• Journal of the Korean Ceramic Society
• /
• v.27 no.2
• /
• pp.187-194
• /
• 1990

Effects of MnO2 addition ranged from 0.0wt% to 5.0wt% on the microstructure and dielectric and piezoelectric properties of the Pb(Zr0.52 Ti0.48)O3 Ceramics have been investigated. The solubility limit of MnO2 in Pb(Zr0.52 Ti0.48)O3 is about 0.5wt%, and MnO2 as a valence state of Mn3+ is substituted for (Zr, Ti) lattice site in PZT solid-solution. The addition of MnO2 up to 0.5wt% in Pb(Zr0.52 Ti0.48)O3 brings increase of density, but decreased of grain size and tetragonality. Dielectric constant slightly decreases, but both coupling factor(Kp) and mechanical quality factor(Qm) increase with the addition of MnO2. However, excess amount of MnO2 addition more than 0.75wt% results in rapid decrease of resistance. Dielectric constant and tan $\delta$ increase due to the second phase and inhomogeneous Mn distribution.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 1996.11a
• /
• pp.54-58
• /
• 1996

In this paper, the structure, dieletric and piezoelectric properties of Pb(Fe$_{\frac{1}{2}}$/Sb$_{\frac{1}{2}}$$O_3$+ Pb(Zr$_{0.52}$ Ti$_{0.48}$ )O$_3$system ceramics were investigated and the effects of donor Nb$^{+5}$ on these properties were characterized for the application of the actuator. In xPb(Fe$_{\frac{1}{2}}$Sb$_{\frac{1}{2}}$)O$_3$+ (1-x) Pb(Zr$_{0.52}$ Ti$_{0.48}$ )O$_3$system ceramics, tetragonality decreased as x and Nb$_2$O$_{5}$ wt% were increased. In 0.05Pb(Fe$_{\frac{1}{2}}$Sb$_{\frac{1}{2}$}$)O$_3$+ 0.95 Pb(Zr$_{0.52}$ Ti$_{0.48}$ )O$_3$system, grain size was smallest but showed best dielectric and piezoelectric properties. The specimen sintered at 120$0^{\circ}C$ in 0.05pb(Fe$_{\frac{1}{2}}$Sb$_{\frac{1}{2}}$ )O$_3$+ 0.95 Pb(Zr$_{0.52}$ Ti$_{0.48}$ )O$_3$+ Nb$_2$O$_{5}$ 0.6wt% exihibited best piezoeletric properties such as $K^{p}$ =64%, d$_{33}$ =490 [$\times$10$^{-12}$ C/N] and strain was 1320[$\times$10$^{-6}$ Δ$\ell$/$\ell$]at AC 6kV/cm

• Journal of the Korean Ceramic Society
• /
• v.28 no.4
• /
• pp.297-304
• /
• 1991

Dielectric hysteresis characteristics of Pb(Zr0.52Ti0.48)O3 ceramics have been investigated as a function of the amount of MnO2 addition ranged from 0.0 wt% in Pb(Zr0.52Ti0.48)O3 ceramics enhanced the dielectric strength, aging effect and remanent polarization, while reduced the coercive field. These results could be explained by the effect of Mn-Vo association due to the substitution of Mn for the (Zr, Ti) site in PZT.

• Journal of the Korean Ceramic Society
• /
• v.32 no.3
• /
• pp.378-384
• /
• 1995

Effects of $La_2O_3$, $MnO_2$ on the dielectric and piezoelectric properties of $0.02Pb(Y_{2/3}W_{1/3}O_3-0.98Pb(Zr_{0.52}Ti_{0.48})O_3$ system were investigated. The addition of La2O3 to the system enhanced electromechanical coupling factor (kp), piezoelectric constant (d33), but hardly changed mechanical quality factor (Qm). On the other hand, the addition of $MnO_2$ increased Qm significantly, but did not degrade kp and d33 so much. The piezoelectric properties of $0.02Pb(Y_{2/3}W_{1/3}O_3-0.98Pb(Zr_{0.52}Ti_{0.48})O_3$ containing 0.1wt% $La_2O_3$, 0.4wt% $MnO_2$ were very good and kp, d33, Qm were 55%, 350$\times$10-12C/N, 780, respectively. The size of the grains was proportional to the change of c/a (tetragonality) ratio caused by the addition of $La_2O_3$ and $MnO_2$, and dielectric, piezoelectric properties were sensitive to the amountof pyrochrole phase.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 1995.05a
• /
• pp.14-16
• /
• 1995

Pb($Zr_{0.52}Ti_{0.48}$)$O_3$ ceramic thin films were fabricated from an alkoxide-based solution by Sol-Gel method. Pb($Zr_{0.52}Ti_{0.48}$)$O_3$ co-ramic thin films were formed by spin coating method on Pt/$SiO_2$/Si substrate at 4000[rpm] for 30 [sec]. Coated specimens were dried on the hot-plate at 400[$^{\circ}C$] for 10[min]. The coating process was repeated 6 times and then sintered at temperature between 500 ~ 800[$^{\circ}C$] for 1 hour. The ferroelectric perovskite phases precipitated under the sintering of 700[$^{\circ}C$] for 1 hour. Pb($Zr_{0.52}Ti_{0.48}$)$O_3$ thin film sintered at 700[$^{\circ}C$] for 1hour showed good dielectric constant (2133) and dielectric loss (2.2[%]) Properties. The switching voltage, switching time and leakage currents density were 3.0[V], 1.7[${\mu}$sec] , 160[pA/$\textrm{cm}^2$] repectively.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 1994.11a
• /
• pp.168-170
• /
• 1994

Pb($Zr_{0.52}$$Ti_{0.48}$)$O_3$ ceramic thin films were fabricated from an alkoxide-based solution by Sol-Gel method. Pb($Zr_{0.52}$$Ti_{0.48}$)$O_3$ ceramic thin films were formed by spin coating method on Pt/$SiO_2$Si substrate at 4000ppm for 30 seconds. The coating process was repeated 6 times and then heat-treated at temperature between 500∼800[$^{\circ}C$] for 1 hour. The final thickness of the thin films were about 4800[A]. The ferroelectric perovskite phases precipitated under the heat-treated at 700[$^{\circ}C$] for 1 hour. Pb($Zr_{0.52}$$Ti_{0.48}$)$O_3$ thin films heat-treated at 700[$^{\circ}C$] for 1 hour showed good dielectric and ferroclectric properties.

• Proceedings of the KIEE Conference
• /
• 1994.07b
• /
• pp.1454-1456
• /
• 1994

$Pb(Zr_{0.52}Ti_{0.48})O_3$ ceramic thin films were fabricated from an alkoxide-based solution by Sol-Gel method. $Pb(Zr_{0.52}Ti_{0.48})O_3$ ceramic thin films were formed by spin coating method on $Pt/SiO_2/Si$ substrate at 3000rpm for 30 seconds. The coating process was repeated 6 times and then heat-treated at temperature between 500 - $800[^{\circ}C]$ for 1 hour. The final thickness of the thin films were about 4800[A]. The 100% ferroelectric perovskite phases precipitated under the heat treated at $700[^{\circ}C]$ for 1 hour. $Pb(Zr_{0.52}Ti_{0.48})O_3$ thin films heat-treated at $700[^{\circ}C]$ for 1 hour showed good dielectric constant (812) property.

• Journal of the Korean Ceramic Society
• /
• v.48 no.5
• /
• pp.471-478
• /
• 2011

Investigations of crystal structure and phase transition of $Pb(Zr_{0.52}Ti_{0.48})O_3$ ceramics doped with A-site substitution impurity (La, Nd) or B-site substitution impurity (Sb, Nb) at 2 mol% concentration were carried out. X-ray diffraction patterns of impurities doped $Pb(Zr_{0.52}Ti_{0.48})O_3$ ceramics have been measured at pressures up to ~5 GPa with diamond anvil cell and synchrotron radiation. The patterns were obtained at room temperature using methanol-ethanol mixture as pressure-transmitting media. In order to refine the crystal structure, Rietveld analysis has been performed. The structures of impurities doped $Pb(Zr_{0.52}Ti_{0.48})O_3$ ceramics are tetragonal in space group P4mm at ambient pressure and are transformed into a cubic phase in space group Pm$\bar{3}$m as the pressure increases. In this study, when A-site substitution donor $La^{3+}$ or $Nd^{3+}$ ion was added to $Pb(Zr_{0.52}Ti_{0.48})O_3$ ceramics, the phase transition phenomena showed up at the pressure of 2.5~4.6 GPa, but when B-site substitution donor $Nb^{5+}$ or $Sb^{5+}$ ion was added to it, the phase transition appeared at relatively lower pressure of 1.7~2.6 GPa.

• Journal of the Korean Ceramic Society
• /
• v.30 no.1
• /
• pp.1-6
• /
• 1993

Dielectric and piezoelectric porperties of pseudoternary xPb(Al2/3W1/3)O3-(1-x)Pb(Zr0.52Ti0.48)O3 (x=1~10mol%) ceramic system have been investigated as a function of the amount of PAW[Pb(Al2/3W1/3)O3] and sintered from 110$0^{\circ}C$ to 120$0^{\circ}C$ for 1hr. As the amount of PAW increases, the c/a of tetragonal structure decreases. The grain size was reduced with increasing the amount of PAW addition. However, the density, dielectric constant and electromechanical coupling factor(kp) exhibited a maximum value at the amount of 5mol% PAW addition.

• Electrical & Electronic Materials
• /
• v.8 no.5
• /
• pp.606-610
• /
• 1995

In this study, Pb(Z $r_{0.52}$ $Ti_{0.48}$) $O_{3}$ ceramic thin films were fabricated from an alkoxide-based by Sol-Gel method. Pb(Z $r_{0.52}$ $Ti_{0.48}$) $O_{3}$ stock solution was made and spin-coated on the Pt/ $SiO_{2}$/Si substrate at 4000[rpm] for 30[sec.]. Coated specimens were chied at 400[.deg. C] for 10[min]. The coating process was repeated 6 times and then heat-treated at 500-800[.deg. C] and 1 hour. The final thickness of the thin films were about 4800[.angs.]. The ferroelectric perovskite phases precipitated under the sintering of 700[.deg. C] for 1 hour. Pb(Z $r_{0.52}$ $Ti_{0.48}$) $O_{3}$ thin films sintered at 700[.deg. C] for 1 hour showed good dielectric and ferroelectric properties.