• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2004년도 추계학술대회 논문집 Vol.17
• /
• pp.341-344
• /
• 2004

The superconducting properties of $YBa_2Cu_3O_x$ with different content impurities of PbO and $BaPbO_3$ were studied. When the PbO was used as an additive in $YBa_2Cu_3O_x$, although the melting point could be reduced, the superconductivity became poor. From the XRD pattern of the sintered mixture of $YBa_2Cu_3O_x$ and PbO it was known that there is a reaction between $YBa_2Cu_3O_x$ and PbO, and the product is $BaPbO_3$. In the process of the reaction the superconducting phase of $YBa_2Cu_3O_x$ was decreased and $BaPbO_3$ would be the main phase in the sample. Therefore, $BaPbO_3$ was chosen as the impurity additive for the comparative study. The single phase of $BaPbO_3$ was synthesized by the simple way from both mixtures of $BaCO_3$ and PbO, $BaCO_3$ and $PbO_2$. Different contents of $BaPbO_3$ (10%, 20%, 30%) were added in the $YBa_2Cu_3O_x$. By the Phase analysis in the XRD patterns it was proved that there was no reaction between $YBa_2Cu_3O_x$ and $BaPbO_3$. When $BaPbO_3$ was used as impurity in $YBa_2Cu_3O_x$ the superconductivity was much better than PbO as an impurity additive in $YBa_2Cu_3O_x$.

• 한국전기전자재료학회논문지
• /
• 제15권3호
• /
• pp.269-274
• /
• 2002

(Sm/Y)-Ba-Cu-O system high Tc composite superconductors with/without $CeO_2$ additive were directionally grown by zone-melting process, haying large temperature gradient, In air atmosphere. Cylindrical green rods of $({Sm/y})_{1.8}Ba_{2.4}Cu_{3.4}O_x$ [(Sm/Y)1.8] composite oxides by cold isostatic pressing(CIP) method using rubber mold were fabricated. The microstructure and superconducting properties were investigated by XRD, SEM, TEM and SQUID magnetometer. The size of nonsuperconducting $({Sm/y})_2BaCuO_5$ inclusions of the melt-textured (Sm/Y)1.8 sample with CeO$_2$ additive were remarkably reduced and uniformly distributed within the superconducting (Sm/Y)1.8 matrix. Both samples, with/without $CeO_2$ additive, showed an onset Tc $\geq$ 90 K and sharp superconducting transition. The critical current density Jc value of the $CeO_2$ addictive were $1{\times}10^5A/\textrm{cm}^2$ in 77 K, 0 Tesla.

• 한국전기전자재료학회논문지
• /
• 제29권2호
• /
• pp.110-113
• /
• 2016

(YNdSm)-Ba-Cu-O system high Tc composite superconductors were directionally grown by zone melting process, having large temperature gradient, in air atmosphere. Cylindrical green rods of $(YNdSm)_{1.8}Ba_{2.4}Cu_{3.4}O_x$ [(YNS)1.8]composite oxides by CIP (cold isostatic pressing) method using rubber mold were fabricated. The microstructure and superconducting properties were investigated by XRD, TEM and SQUID magnetometer. The size of nonsuperconducting $(YNdSm)_2BaCuO_5$ inclusions of the melt-textured (YNS)1.8 sample with $CeO_2$ additive were remarkably reduced and uniformly distributed within the superconducting (YNS)1.8 matrix. (YNS)1.8 samples, with / without $CeO_2$ additive, showed an onset $T_c{\geq}90K$ and sharp superconducting transition. The critical current density $J_c$ value of the (YNdSm)1.8 superconductor with $CeO_2$ additive were 840 A, $1.2{\times}104A/cm^2$ in 77 K, 0 Tesla by direct current transport method.

• 대한전기학회:학술대회논문집
• /
• 대한전기학회 2003년도 추계학술대회 논문집 전기물성,응용부문
• /
• pp.107-109
• /
• 2003

This paper was to measure the structure, piezoelectric properties of $0.03Pb(Mg_{0.5}W_{0.5})O_3$ - $0.12Pb(Sb_{0.5}Nb_{0.5})O_3$ - $0.85Pb(Zr_{0.52}Ti_{0.48})O_3$ + $0.5[wt%]MnO_2$ ceramics dropped with additive CuO after manufacturing the specimens with a general method. It is shown that X-ray diffraction pattern variation of lines (211) have tendency to move minutely by addition of additive CuO. According to dropping with Cu, the dielectric constant at 20[$^{\circ}C$] reduced to CuO 3.0[wt%]. In case of sintering at 1050[$^{\circ}C$], dielectric constant was maximum value 623.59 at CuO 1.0[wt%]. Dielectric loss was maximum value 2.7[%] at Cu 2.0[wt%] in case of sintering at 1050[$^{\circ}C$].

• 대한전기학회논문지:전기물성ㆍ응용부문C
• /
• 제52권6호
• /
• pp.241-248
• /
• 2003

$Bi_{1.84}Pb_{0.34}Sr_{1.91}Ca_{2.03}Cu_{3.06}O_{10+\delta}$ high $T_{c}$ superconductors containing Ag as an additive were fabricated by a solid-state reaction method. The superconducting properties, such as the structural characteristics, the critical temperatures, the grain size and the image of mapping on the surface were investigated. Samples with Ag and Au of 50 wt% each were sintered at various temperature(820~$850^{\circ}C$). The structural characteristics, the microstructure of surface and the critical temperature with respect to the each samples were analyzed by XRD and SEM, EDS and four-prove methode respectively. The critical temperature showed the result which the Ag additive samples are higher than Au additive samples. The microstructure of the surface showed the tendency which the Ag additive samples become more minuteness than Au additive samples.

• 한국자기학회지
• /
• 제5권5호
• /
• pp.556-560
• /
• 1995

The absorption properties of Cu-Zn ferrite/rubber composite microwave absorbers with PZT(Lead Zirconate Titanate) additive were evaluated. The composite specimens have prepared by molding and curing the mixture of matrix rubber and Cu-Zn ferrite powders which are synthesized by the coprecipitation method using Fe Cl/sub 3/ .center dot. 6H/sub 2/O, CuCl/sub 2/ .center dot. 2H/sub 2/O and Zn Cl/sub 2/ as a starting raw materials. PZT is used as another filler particles to adjust the material constants of Cu-Zn ferrite/rubber composite specimens. We have found that the material constants of specimens could be controlled by various PZT mixing ratio. On the Cu-Zn ferrite/rubber composite specimens with PZT 10[wt%] additive, the reflection losses were larger than 30[dB] in the frequency range from 2.72 to 4.4[GHz]' by adjusing the thickness.

• 한국자기학회지
• /
• 제16권4호
• /
• pp.201-205
• /
• 2006

$(Ni_{0.2}Cu_{0.2}ZnO_{0.2})_{1.02}(Fe_{2}O_{3})_{0.98}$의 기본 조성에 첨가제 $Bi_2O_3$와 $ZrO_2$ 첨가량과 소결 온도를 변화시켜 시편의 전자기적 특성 및 미세 구조를 조사하였다. 그 결과 XRD pattern을 통하여 완전한 spinel 구조를 가짐을 확인 할 수 있었으며 소결 온도와 첨가제의 양의 증가에 따라 소결 밀도, 입자 크기가 증가 하였으며, 소결 온도가 증가하고 첨가제의 양이 감소할수록 시편의 투자율이 크게 관찰되었다. 또한, $Bi_2O_3$의 첨가가 입자의 크기와 투자율 변화등 전자기적 특성에 더욱 더 많은 영향을 미치는 것으로 조사되었다.

• 한국결정성장학회지
• /
• 제15권5호
• /
• pp.188-192
• /
• 2005

High $T_c(Y_{0.5}Nd_{0.25}Sm_{0.25})Ba_2Cu_3O_y[(YNS)-123]$ superconductors with/without $CeO_2$ additive were systematically investigated by the zone melt growth process in air. Cylindrical green rods of (YNS)-123 oxides were fabricated by cold isostatic pressing (CIP) method using rubber mould. A sample prepared by this method showed well-textured microstructure, and $(Y_{0.5}Nd_{0.25}Sm_{0.25})_2BaCuO_5[(YNS)211]$ nonsuperconducting inclusions were uniformly dispersed in large $(Y_{0.5}Nd_{0.25}Sm_{0.25})Ba_2Cu_3O_y$[(YNS)123] superconducting matrix. In this study, optimum melting temperature and growth rate were $1100^{\circ}C$ and 3 mm/hr, respectively. The directionally melt-textured (YNS)-123 sample with $CeO_2$ additive showed an onset critical temperature $(T_c)\;T_c{\geq}93K$ and sharp superconducting transition.

• 전기화학회지
• /
• 제18권1호
• /
• pp.7-16
• /
• 2015

전기도금공정을 이용하여 상온에서 제조된 Cu박막의 특성에 미치는 피로인산구리용액의 화학성분($Cu^{2+}$ 농도, $K_4P_2O_7$ 농도, 첨가제 농도)의 영향에 대한 연구를 수행하였다. 전류효율은 도금용액의 $Cu^{2+}$ 농도가 0.3 M까지 높아짐에 따라 거의 100%까지 증가하는 경향을 나타내었다. $K_4P_2O_7$ 농도는 1.5~1.8 M 농도에서 전류효율의 감소를 나타내었으나, 0.9~1.3 M과 2.1~2.4 M에서는 거의 100%의 전류효율을 나타내었다. 첨가제의 농도 변화는 전류효율에는 거의 영향을 미치지 않았다. 전기도금 된 Cu 박막의 잔류응력은 도금용액의 $Cu^{2+}$ 농도가 0.15 M 이하에서는 약 20 MPa로 측정되었으나, $Cu^{2+}$ 농도가 증가함에 따라 증가하다가 0.25 M 에서 약 120 MPa의 최대치를 나타내었다. 한편 도금용액의 $K_4P_2O_7$ 농도가 0.9 M로부터 2.4M로 증가할수록 잔류 응력은 80MPa로부터 0 MPa까지 감소하는 경향을 나타내었으며, 첨가제의 농도는 잔류응력에 영향을 미치지 않은 것으로 관찰되었다. 표면형상의 경우 $Cu^{2+}$ 농도와 $K_4P_2O_7$ 농도는 상당한 영향을 미쳤으나, 첨가제는 약간의 영향만을 나타내었다. XRD 분석 결과 $Cu^{2+}$ 농도와 $K_4P_2O_7$ 농도는 Cu 박막의 미세조직에 상당한 영향을 미쳤으나, 첨가제는 거의 영향을 미치지 않는 것으로 나타났다. $Cu^{2+}$ 농도와 $K_4P_2O_7$ 농도가 증가할수록 (111) 피크의 강한 우선방향성이 나타내었다.

• 한국전기전자재료학회논문지
• /
• 제15권4호
• /
• pp.308-313
• /
• 2002

Samples with the norminal composition, $Bi_{2-x}Au_xSr_2CaCu_2O_{8+\delta}$ (x = 0, 0.05. 0.1, 0.15) were prepared by the solid-state reaction method. The superconducting properties, x-ray powder diffraction patterns, critical temperature and microstructure of surface were measured the samples. x-ray patterns show the single phase(2212) nature of the samples. But, the peaks of 2201 at $2\theta=30^{\circ}$ and Au peak at $2\theta=38.31^{\circ}$ are observed in the Au additive samples. The grain sire are enlarged with the increase of x. As the result of enlargement the grain size, the onset and offset critical temperature($T_c^{on}$,$T_c^{zero}$) increased with increase of x.