• Proceedings of the Korea Concrete Institute Conference
• /
• 2009.05a
• /
• pp.345-346
• /
• 2009

This research focused on large variation of the result of Ca(OH)$_2$ quantity by TG/DTA test or micro-pore size by MIP test. Assume that sample postion has influenced on experimental result, therefore, relationship between sampling position and the experimental result was studied As a result of the research, it is obvious that samples from inside(P-3) shows more Ca(OH)$_2$ and less porosity than samples from outside(P-1).

• Journal of the Korean Recycled Construction Resources Institute
• /
• v.11 no.2
• /
• pp.145-152
• /
• 2023

In this study, microscopic observation was made on the surface of cement paste immersed in an aquatic environment for 100 days at electrochemical treatment to mitigate the leaching of alkali ions. To quantitatively rank the hydration products, unhydrated grains and porosity in the interfacial region, the backscattered electron(BSE) images were obtained by scanninng electron microscopy. As a result, it was found that the porosity on the surface was significantly reduced by the electrochemical treatment, while unhydrated grains were more or less increased presumably limited hydration reaction under electric charge. At electrochemical treatment, Ca²⁺ ions present in C-S-H gel could be precipitated with OH^- to form Ca(OH)₂ then to lower C-S-H gel and simultaneously to enhance Ca(OH)₂. Substantially, the risk of alkali leaching could be lowered by the limited ionized matrix under electrochemical treatment.

• Journal of the Korea institute for structural maintenance and inspection
• /
• v.24 no.3
• /
• pp.96-103
• /
• 2020

As a basic study for the application of natural zeolite as a concrete admixture, the compressive strength, activity factor, Ca(OH)₂ quantitative analysis and XRD experiments were investigated. It is thought that SiO₂, which is abundant in natural zeolite, affects the strength development by reacting with the hydration product of cement in all specimens in which natural zeolite was added according to powder level and substitution rate. As the substitution rate increases, the compressive strength decreases, which is considered to be due to the decrease in the amount of C₃S and C₂S minerals in the clinker, which affects the strength expression compared to the cement content of the reference mortar. The XRD crystal structure did not show a significant difference from the reference mortar, and it was confirmed that the Z2-10 (Blaine: 15,600㎠ / g) specimen with 10% substitution of natural zeolite was the best among the experimental levels. Substitution amount for use as concrete admixture is 10% substitution is most ideally seen.

• Analytical Science and Technology
• /
• v.18 no.4
• /
• pp.298-308
• /
• 2005

The methods for determining C-14 and tritium contents in the spent nuclear fuel sample were developed. The carbon-14($^{14}CO_2$) released during the dissolution of the spent fuel sample and $CaCO_3$ ($CO_2$ carrier) with 8 M $HNO_3$ at $90^{\circ}C$ was collected in trap containing 1.5 M NaOH. The volatile radioactive iodine evolved when the spent fuel was dissolved, was trapped on to Ag-silicagel (Ag-impregnated silicagel) adsorbent in column which is connected to two NaOH traps. The solutions which contain tritium as HTO after fuel dissolution were decontaminated by deionization with a mixture of cation and anion exchange resins and inorganic ionexchangers. The amount of C-14 in the trap solutions and the HTO concentration in the resulting deionization water were then determined by liquid scintillation counting.

• Journal of the Mineralogical Society of Korea
• /
• v.25 no.3
• /
• pp.143-153
• /
• 2012

Mica-type minerals (illites) in the shales of the Jigunsan formation at Seokgaejae in Samchuk-City, Gangwon-do are studied using electron probe micro analysis (EPMA). The average chemical formula of the mica-type mineral obtained from the quantitative analysis is $(K_{1.17}Na_{0.04}Ca_{0.01})(Al_{2.80}Mg_{1.17}Fe_{0.78})(Si_{6.34}Al_{1.66})O_{20}(OH)_4$, which shows a chemical formula within the range of illite. These illites so called can be considered as mixed-phases among muscovite, pyrophyllite and chlorite due to the low contents of interlayer cations and high Mg, Fe. The formula of illite is separated into those three minerals and the method for the separation is newly formulated and proposed in this study. From the formula of illite, the content of muscovite is estimated from K (Na and Ca included), the content of chlorite by Mg+Fe, and the rest remains as pyrophyllite. The chemical formula of muscovite can be calculated by subtracting the compositions of pyrophyllite and chlorite from the analyzed composition of illite using an ideal formula for pyrophyllite and analyzed average formula for chlorite. The calculated formula of muscovite is supposed to be stoichiometric in principle. The result of the separation of analyzed illite is 61% muscovite, 27.3% chlorite and 11.7% pyrophyllite and the calculated formula of muscovite after separation is $(K,Na,Ca)_{2.00}Al_{3.69}(Si_{6.75}Al_{1.25})O_{20}(OH)_4$. The calculated formula of muscovite slightly low in Al content can be considered to be reasonable in general when the low content of Al in the rock and the uncertainties of chlorite compositions used in the calculation are counted. This supports that the method of separation proposed in this study is also applicable.

• Journal of Sericultural and Entomological Science
• /
• v.45 no.1
• /
• pp.34-45
• /
• 2003

Silk was treated with calcium hydroxide for degumming at different treatment times, temperatures and Ca(OH)$_2$ concentration to optimize degumming conditions in this thesis. After degumming, soluble and insoluble sericin were seperated and then the soluble sericin was characterized by measuring the average degree of polymerization (D.P.), lysinoalanine (LAL) content, DSC, and by amino acid analysis. And degummed silk fibroin was characterized by measuring tenacity and SEM. Degumming loss was increased by increasing the treatment time and temperature until about 30 minutes. After then, a slight difference was found along with treatment times at the Ca(OH)$_2$ concentrations of 0.07% and 0.1% solutions. After degumming, insoluble sericin ratio on degumming solution was increased by increasing treatment temperature at Ca(OH)$_2$ 0.04% solution. At the concentration Ca(OH)$_2$ of 0.07%, a soluble ratio was almost 100% regardless of treatment time and temperature. At the beginning of treatment, insoluble ratio was high at Ca(OH)$_2$ 0.1% solution but it was decreased by increasing treatment time. At the Ca(OH)$_2$ concentration of 0.04%, D.P. of soluble sericin was maintained as a constant value of 10 at 100$^{\circ}C$ although treatment time was increased. However, at 80$^{\circ}C$ and 90$^{\circ}C$, it was hard to prepare a soluble sericin having a constant D.P. by increasing treatment time. At the Ca(OH)$_2$ concentration of 0.07%, D.P. was almost 10 irrespective of treatment temperature and time. Soluble sericins with high D.P. of 20∼30 were obtained at 0.1% and 100$^{\circ}C$. LAL was not detected in soluble sericin. As the results of amino acid analysis, it showed that Ca(OH)$_2$ degumming reduced the contents of hydroxy amino acids like Ser., Thr. and Tyr. In DSC analysis of soluble sericin, endothermic peak by thermal deformation and pyrolysis showed at 189$^{\circ}C$ and at 299$^{\circ}C$, respectively. The tenacities of degummed silk were 15∼30% lower than that of raw silk. And it was decreased with increasing treatment time. From the morphological study, the thickness of degummed silk fibroin became thinner by increasing degumming loss. The roughness of a silk fibroin surface was appeared as treatment concentration was increased.

• Journal of the Korea Concrete Institute
• /
• v.26 no.6
• /
• pp.723-730
• /
• 2014

The usage of Ground Granulated Blast Furnance Slag (GGBFS) has been increased recently. Studies on the cement hydration model incorporating GGBFS as well as the properties of cement paste done with GGBFS such as compressive strength, hydration products and hydration heat have been the subjects of many researches. However, studies on the reaction degree of GGBFS that affect the properties of cement paste incorporating GGBFS are lacking globally and specially in Korea. Thus, in this study, the reaction degree of GGBFS using the method if selective dissolution, compressive strength, the amount of chemical bound water and $Ca(OH)_2$ were measured and analysed in accordance with water-binder ratio, replacement ratio of GGBFS, and curing temperature. The results show that the reaction degree of GGBFS, the amount of chemical bound water and $Ca(OH)_2$ in cement paste with GGBFS were higher in conditions where the replacement ratio of GGBFS was low and both water-binder ratio and curing temperature were high. Finally, the reaction degree of GGBFS was achieved at a value between 0.3~0.4.

• Journal of the Korea Concrete Institute
• /
• v.25 no.2
• /
• pp.209-215
• /
• 2013

This study is aimed to identify the method to use the CaO-$Al_2O_3$ system of rapidly cooled steel making slag (RCSS) as the environment-friendly inorganic accelerating agent by analyzing its physical and chemical properties. The fraction of rapidly cooled steel making slag is distinguished from its fibrous, and the contents of CaO and $Fe_2O_3$ are inversely proportional across different fractions. In addition, as the content of CaO decreased and the content of $Fe_2O_3$ increased, the loss ignition tended to become negative (-) and the density increased. The pore distribution by mercury intrusion porosimetry is very low as compared to the slowly cooled steel-making slag, which indicates that the internal defect and the microspore rate are remarkably lowered by the rapid cooling. To analyze the major minerals the rapidly cooled steel-making slag, XRD, f-CaO quantification and SEM-EDAX analysis have been performed. The results shows that f-CaO does not exist, and the components are mainly consisted of $C_{12}A_7$ and reactive ${\beta}-C_2S$.

• Applied Chemistry for Engineering
• /
• v.2 no.3
• /
• pp.270-278
• /
• 1991

Carboxymethyl chitin(CM-chitin) was prepared by the reaction of alkali chitin with monochloroacetic acid in isopropyl alcohol. According to the pH variation, the adsorptivity of this chelating polymer to the alkali-earth metal ions such as $Ca^{2+},\;Mg^{2+}$, $Sr^{2+}$, $Ba^{2+}$ ions was determined by batch method. The adsorption tendency of this chelating polymer to most metal ions was increased with the increase of pH. The highest degree of adsorption was observed toward $Ca^{2+}$ ion among the alkali-earth metal ions. The selectivity adsorption property toward $Ca^{2+}$ ion was examined in the solution of $Ca^{2+}$ and $Mg^{2+}$ ions, and it was observed that CM-chitin showed excellent selectivity to $Ca^{2+}$ ion than $Mg^{2+}$ ion. $Mg^{2+}$ ion bound to CM-chitin molecule in the presence of $Ca^{2+}$ ion owing to low equilibrium constant. In the adsorption experiment of $Ca^{2+}$ and $Mg^{2+}$ ions to the CM-chitin under coexistence of $Na^+$ and $K^+$ ions, it observed that adsorptivity of only $Ca^{2+}$ ions was not affected by these monovalent cations.

• Journal of the Korea institute for structural maintenance and inspection
• /
• v.9 no.3
• /
• pp.120-128
• /
• 2005

In the construction industry, due to the cost rise of raw material for concrete, we have looked into recycling by-products which came from foundry. When using the Ground Granulated Blast-Furnace Slag(SG), it is good for enhancing the qualities of concrete such as reducing hydration heat, increasing fluidity, long-term strength and durability, but it has some problems : construction time is increased or the rotation rate of form is decreased due to low development of early strength. In this study, therefore, to enhance the early strength of SG mortar, we used some alkali activators(KOH, NaOH, $Na_2CO_3$, $Na_2SO_4$, water glass, $Ca(OH)_2$, alum. This paper deals with reacted products, setting time, heat evolution rate, flow and the strength development of SG cement mortar activated by alkali activators. From the results, if alkali activators were selected and added properly, SG is good for using as the materials of mortar and concrete.