• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2008.04a
• /
• pp.67-68
• /
• 2008

A simple bi-layer structure of organic light emitting diode (OLED) was used to study the characteristics of anode preparation. Indium tin oxide (ITO) anode surface treatment of OLEDs was performed to get the optimum condition for the ITO anode. The ITO surface was treated by $O_2$ or $O_2$ / Ar mixed gas plasma with different processing time. The electrical characteristics of OLED were improved by plasma treatment. The operating voltage of OLED with $O_2$ or $O_2$/Ar mixed gas plasma treated anodes decreases from 8.2 to 3.4 V and 3.2V, respectively. The $O_2$ /Ar mixed gas plasma treatment results in better electrical property.

• Journal of the Korea Institute of Information and Communication Engineering
• /
• v.4 no.5
• /
• pp.1127-1134
• /
• 2000

$RuO_2$ thin films are prepared by RP magnetron reactive sputtering and their characteristics of crystalliBation,microstructure, surface roughness and resistivity are studied with various O2/(Ar+O2)ratios and substrate temperatures. As O2/(Ar+O2) ratio decreases and substrate temperature increases, the preferred growing plane of$RuO_2$ thin films are changed from (110) to (101) plane. With increase of the 021(Ar+O2) ratio from 2075 to 50%, the surface roughness and the resistivity of $RuO_2$ thin films increase from 2.38nm to 7.81nm, and from $103.6 \mu\Omega-cm\; to \; 227 \mu\Omega-cm$, respectively, but the deposition rate decreases from 47nm/min to 17nm/min. On the other hand, as the substrate temperature increases from room temperature to$500^{\circ}C$, resistivity decreases from $210.5 \mu\Omega-cm\; to \; 93.7\mu\Omega-cm$. $RuO_2$ thin film deposited at $300^{\circ}C$ shows a excellent surface roughness of 2.38 m. As the annealing temperature increases in the range between $400^{\circ}C$ and $650^{\circ}C$, the resistivity decreases because of the improvement of crystallinity. We find that RuO$_2$ thin film deposited at 20% of 02/(Ar+O2) ratio and $300^{\circ}C$ of substrate temperature shows excellent combination of surface smoothness and low resistivity so that it is well qualified for bottom electrode for ferroelectric thin films.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2004.07b
• /
• pp.607-610
• /
• 2004

The Pb $(Zr_{0.52}Ti_{0.48})O_3/(Ba_{0.6}Sr_{0.4}TiO_3$ [PZT(52/48)/BST(60/40)] heterolayered thin films were fabricated on the Pt/Ti/$SiO_2$/Si by RF sputtering method. The structural properties of the PZT(52/48)/BST(60/40) heterolayered thin films were investigated with Ar/$O_2$ ratio condition. All the PZT(52/48)/BST(60/40) heterolayered thin films had shown the PZT(111), (200) and BST(200) Peaks of the tetragonal structure. Increasing the Ar/$O_2$ ratio, the average roughness was increased. The thickness ratio of the to the PZT and BST thin film was 1:2. In the case of the PZT(52/48)/BST(60/40) heterolayered thin films with Ar/$O_2$ ratio of 80/20, the average roughness was 3.4 [nm].

• The Korean Journal of Ceramics
• /
• v.2 no.1
• /
• pp.43-47
• /
• 1996

$RuO_2$ thin films deposited directly on Si substrate by RF magnetron sputtering method using $RuO_2$ target have been investigated. Special interest was focused on the effect of process parameter on the surface roughness of $RuO_2$ films. Crystallization behavior and electrical properties of the films deposited at $300^{\circ}C$ were superior to those deposited at room temperature. Metallic Ru phase was formed in pure Ar and this phase had resulted poor adhesion after post annealing process in oxidizing ambient. Microstructural analysis reveals that the size of the $RuO_2$ crystallites gets smaller and the surface becomes smoother as the $O_2$ partial pressure or film thickness decreases. Irrespective of the $O_2/Ar$ ratio, resistivity of $RuO_2$ films ranged in $50~70 {\mu}{\Omega}-cm$. As the film thickness decreases, there is a thickness where the resistivity rises abruptly. Such an onset thickness turned out to be dependent n the $O_2$/Ar ratio.

• Korean Journal of Materials Research
• /
• v.6 no.6
• /
• pp.618-625
• /
• 1996

고주파 마그네트론 스퍼터링(RF magnetron sputtering)법을 이용하여 자동차유리 성에 제거용 주석첨가 인듐산화물(indium tin oxide;ITO) 투명저항박막의 증착과 그 전기 및 광학 특성을 연구하였다. 기판온도는 A, T.-30$0^{\circ}C$, O2/(Ar+O2)비는 0-0.3로 변화시키며 실험하였다. 기판온도가 높아질수록, 그리고 O2/(Ar+O2)비가 높아질수록 박막의 증착속도는 감소하였다. 또한, 기판온도가 높아질수록 In2O3(400) 방향의 결정성은 감소하고, In2O3(222)와 (400) 피크만이 잔존하였다. 기판온도가 높아질수록 가시광영역의 광투과도는 향상되었고, 면저항은 20$0^{\circ}C$까지는 감소하였으나 20$0^{\circ}C$이상에서는 거의 일정하였으며, 결정립 크기는 온도가 높아질수록 증가하였다. 박막의 면저항은 O2/(Ar+O2)비가 0.1에서는 감소하고, 그 이상에서는 증가하였으며, 광투과도는 O2/(Ar+O2)비에 거의 영향을 받지 않았다.

• Korean Journal of Crystallography
• /
• v.6 no.2
• /
• pp.134-140
• /
• 1995

SAW properties of SiNx/ZnO bilayer thin film structure were analyzed. ZnO thin films were deposited by rf magnetron sputter using O2 gas as an oxidizer. Structure of ZnO thin films was affected by Ar/O2 ratio. At the gas ratio of Ar/O2=67/33, the standard deviation of X-ray rocking curve of (002) preferred ZnO thin film was 2.17 degree. This value is sufficient to use ZnO thin films as an acoustic element. SAW velocity of glass/SiNx(7000Å)/Al/ZnO(5μm) structure was max. 2.2% faster than that of ZnO/glass.

• Proceedings of the Korean Institute of Navigation and Port Research Conference
• /
• 2000.11a
• /
• pp.21-24
• /
• 2000

Ferroelectric YMnO$_3$thin films are excellent dielectric materials for high integrated ferroelectric random access memory (FRAM) with metal-ferroelectric-silicon field effect transistor (MFSFET) structure. In this study, YMnO$_3$thin films were etched with Cl$_2$/Ar gas chemistries in inductively coupled plasma (ICP). The maximum etch rate of YMnO$_3$thin films is 285 $\AA$/min under Cl$_2$/Ar of 10/0, 600 W/-200 V and 15 mTorr. The selectivities of YMnO$_3$over CeO$_2$and $Y_2$O$_3$are 2.85, 1.72, respectively. The results of x-ray photoelectron spectroscopy (XPS) reflect that Y is removed dominantly by chemical reaction between Y and Cl, while Mn is removed more effective by Ar ion bombardment than chemical reaction. The results of secondary ion mass spectrometer (SIMS) were equal to these of XPS. The etch profile of the etched YMnO$_3$film is approximately 65$^{\circ}$and free of residues at the sidewall.

• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 2009.05a
• /
• pp.264-265
• /
• 2009

본 연구에서 유도결합 플라즈마 식각 장치외 $BCl_3/Ar/Cl_2$ 가스 혼합비를 이용하여 ZnO 박막을 식각 하였을 때, 식각 된 ZnO 박막의 표면 반응에 관하여 관찰하였다. ZnO 박막의 식각 실험 조건은 RF 전력 700 W, 직류바이어스 전압 - 150 V, 공정 압력 15 mTorr로 고정하였고, $Cl_2/(Cl_2+BCl_3+Ar)$ 가스 혼합비를 변경하면서 식각 실험을 수행하였다. $Cl_2$ 가스가 3 sccm 일 때, ZnO 박막의 식각속도는 53 nm/min으로 가장 높았으며, 이때 ZnO 박막에 대한 $SiO_2$의 선택비는 0.89 이었다. 식각된 ZnO 박막의 표면은 XRD (X-ray diffraction)와 AFM(atomic force microscopy)를 이용하여 결정상의 변화와 표면의 거칠기를 분석하였다. AFM 분석 결과에서 Ar, $BCl_3$와 $Cl_2$ 플라즈마를 이용하여 식각된 시료의 표면 거칠기 근 값이 식각전의 시료나 $BCl_3/Ar/Cl_2$ 플라즈마로 식각된 시료보다 큰 것을 확인하였다. 이는 식각된 시료에서의 Zn 양의 감소나 비휘발성 식각 잔류물에 의한 영향으로 판단된다. SIMS(secondary ion mass spectrometery) 분석을 통해 검증 하였다.

• Proceedings of the KIEE Conference
• /
• 2002.07c
• /
• pp.1488-1490
• /
• 2002

The (Bi,Ba,Sr)$TiO_3$[BBST] thin films were fabricated on Pt/Ti/$SiO_2$/Si substrate by RF sputtering method. We investigated the effects of Ar/$O_2$ rates on the structural properties of BBST thin films. Decreasing the $O_2$ rates, the intensity of $BaBi_4Ti_4O_{15}$ and $Bi_4Ti_3O_{12}$ peaks were increased but the $(Ba_{0.5}Sr_{0.5})TiO_3$ peak was decreased. In the case of BBST thin films deposited with condition of 90/10 (Ar/$O_2$) ratio, the composition of Ba/Sr/Bi was 0.35/0.4/0.25. Also, in the BBST thin films deposited with condition of 80/20(Ar/$O_2$) ratio, the composition of Br,Sr and Ti were relatively uniform. But the component of Bi and Ti were diffused into the Pt layers.

• Journal of the Institute of Electronics Engineers of Korea SD
• /
• v.38 no.12
• /
• pp.8-13
• /
• 2001

Cerium oxide ($CeO_2$) thin film has been proposed as a buffer layer between the ferroelectric thin film and the Si substrate in Metal-Ferroelectric-Insulator-Silicon (MFIS) structures for ferroelectric random access memory (FRAM) applications. In this study, $CeO_2$ thin films were etched with $Cl_2$/Ar gas mixture in an inductively coupled plasma (ICP). Etch properties were measured for different gas mixing ratio of $Cl_2$($Cl_2$+Ar) while the other process conditions were fixed at RF power (600 W), dc bias voltage (-200 V), and chamber pressure (15 mTorr). The highest etch rate of $CeO_2$ thin film was 230 ${\AA}$/min and the selectivity of $CeO_2$ to $YMnO_3$ was 1.83 at $Cl_2$($Cl_2$+Ar gas mixing ratio of 0.2. The surface reaction of the etched $CeO_2$ thin films was investigated using x-ray photoelectron spectroscopy (XPS) analysis. There is a Ce-Cl bonding by chemical reaction between Ce and Cl. The results of secondary ion mass spectrometer (SIMS) analysis were compared with the results of XPS analysis and the Ce-Cl bonding was monitored at 176.15 (a.m.u). These results confirm that Ce atoms of $CeO_2$ thin films react with chlorine and a compound such as CeCl remains on the surface of etched $CeO_2$ thin films. These products can be removed by Ar ion bombardment.