• 한국응용과학기술학회지
• /
• 제31권2호
• /
• pp.190-196
• /
• 2014

The sol-gel method was used to prepare binary metal oxide ($IrO_2-RuO_2$) pH sensor. The electrodes that mole percent compositions (mol%) of $IrO_2$ and RuO2 were 70:30 and 30:70 were selected. The characterizations of Nernstian response over pH range, response rate, interference on alkaline metals and reproducibility were investigated. Also the electroanalytical properties of these electrodes were evaluated in comparison with a commercial glass pH electrode. The composition of $IrO_2:RuO_2$ 70:30 mol% was chosen as better electrode formulation. The electrode was not susceptible to the action of interfering ions such as $Li^+$, $Na^+$ and $K^+$.

• 한국진공학회지
• /
• 제5권1호
• /
• pp.67-72
• /
• 1996

$RU_{1-x}Ir_xO_2$ films were deposited on the quartz substrate by a spray pyrolysis method. The x-ray diffraction patterns showed that the structure of the $RU_{1-x}Ir_xO_2$ film was tetragonal and the lattice constant $a_o$ and $c_o$ were increased from 4.495 A to 4.058 A and from 3.092A to 3.156 A, respectively as the Ir composition varied from 0.0 to 1.0. The $RU_{1-x}Ir_xO_2$ film was metallic and the resistivity of the samples was increased from $7{\times}10^{-5}{\Omega}\textrm{cm}$ to $48{\times}10^{-5}{\Omega}\textrm{cm}$ with increasing the Ir x. The surface of the sample was slightly roughed, the grain size and the grain boundary width were increased as the Ir composition varied from 0.0 to 1.0.

• 한국표면공학회:학술대회논문집
• /
• 한국표면공학회 2016년도 추계학술대회 논문집
• /
• pp.191.2-191.2
• /
• 2016

$TiO_2$는 우수한 화학적 및 물리적 안정성 때문에 수전해 장기간 사용에 적합한 전기화학 전극으로 여겨진다. 큰 표면적을 갖는 $TiO_2$를 제조하기 위한 수많은 방법 중 양극산화(anodization)는 비교적 간단하고 저렴한 공정으로 인하여 매우 실용적인 방법으로서 알려져 있다. 특히, 고도로 정렬 된 $TiO_2$ 나노튜브($TiO_2$ NTs) 의 경우에는 분말상과 달리 전극제조를 위해 추가적인 접착제를 필요하지 않다. 그러나, $TiO_2$는 일반적으로 절연 특성을 나타내기 때문에 전극의 활용을 위해서는 본질적으로 촉매의 사용이 불가피하다. 다수의 전기 촉매 중, $IrO_2$와 $RuO_2$는 수전해 분야에 잘 알려진 산화 촉매이다. 그럼에도 불구하고, 특유의 높은 종횡비 때문에 $TiO_2$ 나노튜브에 전기 촉매를 균일하게 도핑하는 것은 많은 어려움이 따른다. 이를 해결하기 위한 방법으로 $RuO_2$를 도핑하기 위한 단일공정 $TiO_2$ 양극산화 기술이 보고된 바 있다. 본 연구에서는 2원 촉매($IrO_2$ 및 $RuO_2$)를 $TiO_2$ 나노튜브에 도핑하기 위한 단일공정 양극산화 기술에 대하여 연구하였다. 전구물질로써 $KRuO_4$($RuO_2$ 전구체)와 IrOx 나노입자(IrOx NPs, $IrO_2$ 전구체)를 사용하였다. 특히, IrOx를 나노 입자는 $IrCl_3$로부터 중간 매체로 합성된다. IrOx는 단일공정 양극산화 중에 $TiO_2$ 나노튜브 상에 도핑 가능한 이온 형태인 $IrO_4$-로 전환될 수 있다. 제조된 시료는 열처리 후 바로 전극으로 사용되었으며 SEM, XPS, TEM, ICP-OES 등으로 정성, 정량 분석을 수행하였다. LSV와 EIS를 통해 전기화학적 성능 평가가 이루어졌으며, LSV를 통해 포집한 기체는 가스 크로마토그래피를 사용하여 정량분석한 후 그 효율을 측정하였다.

• 공업화학
• /
• 제18권6호
• /
• pp.552-556
• /
• 2007

연구에서는 $TiO_2$ 담체에 귀금속(Pd, Ru, Ir)을 담지시켜 촉매를 제조하였다. 금속분산의 향상을 위해 $H_2O-H_2$ 전처리 기술이 이용되었고, 반응물로서 xylene, toluene 그리고 MEK를 사용하였다. 단일금속과 합금금속의 촉매들은 함침법에 의해 준비하였고, XRD, XPS 분석을 통하여 특성 분석하였다. Pd-Ru, Pd-Ir 촉매는 다양한 활성점을 나타내었고, 그것은 Pd의 metal 영역를 강화시켰다. 합금금속으로 이루어진 촉매가 단일 금속으로 이루어진 촉매에 비해 VOCs 전환율이 더 높았다. $H_2O-H_2$ 전처리 기술은 Pd 입자를 고르게 분산시켰다. 이는 촉매의 효율을 증진시키는 효과를 보여주었다. 본 연구에서 Pd에 소량의 Ru, Ir 첨가는 VOCs의 산화반응을 증진시켰고, $TiO_2$ 담체상에서 $H_2O-H_2$ 전처리는 VOCs의 제거효율을 증진시켰다.

• Environmental Engineering Research
• /
• 제24권4호
• /
• pp.646-653
• /
• 2019

Recovery of valuable metals in the industrial wastewater and sludge has attracted an attention owing to limited metallic resources in the earth. In this study, we firstly fabricated Ti/Ir-Ru electrodes by spin coating technique for effective recovery of Cu in electrowinning process. Two different Ti/Ir-Ru electrodes were fabricated using 100 and 500 mM of precursors (i.e., Ir-Ru). SEM-EDX and AFM revealed that Ir and Ru were homogenously distributed on the surface of Ti plate by the spin coating, in particular the electrode prepared by 500 mM showed distinct boundary line between Ir-Ru layer and Ti substrate. XRD, XPS, and cyclic voltammetry also revealed that characteristics of IrO₂, RuO₂, and TiO₂ and its electrocatalytic property increased as the concentration of coating precursor increased. Finally, we carried out Cu recovery experiments using two Ti/Ir-Ru as anodes in electrowinning process, showing that both anodes showed a complete removal of Cu (1 and 10 g/L) within 6 h reaction, but much higher kinetic rate constant was obtained by the anode prepared by 500 mM. The findings in this study can provide a fundamental knowledge for surface characteristics of Ti/Ir-Ru electrode prepared by spin coating method and its potential feasibility for effective electrowinning process.

• 한국세라믹학회지
• /
• 제39권6호
• /
• pp.582-588
• /
• 2002

Ti 기판에 TiO$_2$ 중간층을 플라즈마 용사법으로 증착 후 IrO$_2$-RuO$_2$ 박막을 졸-겔과 dip coating법으로 제조하였다. 코팅 층의 접착력을 향상시키기 위하여 유기화합물과 glass brit을 첨가하였다. Taguchi법의 망대특성과 Lls(2$^1$$\times$3$^{7}$ )의 직교배열표를 이용하여 IrO$_2$-RuO$_2$ 박막의 최적조건인 인자와 수준 조합의 최적화를 전류밀도를 측정 분산분석하였다. 최적의 코팅조건은 각각 ethyl cellulose의 점도는 100cp, 건조온도 및 시간은 17$0^{\circ}C$ 20분, 열처리온도 및 시간은 75$0^{\circ}C$ 10분, 전도성 분말과 glass frit의 무게비는 99:5, 최종열처리시간은 120분, 주입산소량은 5sccm이었다. 분산분석결과, 유의수준이 $\alpha$=0.1인 통계적으로 90%신뢰공정이었다.

• 대한화학회지
• /
• 제62권4호
• /
• pp.269-274
• /
• 2018

금속산화물 고분자 복합재료전극 제조기법을 수소이온 감응성이 높은 $RuO_2$에 적용하여 표면연마가 가능한 나노 $RuO_2$ 복합재료 pH전극을 제조하였다. $RuO_2$ 함량 53 wt%을 가지는 나노 $RuO_2$ 복합재료 전극의 경우 나노 $IrO_2$ 복합재료 전극과 비슷한 수소이온 감응특성을 나타내었다. pH 1~9의 범위에서 이론치에 가까운 -58.7 mV/pH의 감응기울기, 1초 이하의 감응속도, 평균 $-57.0{\pm}0.3mV/pH$ (n=5)의 표면재생성, 장기 안정성 등 제반 특성과 전기화학적으로 활성이 높은 화학종에 의한 방해효과도 비슷하게 나타났다. 그러나 pH 10 이상의 염기성 용액에서의 감응기울기와 감응속도는 나노 $IrO_2$ 복합재료전극에 비하여 현저히 떨어지는 결과를 보였으며 이는 복합재료 매질 속의 금속산화물 함량에 따른 물리적 성질 차이에 따른 것으로 추측된다.

• 한국표면공학회:학술대회논문집
• /
• 한국표면공학회 2000년도 추계학술발표회 초록집
• /
• pp.65-66
• /
• 2000

• 한국표면공학회:학술대회논문집
• /
• 한국표면공학회 2000년도 추계학술발표회 초록집
• /
• pp.63-64
• /
• 2000

• 청정기술
• /
• 제22권1호
• /
• pp.16-28
• /
• 2016

섬유산업은 염색폐수의 농도가 높고 방출량이 많아 고도의 공해산업으로 알려져 있다. 염색폐수에는 색도물질 뿐만 아니라 다량의 유기화합물과 불용성 물질이 섞여 있다. 합성염료 중 아조(azo) 염료는 특히 오염물질의 배출이 많은 것으로 알려져 있다. 전기화학적 폐수처리방법은 전극의 산화·환원반응에 의해 색도와 유기물 등을 처리하는 방법으로 다른 폐수처리방법들에 비해 반응기가 작고 경제적이고 간단하며 오염물제거속도가 빠르다. 본 연구에서는 diazo 화합물인 CI Direct Blue 15 염색 폐수의 전기화학적 분해특성을 연구하였다. 실험은 전극재질과 조업조건을 달리하여 그에 따른 분해효율을 알아보고자 하였으며, 탈색 효율을 향상시킬 수 있는 최적전극 재질과 조업조건을 알아보고자 하였다. 조업조건으로는 전해질 농도, 전류밀도, 반응 온도, 초기 pH의 영향을 검토하였다. 음극은 stainless steel 전극을 사용하였고, 양극은 graphite와 RuO₂/Ti, PtO₂/Ti, IrO₂/Ti를 사용하여 조업조건에 따른 각 전극의 염색폐수 분해성능 실험을 수행하였다. 그 결과 전해질의 농도와 전류밀도 증가에 따라 전기분해 효율은 증가하였다. 양극 재질에 따른 전기분해 효율은 산성 전해질 조건에서 RuO₂/Ti > PtO₂/Ti > IrO₂/Ti > graphite 순이었고 중성과 염기성에서는 RuO₂/Ti > IrO₂/Ti > PtO₂/Ti > graphite의 순으로 나타났다. 따라서 염색 폐수의 전기분해 처리에는 RuO₂/Ti와 IrO₂/Ti가 가장 효율적인 양극재질이었다.