• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.15 no.4
• /
• pp.141-144
• /
• 2005

[ $(Y_{0.5}Sm_{0.25}Nd_{0.25})Ba_2Cu_3O_y$ ] [(YSN)-123] high $T_c$ composite superconductors with $CeO_2$ addition were systematically investigated by top seeded melt growth (TSMG) process in air atmosphere. A melt textured $NdBa_2Cu_3O_y$ (Nd-123) single crystal was used as a seed for achieving the c-axis alignment large grains perpendicular to the surface of (YSN)-123 composite oxides. The size of $(Y_{0.5}Sm_{0.25}Nd_{0.25})_2BaCuO_5$ [(YSN)211] nonsuperconducting inclusions of the melt textured (YSN)-123 samples with $CeO_2$ addition were remarkably reduced and uniformly distributed within the (YSN)123 superconducting matrix except in the region very close to the Nd-123 seed crystal. The sample showed a sharp superconducting transition of 91 K.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2007.06a
• /
• pp.243-243
• /
• 2007

We have studied the electrical properties and microstructure of $(Y_{0.5}Nd_{0.25}Sm_{0.25})Ba_2Cu_3O_y[(YNS)-123]$ Oxides by rod-type seeded melt growth process(RSMG) in air atmosphere. Rod-type $NdBa_2Cu_3O_y${Nd-123) seed crystals made a extrusion process method, were used for achieving the ab-plane alignment having large grains perpendicular to the center of (YNS)-123 samples. The observations using SEM and TEM micrographs of the melt-textured (YNS)-123 samples revealed that the nonsuperconducting $(Y_{0.5}Nd_{0.25}Sm_{0.25})Ba_2Cu_3O_y[(YNS)-211]$ inclusions are uniformly distributed in the superconducting matrix. The microstructure and electrical properties were investigated by XRD, SEM, TEM and DC SQUID magnetometer. The sample showed a sharp superconducting transition at 90 K. The magnetization values of the (YNS)-123 sample exhibited the enhanced electrical properties, compared with $YBa_2Cu_3O_y$(Y-123) sample.

• Progress in Superconductivity and Cryogenics
• /
• v.4 no.1
• /
• pp.21-25
• /
• 2002

The effect of Ca-doping on the superconducting properties of Nd-Ba-Cu-O bulk superconductors, fabricated by the oxygen-controlled melt growth process, has been systematically investigated. Various c-axis textured bulk samples were grown using precursors with the nominal compositions of $Nd_{1.8-x}Ca_{x]Ba_{2.4}Cu_{3.4}O_{y}$ (x= 0.00, 0.02, 0.05, 0.10, 0.15) in a reduced oxygen atmosphere of 1%O$_2$ in Ar. Magnetization measurements revealed that the critical temperatures(Tc) were almost linearly depressed from 95K to 86K with increasing the Ca dopant from x : 0.0 to 0.15, respectively, and thus critical current densities(Jc) at 77K and for H//c-axis of specimens were gradually degraded with increasing x. Compositional analyses revealed that although the amounts of the Ca dopant both in $NdBa_2Cu_2O_y(Nd123) and Nd_4Ba_2Cu_2O_{10}(Nd422)$,/TEX> were increased with increasing x, only less than half of the initial Ca compositions were detected in melt-grown Ca-doped Nd-Ba-Cu-O bulk crystals. The supression of Tc is attributed to an increased Nd substitution for the Ba site in the Nd123 superconducting matrix with increasing the amount of the Ca dopant.

• KIEE International Transactions on Electrophysics and Applications
• /
• v.5C no.6
• /
• pp.251-256
• /
• 2005

Directionally melt-textured high $T_c\;(Y_{0.5}Nd_{0.25}Sm_{0.25})Ba_{2}Cu_{3}O_y$ [(YNS)-123] superconductor was systematically investigated by the zone melt growth process in air. A sample prepared by this method showed well-textured microstructure, and $(Y_{0.5}Nd_{0.25}Sm_{0.25})_{2}BaCuO_5$[(YNS)211] inclusions were uniformly dispersed in large $(Y_{0.5}Nd_{0.25}Sm_{0.25})Ba_{2}Cu_{3}O_y$ [(YNS)123] matrix. High irreversibility field and magnetization hysteresis loop of the zone melt-textured (YNS)-123 sample exhibited the enhanced flux pinning, compared with $YBa_{2}Cu_{3}O_y$ (Y-123) sample without RE(rare earth). Critical current density of (YNS)-123 sample was $2.5{\times}10^4\;A/cm^2$ at 2 T and 77 K.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.15 no.5
• /
• pp.188-192
• /
• 2005

High $T_c(Y_{0.5}Nd_{0.25}Sm_{0.25})Ba_2Cu_3O_y[(YNS)-123]$ superconductors with/without $CeO_2$ additive were systematically investigated by the zone melt growth process in air. Cylindrical green rods of (YNS)-123 oxides were fabricated by cold isostatic pressing (CIP) method using rubber mould. A sample prepared by this method showed well-textured microstructure, and $(Y_{0.5}Nd_{0.25}Sm_{0.25})_2BaCuO_5[(YNS)211]$ nonsuperconducting inclusions were uniformly dispersed in large $(Y_{0.5}Nd_{0.25}Sm_{0.25})Ba_2Cu_3O_y$[(YNS)123] superconducting matrix. In this study, optimum melting temperature and growth rate were $1100^{\circ}C$ and 3 mm/hr, respectively. The directionally melt-textured (YNS)-123 sample with $CeO_2$ additive showed an onset critical temperature $(T_c)\;T_c{\geq}93K$ and sharp superconducting transition.

• Transactions on Electrical and Electronic Materials
• /
• v.6 no.6
• /
• pp.284-288
• /
• 2005

We have systematically studied the superconducting properties and flux pinning enhancement of $(Y_{0.33}Sm_{0.33}Nd_{0.33})\;Ba_2Cu_3O_y$ [(YSN)-123] composite oxides by melt growth process in air. A sample prepared by this method showed well-textured microstructure, and $(Y_{0.33}Sm_{0.33}Nd_{0.33})\;BaCuO_5$ [(YSN)211] nonsuperconducting particles were uniformly dispersed in large (YSN) 123 superconducting matrix. The sample showed a sharp superconducting transition at 91 K. The magnetization measurements of the (YSN)-123 sample exhibited the enhanced flux pinning, compared with $YBa_2Cu_3O_y$ (Y-123) sample without Sm and Nd. Critical current densities of (YSN)-123 sample was $2.5{\times}10^4 A/cm^2$ at 2 T and 77 K.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.13 no.2
• /
• pp.83-87
• /
• 2003

$(Nd/Y)_{1.8}Ba_{}2.4Cu_{3.4}O_{7-x}$high $T_c$ superconductor was directionally grown by floating Bone melt growth process with a large temperature gradient in air. Cylindrical green rods of (Nd/Y)1.8 oxides were fabricated by cold isostatic pressing (CIP) method using rubber mold. Microstructures were observed by SEM and TEM and superconducting properties were measured by a SQUID magnetometer. Nonsuperconducting $(Nd/Y)_2BaCuO_5$ inclusions were uniformly distributed within the superconducting $(Nd/Y)Ba_2Cu_3O_x$ matrix. The directionally melt-textured (Nd/Y) 1.8 superconductor showed an onset Tc $\geq$ 90 K and a sharp superconducting transition.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2001.11b
• /
• pp.85-88
• /
• 2001

The NdBaCuO superconductor samples were Zone-melted in low oxygen partial pressure (1% $O_{2}+ 99% Ar$ ). The Zone-melting temperature was decreased about $120^{\circ}C$ from $1060^{\circ}C$ the zone-melting temperature in air. Thus the loss of liquid phase ($BaCuO_{2}$ and CuO) was reduced during the zone-melting process. The content of non-superconducting phase Nd422 in zone-melted NdBaCuO samples was clearly decreased, so was the substitution of Nd for Ba. The superconductivity of zone-melted $Nd_{1+x}Ba_{2-x}Cu_{3}O_{y}$ prepared under low oxygen partial pressure was distinctively improved.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2001.11a
• /
• pp.85-88
• /
• 2001

The NdBaCuO superconductor samples were Zone-melted in low oxygen partial pressure (1% O$_2$+99% Ar). The Zone-melting temperature was decreased about 120$^{\circ}C$ from 1060$^{\circ}C$ the zone-melting temperature in air. Thus the loss of liquid phase (BaCuO$_2$ and CuO) was reduced during the zone-melting process. The content of non-superconducting phase Nd422 in zone-melted NdBaCuO samples was clearly decreased, so was the substitution of Nd for Ba. The superconductivity of zone-melted Nd$\sub$1+x/Ba$\sub$2-x/Cu$_3$O$\sub$y/ prepared under low oxygen partial pressure was distinctively improved.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2005.07a
• /
• pp.280-281
• /
• 2005

We have studied the superconducting properties and flux pinning enhancement of $(Y_{0.5}Nd_{0.25}Sm_{0.25})_{1.8}Ba_{2.4}Cu_{3.4}O_y$ [(YNS)-1.8] composite oxides by melt growth process in air. A sample prepared by this method showed well-textured microstructure, and $(Y_{0.5}Nd_{0.25}Sm_{0.25})_2BaCuO_5$ [(YNS)211] nonsuperconducting particles were uniformly dispersed in large (YNS)123 superconducting matrix. The sample showed a sharp superconducting transition at 91 K. The magnetization measurements of the (YSN)-1.8 sample exhibited the enhanced flux pinning, compared with $YBa_2Cu_3O_y$ (Y-123) sample without Sm and Nd.