• 한국전기전자재료학회논문지
• /
• 제22권5호
• /
• pp.397-404
• /
• 2009

Effects of ceramic filler types and dose on the low temperature sintering and dielectric properties of ceramic/$CaO-Al_2O_3-SiO_2$ (CAS) glass composites were investigated. All of the specimens were sintered at $850{\sim}900^{\circ}C$ for 2 h, which conditions are required by the low-temperature co-firing ceramic (LTCC) technology. Ceramic fillers of $CaCO_3$, $Al_2O_3$, $CaCO_3-Al_2O_3$ mixture, and $CaCO_3-Al_2O_3$ compound ($CaAl_2O_4$), respectively, were used. The addition of $Al_2O_3$ yielded the crystalline phase of alumina, which was associated with the inhibition of sintering, while, $CaCO_3$ resulted in no apparent crystalline phase but the swelling was significant. The additions of $CaCO_3-Al_2O_3$ mixture and $CaAl_2O_4$, respectively, yielded the crystalline phases of alumina and anorthite, and the sintering properties of both composites increased with the increase of filler addition and the sintering temperature. In addition, the $CaAl_2O_4$/CAS glass composite, sintered at $900^{\circ}C$, demonstrated good microwave dielectric properties. In overall, all the investigated fillers of 10 wt% addition, except $CaCO_3$, yielded reasonable sintering (relative density, over 93 %) and low dielectric constant (less than 5.5), demonstrating the feasibility of the investigated composites for the application of the LTCC substrate materials.

• 대한화학회지
• /
• 제53권6호
• /
• pp.635-639
• /
• 2009

여러 $CO_2-O_2$ 혼합기체에서 인도산 분말숯의 연소반응실험을 수행하였다. 샘플을 분쇄하여 58 마이크론보다 작은 채로 거르고 질소분위기에서 숯으로 만들었다. CPRI 방갈로에 있는 열분석기 (TGA-50)을 사용해 실험을 하였다. $CO_2-O_2$ 혼합기체는 몰비로 (80-20, 60-40, 40-60, 20-80)을 사용하였다. 활성화에너지 (E) 및 지수앞자리인자 (A)을 통합접근 및 수정된 Arrhenius식을 사용해 계산하였다.

• 한국연소학회:학술대회논문집
• /
• 한국연소학회 2001년도 제23회 KOSCO SYMPOSIUM 논문집
• /
• pp.90-96
• /
• 2001

Catalytic ignition of $H_2/O_2/CO_2$ mixtures over platinum catalyst is experimentally investigated by using microcalorimetry. For comparison, $N_2$ and Ar is also used as diluent gas. The gas mixture flows toward platinum foil heated by electric current at atmosphere pressure and ambient temperature. The ignition temperature range 350-445K according to the fuel ratio, dilution ratio and diluent gas. It increases as the fuel ratio and dilution ratio increase. $H_2/O_2$ mixture with $CO_2$ ignites at higher temperature than with other diluents by 30-50K. Several experimental evidences show the inhibition effects of $CO_2$ in $H_2-O_2$ heterogeneous reaction is considerable

• 한국추진공학회:학술대회논문집
• /
• 한국추진공학회 2008년도 제30회 춘계학술대회논문집
• /
• pp.244-247
• /
• 2008

ISL의 초폭굉 모드 램 가속기 실험을 바탕으로 하여 혼합기 강도를 조정하여 수치해석을 수행하였다 ($3.0CO_2$ 희석과 $2.5CO_2$ 희석). 계산결과 $3.0CO_2$ 희석의 경우는 초기 점화가 이루어지지 않아 탄체가 가속되지 않은 반면 $2.5CO_2$ 희석을 한 경우에는 점화가 이루어지고 높은 가속을 보임을 알 수 있었다. 이것은 탄체의 가속성능이 혼합기의 강도에 단순히 비례하지 않으며 점화가 가능한 최소한의 혼합기 강도 이상에서만 초폭굉 모드 램 가속기가 정상적으로 작동함을 알 수 있었다.

• 한국세라믹학회지
• /
• 제26권6호
• /
• pp.783-788
• /
• 1989

The reason of abnormal expansion in BaTiO3 synthesized in the equimolecular mixture and synthesized in Ba-rich region were investigated at the point of crystal and microstructure. The shrinkage and the expansion of the mixtures in BaCO3-TiO2 system were determined by the mass of BaCO3 added to the equimolecular BaCO3 and TiO2, Ba2TiO4 which was much formed and BaTi2O3 were important crystal in the reaction of Ba-rich region. Sintering phenomena of unreacted BaCO3 activity and the secondary phase caused to generate microcracks in the specimens.

• 한국분말재료학회지
• /
• 제12권5호
• /
• pp.336-344
• /
• 2005

In the present study, the focus is on the effect of cobalt oxide powder in the carbothermal reduction of the titanium-cobalt-oxygen based oxide powder by solid carbon for the optimizing synthesis process of ultra fine TiC/Co composite powder. The titanium-cobalt-oxygen based oxide powder was prepared by the combination of the spray drying and desalting processes using the titanium dioxide powder and cobalt nitrate as the raw materials. The titanium-cobalt-oxygen based oxide powder was mixed with carbon black, and then this mixture was carbothermally reduced under flowing argon atmosphere. Changes in the phase structure and thermal gravity of the mixture during carbothermal reduction were analysed using XRD and TGA. Titanium-cobalt-oxygen based oxide powder desalted at $600^{\circ}C$ had a mixture of $TiO_2\;and\;Co_{3}O_4$. And the one desalted at $800^{\circ}C$ had a mixture of $TiO_2\;and\;CoTiO_3$. In the case of the former powder, the reduction of cobalt oxide powder in the titanium-cobalt-oxygen based oxide powder occurred at lower temperature than the latter one. However, the carbothermal reduction of titanium dioxide powder in the titanium-cobalt-oxygen based oxide powder with a mixture of $TiO_2\;and\;Co_{3}O_4$ occurred at higher temperature than the one with a mixture of $TiO_2\;and\;CoTiO_3$. And also, the former powder showed a lower TiC formation ability than the latter one.

• 한국자기학회지
• /
• 제6권4호
• /
• pp.204-210
• /
• 1996

제철소의 부산물인 mill scale과 $Fe_{2}O_{3}$, 그리고 이들의 혼합물을 사용하여 M형 ferrite를 제조하였다. $Fe_{2}O_{3}$와 $BaCO_{3}$의 몰비를 5.2~6.0으로 변화시킨 혼합물의 하소 및 소결은 각각 $1150^{\circ}C,\;1250^{\circ}C$에서 2시간 행하였으며, 하소시에 mill scale 중의 불순물 성분인 $SiO_{2},\;Al_{2}O_{3},\;MgO,\;CaO\;및\;Na_{2}O$를 적당량 첨가한 시편으로 자기적 특성과 형상을 조사하였다. $Na_{2}O$를 첨가한 시편은 미반응의 $Fe_{2}O_{3}$와 중간 화합물인 $BaFe_{2}O_{4}$의 영향으로 자기적 특성이 감소하였으나, $BaO.5.6Fe_{2}O_{3}$ 조성에 $SiO_{2}$와 $Al_{2}O_{3}$의 첨가는 특성의 증진을 보였으며, 특히 $Al_{2}O_{3}$는 $M_{s}$ 값은 감소시켰으나 $_{B}H_{c}$ 값을 증가시켰다. BM($BaCo_{3}$와 mill scale의 혼합물)과 BFM($BaCO_{3},\;Fe_{2}O_{3}$, mill scale의 혼합물) 소결 시편의 ${(BH)}_{max}$는 각각 0.86, 1.04 MGOe였으며, $440^{\circ}C$ 부근에서 자기 특성의 변화를 보였다.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2000년도 하계학술대회 논문집
• /
• pp.452-455
• /
• 2000

Diamond thin films were synthesized on WC-Co substrate at various experimental parameters using 13.56MHz RF PACVD(radio frequency plasma-assisted chemical vapor deposition). In order to increase the nucleation density, the WC-Co substrate was polished with 3$\mu\textrm{m}$ diamond paste. And the WC-Co substrate was pretreated in HNO$_3$: H$_2$O = 1:1 and O$_2$ plasma. In H$_2$-CH$_4$gas mixture, the crystallinity of thin film increased with decreasing CH$_4$concentration at 800W discharge power and 20torr reaction pressure. In H$_2$-CH$_4$-O$_2$gas mixture, the crystallinity of thin film increased with increasing O$_2$concentration at 800W discharge power, 20torr reaction pressure and 4% CH$_4$concentration.

• 한국분말재료학회지
• /
• 제19권4호
• /
• pp.310-316
• /
• 2012

Nanocrystalline $BaTiO_3$ powder could be synthesized by solid-state reaction using the mixture which was prepared by a high energy milling process in a bead mill for $BaCO_3$ and nanocrystalline $TiO_2$ powders mixture. Effect of the milling time on the powder characteristic of the synthesized $BaTiO_3$ powder was investigated. Nanocrystalline $BaTiO_3$ with a particle size of 50 nm was obtained at $800^{\circ}C$. High tetragonal $BaTiO_3$ powder with a tetragonality(=c/a) of 1.009 and a specific surface area of $7.6m^2/g$ was acquired after heat-treatment at $950^{\circ}C$ for 2 h. High energy ball milling was effective in decreasing the reaction temperature and increasing the tetragonality.

• 대한전기학회논문지:전기물성ㆍ응용부문C
• /
• 제53권7호
• /
• pp.387-394
• /
• 2004

Diamond films were deposited on the cemented tungsten carbide WC-Co cutting insert substrates by using both microwave plasma chemical vapor deposition(MWPCVD) and radio frequency plasma chemical vapor deposition (RFPCVD) from $CH_4$$-H_2$$-O_2$ gas mixture. Scanning electron microscopy and X-ray diffraction techniques were used to investigate the microstructure and phase analysis of the materials and Raman spectrometry was used to characterize the quality of the diamond coating. Diamond films deposited using MWPCVD from $CH_4$$-H_2$$-O_2$ gas mixture show a dense, uniform, well faceted and polycrystalline morphology. The compressive stress in the diamond film was estimated to be (1.0∼3.6)$\pm$0.9 GPa. Diamond films which were deposited on the WC-Co cutting insert substrates by RFPCVD from $CH_4$$-H_2$$-O_2$ gas mixture show relatively good adhesion, very uniform, dense and polycrystalline morphology.