$NH_4Cl$을 염소화제로 사용하여 시약 PbS와 Pb함유 자연광물인 방연광의 염소화 반응에 대해 조사하였다. 방연광의 적정 염소화 반응조건은 반응온도 $425^{\circ}C$, 방연광에 대한 $NH_4Cl$의 무게비 4.0, 반응시간 2시간이었다. 이 조건하에서 방연광중의 PbS는 $NH_4Cl$에 의해 효과적으로 $PbCl_2$로 염소화되었으며 그 전화율은 90%였다. 방연광의 염소화 반응에서 염소화제로 사용한 $NH_4Cl$은 $NH_3$와 HCl로 효과적으로 분리되었으며 양론적으로 90%의 $NH_3$를 회수할 수 있었다.

• Electronic Materials Letters
• /
• 제14권6호
• /
• pp.700-711
• /
• 2018

CdS synthesized by the chemical bath method at $70^{\circ}C$, has been used as an electron transport layer in the planar structure of the perovskite solar cells. A two-step spin process produced a mixed halide perovskite of $CH_3NH_3PbI_{3-x}Cl_x$ and a mixture of $PbCl_2$ and $PbI_2$ was deposited on CdS, followed by a sub-sequential reaction with MAI ($CH_3NH_3I$). The added $PbCl_2$ to $PbI_2$ in the first spin-step affected the structure, orientation, and shape of lead halides, which varied depending on the content of Cl. A small amount of Cl enhanced the surface morphology and the preferred orientation of $PbI_2$, which led to large and uniform grains of perovskite thin films. In contrast, the high content of Cl produces a new phase PbICl in addition to $PbI_2$, which leads to the small and highly uniform grains of perovskites. An improved surface coverage of perovskite films with the large and uniform grains maximized the performance of perovskite solar cells at 0.1 molar ratio of $PbCl_2$ to $PbI_2$. The depth profiling of elements in both lead halide films and mixed halide perovskite films were measured by Rutherford backscattering spectroscopy, revealing the distribution of chlorine along with the thickness, and providing the basis for the mechanism for enhanced preferred orientation of lead halide and the microstructure of perovskites.

• 한국세라믹학회지
• /
• 제24권4호
• /
• pp.397-403
• /
• 1987

Pb(Zr0.52Ti0.48)O3 powders were prepared by hydrothermal synthesis. Using soluble salts such as Pb(NO3)2, TiCl4 and ZrOCl2$.$8H2O and oxide such as PbO and TiO2 as starting materials, PZT powder was hydrothermally synthesized at the temperature range between 150$^{\circ}C$ and 200$^{\circ}C$. The result showed that reactivity by alkali was decreased in the sequence of Pb(NO3)2, TiCl4, ZrOCl2, PbO, TiO2 and ZrO2. Using the first three soluble salts, PZT powder was synthesiged at 150$^{\circ}C$ for 1hr. In PbO-TiCl4-ZrOCl2 system, PZT powder was synthesized at 150$^{\circ}C$ for 8rs. In Pb(NO3)2-TiO2-ZrOCl2 system, PZT powder was synthesized at 150$^{\circ}C$ for 16hrs, in PbO-TiO2-ZrOCl2 system, the powder was synthesized at 200$^{\circ}C$ for 8hrs.

• 자원리싸이클링
• /
• 제9권4호
• /
• pp.3-15
• /
• 2000

전기로 더스트 중에 함유된 Zn, Pb, Cl, Fe, Cu 및 Cd의 건식 환원반응기구를 규몽하고자 탄소뿔 첨가한 더스트 Briquette를 제조하여 Ar 가스 분위기 하의 $800^{\circ}C$ ~ $1100^{\circ}C$반응온도에서 실험을 행하였다. 탄소에 의한 Zn 화합물으 환원반응은 온도상승에 따라 민감하게 나타났으며 반응초기에는 화학반응에 의한 음속단계로 활성화에너지 값은 약 120.6 kl/mole이었다. 한편, Pb와 Cl은 $PbCl_2$의 형태로 휘발되었으며 이들의 휘발제거율은 거의 일치하였다. 또한, 환원제를 첨가하지 않는 경우가 환원제 첨가시 보다 휘발제거율이 빨라 Pb의 대부분은 염화휘발에 의해 제거됨을 알 수 있었다. Cu는 염화휘발에 의해 최대 약 30% 제거되고 나머지 대부분은 Fe와 함께 더스트 중에 잔존하여 Cd은 $1000^{\circ}C$에서 15분만에 거의 100%의 휘발제거율을 나타내었다.

• Bulletin of the Korean Chemical Society
• /
• 제21권3호
• /
• pp.317-320
• /
• 2000

Layered $K_2NiF_4$type ($C_nH_{2n+1}NH_3)_2PbCl_4$(n=6, 8 and 10) system, or alkylammonium tetrachloroplumbate compound, has been synthesized from $PbCl_2$ and $C_nH_{2n+1}NH_3Cl$ solutions under argon ambient pressure for 12hrs at $90^{\circ}C$. The crystal structure of the compound has been analyzed using X-ray powder diffaction in the range of $5^{\circ}{\leq}2{\theta}{\leq}55^{\circ}$, and all samples assigned to an orthorhombic system. Local distances of the Pb-Cl bond have been determined by Pb $L_{III}$-edge extended X-ray absorption fine structure (EXAFS) spectroscopy. The vibration modes of alkylammonium chains and the absorpton peaks of an excition have been examined by FT-IR and UV-Vis. reflectance spectra, respectively. The phase transition temperatures of the compounds have been studied by using DSC. According to the thermal analysis, two phase transition temperatures have been observed in the compositons of n=8 and 10.

• 동의생리병리학회지
• /
• 제16권1호
• /
• pp.154-159
• /
• 2002

There are several types of salts that can be classified into raw salt(Chunil salt), purified salts(NaCl reagent grade) and processed salts(Bamboo salt, Purple bamboo salt using in this study) in Korea. Salts has been utilized for the food as well as for the drug in the Oriental Medicine. Purple bamboo salt(PB-salt) was made by heating up to 1300℃ nine times after putting the raw salts in the bamboo. Since salt is generally known to cause the blood pressure to elevate, this study was conducted to investigate the effect of PB-salt on an adverse reaction of the blood pressure elevation. The experiment was performed with the 2 protocols ; 1. Effect of NaCl and PB-salt administration i.v. with the different the concentration(250, 500, 750, 1000mg/kg) on a mean artery blood pressure(MAP) change. 2. Effect of 500mg/kg NaCl and PB-salt administration p.o. for 6 days on the systolic blood pressure change. The results were as follows; The results were as follows; In a short minute change of blood pressure by direct method, PB-salt adminstration did not induced the hypertension unlike NaCl adminstration. In a date change of blood pressure by indirect method, systolic blood pressure was increased about 12-18% in the NaCl administration group, whereas within 6% in the PB-salt administration group from 2 days to 5 days. These results suggest that PB-salt might have some unidentified ingredient to be changed in the course of processing, making it superior to other salts.

• 자원리싸이클링
• /
• 제6권1호
• /
• pp.35-39
• /
• 1997

EAF Dust 중 염화물의 존재형태를 파악하고, 온도에 따른 휘발 거동과 제거에 관하여 알아보기 위해 실험을 하였다. 두시료의 화학성분은 더스트A의 경우 27.3%FE, 21.8%Zn, 3.15%Pb, 3.51%Cl이고 더스트B의 경우 33.92%FE, 15.94%Zn, 2.73%Pb, 3.98%Cl를 함유하다. EAF Dust 중 염화물의 존재형태를 X선회절분석과 수침출을 통해 분석한 결과 염화물의 존재형태는 NaCl, KCl, Ph(OH)Cl로서 주로 존재함을 알았다. 온도에 따른 Chlorine의 휘발율을 산화성분위기와 환원성분위기에서 살펴본 결과, 각각 110$0^{\circ}C$에서 1시간 유지하였을 경우 산화성분위기에서는 99%까지, 환원성분위기에서는 96%까지 휘발제거되었다.

• Corrosion Science and Technology
• /
• 제17권3호
• /
• pp.116-122
• /
• 2018

The secondary coolant of a nuclear power plant has small amounts of various impurities (S, Pb, and Cl, etc.) introduced during the initial construction, maintenance, and normal operation. While the concentration of impurities in the feed water is very low, the flow of the cooling water is restricted, so impurities can accumulate on the Top of Tubesheet (TTS). This environment is chemically very complicated and has a very wide range of pH from acidic to alkaline. In this study, the characteristics of the oxide and the mechanism of stress corrosion cracking (SCC) are investigated for Alloy 690 TT in alkaline solution containing Pb, Cl, and S. Reverse U-bend (RUB) specimens were used to evaluate the SCC resistance. The test solution comprises 3m NaCl + 500ppm Pb + 0.31m $Na_2SO_4$ + 0.45m NaOH. Experimental results show that Alloy 690 TT of the crevice environment containing Pb, S, and Cl has significant cracks, indicating that Alloy 690 is vulnerable to stress corrosion cracking under this environment.

• 유기물자원화
• /
• 제26권2호
• /
• pp.33-41
• /
• 2018

매년 가로수로부터 많은 양의 낙엽이 발생하고 이는 적절하게 수거하여 처리해야 한다. 왕벚나무는 우리나라에서 일반적인 가로수이다. 왕벚나무 잎(CL)과 그것으로부터 제조된 바이오차(CB)의 Pb(II) 흡착특성에 관한 회분식 실험을 수행하였다. 바이오차는 $800^{\circ}C$에서 90분간 탄화시켜 제조하였다. 흡착특성을 규명하기 위해 동력학적 및 등온 흡착실험을 수행하였다. 탄화과정은 바이오차의 탄소함량과 pH 값을 증가시키고 수소와 산소함량을 감소시켰다. 또한, 잘 발달된 공극 구조가 바이오차의 표면에 관찰되었다. CL과 CB에 의한 Pb(II) 흡착은 2차 속도모델에 의해 적절하게 설명될 수 있는 것으로 나타나 흡착반응의 속도가 물리적 흡착보다는 화학적 흡착에 의해 결정됨을 알 수 있었다. CB는 CL에 비해 더 빠른 흡착반응과 높은 흡착용량을 가지는 것으로 나타났다. Pb(II)의 등온흡착 특성은 Langmuir 모델에 의해 보다 적절하게 설명될 수 있는 것으로 나타났다. Langmuir 상수, $Q^0$에 의해 설명되는 최대흡착용량은 CL이 37.31 mg/g, CB가 94.34 mg/g으로 나타났다.

• 공업화학
• /
• 제5권5호
• /
• pp.862-870
• /
• 1994

출발물질로 $Pb(NO_3)_2$, $Mg(NO_3)_2$, $NbCl_5$를 선정하여 이들을 수용액상으로 $Pb(Mg_{1/3}Nb_{2/3})O_3$조성에 맞도록 각 수용액을 정확히 취하여 $Pb(Mg_{1/3}Nb_{2/3})O_3$ 1M용액이 되도록 조제하였다. 이 혼합용액은 상온에서 $PbCl_2$를 형성하므로 $70^{\circ}C$로 가열하여 $PbCl_2$를 용해시킨 후, 침전제 oxine을 가하여 pH 8~10에서 공침물을 얻었다. 이 침전물을 여과, 건조의 공정을 거처 $700{\sim}1000^{\circ}C$로 5시간 하소하여 $Pb(Mg_{1/3}Nb_{2/3})O_3$을 합성하였으며 합성된 분말은 평균입경이 $0.3{{\mu}m}$ 정도이고 모양은 구형이었다. 그리고 합성된 분말을 $2000Kg/cm^2$의 압력으로 성형하고, $1100{\sim}1200^{\circ}C$로 소성하여 이론밀도의 97.4%인 소결체를 얻었고 이때의 유전율은 1kHz에서 17000이고 유전손실은 상온에서 0.02%이었다.