• Electrical & Electronic Materials
• /
• v.9 no.10
• /
• pp.991-1000
• /
• 1996

PbTiO$_{3}$-PbZrO$_{3}$-Pb(Ni$_{1}$3/Nb$_{2}$3/O$_{3}$) (PZT-PNN) thin films were prepared from corresponding metal organics partially stabilized with diethanolamine by the sol-gel spin coating method. Each mol ratio of PT:PZ:PNN solutions were #1(50:40:10), #2(50:30:20), #3(45:35:20), #4(40:40:20), #5(40:50:10), #6(35:45:20) and #7(30:50:20) respectively. The spin-coated PZT-PNN films were heat-treated at 350.deg. C for decomposition of residual organics, and were sintered from 450.deg. C to 750.deg. C for crystallization. The substrates, such as Pt and Pt/TiN/Ti/TiN/Si were used for the spin coating of PZT PNN films. The perovskite phase was observed in the PZT-PNN films heat-treated at 500.deg. C. The crystalline of the PZT-PNN films was optimized at the sintering of 700.deg. C. By the result of AES analysis, It is confirmed that the films of TiN/Ti/TiN was a good diffusion barrier and that co-diffusion into the each films was not observed.

• Electrical & Electronic Materials
• /
• v.6 no.3
• /
• pp.241-247
• /
• 1993

본 연구에서는 투광성 0.085Ba(L $a_{1}$2/N $b_{1}$2/) $O_{3}$- 0.915Pb(Z $r_{y}$ $Ti_{1-y}$) $O_{3}$(0.45.leq.y.leq.0.70)세라믹을 2단 소성법으로 제작한 후, PbZr $O_{3}$조성 및 온도에 따른 구조적, 강유전적특성을 측정하였다. XRD측정 결과, PbZr $O_{3}$조성이 감소할수록 결자상수 및 단위격자 체적은 감소하였으며 시편의 결정구조는 입방정계에서 능면체정계, 정방정계로 변화되었다. 8.5/60/40시편의 경우 포화분극, 잔류분극 및 항전계가 각각 33.28[.mu.C/$cm^{2}$], 4.15[kV/cm]로 전형적인 메모리 특성을 나타내었으며 PbZr $O_{3}$조성이 증가함에 따라 강유전 이력곡선은 slim loop특성을 나타내었다. 잔류분극은 온도가 증가함에 따라 감소하였으며 특히 PE-FE상경계 부근에 위치한 조성의 경우, 상전이 온도 이하의 온도에서 급격히 감소하는 경향을 나타내었다.다.

• Journal of the Korean Ceramic Society
• /
• v.25 no.5
• /
• pp.488-494
• /
• 1988

Effects of MnO2 addition on themicrostructure, dielectric and piezoelectric properties of Rhombohedral, Tetragonal and Morphotropic phase boundary(MPB) in Pb(Ni1/3Nb2/3)O3-PbTiO3-PbZrO3 system were investigated and respectively the amount of MnO2 addition was 0, 0.2, 0.5, 1.0, 3.0wt%. In the tetragonal region, compared with the Rhombohedral and Morpotropic phase boundary, Mechanical quality factor(Qm), Curie temperature(Tc) and Dissipation factor were promoted by addition of MnO2. According to the results of the microstructure, dielectric and piezoelectric properties, the solid solution range of MnO2 addition in this system was 0.2-0.5wt%.

• Journal of the Korean Ceramic Society
• /
• v.35 no.9
• /
• pp.969-973
• /
• 1998

Pb(Zr, Ti)O3 (PZT) (Zr:Ti= 52: 48) thin films were prepared on MgO(100) substrates by dipping-py-rolysis process using metal naphthenates as starting materials. Thin films were fabricated by spin coating technique and the precursor films were prefired at 20$0^{\circ}C$ in air for 0.5, 1, 2, 3, and 24 h followed by final heat treatment at 75$0^{\circ}C$ for 30min. Film prefired for 24 h lost orientational properties and pole figure analysis showed the lost of the epitaxial relationship between the films and substrate while highly a/c-axis oriented thin films were obtained for the samples prefired for 1, 2, and 3h.

• Journal of the Korean Chemical Society
• /
• v.46 no.3
• /
• pp.242-251
• /
• 2002

We report the synthesis and characterization of the perovskite nanotubes made by sol-gel template syn-thesis.Both lead titanate (PbTiO3 : PT), lead zirconate (PbZrO3 : PZ) and lead zirconium titanate (PbZrO3 -PbTiO3 : PZT) solid solution nanotubes were prepared with a chelate sol-gel of titanium isopropoxide (Ti(OPri)4 ), zirconium tet-rabutoxide (Zr(OBu)4 ) and the respective lead acetate (Pb(OAc)2 -3H2O). WhatmanRanodisc membranes, with a 200nm pore size, served as the template. After the removal of the template in the 6M-NaOH, scanning electron microscopy shows that the shapes formed are 200 nm outer diameter tubes with 50mm lengths. Transmission electron microscopy and electron diffraction reveal that the tubes are polycrystalline. The PT nanotubes so far have shown an anomalous transition temperature, 234.4$^{\circ}C$ as measured by DSC with a small particle size, 15.4 nm determined by X-ray analysis with the aid of Scherrer's equation.

• Journal of the Korean Ceramic Society
• /
• v.28 no.4
• /
• pp.297-304
• /
• 1991

Dielectric hysteresis characteristics of Pb(Zr0.52Ti0.48)O3 ceramics have been investigated as a function of the amount of MnO2 addition ranged from 0.0 wt% in Pb(Zr0.52Ti0.48)O3 ceramics enhanced the dielectric strength, aging effect and remanent polarization, while reduced the coercive field. These results could be explained by the effect of Mn-Vo association due to the substitution of Mn for the (Zr, Ti) site in PZT.

• Journal of the Korea Academia-Industrial cooperation Society
• /
• v.6 no.6
• /
• pp.457-460
• /
• 2005

Nano-sized titanium oxide and zirconium oxide powders were synthesized by hydrolysis of titanium isopropoxide $[Ti(OC_3H7)_4]$ and zirconium tetrachloride ($ZrC1_4$) via a sol-gel technique. Lead titanate powders were prepared by mixing $TiO_2$ precursors with PbO slurry made with dilute $NH_4OH$. Lead zirconate titanate powders were, then, synthesized by mixing $PbTiO_3$ with $ZrO_2$ powders. The goal of this research was to obtain the $PbZrTiO_3(PZT)$ powders and sintering these powders at low temperature. The $PbTiO_3$ and PZT powders after firing were analyzed by X-ray diffraction(XRD) and transmission electron microscopy(TEM) was utilized to observe the shape and size of the synthesized nano-particles. In the XRD pattern, the well-crystallized PZT phase could be obtained in consequence of firing at $900^{\circ}C$. SEM micrographs also showed that grains of PZT were relatively well grown with the size of the range of $2{\~}4{\mu}m$. The densified perovskite structure of $PbZrTiO_3$ could be obtained by sintering at temperature as low as $900^{\circ}C$. Characterization of the samples showed improved piezoelectric properties.

• The Transactions of the Korean Institute of Electrical Engineers
• /
• v.44 no.5
• /
• pp.644-648
• /
• 1995

Transparent xBa(La$_{1}$2/Nb$_{1}$2/)O$_{3}$-(1-x)Pb(Zr, Ti)O$_{3}$ (x=8.5, 9.0[mol.%], Zr/Ti=70/30~40/60) ceramics were fabricated by the two-stage sintering method, the electrooptic properties were investigated with Ba(La$_{1}$2/Nb$_{1}$2/)O$_{3}$ content and Zr/Ti composition ratio. Decreasing the Zr/Ti ratio, the electrooptic property was changed from a quadratic electrooptic effect to a linear electrooptic effcet. In the BLN-PZT 9.0/50/50 specimen having the tetragonal structure, the linear electrooptic coefficient had the highest value of 6.01*10$^{-10}$ [m/V] and in the BLN-PZT 9.0/55/45 specimen which located near the MPB region, the quadratic electrooptic coefficient had the highest value of 10.53*10$^{-16}$ [m$^{2}$/V$^{2}$].

• Electrical & Electronic Materials
• /
• v.9 no.7
• /
• pp.652-659
• /
• 1996

Sintering characteristics and electrical properties of xPb(Mg$_{1}$8/Te$_{1}$8/Mn$_{1}$4/Nb$_{1}$2/) $O_{3}$-(1-x) Pb (Zr$_{1}$2/ $Ti_{1}$2/) $O_{3}$ (x=0.075, 0.1, 0.125) ceramics are investigated. A sintering temperature of ceramics could be reduced to 950.deg. C by a reaction between PbO and B site compound material. The physical properties of 0.1Pb(Mg, Te, Mn, Nb) $O_{3}$ - 0.9Pb(Zr, Ti) $O_{3}$ bulk ceramic with 3wt% glass frit(0.857PbO-0.143W $O_{3}$) were following : den = 7.95 g/cm$^{3}$, T$_{c}$=340.deg. C, .epsilon.$_{33}$= 754, k$_{31}$=0.3 and Q.=1780. The 3-layer piezoelectric transformer by using a tape casting method showed a good monolithic structure, and its voltage setup ratio was 2.5 times higher than that of a single device by using bulk ceramics.s.s.

• Korean Journal of Materials Research
• /
• v.10 no.4
• /
• pp.282-289
• /
• 2000

$PbTiO_3$ films were fabricated by electron cyclotron resonance plasma enhanced chemical vapor deposition(ECR-PECVD). Deposition characteristics of $PbTiO_3$films on $RuO_2$ and Pt substrates were investigated with varying the flow rate of metalorganic source and substrate temperature. The residence time of Pb-oxide molecules in much longer on $RuO_2$ than on Pt substrate, while the perovskite nucleation is more difficult on $RuO_2$ than on Pt substrate. Therefore, the process conditions to obtain the single perovskite $PbTiO_3$ phase are more restricted on $RuO_2$ than on Pt substrates. An introduction of Ti-oxide seed layer increases perovskite nucleation density and thus enlarges the process window to obtain the single perovkite phase. The introduction of Ti-oxide seed layer make the PZT film that Ti-components of $PbTiO_3$ are partially substituted with Zr atoms have single perovskite phase for the wide range of Zr/(Zr+Ti) concentration ratios.