• Composites Research
• /
• v.33 no.5
• /
• pp.247-250
• /
• 2020

In this study, the possibility of manufacturing a magnesium (Mg) composites reinforced with continuous silicon carbide (SiC) fibers was examined using a liquid pressing process. We fabricated uniformly dispersed SiC fiberAZ91 composites using a liquid phase pressing process. Furthermore, the precipitates were controlled through heat treatment. As a continuous Mg₂Si phase was formed at the interface between the SiC fiber and the AZ91 matrix alloy, the interfacial bonding strength was improved. The tensile strength at room temperature of the prepared composite was 479 MPa, showing excellent mechanical properties.

• Korean Journal of Metals and Materials
• /
• v.47 no.4
• /
• pp.223-227
• /
• 2009

The precipitates, hardness, and tensile properties of Al-6.2Si-2.9Cu AC2B alloy were investigated with respect to solution treatment time at $500^{\circ}C$. $Al(Cu)-Al_2Cu$ eutectic, Si, ${\theta}-(Al_2Cu)$, and $Q-(Al_5Cu_2Mg_8Si_6)$ phases were observed in the as-cast specimen. With increasing the solution treatment time at $500^{\circ}C$, the $Al(Cu)-Al_2Cu$ eutectic and ${\theta}-(Al_2Cu)$ phases were gradually reduced and finally almost disappeared in 5 h. The mechanical properties, such as hardness, tensile strength, and elongation, were improved with solution treatment time until about 5 h due to the dissolution of the $Al_2Cu$ particles. With further holding time, the mechanical properties did not change much. The solution treated specimens for over 5 h at $500^{\circ}C$ exhibit almost the same tensile properties even after aging at $250^{\circ}C$ for 3.5 h. Accordingly, the optimal solution treatment condition of the Al-Si-Cu AC2B alloy is considered to be 5 h at $500^{\circ}C$.

• Journal of the Korean Ceramic Society
• /
• v.17 no.3
• /
• pp.151-157
• /
• 1980

Crystallization phenomena of glasses of fused natural basalt rocks were studied by DTA, X-ray phase analysis, electron microscopy, and other techniques. Crystallization was catalyzed by the addition of either chromite ore or $P_2O_5$, both up to 5 wt %. Various heat treatments were used, and their influences on controlling the microstructures and properties of the products were studied to develop high strength glass-ceramic material of the $CaO-Al_2O_3(Fe_2O_3)-MgO(FeO)-SiO_2$ system from the domestic basalts. Magnetite precipitates were found to be a nucleation initiator in every case of the crystallization. Diopside, anorthite, clinoenstatite and monticellite were identified as silicate crystalline phases contained in the crystallized products. The crystallite size was in the range of 0.1-2.5$\mu\textrm{m}$. The fine crystallites were approximately cubic, but large crystallites were either plate or needle shape. The thermal expansion coefficient, microhardness and modulus of rupture of glass-ceramics were ranged from 78.5 to 81.8$\times$10-7 cm/cm/$^{\circ}C$, from 820 to 930kg/$\textrm{mm}^2$, and from 1800 to 2800kg/$\textrm{cm}^2$, respectively.

• Transactions of Materials Processing
• /
• v.12 no.6
• /
• pp.588-596
• /
• 2003

The relationships between evolution of microstructure and mechanical properties of porous Al-3Si-2Mg-2Cu alloy after the foaming and various heat treating were investigated. The foamed alloy having various densities were manufactured by powder compact foaming and heat treated. Then compression test was performed with deformation rate of 0.5/s. The ultimate compression strength was not changed after solution heat treatment but the flow curve after ultimate strength showed very smooth and uniform plateau region. This change of flow curve means that the deformation mechanism is altered from brittle fracture to ductile deformation and the energy absorption property of Al foam is dramatically improved. The improvement of energy absorption without any detriment of mechanical properties is due to that the very brittle precipitation like Al-Cu and Al-Mg was uniformly dissolved in Al matrix after solution heat treatment. And various mechanical properties of Al alloy porous material were improved by 40% with aging of $200^{\circ}C$ and 50min. These improvements are ascribe to the various fine precipitates like $\Omega$ and $\theta$'.

• Journal of Powder Materials
• /
• v.10 no.1
• /
• pp.15-20
• /
• 2003

Hybrid $A1_2O_3-TiC$ ceramic particle reinforced 6061 and 5083 Al composite powders were prepared by the combination of twin rolling and stone mill crushing process, followed by consolidating processes of cold compaction, degassing and hot extrusion. The composite bar consists of lamellar structure of ceramic particle rich area and matrix area, in which the hybrid was decomposed into each TiC of about $3-4\mutextrm{m}$ and $AI_2O_3$ particles of about $1-2\mutextrm{m}$ in diameter. It also found that fine $Mg_2Si$ precipitates of about 30 nm were embedded in the matrix, which have grains of about 3 $\mutextrm{m}$. Higher UTS was measured at the 5083 composite bar compared to the conventionally fabricated composite, due to again refinement effect by the rapid solidification. No particle was shown to form in the interface between the matrix and reinforcement, whereas carbon was diffused into the matrix.

• Korean Journal of Materials Research
• /
• v.13 no.6
• /
• pp.374-380
• /
• 2003

The effect of forging parameters, including different forging stock, strain rate and strain, on the mechanical properties of hot-forged Al 6061-T6 was investigated. The forging was conducted using either hydraulic press, crank press or hammer press, respectively, at a forging temperature of $400^{\circ}C$. When using an extruded bar as a forging stock, the tensile strength was lower for the specimens prepared by hammer forging than those by crank press forging. It was found that the coarsening of recrystallized grain was responsible for the decrease in tensile strength with hammer forging. Systematic studies on the effects of strain and strain rate on the tensile properties of hot-forged Al 6061-T6 products using extruded bar as a forging stock further suggested that the coarsening of recrystallized grains and$ Mg_2$Si precipitates complexed the observed trends in the tensile behavior. In case of hot forging with continuous cast bar as a forging stock, on the other hand, the mechanical properties of the specimen were largely improved with hammer press compared to those with crank press, which appeared to be due to the homogenization of microstructure.

• Economic and Environmental Geology
• /
• v.50 no.4
• /
• pp.257-266
• /
• 2017

Batch experiments were performed to develop the method for the pH reduction of recycled aggregate by using $scCO_2$ (supercritical $CO_2$), maintaining the pH of extraction water below 9.8. Three different aggregate types from a domestic company were used for the $scCO_2$-water-recycled aggregate reaction to investigate the low pH maintenance of aggregate during the reaction. Thirty five gram of recycled aggregate sample was mixed with 70 mL of distilled water in a Teflon beaker, which was fixed in a high pressurized stainless steel cell (150 mL of capacity). The inside of the cell was pressurized to 100 bar and each cell was located in an oven at $50^{\circ}C$ for 50 days and the pH and ion concentrations of water in the cell were measured at a different reaction time interval. The XRD and SEM-EDS analyses for the aggregate before and after the reaction were performed to identify the mineralogical change during the reaction. The extraction experiment for the aggregate was also conducted to investigate the pH change of extracted water by the $scCO_2$ treatment. The pH of the recycled aggregate without the $scCO_2$ treatment maintained over 12, but its pH dramatically decreased to below 7 after 1 hour reaction and maintained below 8 for 50 day reaction. Concentration of $Ca^{2+}$, $Si^{4+}$, $Mg^{2+}$ and $Na^+$ increased in water due to the $scCO_2$-water-recycled aggregate reaction and lots of secondary precipitates such as calcite, amorphous silicate, and hydroxide minerals were found by XRD and SEM-EDS analyses. The pH of extracted water from the recycled aggregates without the $scCO_2$ treatment maintained over 12, but the pH of extracted water with the $scCO_2$ treatment kept below 9 of pH for both of 50 day and 1 day treatment, suggesting that the recycled aggregate with the $scCO_2$ treatment can be reused in real construction sites.