CO2 감지용 La2O3-SnO2 계 후막형 소자를 제조하여 CO2가스에 대한 기초 감지 특성을 조사하였고, 감지 분말의 입자크기와 제조방법에 따른 감도 변화를 고찰하였다. 후막 소자는 40$0^{\circ}C$의 작동온도와 4wt.%의 La2O3가 첨가되 srjt에서 가장 좋은 감도를 나타내었고, 낮은 습도영역에서 우수한 감지 특성을 보였다. 분말 혼합법에 의해 제조된 소자에 있어서 La2O3와SnO2 분말의 입자가 미세할수록 우수한 감도를 나타내었고, La2O3의 입도가 SnO2의 입도 보다 감도에 더 큰 영향을 주었다. SnO2 후막 표면에 La 용액을 코팅하여 제조된 센서는 가장 우수한 CO2 감도특성을 보였다.

• Journal of the Korean Ceramic Society
• /
• v.20 no.2
• /
• pp.93-98
• /
• 1983

The sensitivity characteristics of $SnO_2$-based gas sensor prepared by sintering method have been studied at the presence of CO and Propane gas. Samples mixed with 1wt% $La_2O_3$ and 1wt% $PdCl_2$ showed highest sensitivity to CO and propane gas at 250$^{\circ}$C but the addition of $CeO_2$ did not enhance the sensitivity. For slectivity for gas a $SnO_2-La_2O_3$ (1wt%) sample without $PdCl_2$ showed better results. A sample sintered sintered at 115$0^{\circ}C$ has shown the optimum condition in sensitivity and electroding

• Journal of information and communication convergence engineering
• /
• v.4 no.1
• /
• pp.18-22
• /
• 2006

A small-sized gas identification system has been fabricated and characterized using an integrated gas sensor array and artificial neural-network. The sensor array consists of four thick-film oxide semiconductor gas sensors whose sensing layers are $In_{2}O_{3}-Sb_{2}O_{5}-Pd-doped\;SnO_2$ + Pd-coated layer, $La_{2}O_{5}-PdCl_{2}-doped\;SnO_2,\;WO_{3}-doped\;SnO_{2}$ + Pt-coated layer and $ThO_{2}-V_{2}O_{5}-PdCl_{2}\;doped\;SnO_{2}$. The small-sized gas identification instrument is composed of a GMS 81504 containing an internal ROM (4k bytes), a RAM (128 bytes) and four-channel AD converter as MPU, LEDs for displaying alarm conditions for three gases (liquefied petroleum gas: LPG, liquefied natural gas: LNG and carbon monoxide: CO) and interface circuits for them. The instrument has been used to identify alarm conditions for three gases among the real circumstances and the identification has been successfully demonstrated.

• Journal of the Korean Ceramic Society
• /
• v.23 no.3
• /
• pp.53-61
• /
• 1986

A gas sensor which has been made by wet process had fabricated by coating each of the mixture on alumina tube and firing at 85$0^{\circ}C$ for 3hrs. A gas concentration such $H_2$, CO, $C_3H_8$, $C_2H_2$ and $CH_4$ vs its detection voltage characteristics has been in-vestigated on $SnO_2-In_2O_3-MgO$ system doped with PdO, $La_2O_3$, $ThO_2$, NiO and $Nb_2O_5$ The optimum sensitivity composition for various gases were 90w/o $SnO_2$-9w/o $In_2O_3$-1w/o MgO for $H_2$, $C_2H_2$ CO and $C_3H_8$ and 95w/o $SnO_2$-4w/o $In_2O_3$-1w/o MgO for $CH_4$. The sample which has been made by wet process than dry process had predominated sensitivity for each gases and particle size of the sample coprecipitated with PH=9 was 0.1${\mu}{\textrm}{m}$ The $SnO_2$-In2_O_3-MgO$ system doped with 2w/o $Nb_2O_5$ and NiO was the most sensitive for $H_2$ and $C_2H_2$ gas. In $SnO_2$-In2_O_3-MgO$ system doped with $ThO_2$ the sensitivity of $H_2$ gas was decreased but CO gas was in-creased when dopant con was increased.