• Journal of Magnetics
• /
• 제9권2호
• /
• pp.27-33
• /
• 2004

Magnetic properties of $Nd_4Fe_{77.5}B_{18.5}$ compound in term of exchange coupling between $Nd_2Fe_{14}B$ and $Fe_3B$ magnetic nano crystals in melt spun powders were characterized by varying the quenching speed in mass production line. The exchange coupled phenomenon was characterized as functions of nano crystal size and volume fraction of each magnetic phase which was possible by employing Henkel plot (${\delta}M$) and refined Mossbauer spectroscopy. The optimized magnetic properties obtained from the present volume production line were: $B_r= 11.73 kG,{_i}H_c/ = 3.082 kOe$, and $(BH)_{max} = 12.28 MGOe.$ The volume fraction of each magnetic phase for those conditions giving the grain size of 10 nm were ${\alpha}-Fe; 4.2%, Fe_3B; 60.1 %$, and $Nd_2Fe_{14}B; 35.7%$. The superior magnetic properties in the $Nd_2Fe_{14}Fe_3B$ based nanocomposites were confirmed to be dependant on the volume fraction of $Fe_3B$.

• 한국자기학회지
• /
• 제9권3호
• /
• pp.154-158
• /
• 1999

Nd 함유량을 2~6at.%로 변화시킨 $\alpha$-(Fe, Co)-B-Nb-Cu 초미세결정립합금의 미세조직 및 자기특성을 조사하였다. 급속응고된 Ndx(Fe0.9Co0.1)90-xB6Nb3Cu1(2$\leq$x$\leq$6, 1at.% 간격) 합금은 x=3 이상에서 비정질상으로 제조되었다. 제조된 비정질합금은 열처리에 의해 $\alpha$-(Fe, Co) 및 Nd2(Fe, Co)14B1상으로 구성된 초미세결정립합금으로 결정화 되었다. 최적열처리조건에서 잔류자화는 Nd의 증가에 따라 감소하며, x=3에서 1.55T로 최대 값을 나타내었다. 보자력은 Nd함유량 증가에 따라 직선적으로 증가하여 x=6에서 4.6kOe이었으며, 최대에너지적은 10.6MGOe였다.

• 한국표면공학회:학술대회논문집
• /
• 한국표면공학회 2017년도 춘계학술대회 논문집
• /
• pp.119.1-119.1
• /
• 2017

Fe-(10, 24 wt.%) Gd-B 합금을 진공 주조하고 상분석과 내식성 평가 및 표면 경도를 측정하였다. 주조된 Fe-10 wt.% Gd-B 합금의 상은 주로 $Fe_2Gd$, $Fe_3Gd$, $B_4FeGd$, $GdB_2$이었으며, Fe-24 wt.% Gd-B 합금은 주로 $Fe_2Gd$, $Fe_3Gd$, $Fe_9Gd$, $Fe_{17}Gd_2$, $B_4FeGd$, $GdB_2$이었다. 인공해수 분위기에서의 부식 속도와 부식 전위는 각각 2.771, 2.914 [$mA/cm^2$]과 -623.9, -607.8 [$mV_{SHE}$]이었다. 표면 경도는 각각 220, 208 [Hv] 이었다. Gd 함량이 증가할수록 부식 속도는 증가하였고 표면 경도는 감소하는 경향을 보였다.

• 한국자기학회지
• /
• 제5권5호
• /
• pp.880-894
• /
• 1995

B의 함유량을 6 at% 고정하고 Nd함유량을 3~5 at%로 변화시킨 $\alpha$-Fe기 Nd-Fe-B 합금의 자기특성이 조사 되었다. 급속응고법으로 제조된 $Nd_{x}{(Fe_{0.9}Co_{0.1})}_{90-x}B_{6}Nb_{3}Cu_{1}(x=\;3,\;4,\;5)$ 비정질합금은 열처리에 의하여 초미세결정립으로 결정화하며, Nd의 함유량에 따라 잔류자화 및 보자력이 변한다. x=3의 경우 최적열처리조건에서 $\alpha$-Fe(Co) 부피분율의 증가로 잔류자 화는 증가하나, 보자력은 감소한다. 그러나 Nd 함유량의 증가는 $Nd_{2}{(Fe,\;Co)}_{14}B$ 부피분율의 증가로 인하여 잔류자화는 감소하나 보자력은 향상된다. $640^{\circ}C$, 10 min 열처리조건에서 $Nd_{5}{(Fe_{0.9}Co_{0.1})}_{85}B_{6}Nb_{3}Cu_{1}$의 결정립크기는 약 20 nm이며, 잔류자화, 보자력 및 최대에너지적 은 각각 1.35 T, 219 kA/m (2.75 kOe) 및 $129\;kJ/m^{3}$ (16.2 MGOe)으로 가장 우수하다.

• 한국자기학회지
• /
• 제5권5호
• /
• pp.412-415
• /
• 1995

By adding 1wt.% $HfB_{2}$ into $Nd_{3-4}Fe_{77-78.5}B_{18.5}$ alloys, the grain growth of $Fe_{3}B/Nd_{2}Fe_{14}B$ composite phases during annealing was found to be hindered by 40~50%. It is proposed that the addition of $HfB_{2}$ leads to the formation of fine dispersoids of $HfB_{2}$ in the $Fe_{3}B/Nd_{2}Fe_{14}B$ composite magnet. The maximum energy product($(B.H)_{max}$) as well as intrinsic coercivity($_{i}H_{c}$) for the $Nd_{3}Fe_{78.5}B_{18.5}\;+\;1wt.%\;HfB_{2}$ alloy were enhanced by more than 25% $(B.H)_{max}=10\;MGOe,\;_{i}H_{c}=2.5\;kOe)$ due to the addition of $HfB_{2}$ while remanent magntization($B_{r}$) was reduced slightly. Itis deduced that the formation of fine dispersoids will also play a role of magnetic domain pinning.

• Journal of Magnetics
• /
• 제13권3호
• /
• pp.102-105
• /
• 2008

This study examined the feasibility of the combining HDDR-process (hydrogenation, disproportionation, desorption and recombination) with mechanical milling to prepare single domain $Nd_2Fe_{14}B$ particles from a Nd-Fe-B alloy ingot. The $Nd_{15}Fe_{77}B_8$ alloy was HDDR-treated and then subjected to a roller-milling. In the HDDR-treated $Nd_{15}Fe_{77}B_8$ alloy, very small $Nd_2Fe_{14}B$ grains comparable to their critical single domain size(0.3 ${\mu}m$) were observed. These fine individual grains were separated successfully along the grain boundaries by a roller-milling. The separated $Nd_2Fe_{14}B$ grains were found to be single domain particles. These results suggest that single domain particles of the $Nd_2Fe_{14}B$ phase can be prepared from a Nd-Fe-B ingot alloy by combining a HDDR-process with mechanical milling.

• 한국주조공학회지
• /
• 제23권2호
• /
• pp.77-85
• /
• 2003

Some alloying elements such as Cr, B, Ti and Si were added individually or as a mixture to Fe-30 at.%Al alloys. The alloys were melted using an arc furnace and then heat-treated for homogenization at 1000$^{\circ}C$ for 7 days and followed by rolling at 1000$^{\circ}C$. The alloying elements on rolling characteristics were investigated by the microstructures and fracture mode before and after rolling. The microstructures before rolling showed that all of the alloys had equiaxed grains. On the other hand, the microstructures of rolling plane as well as its perpendicular plane became elongated after rolling. The alloys such as Fe-30Al, Fe-30Al-3Ti, Fe-30Al-0.5B, Fe-30Al-5Cr and Fe-30Al-3Ti-0.5B revealed better rolling behaviour from the point that intergranular and cleavage fractures were not fundamentally occurred. But the addition of 5Ti or 3Si to Fe-Al alloys had detrimental effects. The Ti-added alloy system such as Fe-30Al-5Ti, Fe-30Al-5Ti-5Cr, Fe-30Al-3Ti-5Cr and Fe-30Al-5Ti-0.5B were cracked through grain and showed cleavage fracture. The Si-added alloy system such as Fe-30Al-5Si, Fe-27Al-3Si and Fe-27Al-5Cr-3Si were cracked along the grain boundary and showed intergranular fracture. $DO_3{\leftrightarrow}B_2$ transition temperature of Fe-30at.%Al alloy was 520$^{\circ}C$, whereas the addition of 3Ti and 3Ti+0.5B comparably increased the temperature to 797 and 773$^{\circ}C$, respectively.

• 한국세라믹학회지
• /
• 제45권7호
• /
• pp.418-422
• /
• 2008

The preparation of FeB by SHS in $B_2O_3-Mg-Fe-Fe_3O_4$ system was investigated in this study. In the preparation of FeB, the effects of the initial pressure of inert gas in reactor, the content of Mg and $Fe_3O_4$ in mixture on the reactivity and reaction products was investigated. The minimum initial pressure of inert gas in reactor for SHS reaction in this system was 25 atm, and as the pressure increased, the concentration of unreacted Mg decreased and combustion temperature increased. At the initial inert gas pressure in reactor of 25 atm, the optimum composition for the preparation of pure FeB was $1.5B_2O_3$+3.43Mg+ 1.7Fe+$0.1Fe_3O_4$. The FeB synthesized in this condition had an irregular shape and the particle size of $5\;{\mu}m$.

• 한국자기학회지
• /
• 제5권5호
• /
• pp.427-431
• /
• 1995

The influence of Nd and B contents on the magnetic properties and structures of ${\alpha}-Fe$ based Nd-(Fe,Co)-B-Mo-Cu alloys was investigated. $Nd_{4}{(Fe_{0.9}Co_{0.1})}_{92-x}B_{x}Mo_{3}Cu_{1}$ and $Nd_{x}{(Fe_{0.9}Co_{0.1})}_{86-x}B_{10}Mo_{3}Cu_{1}$ amorphous alloys prepared by rapid solidification process were crystallized to form nanocrystalline structure. The increase of B content in $Nd_{4}{(Fe_{0.9}Co_{0.1})}_{92-x}B_{x}Mo_{3}Cu_{1}$ nanocrystalline resulted in the change of stucture of soft phase in the sequence of ${\alpha}-Fe$->${\alpha}-Fe+Fe_{3}B$->$Fe_{3}B$. The coercivitis of the alloys were increased with increasing B content and was 263 kA/m at x=18. On the contrary, the remanence has shown an opposite trends. The increase of Nd content in $Nd_{x}{(Fe_{0.9}Co_{0.1})}_{86-x}B_{10}Mo_{3}Cu_{1}$ nanocrystalline containing ${\alpha}-Fe$ as main phase had no effect on the structure and improved coercivity up to 256 kA/m. However, the remanence was decreased from 1.4 T to 1.15 T according to the increase of Nd content.

• 한국분말재료학회지
• /
• 제20권3호
• /
• pp.169-173
• /
• 2013

High-coercive (Nd,Dy)-Fe-B magnets were fabricated via dysprosium coating on Nd-Fe-B powder. The sputtering coating process of Nd-Fe-B powder yielded samples with densities greater than 98%. $(Nd,Dy)_2Fe_{14}B$ phases may have effectively penetrated into the boundaries between neighboring $Nd_2Fe_{14}B$ grains during the sputtering coating process, thereby forming a $(Nd,Dy)_2Fe_{14}B$ phase at the grain boundary. The maximum thickness of the Dy shell was approximately 70 nm. The maximum coercivity of the Dy sputter coated samples(sintered samples) increased from 1162.42 to 2020.70 kA/m. The microstructures of the $(Nd,Dy)_2Fe_{14}B$ phases were effectively controlled, resulting in improved magnetic properties. The increase in coercivity of the Nd-Fe-B sintered magnet is discussed from a microstructural point of view.