• 한국세라믹학회지
• /
• 제43권9호
• /
• pp.582-587
• /
• 2006

Decomposition behavior of $ferro-Si_3N_4$was investigated with varying temperature and holding time in mud components for high temperature refractory applications. Porosities gradually increased with increasing temperature and holding time due to the carbothermal reduction of $Si_3N_4\;and\;SiO_2$. Silicon monoxide (SiO) as a intermediate resulted from evaporation of $Si_3N_4\;and\;SiO_2$ reacted with C sources to generate needle-like ${\beta}-SiC$ and Fe in $Si_3N_4$ acted as a catalyst in order to enhance growth of SiC grain with the preferred orientation. SiC generation yield increased with increasing holding time, all of the $Si_3N_4\;and\;SiO_2$ affected on SiC formation up to 2h. However, SiC generation was only dependent on residual $SiO_2$ over 2h, because the carbothermal reduction reaction of $Si_3N_4$ was no longer possible at that time.

• 한국세라믹학회지
• /
• 제32권12호
• /
• pp.1331-1336
• /
• 1995

The glass-ceramics for ferro-electric were made from compositions of 70PbO.16TiO2.8SiO2.4B2O3.2AlPO4 (wt%) and 67.5PbO.20TiO2.8.5SiO2.2B2O3.2AlPO4 (wt%). The crystallization kinetics for PbTiO3 crystalline phase formation from glass was studied using non-isothermal DSC techniques. The values of activation energy, ΔE using variables of heating rate and temperature were calculated at various reaction fractions obtained from peak area over DSC. The results indicated that activation energy was lowest at 60% reaction fractions and the activation energy of glass containing 20.0 wt% TiO2 is higher than that of glass containing 16.0 wt% TiO2. The crystallization mechanism was three dimensional growth (n=4).

• 한국재료학회지
• /
• 제11권5호
• /
• pp.367-371
• /
• 2001

RF magnetron sputtering 법으로 T $a_2$ $O_{5}$ 세라믹 타겟과 S $r_2$N $b_2$ $O_{7}$ 세라믹 타겟을 동시 sputtering하여 저유전율 S $r_2$(T $a_{1-x}$ , N $b_{x}$)$_2$ $O_{7}$(STNO) 박막을 p-type Si (100) 기판 위에 증착하여 NDRO 강유전체 메모리 (Non-destructive read out ferro-electric random access memory)에 사용되는 Pt/STNO/Si (MFS) 구조의 응용 가능성을 확인하였다. Sr$_2$Nb$_2$ $O_{7} (SN O)$ 타겟과 T $a_2$ $O_{5}$ 타겟의 출력의 비를 100w/100w, 70w/100w, 그리고 50w/100w로 조절하면서 x 값을 달리하여 조성을 변화시켰다. 성장된 박막을 8$50^{\circ}C$, 90$0^{\circ}C$, 그리고 9$50^{\circ}C$에서 1시간 동안 산소 분위기에서 열처리하였다. 조성과 열처리 온도에 따른 구조적 특징을 XRD에 의해 관찰하였으며 표면특성은 FE-SBM에 의해 관찰하였고, C-V 측정과 I-V 측정으로 박막의 전기적 특성을 조사하였다. SNO 타겟과 T $a_2$ $O_{5}$ 타켓의 출력비에 따른 STNO 박막의 성장 결과 70W/170W의 출력비에서 성장된 STNO박막에서 Ta의 양이 상대적 맡은 x=0.4였으며 가장 우수한 C-V 특성 및 누설 전류 특성을 보였다. 이 조성에서 성장된 STNO박막은 3-9V외 인가전압에서 메모리 윈도우 갑이 0.5-8.3V였고 누설전류밀도는 -6V의 인가전압에서 7.9$\times$10$_{-8}$A /$\textrm{cm}^2$였다.