• 한국자기학회지
• /
• 제5권5호
• /
• pp.683-686
• /
• 1995

Using by the x-ray diffractometry(XRD), the thermomagnetic analysis(TMA), a scanning electron microscopy (SEM-EDX), we knew that the $(Sm_{0.5}RE_{0.5})Fe_{11}Ti$ (RE=Ce,Pr,Nd,Sm,Gd,Tb) compounds were formed to tetragonal $ThMn_{12}$-type structure having a uniaxial magnetocrystalline anisotropy with easy magnetization c-axis. The intrinsic magnetic properties of those were determined by fitting the two magnetization curves of experimental and calculation magnetization. The anisotropy constant $K_{1}$ of this compounds was in the range of $1.75\;-\;9.2\;MJ/m^{3}$ and approximately one order higher than $K_{2}$. $SmFe_{11}Ti$ had the highest anisotropy of $K_{1}\;=\;9.2\;MJ/m^{3}$, $K_{2}\;=\;0.4\;MJ/m^{3}$ and ${\mu}_{o}H_{A}=\;19.8\;T$ among the compounds, substitution of any other rare earth elements for Sm decreased magnetocrystalline anisotropy.

• Journal of Ceramic Processing Research
• /
• 제19권5호
• /
• pp.372-377
• /
• 2018

MgO or gadolinium-doped ceria (GDC, $Ce_{0.9}Gd_{0.1}O_{2-{\delta}}$) was added as a promoter to improve the oxygen transfer kinetics of $MgMnO_3$ oxygen carrier material for chemical looping combustion. Neither MgO nor GDC reacted with $MgMnO_3$, even at the high temperature of $1100^{\circ}C$. The average oxygen transfer capacities of $MgMnO_3$, 5 wt% $MgO-MgMnO_3$, and 5 wt% $GDC-MgMnO_3$ were 8.74, 8.35, and 8.13 wt%, respectively. Although the addition of MgO or GDC decreased the oxygen transfer capacity, no further degradation was observed during their use in 5 redox cycles. The addition of GDC significantly improved the conversion rate for the reduction reaction of $MgMnO_3$ compared to the use of MgO due to an increase in the surface adsorption process of $CH_4$ via oxygen vacancies formed on the surface of GDC. On the other hand, the conversion rates for the oxidation reaction followed the order 5 wt% $GDC-MgMnO_3$ > 5 wt% $MgO-MgMnO_3$ >> $MgMnO_3$ due to morphological change. MgO or GDC particles suppressed the grain growth of the reduced $MgMnO_3$ (i.e., (Mg,Mn)O) and increased the specific surface area, thereby increasing the number of active reaction sites.

• 한국결정성장학회:학술대회논문집
• /
• 한국결정성장학회 1996년도 제11차 KACG 학술발표회 Crystalline Particle Symposium (CPS)
• /
• pp.55-85
• /
• 1996

지르코니아 분말은 ZrO2 결정상이 온도변화에 따라 부피변화를 수반하는 상전이변태를 나타낸다. 단사정 ZrO2가 110$0^{\circ}C$에서는 정방정으로, 2$700^{\circ}C$ 내외에서는 입방정으로 결정구조가 가역적으로 변한다. 이 ZrO2에 금속산화물을 고용시키면 형석 (CaF2:Florite)형의 입방정 결정구조가 실온에서도 안정하게 존재하게 된다. 안정화제 산화물은 caO, MgO등 2가 산화물외에 3가 또는 4가의 금속산화물로서 Sc2O3, Y2O3, Sm2O3, Nd2O3, Gd2O3, Y2O3, CeO2 등이며 이들은 금속이온의 원자가가 변하기 쉬운 희토류 산화물이다. 안정화 지르코니아는 형석형 결정구조이며 결정화학적으로 보면 금속양이온이 산소이온에 대해서 정육면체형의 8배위를 하고 있다. 이때 이온반경비(양이온/음이온)에 따라 Zr+4자리와 O-2자리의 격자위치와 모양이 형성되므로 비틀어진 정육면체구조이건 이상적인 정육면체 형석구조를 이룬다. 이는 지르코니아의 결정상의 2상-3상인 부분안정화 지르코니아다결정체(PSZ : partially stabilized zirconia)이거나 단일상-2상인 정방정 지르코니아다결정체(TZP : tetragonal zirconia polycrystal)의 결정구조를 가지는데 기인한다. PSZ는 주로 MgO, CaO를 안정화제로 고용시켜 입방정 영역에서 소결하고 이를 다시 입방정과 정방정의 상 영역에서 열처리하여 입방정 입자내부에 정방정을 석출 형성시킨 것이며 TZP는 Y2O3 및 CeO2를 고용시켜 PSZ와 다르게 일반적인 상압소결한 정방정 결정상의 미립자이다. 산화지르코늄 분말은 지르콘사에서 열분해시킨 지르코늄소결.융해괴(caustic fusion clinker)를 산처리하여얻어진 지르코늄산용액(zirconyl acid solution : cloride, sulfide, nitride 등)으로부터 제조된다. 고순도 산화지르코늄은 용액 결정석출법에 의해 ZrOCl2.8H2O, 5ZrO2.3SO3.15H2O, ZrO(NO3)2.xH2O 등의 지르코늄 수화물만을 재결정화시킨 것으로부터 얻을 수 있으며 이 지르코늄염 수용액으로부터 입자미세구조를 효과적으로 제어하여 산화지르코늄 및 안정화 지르코니아 분말제조가 가능하다. 안정화 지르코니아 분말은 ZrO2와 안정화산화물의 고용을위하여 가열처리를 필요로 하며 일정온도에서 최적상태로 숙성하므로서 2가지 상(phase) 이상의 고용체를 가지게 된다. 안정화 지르코니아 분말은 고용처리온도를 낮추고 효과적으로 생성시키기 위해서는 지르코늄 및 안정화제염을 혼합하고 습식 직접합성하여 저온에서 고용체의 합해진상 영역을 생성시키는 것이다. 이는 지르코니아 원료분말의 미세구조를 제어하므로서 가능하며 이때 화학성분조성과 크기형태가 균일하게 분포된 입자분말을 얻을 수 있다.

• 암석학회지
• /
• 제6권1호
• /
• pp.19-33
• /
• 1997

본역의 지질은 백악기 경상누층군의 퇴적암, 이를 관입 또는 분출한 중성화산암류, 산성화산암류 및 제 4기 충적층으로 구성된다. 중성화산암류는 화성쇄설화산각력암, 석질화산력응회암, 안산암용암으로 구성되며, 산성화산암류는 데사이트질용결응회암 및 유문암용암, 유문암질응회암으로 구성된다. 본 연구에서는 중성 및 산성 화산암류에 대해 암석기재학적 연구와 신선한 시료 10개에 대한 암석화학적 특성을 고찰하고, K-Ar법에 의한 절대연대 측정을 실시하였다. 현미경 관찰에서 안산암용암은 사장석이 주 반정광물로 나타나며, 기질은 미정질 내지 은미정질로서 반정광물과 동일한 필로택시틱 조직을 보인다. 안산암질각력암은 퇴적암 및 안산암의 자력 암편을 포함한다. 테사이트질용결응회암은 현저한 파라택시틱 조직을 보이며, 유문암용암은 유상구조를 잘 보여 주고, 안산암의 암편을 함유하고 용결구조가 현저한 화산력용결응회암이 나타나는데, 유문암용암에서 기질의 함량은 80.9~ 89.3%에 이른다. 주 반정광물은 사장석이며 부분적으로 녹염석, 녹니석, 방해석, 제오라이트, 푸로필라이트 등으로 2차 변질되어 나타난다. 본역의 화산암류는 Norm값에 의한 Q-A-P 도표에서 현무암질안산암, 안산암, 데사이트, 유문암의 일련의 분화과정을 나타내고 대부눈 칼크알칼리 계열에 속한다. 화산암류의 화학조성은 $SiO_2$ 함량이 57.61~75.40 %이며, MgO, CaO, $Fe_2O_3$, $Al_2O_3$, $Ti_2$, MnO, $P_2O_5$ 등은 $SiO_2$함량이 증가함에 따라 연속적으로 증가하는 경향을 보인다. 주성분원소 및 미량 원소의 변화도에서 안산암질에서 유문암으로 분화되는, 즉 마그마의 정출 분화 특징을 뚜렷이 보여준다. REE 양상 및 spider 도표에서 일정한 분화 경향을 보이며 나란하다. spider 도표에서 본역의 화산암류는 Th, La, Nd, Gd 등이 부화되어 있으며, Ba, Nb, Sr, Hf, Zr 등이 결핍되어 있는 특징을 나타낸다. 안산암에서 유문암으로 분화가 진행될수록 Cs, Sr, Eu이 점차 결핍되는 경향이, Th가 증가하는 경향이 있고, Ba, Nb, Sr, Eu의 부(-)의 이상값이 점차 커지는 경향을 보인다. 희유 원소의 변화 경향에서 안산암과 중성 암맥, 데사이트와 유문암의 경향이 서로 일치함을 볼 수 있다. 주성분 원소 및 미량 원소 함량 변화는 본역의 화산암이 안산암으로부터 일연의 분별결정작용 산물임을 암시하며, 또한 $Al_2O_3$와 CaO 함량의 관계도, Th/Yb 비에 대한 Ta/Yb 비의 관계도, $Ce_N/Yb_N$ 대 $Ce_N$의 관계도에 따른 판별에서도 분별결정작용의 경향을 따르고 있다. 본역의 화산암은 $K_2O$, $Na_2O$, CaO 삼각도에서 도호의 영역에, Ba/La비, La/Th비에 의한 판별도에서 조산대의 high-K suite에 속한다. Rb 대 (Y+Nb)의 판별도 및 Hf-Th-Ta 지구조 판별도에서 지판이 침강 섭입하는 지판 경계부(destructive plate margin) 중 화산호의 조구적 영역에 도시된다. 본역의 화산암을 생성시킨 마그마는 $Al_2O_3$와 CaO 함량의 관계도, mode에서 나타나는 사장석 반정, 분화가 진행될수록 부의 Eu 이상이 증가하는 것 등에서 사장석의 분별이 우세한 분별결정작용을 거쳤음을 알 수 있다. 안산암질암을 관입한 중상 암맥에서 측정한 암석 년령은 $97.0{\pm}6.8~94.5{\pm}6.6$, 데사이트질암은 $68.9{\pm}4.8,\61.5{\pm}4.9~60.7{\pm}4.2$Ma으로 측정되었고, 이것은 백악기 유천층군과 대비되며, 백악기 유천층군 암석의 지화학적 자료와 본역 화산암의 지화하적 자료는 판별도 등에서 같은 영역에 도시된다.

• 한국세라믹학회지
• /
• 제55권5호
• /
• pp.492-497
• /
• 2018

This paper reports the efficacy of tape casting using an Ag-10 wt% CuO filler for the successful joining of a sintered $Ce_{0.9}Gd_{0.1}O_{2-{\delta}}-La_{0.7}Sr_{0.3}MnO_{3{\pm}{\delta}}$ (GDC-LSM) ceramic with a SUS 460 FC metal alloy by reactive air brazing. The as-prepared green tape was highly flexible without drying cracks, and the handling was easy when used as a filler material for reactive air brazing. Heat treatment for the GDC-LSM/SUS 460 FC joint was performed at $1050^{\circ}C$ for 30 min in air. Microstructural observations indicated a reliable and compact joining. The room temperature mechanical shear strength of the as-brazed joints was $60{\pm}8MPa$ with a cohesive failure. The flexural strength of joints was measured from room temperature up to $850^{\circ}C$, where the strength retention revealed to be almost 100% at $500^{\circ}C$. However, the joints showed a degradation in strengths at 800 and $850^{\circ}C$, exhibiting strength retentions of 57% and 37%, respectively.

• 한국진공학회:학술대회논문집
• /
• 한국진공학회 2016년도 제50회 동계 정기학술대회 초록집
• /
• pp.402.1-402.1
• /
• 2016

The performance of solid oxide fuel cells (SOFCs) is directly related to the electrocatalytic activity of composite electrodes in which triple phase boundaries (TPBs) of metallic catalyst, oxygen ion conducting support, and gas should be three-dimensionally maximized. The distribution morphology of catalytic nanoparticle dispersed on external surfaces is of key importance for maximized TPBs. Herein in situ grown nickel nanoparticle onto the surface of fluorite oxide is demonstrated employing gadolium-nickel co-doped ceria ($Gd0.2-xNixCe0.8O2-{\delta}$, GNDC) by reductive annealing. GNDC powders were synthesized via a Pechini-type sol-gel process while maximum doping ratio of Ni into the cerium oxide was defined by X-ray diffraction. Subsequently, NiO-GNDC composite were screen printed on the both sides of yttrium-stabilized zirconia (YSZ) pellet to fabricate the symmetrical half cells. Electrochemical impedance spectroscopy (EIS) showed that the polarization resistance was decreased when it was compared to conventional Ni-GDC anode and this effect became greater at lower temperature. Ex situ microstructural analysis using scanning electron microscopy after the reductive annealing exhibited the exsolution of Ni nanoparticles on the fluorite phases. The influence of Ni contents in GNDC on polarization characteristics of anodes were examined by EIS under H2/H2O atmosphere. Finally, the addition of optimized GNDC into the anode functional layer (AFL) dramatically enhanced cell performance of anode-supported coin cells.

• 한국결정성장학회:학술대회논문집
• /
• 한국결정성장학회 2000년도 Proceedings of 2000 International Nano Crystals/Ceramics Forum and International Symposium on Intermaterials
• /
• pp.65-86
• /
• 2000

Rare earth-doped ceria powders with a composition of Ce0.8R0.2O1.9(R=Yb, Y, Gd, Sm, Nd and La) were prepared by heating the oxalate coprecipitate. The green compacts began to shrink at 600$^{\circ}$-700$^{\circ}C$. The relative density after the sintering at 1200$^{\circ}$ and 1400$^{\circ}C$ became higher for the higher green density. The samples were densified above 98% relative density by the sintering ant 1600$^{\circ}C$ for 4 h and the grain sizes (4.7-7.6$\mu\textrm{m}$) showed a tendency to become larger with increasing ionic radius of doped-rare earth element. In the intial stag of sintering at 700$^{\circ}$-800$^{\circ}C$, the dominant mass transport process changed from lattice diffusion to grain boundary diffusion to grain boundary diffusion with heating time. The porosity during the intermediated and final stage of the sintering at 1200$^{\circ}$ and 1400$^{\circ}C$ decreased by the mass transport through lattice diffusion with grain growth.

• Nuclear Medicine and Molecular Imaging
• /
• 제42권6호
• /
• pp.469-477
• /
• 2008

목적: 소동물용 PET은 우수한 공간분해 능과, 민감도가 요구된다. 본 연구에서는 256개의 개별적 채널을 4개로 줄여 검출위치를 추정할 수 있는 회로를 설계하고 제작하였으며, 256($16{\times}16$)개의 양극 출력 채널을 가지는 고집적도의 광전자증배관 및 $L_{0.9}GSO$ 섬광결정과 결합하여 그 성능을 검증하였다. 대상 및 방법: 설계한 회로를 제작하기에 맞서 전자회로 시뮬레이션을 통해 성능을 예상하였다. 회로의 검증과 성능분석을 위하여 위치결정회로, H9500(Hamamatsu Photorucs K.K., 일본) 광전자증배관, $1.5{\times}1.5{\times}7.0\;mm^3$ $L_{0.9}GSO$ 섬광결정으로 두 개의 검출단을 제작하고 $3.7{\times}10^5$ Bq의 $^{22}Na$ 방사선원을 사용하여 동시이벤트를 검출하였다. 첫 번째 검출단은 $L_{0.9}GSO\;29{\times}29$ 섬광결정블록을 단층으로 구성하였고, 두 번째 검출단은 $L_{0.9}GSO\;29{\times}29$와 $28{\times}28$ 섬광결정블록을 x와 y방향으로 각각 섬광결정 단면 길이의 반만큼 오프셋을 두어 접합하였다. 또한 측정된 데이터를 실제 섬광결정 영역으로 보정하기 위하여 섬광결정지도를 구했다. 결과: 평면영상을 통해 각 섬광결정들이 잘 구분되는 것을 확인할 수 있었고, 회로 개선 후 주변부의 섬광결정들이 마지막 줄까지 명백히 구분되었다. 각 섬광결정들의 에너지 분해능은 11.6%(표준편차 1.6)이었다. 결론: 본 연구에서 제안한 위치결정회로는 실험을 통해 소동물용 PET개발에 있어 만족할만한 성능을 보여주었다. 향후 더욱 정밀한 시스템을 제작하기 위해서는 다중양극 광전자증배관의 이득 불균일을 보정하기 위한 연구가 진행되어야 할 것이다.