• Progress in Superconductivity and Cryogenics
• /
• v.7 no.4
• /
• pp.1-3
• /
• 2005

Superconducting $MgB_2$ fibers are in-situ grown by a diffusion method. The fibers are prepared by exposing B filaments to Mg vapor inside a folded Ta foil over a wide range of temperature and growth time. The materials are sealed inside a quartz tube by gas welding. The as - grown fibers are characterized by scanning electron microscopy and energy dispersive x - ray analysis. The fibers have a diameter of about $110{\mu}m$. Surface morphology of the fibers looks dependent on growth temperature and mixing ratio of Mg and B. Radial distribution of Mg ions into B is observed and analyzed over the cross - sectional area. Transport properties of the $MgB_2$ fibers are examined by a physical property measurement system. The $MgB_2$ fibers grown at $900^{\circ}C$ for 2 hours show a superconducting transition at 39.8K with ${\Delta}T_c<$ 2.0 K. Resistance at room temperature $MgB_2$ is 3.745 $\Omega$ and residual resistivity ratio (RRR) is estimated as 4.723.

• Progress in Superconductivity and Cryogenics
• /
• v.17 no.3
• /
• pp.1-4
• /
• 2015

Production of $MgB_2$ film on metallic Hastelloy with SiC as the buffer layer was achieved by means of hybrid physical-chemical vapor deposition technique, whereas SiC buffer layers with varied thickness of 170 and 250 nm were fabricated inside a pulsed laser deposition chamber. Superconducting transition temperature and critical current density were verified by transport and magnetic measurement, respectively. With SiC buffer layer, the reduced delaminated area at the interface of $MgB_2$-Hastelloy and the slightly increased $T_c$ of $MgB_2$ tapes were clearly noticed. It was found that the upper critical field, the irreversibility field and the critical current density were reduced when $MgB_2$ tapes were buffered with SiC buffer layer. Clarifying the mechanism of SiC buffer layer in $MgB_2$ tape in affecting the superconducting properties is considerably important for practical applications.

• Progress in Superconductivity and Cryogenics
• /
• v.24 no.1
• /
• pp.18-22
• /
• 2022

The effect of electron beam (EB) irradiation on superconducting properties and microstructures of MgB₂ bulk superconductors were investigated. At E-beam doses of 1×10¹⁶ e/cm² and 1×10¹⁷ e/cm², the effect of irradiation on a superconducting transition temperature (T_c) of MgB₂ was weak. As a dose increases to 5×10¹⁷ e/cm², T_c decreases by 0.5 K. The critical current density (J_c) measured at 4.2 K and 20 K, and 0 T - 5 T increases slightly as exposure time increases. X-ray diffraction for the irradiation surface of MgB₂ shows that the diffraction intensity of (hkl) peaks decreases proportionally as the exposure time increases. This indicates that the crystallinity of MgB₂ was degraded by irradiation. TEM investigation for the irradiated sample showed distorted lattice structure, which is consistent with the XRD results. The J_c increase and T_c reduction of MgB₂ by irradiation are believed to be caused by the lattice distortion.

• Superconductivity and Cryogenics
• /
• v.12 no.1
• /
• pp.24-28
• /
• 2010

• 한국초전도학회:학술대회논문집
• /
• v.16
• /
• pp.10-10
• /
• 2006

• Superconductivity and Cryogenics
• /
• v.11 no.2
• /
• pp.23-29
• /
• 2009

The unique features of HTS offer opportunities and challenges to a number of applications. In this paper we focus on NMR and MRI magnets, illustrating them with the NMR/MRI magnets that we are currently and will shortly be engaged: a 1.3 GHz NMR magnet, an "annulus" magnet, and an $MgB_2$whole-body MRI magnet. The opportunities with HTS include: 1) high fields (e.g., 1.3 GHz magnet); 2) compactness (annulus magnet); and 3) enhanced stability despite liquid-helium-free operation ($MgB_2$whole-body MRI magnet). The challenges include: 1) a large screening current field detrimental to spatial field homogeneity (e.g., 1.3 GHz magnet); 2) uniformity of critical current density (annulus magnet); and 3) superconducting joints ($MgB_2$magnet).

• 한국초전도학회:학술대회논문집
• /
• 2007.07a
• /
• pp.2-2
• /
• 2007

• Progress in Superconductivity and Cryogenics
• /
• v.16 no.3
• /
• pp.7-9
• /
• 2014

Single-crystal like $MgB_2$ thin film was grown on (000l) $Al_2O_3$ substrate by using hybrid physical-chemical vapor deposition (HPCVD) system. Single crystal properties were studied by X-ray diffraction (XRD) and the full width at half maximum (FWHM) of the (0001) $MgB_2$ peak is $15^{\circ}$, which is very close to that has been reported for $MgB_2$ single-crystal. It indicates that the crystalline quality of thin film is good. Temperature dependence on resistivity was investigated by physical property measurement system (PPMS) in various applied fields from 0 to 9 T. The upper critical field ($H_{c2}$) and irreversibility field ($H_{irr}$) were determined from PPMS data, and the estimated values are comparable with that of $MgB_2$ single-crystals. The thin film shows a high critical temperature ($T_c$) of 40.4 K with a sharp superconducting transition width of 0.2 K, and a high residual resistivity ratio (RRR=21), it reflects that $MgB_2$ thin film has a pure phase structure.

• Progress in Superconductivity and Cryogenics
• /
• v.23 no.4
• /
• pp.14-18
• /
• 2021

The Mg-Powder-Compaction (MPC) process is proposed to fabricate the MgB₂ superconducting wires. Mg powder wall, similar to the Mg metal tube, inside the Nb outer sheath has been made and the stochiometric B powder was inserted into the wall. Even though the very high MgB₂ core density of 2.53 g/cm³ is obtained, the superconducting area fraction of MgB₂ is not high enough for the applications. In this work, an advanced MPC process was adopted by adding Mg powder into B powder. The Mg powder wall in the initial wire was fabricated by controlling the wall thickness while maintaining a constant density, and the mixture of B and Mg powder was filled into the Mg powder wall with the same filling density. It is found that the reduction in the area of the Mg powder wall proceeds similar to the wire, and the Mg powder wall is well maintained at the final wire diameter, which is advantage for the fabrication of long wires. With the advanced MPC process, as the added Mg is increased the densities of MgB₂ core is decreased and the porous structure is formed, it is found that the area fraction of superconducting MgB₂ increase up to the 37.7 % with the improved high critical current density (J_c) and the engineering critical current density (J_e).

• Progress in Superconductivity and Cryogenics
• /
• v.14 no.4
• /
• pp.12-15
• /
• 2012

$MgB_2$ superconductor is highly sensitive to the Mg content. Even if the samples are synthesized with the appropriate looking stoichiometric ratio, the heat treatment leads to the loss of Mg either to ambiance or to MgO. To avoid it, either excess Mg is added in the starting powder or sealed ampoule annealing is employed. In this paper the effect of open Mg sintering ambiance on the ex-situ $MgB_2$ was studied to enhance its superconducting properties. The open Mg ambiance was created to avoid any overpressure of Mg by providing a hole in Fe tube used as sample holder. The decrease in resistivity of the synthesized sample was observed through the increased temperature dependence of electron-phonon interactions. A clear enhancement in the superconducting cross-sectional area and hence the in-field critical current density is obtained.