• 제목/요약/키워드: $Nd_{1+X}Ba_{2-X}Cu_3O_{7-{\delta}}$

검색결과 5건 처리시간 0.022초

Nd1+XBa2-XCu3O7-δ Bulk Superconductor by Zone-melt Process

  • Soh, Dea-Wha;Guo, Fan-Zhan
    • Transactions on Electrical and Electronic Materials
    • /
    • 제3권3호
    • /
    • pp.21-24
    • /
    • 2002
  • Two kinds of $Nd_{1+X}Ba_{2-X}Cu_3O_{7-{\delta}}$, the sintering samples and zone melting samples, were heat-treated under pure Ar at 950$^{circ}C$. The substitution of Nd ion for Ba ion in the $Nd_{1+X}Ba_{2-X}Cu_3O_{7-{\delta}}$ before and after the heat treatment was investigated by XRD. In order to confirm the effects of the heat treatment, the Tc and Jc of samples with/without the heat treatment under Ar were comparatively studied. $Nd_{1+X}Ba_{2-X}Cu_3O_{7-{\delta}}$ samples were oxygenated under pure oxygen at $300^{circ}C$. From the XRD pattern it was found that the sample with x<0.4 was transferred from tetragonal phase to orthorhombic phase after the oxygenation, while the sample with x>0.4 did not show the phase transition even after a long time oxygenation. Therefore, the low oxygen partial pressure (Ar+1 % O$_2$) was used for the ambient atmosphere of the zone-melting samples, which could reduce the melting temperature and depress the substitution of Nd for Ba. After the improvement in the zone-melting process, the Jc value was increased to 2 x $10^4$A/$cm^2$ (0 T, 78 K). The particle orientation and the structure of zone-melted NdBaCuO were studied by the XRD and SEM analysis.

Heat Treatment Condition for Preparing $Nd_{1+x}Ba_{2-x}Cu_{3}O_{7-\delta}$ Superconductors

  • Fan Zhan guo;wha, Soh-Dea;zhan, Si-Ping;Li Yingmel;Lim Byongjae
    • 한국전기전자재료학회:학술대회논문집
    • /
    • 한국전기전자재료학회 2001년도 하계학술대회 논문집
    • /
    • pp.624-627
    • /
    • 2001
  • Two kinds of Nd$_{1+x}$Ba$_{2-x}$Cu$_3$O$_{7-{\delta}}$, the sintering samples and zone melting samples, were heat treated under pure Ar at 95$0^{\circ}C$. The substitution of Nd ion for Ba ion in the Nd$_{1+x}$Ba$_{2-x}$Cu$_3$O$_{7-{\delta}}$ before and after the heat treatment were investigated by XRD. In order to know the effects of the heat treatment, the T$_{c}$ and J$_{c}$ of samples with the heat treatment and those without the heat treatment by Ar were comparatively studied. The results show that the substitution of Nd for Ba decreased, T$_{c}$, and J$_{c}$ increased after the treatment under Ar at 95$0^{\circ}C$. The Nd$_{1+x}$Ba$_{2-x}$Cu$_3$O$_{7-{\delta}}$ samples were oxygenated under pure oxygen at 30$0^{\circ}C$. From the XRD pattern it was found that the sample with x< 0.4 could transfer from tetragonal phase to orthorhombic phase after the oxygenation, but the sample with x>0.4 could not make the phase transition even after a long time oxygenation.ion even after a long time oxygenation.ation.n.ation.ation.

  • PDF

Effect of oxygen pressure on properties of $NdBa_2Cu_3O_{7-{\delta}}$ films on $SrTiO_3$ (100) substrates grown by pulsed laser deposition

  • Wee, Sung-Hun;Moon, Seung-Hyun;Park, Chan;Yoo, Sang-Im
    • 한국초전도ㆍ저온공학회논문지
    • /
    • 제6권4호
    • /
    • pp.9-12
    • /
    • 2004
  • We report a successful fabrication of high-$J_C$ $NdBa_2Cu_3O_{7-{\delta}}$ (NdBCO) films on (100) $SrTiO_3$ substrates by pulsed laser deposition (PLD) in high oxygen pressures ranging from 400 to 800 mTorr. Fabricated NdBCO films exhibited only c-axis orientation, good out-of-plane and in-plane textures, and also excellent superconducting properties, including critical temperature ($T_C$) and critical current density ($J_C$) of above 90 K and the highest of $3.1MA/cm^2$ at 77 K in self-field, implying that NdBCO is a perspective alternative to YBCO for coated conductor. In low oxygen pressures ranging from 100 to 200 mTorr, however, the films showed a-, c-mixed orientation and degraded $T_{C,zero}$ values due to the formation of $Nd_{1+x}Ba_{2-x}Cu_3O_{7-{\delta}}$-type solid solutions with an excessive substitution of $Nd^{3+}$ ions for the $Ba^{2+}$ sites.

다양한 산소분압에서 소결한 NdBCO 초전도체의 열적 안정성 (Thermal Stability of Superconductor NdBCO Sintered at Various Oxygen Partial Pressures)

  • 정준기;김원정;박성창;강성구;임영진;김철진
    • Progress in Superconductivity
    • /
    • 제10권2호
    • /
    • pp.133-138
    • /
    • 2009
  • The $Nd_{1+x}Ba_{2-x}Cu_3O_{7-{\delta}}$(Nd123) superconductor exhibits high performance in high magnetic field and high temperature. We have studied phase stability for Nd123 under reduced oxygen partial pressure and various heat-treatment conditions. The main phase is Nd123 and some samples contain small amounts of Nd422 depending on the temperature and oxygen partial pressure. The decomposition temperature decreases with decreasing oxygen partial pressure from $1052^{\circ}C(P(O_2)$=150 Torr) to about $845^{\circ}C(P(O_2)$=0.1 Torr). The liquidus line was steeper temperature with decreasing oxygen partial pressure. In same condition of oxygen partial pressure, the region of stable Nd123 phase was formed at slightly higher temperature than the region of stable YBCO phase.

  • PDF

PLD법에 의한 혼합된 희토류계$(Nd_{1/3}Eu_{1/3}Gd_{1/3})Ba_2Cu_3O_{7-x}$ 고온 초전도 박막 (Mixed rare earth $(Nd_{1/3}Eu_{1/3}Gd_{1/3})Ba_2Cu_3O_{7-d}$ thin films by PLD)

  • 고락길;배성환;정명진;장세훈;송규정;박찬;손명환;강석일;오상수;하동우;하홍수;김호섭;김영철
    • 한국전기전자재료학회:학술대회논문집
    • /
    • 한국전기전자재료학회 2009년도 춘계학술대회 논문집
    • /
    • pp.3-3
    • /
    • 2009
  • In order to investigate the possibility of using mixed rare earth $(Nd_{1/3}Eu_{1/3}Gd_{1/3})Ba_2Cu_3O_{7-x}$ (NEG123) as the superconducting layer of the HTS coated conductor, the NEG123 thin film was deposited epitaxialy on LAO(100) single crystal and IBAD_YSZ metal templates by pulsed laser deposition. Systematic studies were carried out to investigate the influences of deposition parameters of PLD on the micro structure, texture and superconducting properties of NEG-123 coated conductor. Deposition at oxygen partial pressure of 600 mTorr was needed to routinely obtain high quality NEG123 films with $J_c$'s (77K) over 2 MA/$cm^2$ and Tc's over 90K (${\Delta}T{\sim}2\;K$). We verified from magnetization study that the NEG123 has an improved in-field Jc as the field increases at temperatures between 10 K and 77 K compared with Gd123. The $J_c$ (77K, self field) and the value of onset $T_c$ of NEG123 thin film on LAO substrate was $4.0MA/cm^2$ and 92K, respectively. This is the first report, to the best of our knowledge, of coated conductors with NEG123 film as the superconducting layer which have Ic and Jc over 40 A/cm-width and 1.6 MA/$cm^2$ at 77K, self field. This study shows the possibility of using NEG123 film as the superconducting layer of the HTS coated conductor which can be used in high magnetic field power electric devices.

  • PDF