• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.8 no.3
• /
• pp.396-400
• /
• 1998

The physical properties of KLN single crystals very significantly according to the $Nb_2O_5$ content in grown crystal, therefore, it is very important to control the composition of KLN single crystals. In this study, KLN single crystals of high content $Nb_2O_5$ were grown by temperature fluctuation and TSSG (Top-seeded solution growth) methods with increasing the $Nb_2O_5$ content of starting solution. To investigate the existence of defect due to the increase of $Nb_2O_5$ content, dielectric and optical properties were measured. Due to the increase of defects in grown KLN single crystal, the shift of cutoff-frequency to lower energy and a broad Curie range, which shows the DPT (diffuse phase transition) characteristics, were observed.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.8 no.4
• /
• pp.634-639
• /
• 1998

$Y_2O_3$ and $Nb_2O_5$ co-doped zirconia composites containing 10~30 vol% $Al_2O_3$ with two different particle sizes were sintered for 5 h at $1550^{\circ}C$ to evaluate low-temperature phase stability of the composite using X-ray diffractometry after heat-treatments for 1000 h at $250^{\circ}C$ in air or for 5 h at $180^{\circ}C$ in 0.3 MPa $H_2O$ vapor pressure. No tetragonal to monoclinic phase transformation during degradation, so called enhanced low-temperature phase stability, was observed for all composites. It is concluded that Nb addition to the composite for the phase stability is more effective than $Al_2O_3$ addition. The optimum combination of strength (670 MPa) and fracture toughness ($7.1{\textrm} {MPam}^{1/2}$) were obtained for the composite containing 20 vol% of $Al_2O_3$ with 2.8 $\mu$m to 0.2 $\mu$m, the flexural strength increases but the fracture toughness decreases.

• Journal of the Korean Ceramic Society
• /
• v.39 no.12
• /
• pp.1190-1196
• /
• 2002

Microwave dielectric properties and multilayer characteristics $(1-x)BiNbO_4-xCaNb_2O_6$ (0${\le}$x${\le}$1.0) ceramics were investigated as a function of $CaNb_2O_6$ content. In the composition range of 0.25${\le}$x${\le}$0.75, the mixture phases of $BiNbO_4$ with stibotantalate structure and $CaNb_2O_6$ with columbite structure were detected and secondary phase or phase transition were not detected. Dielectric constant (K) of $(1-x)BiNbO_4-xCaNb_2O_6$ ceramics was largely dependent on the existing phase and could be estimated by the dielectric mixing rule calculated from maxwell equation. Typically, dielectric constant (K) of 26, quality factor (Qf) of 4300 GHz and Temperature Coefficient of resonant Frequency (TCF) of -18 ppm/${\circ}C$ were obtained for $0.5BiNbO_4-0.5CaNb_2O_6$ specimens with 0.8 wt% $CuV_2O_6$ sintered at 1000${\circ}C$ for 3h. The deviation of X-Y shrinkage and camber value of the multilayers obtained from $0.5BiNbO_4-0.5CaNb_2O_6$ green sheet sintered at 850∼950${\circ}C$ for 20 min. were smaller than those of $BiNbO_4$ multilayers.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.10 no.6
• /
• pp.389-393
• /
• 2000

High-quality $Er^{3+}$ doped Mg : $LiNbO_3$single crystal fibers were grown by a micro-pulling down ($\mu$-PD) method. Single crystal fibers were pulled down through the nozzle, at a pulling down rate of 0.5 mm/min and using a Pt crucible with a nozzle 1 mm in diameter in air atmosphere. Defects such as bubbles, cracks and inclusions were not detected in any of the grown crystals. The optical transmission of Er : Mg : $LiNbO_3$crystal was measured and the energy levels of $Er_2O_3$ ion could be calculated. The photoluminescence spectrum of crystal fibers showed an energy band emission with the strongest line corresponding to the $^4I_{3/2}{\to}^4I_{15/2}$transition. The concentration dependence of the entire wavelength region emission intensity upon excitation intensity measured emission intensity for the 3 mol% MgO doped fibers was larger than that for the 1, 5 mol% MgO doped fibers.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.7 no.2
• /
• pp.253-258
• /
• 1997

The characteristics of crystal structure and phase transition with dopants ($Nb_2O_5$= 0.1~0.4 mol% and $Y_2O_3$ : 0.2~0.4 mol%) on the PTCR $BaTiO_3$ system were investigated. In the case of $Nb_2O_5$ additive, the lattice parameter of PTCR $BaTiO_3$ was changed linearly with the increasement of $Nb_2O_5$ which substituted B-site of BaTiO$_3$ and the lattice parameter of c-axis decreased abruptly at 0.3 mol%. These phenonmena were assumed to originate from the distortion of octahedron and we could confirm that the change of lattice parameter accorded with the characteristics of the phase transition temperature. $Y^{3+}$ ions substituted both of A- and B-site until the 0.3 mol% addition, but $Y^{3+}$ substitution preferred A- to B-site above 0.3 mol%. This was affirmed by the variation ,of lattice parameter and the characteristics of phase transition. It also was found that $Y^{3+}$ions in the A-site substituted both of $Ba^{2＋}$ and $Ca^{2＋}$ ions with equal ratio by Rietveld method.

• Electrical & Electronic Materials
• /
• v.6 no.2
• /
• pp.122-128
• /
• 1993

본 연구에서는 0.45Pb(Fe$_{1}$2/Nb$_{1}$2/)O$_{3}$- (0.55-xPb(Fe$_{2}$3/W$_{1}$3/)O$_{3}$ (x=0.20, 0.25, 0.30) 세라믹을 950~990[.deg.C]에서 2시간 유지시켜 일반소성법으로 제작하였다. 제작된 시편에 대해 적층 세라믹 캐패시터로의 응용가능성을 고찰하기 위해 조성비와 소결온도에 따른 구조적, 유전적 특성을 조사하였다. PMN의 첨가량이 증가할수록 결정립 크기는 감소하였으며 상전이 온도는 증가하였다. 소결밀도는 970[.deg.C]에서 소결된 0.45PFN-0.30PFW-0.25PMN 시편에서 7.86[g/cm$_{3}$]의 최대값을 나타내었다. 유전상수는 990[.deg.C]에서 소결된 0.45PFN-0.25PFW-0.30PMN 시편에서 20,751의 최대값을 나타내었으며 유전손실은 모든 조성에서 5[%]이상을 나타내었다.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2007.06a
• /
• pp.298-298
• /
• 2007

Influence of $TiO_2$ on the dielectric properties of the $Bi(Nb_{0.7}Ta_{0.3})O_4$ ceramic with 7 wt% zinc borosilicate(ZBS) glass was investigated as a function of the $TiO_2$ contents with a view to applying this system to LTCC technology. The $Bi(Nb_{0.7}Ta_{0.3})O_4$ ceramic addition of 7 wt% ZBS glass ensured successful sintering below $900^{\circ}C$. But, TCF of $Bi(Nb_{0.7}Ta_{0.3})O_4$ ceramic is large negative values, respectively, it is necessary to adjust to zero TCF for practical applications Therefore, the addition of materials having positive TCF, such as $TiO_2$, might be an effective method for the improvement. In general, increasing addition of $TiO_2$ increased dielectric constant and TCF but it decreased the sinterability and $Q{\tiems}f$ value significantly due to the dielectric property and high sintering temperature of $TiO_2$. $Bi(Nb_{0.7}Ta_{0.3})O_4$ ceramic with 7 wt% ZBS glass and then addition 0.5 wt% $TiO_2$ sintered at $900^{\circ}C$ demonstrated 42 in the dielectric constant(${\varepsilon}_r$), 1,000 GHz in the $Q{\times}f$ value, and $10{\pm}5\;ppm/^{\circ}C$ in the temperature coefficient of resonant frequency(${\tau}_f$).

• Proceedings of the Materials Research Society of Korea Conference
• /
• 1993.05a
• /
• pp.15-15
• /
• 1993

• Korean Journal of Materials Research
• /
• v.8 no.10
• /
• pp.956-960
• /
• 1998

The interfacial reaction between the CoINb bilayer and the $SiO_2$ substrate in the temperature range of $330^{\circ}C$-$800^{\circ}C$ in a vacuum has been investigated by X-ray photoelectron spectroscopy, glancing angle XRD, Auger Electron Spectroscopy and Atomic force microscopy. The Co and Nb were actively interdiffused at $600^{\circ}C$, and the layer inversion completed at $700^{\circ}C$. NbO was formed by interfacial reaction between the Nb interlayer and the $SiO_2$ substrate, while $Nb_20_5$ was formed on the surface by reaction of Nb with oxygen in the ambients. Free Si atoms obtained by the reaction between Nb and $SiO_2$ formed silicides like CoSi and $Nb_5Si_3$ by reacting with Co and Nb remnants. The sheet resistance of the Co/Nb bilayer increased substantially after annealing at $800^{\circ}C$. which is due to the agglomeration of the Co layer to reduce its surface energy.

• Journal of the Korean Ceramic Society
• /
• v.32 no.9
• /
• pp.967-976
• /
• 1995

The possiblity of the existence of a spontaneous relaxor-normal ferroelectric transition was proposed and examined using 1~5 mol% PbZrO3-doped Pb(Ni1/3Nb2/3)O3-PbTiO3 (PNN-PT) systems having tetragonal symmetry at rom temperature. On cooling, the system with 60mol% Pb(Ni1/3Nb2/3)O3 underwent a spontaneous transition from a relaxor to a normal ferroelectric state. A microscopic examination demonstrates that the relaxornormal ferroelectric transition corresponds to a micro-macro domain switching accompanied with thermoelastic martensitic transformation. The long-range macrodomains below the transition temperature were characterized by twinlike 90$^{\circ}$macrodomains with tetragonal symmetry. The relaxor-normal ferroelectric transition was further correlated with the rhombohedral-tetragonal first-order structural transition.