• Journal of the Korean Ceramic Society
• /
• v.34 no.1
• /
• pp.63-69
• /
• 1997

The effects of Cr2O3 content on the properties of direct-bonded MgO-Cr2O3 bricks were investigated in the range of 10 to 30 wt% of Cr2O3. Modulus of rupture of bricks was excellent in about 20 wt% of Cr2O3 content. The corrosion resistance of bricks was improved by increasing Cr2O3 content and was directly pro-portional to the amount of secondary spinels. On the other hand, the spalling resistance of bricks depended on the amount of flux rather than Cr2O3 content.

• Journal of the Korean institute of surface engineering
• /
• v.43 no.5
• /
• pp.238-242
• /
• 2010

In the present work, the influence of oxide on the Cr-Si-N coatings was investigated for the Cr-Si-O-N coatings on AISI 304 and Si wafer deposited by hybrid system, which combines the DC magnetron sputtering technique and arc ion plating (AIP) using Cr and Si target in an $Ar/N_2/O_2$ gaseous mixture. As the O content in the Cr-Si-N coatings increased, the diffraction patterns of the Cr-Si-O-N coatings showed CrN and $Cr_2O_3$ phases. However, as the O content increased to 28.8 at.%, diffraction peak of $Cr_2O_3$ was disappeared in the Cr-Si-O-N coating. The $d_{200}$ value was decreased with increasing of O content. The average grain size increased from about 40 nm to 65 nm as the O content increased. The maximum micro-hardness of the Cr-Si-O-N coating was obtained 4507 Hk at the O content of 24.8 at.%. The average friction coefficient of the Cr-Si-O-N coatings was gradually decreased by increasing the O content and the average friction coefficient decreased from 0.37 to 0.25 by increasing the O content. These results indicated that amorphous phase was increased in the Cr-Si-O-N coatings by increasing of O content.

• Journal of the Korean Ceramic Society
• /
• v.24 no.2
• /
• pp.179-185
• /
• 1987

The microstructure and the electrical conductivity of MgO-doped Cr2O3 were investigated as a function of oxygen partial presure, temperature, and MgO content. The grain size was estimated about 1.0$\mu\textrm{m}$. The solubility limit is increased with oxygen partial pressure. Above the solubility limit of MgO in Cr2O3, the spinel phase(MgCr2O4) is formed by the reaction of MgO and Cr2O3. The electrical conductivity of MgO-doped Cr2O3 within the solubility limit is increased with MgO content. Above the solubility limit, however, it is decreased with increasing MgO content because of the formation of the spinel phase.

• The Transactions of the Korean Institute of Electrical Engineers C
• /
• v.48 no.8
• /
• pp.570-576
• /
• 1999

$LaCrO_3$-dispersed Cr alloys for metallic interconnector of solid oxide fuel cell have been studied as function of $LaCrO_3$ content in the range of 5 to 25 vol.% in order to examine the electric conductivity, the oxidation property and the thermal expansion behavior of these alloys. The $LaCrO_3$-dispersed Cr alloys showed high electrical conductivities of $3~5\times10^4$ S/cm at room temperature, and as the $LaCrO_3$content increased the conductivity decreased slightly. During the cyclic oxidation test at $1100^{\circ}C$, the weight change of the Cr alloys decreased with increasing number of oxidation cycle except first cycle, which is attributed to the vaporization of the oxide scale. More addition of the $LaCrO_3$ content reduced also the weight change of the Cr alloys. These mean that the oxide scale formed at the surface of the Cr alloy becomes stable with increasing number of oxidation cycle and$LaCrO_3$ content. The measured thermal expansion of the Cr alloy was well fitted to that of 8 mol% $Y_2O_3$-stabilized $ZrO_2$ electrolyte. These results demonstrate that $LaCrO_3$-dispersed Cr alloy is a useful material for metallic interconnector of solid oxide fuel cell.

• Journal of Korea Foundry Society
• /
• v.5 no.4
• /
• pp.271-282
• /
• 1985

In order to investigate the mold reaction characteristics of Mn steel and Cr steel castings individually, the mold reaction products were examined by scanning electron microscopy, electron prove microanalyzer and X-ray diffractometer. From this experiment, the results were summarized as follows: 1) The mold reaction depth increased with increase of Mn content, while it decreased with increase of Cr content. 2) Mold reaction depth decreased with Mn content at $1200^{\circ}C$. 3) Mn, among the reaction products, forms a low fusion silicate, Mn $O.SiO_2$ while Cr forms a stable oxide, $CrO_3$ which hindering the reaction between FeO and $SiO_2$ thus the formation of $FeO.SiO_2$ was depressed.

• Transactions of the Korean hydrogen and new energy society
• /
• v.16 no.1
• /
• pp.58-65
• /
• 2005

The $LaCrO_3$-dispersed Cr alloys for metallic interconnect of solid oxide fuel cell were prepared as a function of $LaCrO_3$ content in the range of 5 to 25 vol.% and were sintered at 1500$^{\circ}C$ under an Ar atmosphere with 5 vol.% $H_2$. The sintering and oxidation behaviors of these alloys were examined. The alloys indicated a good sinterability above 95% relative density at a given sintering condition, and their sintering densities is independent on $LaCrO_3$ content. The $LaCrO_3$ particles of the sintered alloys were concentrated on interfaces of Cr particles, and the size of the Cr particles increased with decreasing $LaCrO_3$ content, which is caused by inhibited grain growth of Cr particle by $LaCrO_3$ particle. The oxidation test showed all $LaCrO_3$-dispersed Cr alloys have good oxidation resistance as compared with pure Cr, which is attributed to presence of $LaCrO_3$ at the interface at which the oxidation reaction occurs rapidly. The Cr alloys with about 15 vol.% $LaCrO_3$ are very resistant to oxidation.

• Journal of the Korean Ceramic Society
• /
• v.30 no.5
• /
• pp.339-346
• /
• 1993

Inproving laser efficiency, optimum content of Nd3+ which is active ion and effect of Cr3+ as a sensitizer are investigated in 60SiO2.30Li2O.10CaO host glass. The glasses are fabricated with the addition of Nd3+, Cr3+ and then optical properties such as absorption spectrum, fluorescence spectrum and fluorescence lifetime were studied. Finally, lasing efficiency was measured. From this study, optimum content of Nd2O3 appeared to be 3.5wt% and it was observed that the energy absorbed by optical exicitation of the Cr3+ is transfered to the Nd3+. Addition of Cr2O3 tend to improve characteristic of laser oscillation for the laser glass.

• Korean Journal of Materials Research
• /
• v.13 no.7
• /
• pp.420-423
• /
• 2003

Coatings of TiCrN ion-plated on a steel substrate was oxidized at $800^{\circ}C$ in air, and their oxidation mechanism was presented. During oxidation, substrate elements and Ti and Cr in the coating always diffused outwardly to form the oxide scale. Simultaneously, oxygen from the atmosphere diffused inward1y to react with Ti and Cr to form $TiO_2$and $Cr_2$$O_3$, respectively. Also, the counter-diffusion of cations and oxygen resulted in some oxygen dissolution in the unoxidized TiCrN coating, and Fe dissolution in the oxide scale. When the Ti content in the coating was high, the $TiO_2$-forming tendency was strong, while when the Cr content was high, the $Cr_2$$O_3$-forming tendency was strong.

• Nuclear Engineering and Technology
• /
• v.35 no.1
• /
• pp.14-24
• /
• 2003

This work investigates the effects of Cr$_2$O$_3$ and oxygen potential on grain growth and densification of UO$_2$ pellets. Powder mixtures of UO$_2$ and 0.03-0.4wt% Cr$_2$O$_3$ were pressed and sintered in 3 different gas atmospheres: the $H_2O$-to-H$_2$ ratios were 5$\times$10$^{-4}$ , 1$\times$10$^{-2}$ and 3$\times$10$^{-2}$ In the first gas atmosphere the Cr$_2$O$_3$ contents below 0.2 wt% have an insignificant effect on grain size, but the Cr$_2$O$_3$ contents more than 0.3 wt% promote grain growth in the inner zone of a pellet but not in the outer zone. In both the second and third atmospheres, the grain size increases with the Cr$_2$O$_3$ content. With the same level of Cr$_2$O$_3$ content the grain size is larger in the second atmosphere than in the third. Sintering behavior and developed microstructure are discussed in terms of the reduction of C$r^2$O$^3$ to Cr, the dissolution of C$r^2$O$^3$ in UO$_2$, and liquid phase sintering.

• Journal of the Korean Ceramic Society
• /
• v.22 no.6
• /
• pp.42-52
• /
• 1985

Several $Al_2O_3$-based polycrystalline which had different dopant ratio in the range of 0.5mol% were prepared by doping pure $Cr_2O_3$ $HfO_2$. Single crystalline which had same composition with above polycrystalline were made by means of floating zone method. This study examined the role of each dopant for enhancing the mechanical properties of $Al_2O_3$-based Ceramics. Optical micrographs $({ imes}200)$ of $Al_2O_3-Cr_2O_3$ single crystal showing not only radial crack (rc) on the specimen surface but median crack(mc) and lateral crack(lc) under surface at the edge of indentation mark. Fracture toughness of Al2O3-based Ceramics was increased with $ZrO_2$ content. Alloying effect of $Cr_2O_3$ contributed to the hardness of $Al_2O_3$ based ceramics.