• Archives of Metallurgy and Materials
• /
• v.66 no.4
• /
• pp.959-962
• /
• 2021

In this study, precipitation of Ca in Al-Mg alloys containing a trace of Ca during homogenization was investigated using a transmission electron microscope (TEM) and calculated phase diagrams. TEM result indicated that the Ca-based particles found in the examined sample are Ca₇Mg_7.5Si₁₄. From the calculation of Scheil-Gulliver cooling, it was found that the Ca was formed as Al₄Ca and C36 laves phases with Mg₂Si and Al₁₃Fe₄ from other impurities phase during solidification. No Ca-Mg-Si ternary phase existed at the homogenization temperature in the calculated phase diagram. From the phase diagram of Al-Al₄Ca-Mg₂Si three-phase isothermal at 490℃, it was shown that Ca₇Mg₆Si₁₄ phase co-exists with Al, Mg₂Si and Al₄Ca in the largest region and with only Al and Mg₂Si in Al₄Ca-poor regions. It was thought that the Ca₇Mg₆Si₁₄ ternary phase was formed by the interaction between Mg₂Si and Al₄Ca considering that the segregation can occur throughout the entire microstructures.

• Journal of Korea Foundry Society
• /
• v.35 no.6
• /
• pp.147-154
• /
• 2015

The effects of Sc and Sr elements on the modification of the eutectic $Mg_2Si$ phase and the castability were investigated in the Al-4wt%Mg-0.9wt%Si-0.3wt%Mn-0.15wt%Fe alloy. Measurements of the cooling curve and microstructure observations were performed to analyze the additional effects of Sc and Sr minor elements during the solidification process. A prominent effect found on the modification of the eutectic $Mg_2Si$ phase with additions of the Sr and Sc elements. Here, a fine eutectic $Mg_2Si$ phase and a decrease in the growth temperature of the eutectic $Mg_2Si$ phase were evident with an addition of Sc element up to 0.2 wt%. The growth temperature of the eutectic $Mg_2Si$ phase decreased and the effect on the modification of the eutectic $Mg_2Si$ phase increased with the addition of Sr element up to 0.02 wt%. The addition of 0.02wt%Sr had the strongest effect on the modification of the eutectic $Mg_2Si$ phase, and the resulting microstructure of the eutectic $Mg_2Si$ phase was found to have a fibrous morphology with a decreased aspect ratio and an increased modification ratio. Fluidity and shrinkage tests were conducted to evaluate the castability of the alloy. The addition of 0.02wt%Sr effectively increased the fluidity of the alloy, while an addition of Sc did not show any effect compared to when nothing was added. The maximum filling length was recorded for 0.01wt%TiB-0.02wt%Sr owing to the effect of the fine ${\alpha}$-Al grains. The macro-shrinkage ratio decreased, while the micro-shrinkage ratio increased with the addition of various eutectic modifiers. The highest ratio of micro-shrinkage was recorded for the 0.02wt%Sr condition. However, the total shrinkage ratio was nearly identical regardless of the amounts added in this study.

• Journal of the Korean Society for Heat Treatment
• /
• v.24 no.2
• /
• pp.82-86
• /
• 2011

The influences of Bi addition on morphological modification of $Mg_2Si$ phase and mechanical properties were investigated in Mg-7%Al-0.5%Si casting alloy. It was found that the addition of 0.3%Bi changed the $Mg_2Si$ morphology from coarse Chinese script type to polygonal type, and significantly decreased the size to ~5 ${\mu}m$ or less with the increase of number density. The modification of $Mg_2Si$ phase by the addition of Bi resulted in the improvement of tensile properties of the Mg-Al-Si alloy at RT and $175^{\circ}C$.

• Journal of Korea Foundry Society
• /
• v.32 no.5
• /
• pp.219-224
• /
• 2012

The effects of Mg and Si contents on the microstructure and mechanical properties in Al-Mg alloy (ALDC6) were investigated. The results showed that phase fraction and size of $Mg_2Si$ and $Al_{15}(Fe,Mn)_3Si_2$ phase in the microstructure of Al-Mg alloy were increased as the Mg and Si contents were raised from 2.5 to 3.5 wt%. With Si content of 1.5 wt%, freezing range of the alloy was significantly reduced and solidification became more complex during the final stage of solidification. While there was no significant influence of Mg contents on mechanical properties, Si contents up to 1.5 wt%, strongly affected the mechanical properties. Especially elongation was reduced by about a half with more than 1.0 wt%Si in the alloy. The bending and impact strength were decreased with increased amount of Si in the alloy, as well. The lowered mechanical properties are because of the growth of particle shaped coarse $Mg_2Si$ phase and precipitation of the needle like $\beta$-AlFeSi in the microstructure at the last region to solidify due to presence of excess amount of Si in the alloy.

• Journal of Korea Foundry Society
• /
• v.31 no.1
• /
• pp.18-25
• /
• 2011

Effect of Fe and Mn contents on the tensile properties has been studied in Al-9wt%Si-0.3wt%Mg alloy. As Fe content of Al-9wt%Si-0.3wt%Mg-0.5wt%Mn alloy increased from 0.15wt% to 0.45wt%, tensile strength of as-cast alloy decreased from 192 MPa to 174 MPa, and elongation of the alloy also decreased from 4.8% to 4.2%. Decrease of these properties can be explained as the formation of plate shape, ${\beta}-Al_5FeSi$ phase with high Fe/Mn ratio of the alloy. However when Mn content of Al-9wt%Si-0.3wt%Mg-0.45wt%Fe alloy increased from 0.3wt% to 0.5wt%, tensile strength of T6 aged alloy increased from 265 MPa to 275 MPa, and elongation of the alloy increased from 2.3% to 3.6%. These improvements attribute to chinese script, ${\alpha}-Al_{15}(Mn,Fe)_3Si_2$ phase shape-modified from ${\beta}-Al_5FeSi$ phase with low Fe/Mn ratio of the alloy.

• Journal of Korea Foundry Society
• /
• v.24 no.6
• /
• pp.340-346
• /
• 2004

The plan for obtaining a good combination of strength and castability appeared feasible and the following observations were made. 1. In Al-12Mg-6.6Zn-xSi alloys, more primary $Mg_2Si$ phase formed with reduced $Al_3Mg_2$ phase, as Si content is necessary for an effective solution heat treatment because the solidus temperature is very low silicon contents. 2. A high tensile strength could be obtained in the heat-treated Al-12Mg-5.5Zn-5Si alloy attributed in the heat-treated Al-12Mg-5.5Zn-5Si alloy attributes to fine $MgZn_2$ particles that precipitated uniformly in the matrix. 3. Al-12Mg-5.5Zn-Si alloys showed excellent casting capabilities such as hot cracking resistance and fluidity compared to the reference commercial alloys. 4. The wear resistance of Al-12Mg-5.5Zn-5Si alloy was superior to that of A7075 alloy, and even higher resistance is expected if the morphology and size of primary $Mg_2Si$ phase is carefully controlled.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.5 no.3
• /
• pp.291-298
• /
• 1995

Abstract The growth and dissolution behaviour of reaction phase was studied during dissolution reaction between sintered alumina and $CaMgSiO_4$ at $1600^{\circ}C$ for various times. The formation of $CaO{\cdot}6Al_2O_3$ an intermediate reaction phase, and $CaMgSiO_4$ spinel, the final reaction product were observed during dissolution reaction of alumina into $CaMgSiO_4$ liquid phase. The growth and dissolution shape of $CaO{\cdot}6Al_2O_3$, an intermediate phase, was quite different.

• Resources Recycling
• /
• v.20 no.5
• /
• pp.34-39
• /
• 2011

Metallurgical grade silicon(MG-Si) was melted with Ca at 1500$^{\circ}C$ under Ar atmosphere. The sample was cooled at 10 $^{\circ}C$/min to room temperature and leached in aqua regia. In the present study, the effect of Ca addition and conditions of acid leaching on removal of Fe and P in MG-Si were investigated. CaSi$_2$ phase was formed at the grain boundary of MG-Si melting with Ca. Also FeSi$_2$ phase was precipitated in CaSi$_2$ phase. By the formation of CaSi$_2$ phase, 97% of Fe and 66 % of P were removed from Ca added MG-Si with the particle size of 600~850${\mu}m$ by aqua regia(more than 30%) leaching.

• Journal of the Mineralogical Society of Korea
• /
• v.16 no.2
• /
• pp.161-169
• /
• 2003

A phase transformation study on a synthetic amorphous diopside, $(Ca,Mg)SiO_3$has been carried out up to ∼30 GPa, and ∼$1000^{\circ}C$ using a diamond anvil cell and YAG laser heating system, respectively. A starting amorphous material shows a direct transition to cubic $(Ca,Mg)SiO_3$perovskite at high pressure, which contradicts to the crystalline diopside phase transformation sequence disproportionating into mixtures of the orthorhombic$ MgSiO_3$perovskite and the cubic $CaSiO_3$perovskite phases. This discrepancy might be due to the different starting materials as well as the temperature variations at each specific experiment performed. The present phase transfor mation sequence would modify the mineralogical assemblage in the Earth transition region and the lower mantle depending upon the pressure, temperature and the oxygen partial pressure.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.28 no.2
• /
• pp.74-79
• /
• 2018

To increase corrosion resistance of Mg alloy, AZ31 and AZ91 were PEO treated with different applied voltage and time conditions. We used Na-P and Na-Si system electrolyte. Crystalline phase and morphology were investigated. MgO was Most common crystal phase and vitreous phase could be found. Crystalline phase of $Na_{3.59}Mg_{2.71}(PO_4)_3$ and $Mg_2SiO_4$ also could be found. Porosity of oxidized surface tends to decrease with increasing PEO applied voltage, treat time and concentration of electrolyte, after then, size of pore increased and total number of pore decreased, distinctly.