The microwave dielectric properties and microstructure of the (1-x)$Mg_4Ta_2O_{9-x}TiO_2$(X=0, 0.3, 0.4) ceramic were, investigated. The specimens were prepared by the conventional mixed oxide method with sintering temperature of $1350^{\circ}C$∼$1425^{\circ}C$. According to the XRD patterns, the (1-x)$Mg_4Ta_2O_{9-x}TiO_2$(X=0, 0.3, 0.4) ceramics have the $Mg_4Ta_2O_{9}$ phase(hexagonal). The dielectric constant($\varepsilon$$_{\gamma}$) and density increased with sintering temperature and mole fraction of x. To improve the quality factor and the temperature coefficient of resonant frequency, TiO$_2$($\varepsilon_{r}$=100, $Q{\times}f_{r}$=40,000GHz, $\tau$$_{f}$=＋450 ppm/$^{\circ}C$) was added in $Mg_4Ta_2O_{9}$ ceramics. In the case of the $0.7Mg_4Ta_2O_{9}$-$0.3TiO_2$ and the $0.6Mg_4Ta_2O_{9}$-$0.4TiO_2$ceramics sintered at $1400^{\circ}C$ for 5hr., the microwave dielectric properties were $\varepsilon$$_{\gamma}$=11.72, $Q{\times}f_{r}$=126,419GHz, $\tau_{f}$=-31.82 ppm/$^{\circ}C$ and $\varepsilon_{r}$=12.19, $Q{\times}f_{r}$=109,411GHZ, $\tau$$_{f}$= -17.21 ppm/$^{\circ}C$, respectively.

• 한국자기학회지
• /
• 제11권5호
• /
• pp.222-225
• /
• 2001

1W급의 DC-DC converter에 탑재하기 위해 FeTaN 연자성 자성박막을 이용한 박막형 인덕터를 제조하여 특성을 평가하였다. 자심부분은 2$\mu\textrm{m}$ 두게의 F $e_{78.81}$T $a_{8.47}$ $N_{12.71}$ 연자성 박막을 사용하였으며 코일부분은 100$\mu\textrm{m}$ 두게의 Cu를 사진공정과 전기도금공정을 이용하여 제조하였다. 제조된 박막 인덕터의 디자인은 상호인덕턴스를 효율적으로 증가시킬 수 있는 double rectangular spiral형태였으며 측정된 특성은 DC-DC converter의 작동주파수인 1 MHz에서 인덕턴스 980nH, 저항 1.7 $\Omega$Q 값은 3.55였다.다.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 1998년도 춘계학술대회 논문집
• /
• pp.371-373
• /
• 1998

The SmBa$_2$Cu$_3$O$\sub$x/ single crystals were used as seeds to induced YBCO growth in MTG process. As the result, the large bulk oriented YBCO superconductors were prepared with dimension of plane 21mm and 32mm in diameter and 10mm in height. The typical Jc value of the sample is 6.5${\times}$10$^4$A/$\textrm{cm}^2$ and its flux float force is 4.6N/$\textrm{cm}^2$. The oxygen absorption in large bulk textured YBCO samples in pure oxygen was studied at several constant temperatures. It can be divided into two steps: a chemical reaction step and a diffusion step.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 1998년도 춘계학술대회 논문집
• /
• pp.491-493
• /
• 1998

The SmBa$_2$Cu$_3$O$\sub$x/ single crystals were used as seeds to induced YBCO growth in MTG process. As the result, the large bulk oriented YBCO superconductors were prepared with dimension of plane 21mm and 32mm in diameter and 10mm in height. The typical Jc value of the sample is 6.5${\times}$10$^4$A/$\textrm{cm}^2$ and its flux float force is 4.6N/$\textrm{cm}^2$. The oxygen absorption in large bulk textured YBCO samples in pure oxygen was studied at several constant temperatures. It can be divided into two steps: a chemical reaction step and a diffusion step.

• 한국광학회지
• /
• 제10권2호
• /
• pp.152-156
• /
• 1999

여기밀도 변화에 따른 펄스폭 연속 가변 Quenched Dye Laser(Q이)를 설계 제작하여 그 동작 특성을 분석하였다. 펌핑광원은 펄스폭 20 ns(FWHM), 에너지 150mJ의 XecCl 엑시머 레이저를 사용하였으며, 색소레이저의 활성매질은 Rhodamine 6G로서 에탄올(ethanol)용액에 2.5$\times$10-3[mol/l]의 농도로 용해되었다. 활성길이 5 nm인 색소셀에서 서로 평행한 양면을 공진기로 구성하여 색소레이저의 이완발진 출력특성을 얻었다. 이완발진의 펄스열에서 단일 펄스를 추출하기 위해 QDL를 구성하였다. QDL의 펄스폭을 가변하기 위해 초점거리 f=150 mm 접속렌즈를 이동시켜 색소셀에 조사되는 공간적 펌핑폭을 조절함으로써 여기밀도를 8.8$\times$1023[cm-3s-1]~2.8$\times$1023[cm-3s-1]까지 가변시켰다. 공간적 펌핑폭에 따른 펄스폭 가변 실험을 수행한 결과 QDL의 발진 펄스폭이 86 ps~201 ps 사이에서 연속적으로 가변됨을 알 수 있었다.