• Conservation Science in Museum
• /
• v.1
• /
• pp.61-74
• /
• 1999

Elemental analysis of 40 glass samples from the Northern Tomb and the Southern Tomb of Hwangnam-daech'ong No. 98 was performed. Fourteen compositions of each sample were analyzed quantitatively by SEM-EDS and glass samples were classified by multivariate analysis such as PCA. All of 40 samples were confirmed to be Na₂O-CaO-SiO₂ system with about 20% of Na₂O. Samples were classified into two groups by doing PCA on concentrations of 5 major elements(SiO₂, Al₂O₃, Na₂O, CaO and K₂O). Samples included in group I showed the concentration of Al₂O₃ is about 9.7% and that of CaO, about 2.2%. In group II, concentration of Al₂O₃ is about 3.2% and that of CaO, about 4.9%. Especially yellow grains embedded in sample No. 12 were shown to be PbSnO₃ by micro XRD, which was the first coloring material ever found in Korea. Lead isotope ratios of samples No. 12 and No. 17 which contained lead were measured by TIMS. The origin of lead was traced by means of multivariate analysis such as SLDA. The result showed that lead from southern China and southern Korea had been used for making glass.

• Journal of the Korean Ceramic Society
• /
• v.19 no.4
• /
• pp.281-286
• /
• 1982

The composition of glasses to be suitable for crystallisation of $BaTiO_3$ by heat-treatment and the dielectric properties of the glass-ceramics were investigated. The composition of the family of glasses was defined by the formula $\chi$ $BaTiO_3 + (100-$\chi$)Al_2O_3$.$2SiO_2$ and excess BaO. Data were presented on dielectric constant and loss tangent at various frequencies. The effects of excess BaO on dielectric properties were investigated. The additions of $Na_2O$ and $Nb_2O_5$ shifted the Curite temperature of these glass-ceramics. The glass composition which was able to be melted at 145$0^{\circ}C$ and moulded as homogeneous glass phase without devitrification should contain $Al_2O_3$.$2SiO_2$ more than 30 mole %. The more the amount of additive BaO increased, the more dielectric constant increased. When the maximum heat-treatment temperature was 105$0^{\circ}C$, we obtained higher dielectric constant than that of 95$0^{\circ}C$. The dielectric constant and the dielectric loss were stable at frequencies between 5$\times$104 and 107 cycle per second. When $Na_2O$ and $Nb_2O_5$ were added, the Curie temperature, presented at 14$0^{\circ}C$ to 15$0^{\circ}C$, shifted to lower temperature. Therefore, the glass-ceramics having high dielectric constant at room temperature were obtained.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2007.11a
• /
• pp.274-274
• /
• 2007

LTCC 소재로 응용을 위해 Mg-Si-O계 세라믹스에 glass frit을 첨가하여 소결 및 마이크로파 유전특성에 관한 연구를 진행하였다. $Mg_2SiO_4$를 기본조성으로 하고 $B_2O_3-ZnO-Na_2O-SiO_2-Al_2O_3$계 glass를 20~40wt%로 첨가하여 $900^{\circ}C$에서 1시간 소결하였을 때 glass 함량이 증가함에 따라 밀도$(g/cm^3)$ 및 유전율$(\varepsilon_r)$은 증가하였고 품질계수$(Q{\times}f_0)$ 값은 감소하는 경향을 보였다. $900^{\circ}C$에서 1시간 소결한 소결체의 유전특성은 유전율 $(\varepsilon_r)$ = 6.5, 품질계수 $(Q{\times}f_0)$ = 4,000(GHz), 온도계수 $({\tau}_f)={\pm}10ppm/^{\circ}C$로 우수한 특성을 확인하였다. 그리고 Glass Milling 효과에 따른 glass-ceramics 소결체의 미세구조, 마이크로파 유전특성을 비교 고찰하였다.

• Journal of the Korean Ceramic Society
• /
• v.21 no.1
• /
• pp.41-50
• /
• 1984

The ion-exchange porous glasses were prepared by heat treating and subsequently acid treating the (95-y) $SiO_2$.$yB_2O_3$.$5Na_2O+xAl_2O_3$ glasses with y=55, 45, 35, 25. mole% and x=0, 2, 5, 9 mole% It was then investigated how the cation exchange capacity was affected by the phase separation in these glasses. For that matter such quantities as alkali extraction amount pore volume and specific surface area of the glasses were measured. The phase separation in these glasses was in general suppressed by the addition of $Al_2O_3$ maximally around the composition of 5 mole% $Al_2O_3$ This may be because the micro-phase separation prevailed in the glass of that composition over the macro-phase separation increasing thereby the specific surface area as well as the residual amount Al of after acid-treatment and accordingly the cation exchange capacity. The maximum values of the cation exchange capacity was observed to be about 150meq/100g for the glasses of (40-50) $SiO_2$ (55~45)$yB_2O_3$. $5Na_2O+5Al_2O_3$.

• Journal of the Korean Ceramic Society
• /
• v.30 no.8
• /
• pp.615-622
• /
• 1993

In order to increase chemical durability of thin films in binary system B2O3-SiO2 and Al2O3-SiO2 on the slide glass by the dip-coating technique from TEOS(Tetraethyl Orthosilicate) and boric acid or aluminum nitrate, phosphoric acid(5~20mol%) was added, respectively. Corrosion of acid and alkali of samples treated with 1N, HCl, NaOH and distilled water at 10$0^{\circ}C$ for 15 minute, were measured IR transmittance and variance of transmittance at visible range. Surface structure of thin film was investigated with SEM and formation of crystal phase according to additiion of phosphoric acid was measrued with XRD. In Al2O3-SiO2 system, change of remarkable characteristic was not obtained at the addition of P2O5 but transmittance of thin film was decreased with addition of P2O5 in B2O3-SiO2 system.

• 보존과학연구
• /
• s.35
• /
• pp.5-23
• /
• 2014

The possibility of non-destructive inspection glass beads for verification. Conduct a comparative analysis of the Chungcheong area with glass beads excavated Age-specific characteristics of the glass beads shall be classified by region. Trace amounts of ingredients such as CaO, $Al_2O_3$ (stabilizer), MgO, the difference is negligible. $SiO_2$ (subjects), $Na_2O$ (flux) analysis and the difference between the values was greater than in the other ingredients. Composition differences occurred rough surface to a non-uniform cross-section analysis is considered. Minimize the error value, such as the surface of carbon-coated Study, there are additional requirements. Produced at the time of the social and cultural characteristics of ancient glass and important archaeological materials, and to inform the process of cultural exchange between each region in the production of glass technology era according to the level of science and technology, arts and crafts, can be identified.

• The Korean Journal of Ceramics
• /
• v.1 no.4
• /
• pp.209-213
• /
• 1995

The electrical conductivity was investigated in two series of alkali aluminosilicate glass melts, $25R_2O(R: Na and K)-xAl2O3-(75-x)SiO_2$ at temperatures ranging from 1000 to 140$0^{\circ}C$. The dependences of conductivity or activation energy on $Al_2O_3/R_2O$ of both series in the molten state showed a same behavior. These results in the molten state were compared with previous studies for sodium alkali aluminosilicate glasses in the molten and solid state, and explained in terms of the binding state: $[-O]-R^+\; and\; [AlO_4]-R^+$.

• Cement
• /
• s.51
• /
• pp.20-30
• /
• 1973

1) electron-microprobe를 응용하여 $CaO-SiO_2-Al_2O_3$ 계에서 생성한 $C_2S$, $C_3S$ 에 존재하는 sulfate의 solid, solution을 정량적으로 구할 수 있었으며 이 결과로 $C_2S$ 에 $Al_2O_3$, $SO_3$ 등이 solid soln 등으로 침적되고 이들이 $C_3S$의 생성을 억제한다는 mechanism이 확인되었다. 2) phase equilibrium(상평형)에 의하면 $Na_2SO_4$, $K_2SO_4$는 mineralizer로서 작용하며 $C_3S$ 의 생성을 돕는다. 그러나 $K_2SO_4$ 와 $Al_2SO_3$ 가 결합상태로 존재할 경우는 1,400 $^{\circ}C$에서 광범위한 liquid를 생성하며 quenching하면 glass질과 $\beta-C_2S$ 만이 얻어지고 $C_3S$ 는 생성되지 않는다. 또 이를 1,250 $^{\circ}C$ 까지 서냉하면 $C_2S$ 와 Ca, K, Al, S, 등을 함유한 새로운 물질이 생성된다. 3) $CaO-SiO_2-Al_2O_3-Fe_2O_3$ 계에서 $C_3S$ 의 생성에 미치는 $Na_2SO_4$, $K_2SO_4$ 의 영향을 실험실적으로 검토한 결과 complex interaction이 확인되었으며 $Na_2SO_4$ 는 어떤 경우에는 mineralizing effect를 상실한다는 재미 있는 사실이 발견되었다.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2007.11a
• /
• pp.292-292
• /
• 2007

To apply PDP panel, Soda lime glass(SLG) is cheeper than Non-alkali glass and PD-200 glass but has problems such as low strain temperature and ion diffusion by alkali metal oxide. In this paper suggest the methode that prohibits ion diffusion by deposing barrier layer on SLG. Indium thin oxide(ITO) thin films and barrier layers were prepared on SLG substrate by Rf-magnetron sputtering. These films show a high electrical resistivity and rough uniformity as compared with PD-200 glass due to the alkali ion from the SLG on diffuse to the ITO film by the heat treatment. However these properties can be improved by introducing a barrier layer of $SiO_2\;or\;Al_2O_3$ between ITO film and SLG substrate. The characteristics of films were examined by the 4-point probe, SEM, UV-VIS spectrometer, and X-ray diffraction. GDS analysis confirmed that barrier layer inhibited Na and Ka ion diffusion from SLG. Especially ITO films deposited on the $Al_2O_3$ barrier layer had higher properties than those deposited on the $SiO_2$ barrier layer.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.30 no.2
• /
• pp.66-72
• /
• 2020

The difference of plasma resistance between the CAS glass bulk and coating films were compared. Plasma resistance was confirmed by analyzing the etch rate and the microstructure of the surface when the CAS glass bulk and the glass coating film were etched with CF₄/O₂/Ar plasma gas. CAS glass coating film was etched up to 25 times faster than the glass bulk. A statistically high correlation between the surface roughness and the etching rate of the coating film was derived, and thus, the high surface roughness of the coating film was determined to cause rapid etching. In addition, cristobalite crystals that has a low Ca content and a high Si content, was foamed on the glass coating film. Therefore, the CAS glass coating film is considered to have low plasma resistance compared to the glass bulk.