• 대한전기학회논문지:전기물성ㆍ응용부문C
• /
• 제54권12호
• /
• pp.573-577
• /
• 2005

[$TiO_2$] sol and $SiO_2$ sol were prepared using sol-gel method. As $H_{2}O$/Alkoxide ratios increased, sol had cluster structure and as $H_{2}O$/Alkoxide ratios decreased, sol had linear structure. Gelation time of $TiO_2$ sol was faster than that of $SiO_2$ sol according to the time. In comparison with initial viscosity between $TiO_2$ sol and $SiO_2$ sol, $TiO_2$ sol was highest at $H_{2}O/Ti(OC_{3}H_{7})_{4}=5$, $SiO_2$ sol was almost constant according to $H_{2}O/Si(OC_{2}H_{5})_{4}$ ratios.

• 한국세라믹학회지
• /
• 제41권6호
• /
• pp.471-475
• /
• 2004

졸겔 공정으로 안정한 TiO$_2$, SiO$_2$, PBA(Pseudo Boehemite Alumina) 졸을 제조하였다. 제조한 졸 용액은 비교적 균일한 10∼30nm의 입자크기를 나타내었다. TiO$_2$졸에 SiO$_2$졸의 첨가량이 증가함에 따라, anatase상에서 rutile 상으로 전이되는 상전이 온도를 $600^{\circ}C$ 이상으로 증가시켜 광분해 특성을 향상시켰다. 또한, TiO$_2$ 졸 용액에 SiO$_2$ 졸을 10∼30wt% 첨가하여 120$0^{\circ}C$ 이상의 고온 소성 후에도 anatase가 주된 상으로 소량의 rutile 상이 관찰되었다 또한 SiO$_2$20wt% 첨가 시, 최대의 광분해 특성을 나타내었다. 그러나, PBA 졸의 첨가는 첨가량에 관계없이 광분해 특성에 영향을 주지 않았다.

• 한국환경과학회지
• /
• 제11권6호
• /
• pp.597-603
• /
• 2002

Photocatalytic degradation of phenol was carried out with UV-illuminated TiO$_2$-SiO$_2$ in aqueous suspension. TiO$_2$-SiO$_2$ catalysts were prepared by sol-gel method from the titanium isopropoxide and tetraethylorthosilicate at different Ti/Si ratio and some commercial TiO$_2$ catalysts were used as purchased. All catalysts were characterized by X-ray Diffraction(XRD) and BET surface area analyzer. The effect of reaction conditions, such as initial concentration of phenol, reaction temperature and catalyst weight on the photocatalytic activity was studied. In addition, TiO$_2$-SiO$_2$(49: 1) prepared by sol-gel method showed higher activity than commercial TiO$_2$catalysts on the photocatalytic degradation of phenol. The addition of SiO$_2$ into TiO$_2$hepled to increase the thermal stability of titania which suppressed the formation of anatase into rutile. The photocatalytic degradation of phenol showed pseudo-1st order reaction and the degradation rate increases with decreasing initial phenol concentration.

• 한국세라믹학회지
• /
• 제32권4호
• /
• pp.507-515
• /
• 1995

The monolithic dry gels of the Li2O-Al2O3-TiO2-SiO2 system were prepared by the sol-gel technique using metal alkoxides as starting materials to obtain monolithic glass-ceramics at low temperature without melting. Activation energy for the crystal growth of the gel with 6.05% TiO2, nucleating ageng, for the preparation of Li2O-Al2O3-TiO2-SiO2 system glass-ceramic was 101.14kcal/mol. As a result of the analysis of DTA & XRD, it was confirmed that the crytallization of Li2O-Al2O3-TiO2-SiO2 system glass-ceramic was the most efficient when 6.05% TiO2, nucleating agent, was added. $\beta$-eucryptite solid solution crystals and $\beta$-spodumene solid solution crystals were detected in the sample heat treated above 85$0^{\circ}C$. The sintered gel heat treated at 85$0^{\circ}C$ had the specific surface area of 185$m^2$/g, the pore volume of 0.19cc/g and the average pore radius of 20.8$\AA$. This shows that the sintered gel is also comparatively porous material. In temperature range of 25~85$0^{\circ}C$ thermal expansion coefficient of the specimen which was crystallized for 10hrs at 85$0^{\circ}C$ was 6.7$\times$10-7/$^{\circ}C$, which indicated that the crystallized specimen was turned out to be the glass-ceramic with low thermal expansion.

• 한국세라믹학회지
• /
• 제44권3호
• /
• pp.137-141
• /
• 2007

$La_{2}O_{3}-TiO_{2}-SiO_{2}$ glass, a type that could not obtained so far by the conventional melting method, was prepared successfully using a sol gel process. Glass derived with the sol-gel process has compositions of $5La_{2}O_{3}-5TiO_{2}-90SiO_{2},\;5La_{2}O_{3}-10TiO_{2}-85SiO_{2}$, and $5La_{2}O_{3}-20TiO_{2}75SiO_{2}$. The UV-visible absorption edge of all glass compositions was below 400 nm. The measured density is in the range of 2.55-2.89, and was nearly identical to the calculated density and the refractive index of the glasses derived from the sol-gel ranges from 1.545 to 1.645. The molar additive coefficient of $TiO_{2}$ measured in this ternary system is lower than the calculated value, while the value of $La_{2}O_{3}$ is higher.

• Journal of Ceramic Processing Research
• /
• 제13권spc2호
• /
• pp.373-376
• /
• 2012

Thin films of Ag-SiO2-TiO2 composite oxides with SiO2/TiO2 of 20/80 molar compositions were prepared by the sol-gel method, using tetraethylorthosilicate (TEOS) and titanium isopropoxide (TIP) as precursors. Ag-SiO2-TiO2 films coated on commercial glass substrates have successfully been synthesized using sol-gel method. The Ag-SiO2-TiO2 film with 0.5% Ag-added concentration and 20 mol% SiO2-mixture gives optimal results on crystalline structure, optical property, surface area, and photochromic property. Absorption near the wavelength of the incident light decreased gradually. The reversibility of the two-photon writing process in Ag-SiO2-TiO2 film is clearly seen.

• Bulletin of the Korean Chemical Society
• /
• 제19권11호
• /
• pp.1185-1188
• /
• 1998

Layered nanocomposite, SiO2/TiO2 sol pillared clay, has been prepared by the ion exchange reaction of Na' ion in montmorillonite with positively charged mixed SiO2/TiO2 sol. The nanosized sol particles were synthesized by mixing SiO2 sol solution with TiO2 one, which is obtained by acidic hydrolysis of TEOS and TiCl4, respectively. From powder XRD, the basal spacing (d001) of the sample calcined at 400 ℃ was found to be ca. 60 Å, due to the multistacking of nanosized SiO2 and TiO2 sol particles, which was confirmed by the pore size analysis from 129Xe NMR and micropore analysis calculated from nitrogen adsorption. The BET specific surface area shows the value of 684 m2g-1 (Langmuir 1115 m2g-1), which is the highest among various pillared clays ever reported previously, and the total porosity is found to be 0.51 mlg-1, and the pores are mainly composed of micropore with a size of ca. 11.8 Å. This result agrees with the adsorption capacity obtained from water adsorption. According to diffuse reflectance ultraviolet-visible spectroscopy, it is found that the TiO2 particles stabilized in the interlayer space of montmorillonite are quantum-sized of ca. 20 Å.

• 한국결정성장학회지
• /
• 제8권2호
• /
• pp.307-314
• /
• 1998

졸-겔법을 이용하여 PZT박막을 제조하였다. 출발물질로는 Pb-acetate trihydrate, Zr-normal propoxide와 Ti-ispropoxide를 사용하였으며, 용매로는 2-Methoxyethanol과 iso- Propanol을 사용하였다. 기판에 따른 Pb 이온 및 Si 이온의 확산을 고찰하기 위해 bare Si와 열산화된 $SiO_2/Si$ 그리고 산화된 기판 위에 졸-겔 spin-coating법으로 $TiO_2$를 입힌 $TiO_2/SiO_2/Si$ 기판을 사용하였다. 박막의 치밀화 및 기판과의 접착상태는 SEM을 이용하였고, 상생성 온도는 XRD, 그리고 Pb 이온 및 Si 이온의 확산 정도는 ESCA를 사용하였다. 기판으로 bare Si 및 $SiO_2/Si$를 사용한 경우, $700^{\circ}C$에서 perovskite상을 얻을 수 있었으며, SiO2/Si 기판을 사용하여 Si의 막으로의 확산을 다소 방지할 수 있었다. $TiO_2/SiO_2/Si$기판을 사용한 경우, $500^{\circ}C$에서 perovskite상을 얻을 수 있었고, Pb 이온 및 Si 이온의 확산을 방지할 수 있었다.

• Corrosion Science and Technology
• /
• 제14권2호
• /
• pp.64-75
• /
• 2015

Single $TiO_2$ coating prepared by sol-gel process usually experiences cracks in coating layer. In order to prevent cracks, an inorganic-organic hybrid $TiO_2-SiO_2$ coating was synthesized by combining precursors with an organic functional group. Five different coatings with various ratios of (1:8, 1:4, 1:1, 1:0.25 and 1:0.125) titanium alkoxide (TBOT, Tetrabutylorthotitanate) to organo-alkoxysilane (MAPTS, ${\gamma}$-Methacryloxy propyltrimethoxysilane) on carbon steel substrate were made by sol-gel dip coating. The prepared coatings were analyzed to study the coating properties (surface crack, thickness, composition) by scanning electron microscope (SEM), focused ion beam (FIB), and Fourier transform infrared spectroscopy (FT-IR). Potentiodynamic polarization tests and electrochemical impedance spectroscopy (EIS) were also performed to evaluate the corrosion characteristics of the coatings. Crack free $TiO_2-SiO_2$ hybrid coatings were prepared with the optimization of the ratio of TBOT to MAPTS. The corrosion rates were significantly decreased in the coatings for the optimized precursor ratio without cracks.

• 한국응용과학기술학회지
• /
• 제25권2호
• /
• pp.130-136
• /
• 2008

$xTiO_2$-$ySiO_2$ system photocatalysts were developed by sol-gel method based on the change of production parameters, and their structure of crystallization and the specific surface area were measured. Considering the efficiency of the ethanol and phenol degradation using the catalyst, the conclusions were obtained as follows: By means of X-ray analysis of $xTiO_2$-$ySiO_2$ powder that is obtained from Titanium and Silicon alkoxide by sol-gel process, it is shown that crystal structure of anatase type is a dominating structure and, on the other hand, the structure of rutile also partly exists. The increase of $SiO_2$ contents causes the decrease of the degree of crystallization of the gel, whereas the specific surface area preferentially increases. It is shown that more than 90% of ethanol and phenol are degraded when reaction time is about three and an hours, and the maximum degradation rate of ethanol and phenol is shown in $60TiO_2$-$40SiO_2$ catalyst.