• Laser Solutions
• /
• v.6 no.2
• /
• pp.1-7
• /
• 2003

Defocused CO$_2$ laser beam irradiation strengthening of 60kgf/$\textrm{mm}^2$ grade steel sheet was investigated to obtain the tensile strength similar to that of fully penetrated one by the focused beam. The melted line width by the defocused beam was 3∼4 times larger compared to that of the focused beam. However, the increase of tensile strength with 1 line irradiation by the defocused beam was similar to that of 2~3 lines by the focused beam. The increase(37.6%) of bending strength with 1 line by the defocused beam was higher than the increase(12.9%) of tensile strength. Also, the effect of cooling gas to strengthening was observed.

• Transactions of the Korean Society of Automotive Engineers
• /
• v.10 no.5
• /
• pp.228-234
• /
• 2002

The CO$_2$ laser beam irradiation strengthening of 35kgf/mm$_2$ grade steel sheet is investigated to reduce the weight of bumper beam. The increase of tensile strength is dominated by the number of fully penetrated melting lines. The optimal laser irradiation pattern is obtained by 3-point bending test of hat-type specimens. Laser should be irradiated not only on the center specimen densely in the width direction, but also on the edge densely in the longitudinal direction. Local laser strengthening may be effective for the weight reduction of automobile bumper beam.

• Proceedings of the Optical Society of Korea Conference
• /
• 1990.02a
• /
• pp.45-48
• /
• 1990

CO2 laser beam was focused by a ZnSe lens onto the center of the occlusal surface f extracted lower molars. K-type thermocouple was contacted with the pulp chamber and the changes of temperature in the during and after the laser irradiation were measured as function of the power of laser beam, the time of laser irradiation and thickness of the sample. An empirical formula for temperature effect was derived from the measured data.

• Journal of the Korean Society of Manufacturing Process Engineers
• /
• v.10 no.1
• /
• pp.31-37
• /
• 2011

Recently, the technology of surface treatment is being more important which affects the material cost reduction and substitution to the expensive material. The material used for the mechanical processing should have not only high intensity, but also strength toughness, wear resistance and corrosion resistance. In order to increase the durability and have better quality of the parts using such kind of tooling material, various kinds of research of the surface hardening through many kinds of heat resources is being done and practically applied. In this study, the characteristics of hardening surface zone for high strength of the press die material through laser beam irradiation are researched. In this study, it is experimentally observed by the status of the surface morphology, tensile strength, the hardness distribution of the base metal and wear condition by the surface hardness pattern by the laser beam based on the process parameters of $CO_2$ laser by using SM45C and STD11 used for press tool. Through this research, the characteristics of surface hardened zone for high strength of the thin metal by laser beam irradiation is done.

• Laser Solutions
• /
• v.4 no.2
• /
• pp.21-28
• /
• 2001

The laser strengthening of 35kgf/㎟ and 60kgf/㎟ grade steel sheets is investigated by using CO$_2$ laser beam irradiation. The increase of tensile strength is dominated by the number of fully penetrated melting line. Also. the optimal laser input energy(hardness) and the number of melting line (melting width) are important variables for laser strengthening. Local strengthening by laser beam may be effective for the weight reduction of components where the tailored welded blank can not be applied.

• Restorative Dentistry and Endodontics
• /
• v.10 no.1
• /
• pp.43-53
• /
• 1984

The purpose of this study was to suggest the use of laser energy in the the field of operative dentistry without considerable pulpal damage and significant effects on the dental hard tissue, additionally to find out the methods which could control the temperature rise. The laser beam (CW $CO_2$ laser, output: 6W, beam diameter: 1.5mm) was focused on the center of the occlusal surface of extracted lower molars. A Ge lens (focal length 200mm) was used to focus the primary laser beam. In order to vary the total amount of the same irradiated energy, experimental subjects were devided into three groups: continuously irradiated group, intermittently irradiated group, and water-cooled group after continuous laser irradiation. Temperature changes in the pulp chamber after laser irradiation were measured and recorded by the digital thermometer and recorder. The following results were obtained: 1. Temperatures in the pulp chamber were raised up in the order of the continuously irradiated group, intermittently irradiated group, water-cooled group after continuous laser irradiation. 2. In the continuously irradiated group, the temperature was raised up $1.7^{\circ}C$, $3.8^{\circ}C$, $7.3^{\circ}C$, $17.2^{\circ}C$ after 2, 4, 8, 16 seconds of the irradiation of laser. In the intermittently irradiated group, the changes were $1.2^{\circ}C$, $3.4^{\circ}C$, $6.3^{\circ}C$, $11.1^{\circ}C$, respectively. In the water-cooled group after continuous laser irradiation, the changes were $0.0^{\circ}C$, $0.8^{\circ}C$, $1.6^{\circ}C$, $6.9^{\circ}C$, respectively. 3. The starting time of temperature rise in the pulp chamber had no connection with laser irradiation time.

• Journal of the Korean Society of Safety
• /
• v.16 no.2
• /
• pp.27-35
• /
• 2001

For the purpose of healing the degradation part, $CO_2$ laser beam was irradiated with different irradiation condition (porer, diameter, velocity and beam type) to find out optimum irradiation condition. The test series of hardness, residual stress measurement, and fatigue were carried out after the irradiation. Experimental results show that micro-hardness values on the surface of the irradiated specimens m approximately 2.5 times higher than those of un-irradiated ones. Fatigue tests show that the fatigue life was improved by the compressive residual stress after laser beam irradiation. However, some specimens with different conditions show the shorter fatigue life. It means that laser beam irradiation with optimum irradiation condition and optimum absorb energy, Q can improve the fatigue strength.

• Proceedings of the Korean Society of Laser Processing Conference
• /
• 2004.10a
• /
• pp.22-28
• /
• 2004

Pit and rim formation on the Acrylonitrile Butadiene Styrene(ABS) plastic surface was evaluated after it was irradiated by $CO_2$ and Nd:YAG laser beams. Our results show that thermal effect floor was well observed at the outer wall of pit with $CO_2$ laser irradiated while it was not the case with Nd:YAG laser irradiated. Also the volume and depth of pit formation increase proportionally with the energy intensities of two laser irradiations, but there are significant differences in the slope, width, and FWHM of the Pit formation with two types of laser irradiations. This result shows that $CO_2$ laser irradiation leads to better cooling contraction effect while Nd:YAG laser irradiation induces better recoil pressure effect during the interaction between ABS plastic and laser beam irradiation. The shape of the laser marking could vary significantly depending on the traveling path of molten plastic during injection molding of ABS plastic. Therefore, the selection of material and molding process can have a great impact on the performance of optical storage media.

• Transactions of the Korean Society of Mechanical Engineers B
• /
• v.23 no.11
• /
• pp.1379-1389
• /
• 1999

A new technique for control of size and shape of flame-made particles is Introduced. The characteristic sintering time can be controlled Independently of collision time by heating the particles with irradiation of laser because the sintering time strongly depends on temperature. A coflow oxy-hydrogen diffusion flame burner was used for $SiCl_4$ conversion to silica particle. Nanometer sized aggregates irradiated by a high power CW $CO_2$ laser beam were rapidly heated up to high temperatures and then were sintered to approach volume-equivalent spheres. The sphere collides much slower than the aggregate, which results in reduction of sizes of particles maintaining spherical shape. Light scattering of Ar ion laser and TEM observation using a local sampling device were used to confirm the above effects. When the $CO_2$ laser was irradiated at low position from the burner surface, particle generation due to gas absorption of laser beam occurred and thus scattering intensity increased with $CO_2$ laser power. At high irradiation position, scattering intensity decreased with $CO_2$ laser power and TEM image showed a clear mark of evaporation and recondensation of particles for high $CO_2$ laser power. When the laser was irradiated between the above two positions where small aggregates exist, average size of spherical particles obviously decreased to 58% of those without $CO_2$ laser irradiation with the spherical shape. Even for increased carrier gas flow rate by a factor of three, TEM photograph also revealed considerable reduction of particle size.

• Proceedings of the KIEE Conference
• /
• 1989.07a
• /
• pp.659-661
• /
• 1989

$CO_2$ laser beam was focused a ZnSe lens onto the center of the occlusal surface of extracted lower molars. K-type thermocouple was contacted with the pulp chamber and the changes of temperature in the pulp chamber during and after the laser irradiation were measured as function of the power of laser beam, the time of laser irradiation and thickness of the sample. An empirical formula for temperature effect was derived from the measured data.