultralow refractive index materials because of the direct relation between porosity and index of refraction. Among them, ordered macroporous SiO2 is of potential material since their theoretically low refractive index ~1.10. However, in the conventional synthesis of ordered macroporous SiO2, the time required for the crystallization of organic nanoparticles, such as polystyrene (PS), from colloidal solution into well ordered template is typical long (several days for 1 cm substrate) due to the low interaction between particles and particle - substrate. In this study, polystyrene - polyacrylic acid (PS-AA) nanoparticles synthesized by miniemulsion polymerization method have hydrophilic polyacrylic acid tails on the surface of particles which increase the interaction between particle and with substrate giving rise to the formation of PS-AA film by simply spin - coating method. Less ordered with controlled thickness films of PS-AA on silicon wafer were successfully fabricated by changing the spinning speed or concentration of colloidal solution, as confirmed by FE-SEM. Based on these template films, a series of macroporous SiO2 films whose thicknesses varied from 300nm to ~1000nm were fabricated either by conventional sol - gel infiltration or gas phase deposition followed by thermal removal of organic template. Formations of SiO2 films consist of interconnected air balls with size ~100 nm were confirmed by FE-SEM and TEM. These highly porous SiO2 show very low refractive indices (<1.18) over a wide range of wavelength (from 200 to 1000nm) as shown by SE measurement. Refraction indices of SiO2 films at 633nm reported here are of ~1.10 which, to our best knowledge, are among the lowest values having been announced.

• Korean Journal of Materials Research
• /
• v.14 no.8
• /
• pp.600-606
• /
• 2004

$Zn_{2}SiO_{4}:Mn$ phosphor particles were prepared by a flame spray pyrolysis method. It has been generally known that the high-temperature flame enables fast drying and decomposition of droplets. In the present investigation, the morphology and luminescent property of $Zn_{2}SiO_{4}:Mn$ phosphor were controlled in a severe flame preparation condition. The particle formation in the flame spray pyrolysis process was achieved by the droplet-to-particle conversion without any evaporation of precursors, which made it possible to obtain spherical $Zn_{2}SiO_{4}:Mn$ particles of a pure phase from a droplet. Using colloidal solutions wherein dispersed nano-sized silica particles were adopted as a silicon precursor. $Zn_{2}SiO_{4}:Mn$ particles with spherical shape and filled morphology were prepared and the spherical morphology was maintained even after the high-temperature heat treatment, which is necessary to increase the photoluminescence intensity. The $Zn_{2}SiO_{4}:Mn$ particles with spherical shape, which were prepared by the flame spray pyrolysis and posttreated at $1150^{\circ}C$, showed good luminescent characteristics under vacuum ultraviolet (VUV) excitation.